利用大分子单体技术合成接枝共聚物

大分子单体和小分子共单体共聚是合成接枝共聚物的重要途径之一。本文综述了大分子单体通过各种聚合方式(自由基共聚、离子型共聚、配位共聚、基团转移共聚和逐步共聚)和普通小分子单体的共聚反应,详细讨论了大分子单体和小分子单体的自由基共聚反应动力学,并简要介绍了接枝共聚物的应用背景。     

SYNTHESIS OF MESOPOROUS POLY(STYRENE-co-MALEIC ANHYDRIDE)/SILICA HYBRID MATERIALS VIA A NONSURFACTANT-TEMPLATED SOL-GEL PROCESS*

Mesoporous poly (styrene-co-maleic anhydride)/silica hybrid materials have been prepared. The synthesis wasachieved by the HCl-catalyzed sol-gel reactions of tetraethyl orthosilicate (TEOS) and styrene-maleic anhydride copolymerin the presence of 3-aminopropyl triethoxysilane (APTES) as a coupling agent and citric acid as a nonsurfactant template orpore-forming agent, followed by ethanol extraction. Characterization results from nitrogen sorption isotherms and powder X-ray diffraction indicate that polymer-modified mesoporous materials with large specific surface areas (e.g. 900 m~2/g) andpore volumes (e.g. 0.6 cm~3/g) could be prepared. As the citric acid concentration is increased, the specific surface areas, porevolumes and pore diameters of the hybrid materials increase.     

The evolution of morphology of ordered porous TiO2 films fabricated from sol-gel method assisted ZnO nanorod template

Ordered porous TiO₂ films, including TiO₂ nanotube arrays, are fabricated by a sol-gel dip-coating approach via ZnO nanorod templates obtained from aqueous solution approach. The results indicate that the morphologies of ordered porous TiO₂ films have been great affected by the sol-gel dip-coating cycle number. Open-ended TiO₂ nanotube arrays can be obtained in optimum dip-coating cycle numbers. The TiO₂ nanotubes with the inner diameter matching well with the diameters of ZnO nanorods, are well assembled and separate each other. When the cycle number is less than this optimum value, no intact porous TiO₂ film can be obtained. As the cycle number is larger than this optimum value, an ordered porous TiO₂ film with many throughout holes is formed. The evolutive mechanism of ordered porous TiO₂ films is proposed.     

NMR频率综合器的微机控制

为实现ＰＴＳ系列频率综合器的微机控制，设计了一种简单的控制电路。在微机的控制下，通过该电路与微机的并行通讯口，用Ｃ语言编写的控制程序可以很方便的控制频率综合器的输出频率。控制程序采用菜单操作，电路所需的＋５Ｖ电源由微机提供，整个控制系统简单实用，值得推广。     

三溴偶氮胂催化光度法测定痕量铁

本文研究了硫酸介质中痕量 Fe(Ⅲ)催化加速抗坏血酸、溴酸钾和三溴偶氮胂之间的褪色反应及动力学条件,建立了动力学光度法测定痕量Fe(Ⅲ)的新方法.方法灵敏度为1.82×10~(-12)g·ml~(-1).测定范围为Fe(Ⅲ)0～30ng/25ml.已用于人发和食品中痕量铁的测定.结果满意.     

EFFECT OF MOLECULAR WEIGHT OF PDMS ON MORPHOLOGY AND MECHANICAL PROPERTIES OF PP/PDMS BLENDS

 A series of polydimethylsiloxane (PDMS) with varied molecular weights (Mw = 3  106, 1  106 and 0.5  106) were melt blended with PP to investigate the effect of PDMS molecular weight (MW) on the morphology and mechanical properties of PP/PDMS blends. Scanning electron microscopic (SEM) examination showed that the size of PDMS domains was dependent on the MW of PDMS. It was found that the lower the value of PDMS MW, the better dispersion of the PDMS domains in the PP matrix. Tensile and Izod impact tests revealed that the addition of PDMS with lower MW would lead to a more significant increase in impact strength of the blends compared with the blends with higher MW ones, while the influence of the molecular weight on tensile strengths of the blends was relatively small in the MW range studied. Differential scanning calorimetry (DSC) results also showed that the crystallization temperature of PP was increased with decreasing PDMS MW, indicating a better nucleation capability of lower MW of PDMS. Melting flow rate (MFR) measurements indicated that the processibility of PP could be enhanced by adding PDMS, and again the lower MW PDMS resulted in better data. Our work demonstrates that not only the processibility but also the mechanical properties of PP could be enhanced to a more significant degree by using low MW PDMS than the higher ones.     

水热合成CdS纳米晶体的形貌控制研究

研究了水热合成CdS纳米晶体形貌的化学控制，选择不同的络合试剂为模板,研究其对水热合成CdS纳米晶体形貌的影响.实验发现若以络合试剂乙二胺、甲胺为模板时，产品CdS晶体的形貌分别为（20～30） nm×（200～600） nm和（40～50） nm×（200～600） nm尺寸的纳米棒;而以络合试剂吡啶、 氨为模板时，产品CdS晶体的形貌分别为平均尺寸约30 nm和20 nm的纳米颗粒.用XRD、TEM、XPS、PL和Raman光谱等技术对所得CdS纳米棒进行了表征.同时对水热合成CdS纳米晶体形貌的模板控制机制进行了探讨，提出了一种水热合成CdS纳米棒的络合物结构诱导生长机理.     

甲胺化反应催化剂稀土改性丝光沸石的研究

研究了稀土改性丝光沸石催化剂对常压固定床上甲胺化反应的活性及选择性的影响，结果表明，以钇改性丝光沸石催化剂的活性及对二甲胺的选择性最佳。催化剂表征结果表明，稀土改性丝光沸石主要是引起丝光沸石中Ｂ酸中心发生变化，而对丝光沸石的晶体结构及表面硅铝原子比基本不产生影响。稀土改性能增强催化剂的热稳定性，延长催化剂的寿命。     

Microcalorimetric investigation of the growth of the <Emphasis Type="Italic">Escherichia coli</Emphasis> DH5α in different antibiotics

The effects of Amoxicillin Sodium and Cefuroxime Sodium on the growth of E. coli DH5α were investigated by microcalorimetry. The metabolic power-time curves of E. coli DH5α growth were determined by using a TAM air isothermal microcalorimeter at 37°C. By evaluation of the obtained parameters, such as growth rate constants (k), inhibitory ratio (I), the maximum heat power (P _m) and the time of the maximum heat power (t _m), one found that the inhibitory activity of Amoxicillin Sodium vs. E. coli DH5α is enhanced with the increasing of the Amoxicillin Sodium concentration, and the Cefuroxime Sodium has a stimulatory effect on the E. coli DH5α growth when the concentration is about 1 μg mL⁻¹. The IC₅₀ for the Amoxicillin Sodium and the Cefuroxime Sodium are 1.6 and 2.0 μg mL⁻¹, respectively, it implicates that the E. coli DH5α is more sensitive to Amoxicillin Sodium than Cefuroxime Sodium.