Purcell Effect and Nonlinear Behavior of the Emission in a Periodic Structure Composed of InAs Monolayers Embedded in a GaAs Matrix

Enhancement of spontaneous emission in a resonant Bragg quantum well (QW) structure with 60 periods of triple InAs monolayers embedded in a GaAs matrix is studied experimentally and theoretically. From measurements of the time‐resolved photoluminescence, besides the QW exciton at 1.47 eV, a specific super‐radiant (SR) emission demonstrating nonlinear properties is found. The SR mode shows a near‐quadratic dependence of intensity on excitation power, while its energy position follows the Bragg condition. It is revealed that the SR mode shows a peculiar non‐monotonic dependence of intensity on direction, with a maximum observed at approximately 40°. The enhancement in the SR emission at a specific direction is correlated well with suggested theoretical consideration of the modal Purcell factor for periodic quantum well structures.     

Approaches to improving critical current density of YBCO superconducting thick films deposited by electrophoresis

The irreversibility field (Hirr) of Y-based superconductor is much higher than that of Bi-based superconductor. Y-based superconductor is capable of maintaining stable electrical currents in high magnetic field and electric field, so it is a better suited mate-rial for electric-current applications. Commonly, the Y-based tapes comprise a YBCO thick film deposited on a flexible substrate, typically with an intermediate buffer layer, and an overcoat of noble metal. In this process, the interm…     

用电泳技术制备YBCO高温超导厚膜

介绍了电泳技术制备YBCO高温超导厚膜的实验方法和YBCO高温超导厚膜的电学性质测量 ,讨论了在学生小型科研实验或设计实验中开展此实验的学时安排、注意事项和实验内容的扩展 .     

辽河冷家油田特稠油降粘剂LJVR-1及其性能评价

采用荧光法测定了辽河冷家油田冷47-556井特稠油乳化HLB值,然后以混合型表面活性剂、非离子型表面活性剂为主剂,快速渗透剂为辅剂按一定比例制备了水基降粘剂LJVR-1.实验结果表明,该降粘剂具有良好的乳化降粘性能,开采后易于破乳脱水,是一种较为理想的特稠油降粘剂.     

Exact Solution of a Test Particle in Presence of Thick Domain Walls

We have obtained the exact solution of the equations of motion of a test particle near a thick domain walls. From the solution it has been shown that the domain walls have repulsive gravitational fields.     

MEASUREMENTS OF Fe AND Cu K-Shell IONIZATION CROSS SECTIONS BY SLOW ELECTRON IMPACT

ＭＥＡＳＵＲＥＭＥＮＴＳＯＦＦｅＡＮＤＣｕＫ－ＳｈｅｌＩＯＮＩＺＡＴＩＯＮＣＲＯＳＳＳＥＣＴＩＯＮＳＢＹＳＬＯＷＥＬＥＣＴＲＯＮＩＭＰＡＣＴＬｉＴａｉｈｕａＡｎＺｈｕＬｕｏＺｈｅｎｇｍｉｎｇＣｅｎｔｅｒｆｏｒＲａｄｉａｔｉｏｎＰｈｙｓｉｃｓ，Ｉｎｓ...     

大口径厚液膜毛细管柱的制备

制备出了内径从0.46～0.74mm、液膜厚度从0.9～5.6μm的SE-54大口径厚液膜玻璃毛细管柱,并对它们的性能进行了评价。对低沸点的C_1-C_4烃进行了初步分离。     

Thick Silicate Film by an Interfacial Polymerization

A thick silica gel film, corresponding to the glass film of 10–20 micron in thickness, has been formed at the interface between two immiscible liquids, hexane and water, using E-40, a partially polymerized silicon alkoxide, as the precursor. The film formation was possible using both acid- and base-catalyzed water, but was greatly dependent on the type of catalyst. Only the trace of a film was observed for the system catalyzed with a strong electrolyte such as HCl, HNO₃ or NaOH, while a gel film, corresponding to the glass film of several to 10 micron in thickness was formed with a weak electrolyte such as ammonia, organic acid like acetic acid, citric acid, etc., of similar pH value. The direct introduction of organic base catalyst like triethylamine in hexane was much more effective than the use of ammonia water, suggesting that the polymerization of E-40 to form a gel film takes place in the organic phase, where water molecules, as well as undissociated ammonia or organic acids, can diffuse in.     

The preparation of thick-film glass capillary columns

A detailed method for the routine preparation of glass capillary columns is presented. The method consists of coating a glass tube with quartz powder prior to pulling the tube into a capillary. The inner surface of the capillary consists of an even distribution of quartz particles fused to the walls. This surface has been found readily deactivated by standard procedures and ideal for the preparation of thick-film glass capillary columns. The method has been thoroughly tested in two independent laboratories to ensure that the procedures described are reproducible.     

H2S-sensing properties of SnO2 produced by ball milling and different chemical reactions

In this work, the mechanochemical synthesis of a moderately agglomerated tin oxide (SnO₂) powders and the subsequent preparation of semiconductor gas sensors as prototypes, were studied. Tin (II) chloride (SnCl₂) powder was milled with calcium hydroxide (Ca(OH)₂) and potassium carbonate, (K₂CO₃) powder, respectively, in a ball mill at room temperature and in an air atmosphere. Heat treatment of milled mixtures at 400 °C resulted in the formation of a tetragonal phase, confirmed by X-ray diffraction (XRD). During milling in the presence of water, a high number of hydroxide (OH) groups are formed at the surface. When SnCl₂ was milled with K₂CO₃, no water was produced and the Fourier-transform infrared spectrum (FT-IR) of the powder has no surface hydroxyl deformations. On exposure to hydrogen sulfide (H₂S) gas, the particles, prepared from anhydrous powder, have higher sensitivity than these, prepared from hydrated powder. The SnO₂ thick film, prepared from anhydrous powder may be successfully applied to a H₂S gas sensor.