环氧化合物以三异丁基铝-水-双(2,4-戊二酮基)锌水合物为催化剂的共聚

本文以i-Bu_3Al-H_2O-Zn(acac)_2为催化剂,对环氧氯丙烷、环氧乙烷和环氧丙烷的三元共聚进行了研究。结果表明,这种三元共聚橡胶具有良好的性能,其耐寒性可与丁腈-18相媲美,耐油性比丁腈-18为佳,而耐臭氧老化性是丁腈橡胶所不能比拟的。     

稀土化合物处理高耐磨炭黑填充粉末丁腈橡胶

以经稀土化合物处理的高耐磨炭黑和丁腈胶乳为原料,以凝聚共沉法制备粉末丁腈橡胶.研究了分散剂和稀土化合物对粉末胶颗粒粒径及其硫化胶性能的影响.结果表明,粉末胶颗粒粒径随分散剂用量的增加而减小,随La3+用量的增加而增大.La3+改善了硫化胶的性能,特别是扯断伸长率和拉伸强度.进一步分析得出,硫化胶性能得以改善的根本原因是La3+改善了炭黑粒子在橡胶基体中的分散均匀性及其与橡胶基体的黏结牢固性.     

3-氧代-4-（2,4,5-三氟苯基）丁腈的合成

以2,4,5-三氟苯乙酸为起始原料,经氯化和酰化反应得2-氰基-3-羟基-4-（2,4,5-三氟苯基）丁-2-烯酸乙酯（2）; 2经水解脱羧合成了3-氧代-4-（2,4,5-三氟苯基）丁腈,总收率61.5%,纯度97.6%,其结构经¹H NMR和MS（ESI）确证。     

RP-3航空煤油替代燃料及其化学反应动力学模型

本文提出了40%(摩尔分数, 下同)正癸烷、42%正十二烷、13%乙基环己烷和5%对二甲苯的四组分RP-3 航空煤油替代燃料模型, 并通过实验充分验证了替代燃料模型与实际RP-3 航空煤油在理化特性上的相似性. 采用对冲火焰实验台架, 测量了RP-3航空煤油以及四组分替代燃料的层流火焰传播速度. 对比结果表明本文提出的替代燃料能够准确描述实际RP-3航空煤油的燃烧速率. 进一步发展了包含168组分、1089反应的半详细反应动力学模型, 验证结果表明本文机理能够准确预测RP-3航空煤油着火延迟时间和火焰传播速度.     

丁烯氟虫腈缓释微胶囊的制备及其性能

以丁烯氟虫腈为囊芯化合物,带有相反电性的壳聚糖和海藻酸钠为囊壁材料,采用层层自组装技术制备了丁烯氟虫腈微胶囊,通过流点法筛选出十二烷基苯磺酸钠为丁烯氟虫腈的分散稳定剂。 对制备的微胶囊进行了表征,系统研究了丁烯氟虫腈微胶囊的载药量、包封率、缓释性能和抗光解性能随着组装层数增加的变化规律。 结果表明,组装层数为6~8层的丁烯氟虫腈微胶囊的包封率达到80%以上,达最高释放量所需要的时间为60 h,光解率降到20%以下,综合效果最好。     

烯烃类衍生物的碘三氟甲基化反应

在ZnI2为催化剂,Togni试剂为三氟甲基化试剂,CHCl3为溶剂的条件下,以中等收率(30%~65%)实现烯烃的碘三氟甲基化反应,合成了一系列既含碘又含三氟甲基的酯类、酮类、酰胺类、腈类等化合物,其结构经1H NMR,13C NMR,19F NMR,IR,MS和HR-MS表征。其中4,4,4-三氟-2-碘丁酰胺,4,4,4-三氟-2-碘-N,N-二甲基丁酰胺和6,6,6-三氟-4-碘-3-己酮为新化合物。     

Pingba RP-3喷气燃料中有色组分的鉴定及其特性研究

用中性氧化铝吸附、无水乙酸脱附的方法，对储存中变色的Pingba RP-3喷气燃料中的有色组分进行分离制备。应用有机元素分析、红外光谱、色质联用和裂解色质联用等分析法对富集有色组分的吸附胶质进行了分析鉴定，对燃料的储存特性和有色组分的化学特性进行了考察。结果表明，Pingba RP-3喷气燃料中的有色组分全部集中在吸附胶质中，吸附胶质以含氧化合物为主，其主要成分为烷基苯酚类（及其多聚体）化合物，含氮化合物质量分数极少，未检出含硫化合物。Pingba RP-3在储存中颜色变深的主要原因是胶质中的烷基苯酚类化合物氧化和缩聚。储存过程中喷气燃料的吸附胶质和颜色增加显著，与燃料在一定条件下的氧化反应有关。     

分散固相萃取-超高效液相色谱-串联质谱法测定禽蛋中氟虫腈及其代谢产物

建立了分散固相萃取-超高效液相色谱-串联质谱检测禽蛋中氟虫腈及其代谢产物氟甲腈、氟虫腈硫醚和氟虫腈砜的方法。样品用含1%(体积分数)乙酸的乙腈提取后,加无水硫酸钠、十八烷基键合硅胶(C18-N)及氨基-丙基乙二胺(NH2-PSA)3种净化剂,旋涡振荡,对样品进行净化。以Shim-pack GIST C18色谱柱(50 mm×2.1 mm,2μm)进行分离,以甲醇和1 mmol/L乙酸铵水溶液为流动相进行梯度洗脱,在电喷雾离子源负离子模式和多反应检测(MRM)模式下进行定性定量分析。考察了净化剂中无水硫酸钠、C18-N和NH2-PSA的用量对加标回收率的影响,优化了实验条件。结果表明:4种化合物在0.4~100μg/L范围内线性关系良好,相关系数r2≥0.998 9;回收率为95.09%~103.26%;定量限为0.2μg/kg。该方法前处理简单,回收率高,重复性好,可作为禽蛋中氟虫腈及其代谢产物的有效检测方法。     

欧盟变更杀虫剂最大残留标准

近日,欧盟发出通报(通报号为G/SPS/N/EU/42),欧委会健康与消费者总司规定了杀虫剂2,4-D、氟丁酰草胺(Beflubutamid)、环丙酰草胺(Cyclanilide)、烯唑醇(Diniconazole)、氟虫腈(Fipronil)、双氟磺草胺(Florasulam)、异丙甲草胺(Metolachlor)及弥拜菌素(Milbemectin)的拟定最大残留标准(MRLs)。在某些产品内这些物质的最大残留限量有所变更。     

有机氟键合相高效液相色谱填料的研究 Ⅳ.四氟乙烯五聚体丙氧基键合相的制备、性能及应用

为了发展对极性甾族化合物及含氟化合物有较好分离的填料,我们曾利用不同的氟硅试剂制备了氟酰胺和氟烃键合相填料,最近利用四氟乙烯五聚体丙氧基三甲氧基硅烷(1)与硅胶反应,又制备了一种四氟乙烯五聚体丙氧基键合相填料(4F-OYWG).用于HPLC,发现此键合相亦具有与氟酰胺键合相填料相似的性能,也能加快分析速度,改进峰形拖尾.用其分析了二十个甾族化合物,并与硅胶柱及氟酰胺、氟烃柱进行了比较,其极性小于硅胶及氟酰胺柱,但大于氟烃柱.在分析含有不同链长烃基取代的联苯腈及带有不同取代基的苯胺时,均取得满意结果.故此填料可作为用于HPLC上的一种弱极性的填料.     

Electron beam modification and crosslinking: Influence of nitrile and carboxyl contents and level of unsaturation on structure and properties of nitrile rubber

The structural changes of nitrile rubber with varying nitrile contents, hydrogenated nitrile rubber and carboxylated nitrile rubber in the presence and absence of a polyfunctional monomer, namely trimethylolpropane triacrylate, at different doses of electron beam irradiation, were investigated with the help of FTIR spectroscopy (in the attenuated total reflectance mode), dynamic mechanical thermal analysis and sol–gel analysis. Solid-state NMR with gated high power decoupling technique was used to understand the mechanism of crosslinking of the irradiated samples. The allylic radicals generated in the butadiene chains react to form intermolecular crosslinkages. There was a significant decrease in the concentration of olefinic groups for the nitrile rubber on irradiation. This was also affirmed by the increase in the carbon resonances due to C–C linkages from the NMR technique, indicating more crosslinkages. The spectroscopic crosslink densities were determined and the results were compared with the swelling measurements. The variation in the crosslink clustering for rubbers with different acrylonitrile contents was explained using the NMR technique. The increase in crosslinking was also revealed by the increase in the percent gel content and dynamic storage moduli with radiation doses. The lifetime of spurs formed and the critical dose, an important criterion for overlapping of spurs, were determined for both the grafted and the ungrafted nitrile rubbers of different grades and compared using a mathematical model. The ratio of scissioning to crosslinking for nitrile rubber was determined using Charlesby–Pinner equation. The mechanical properties had also been studied for both the modified and the unmodified systems.     

Surface Modification of Nitrile Rubber by Plasma Polymerization

Radio frequency plasma polymerization of vinylidene fluoride was used to modify the surface properties of nitrile rubber. The chemistry and frictional properties of the plasma films were characterized. FTIR transmission spectra and EDX analysis of plasma polymer films deposited on NaCl windows showed that the degree of fluorination of the plasma polymers increased as plasma power was increased from 25 to 50 W, and then decreased monotonically at higher powers. An estimation of the actual F/C ratio from EDX data indicated that the plasma polymer films contained approximately one fluorine atom for every 2–5 carbon atoms. Sliding friction tests on a Delrin countersurface showed that the coefficient of friction of the plasma treated rubbers was lower than untreated rubber, but slighly higher than rubber coated with silicone oil. Repetitive sliding friction testing showed that silicone oil treated samples had a longer lubricating lifetime than plasma treated samples. However, cyclic friction tests conducted with nitrile rubber o-rings yielded similar frictional behavior and lubricating lifetimes for silicone oil and plasma treatments. There was no correlation between chemical composition and the frictional and wear properties of the plasma films. Environmental scanning electron micrographs showed that the plasma films were brittle and tended to crack and flake off during wear testing.     

Synergistic effect between POSS and fumed silica on thermal stabilities and mechanical properties of room temperature vulcanized (RTV) silicone rubbers

In this paper, both divinyl-hexa[(trimethoxysilyl)ethyl]-POSS (DVPS) and fumed silica were firstly introduced into polydimethylsiloxane (PDMS) system using as the cross-linker and the reinforcing filler respectively. And a series of novel RTV silicone rubbers synergistically enhanced by DVPS and fumed silica were prepared. The cross-linked networks in the novel RTV silicone rubbers have been studied by attenuated total reflection infrared spectroscopy, and the dispersions of POSS and fumed silica in these novel RTV silicone rubbers have been observed by means of scanning electron microscope (SEM). And thermal stabilities, thermo-oxidative stabilities and mechanical properties of these novel RTV silicone rubbers were studied by means of thermal gravimetric analysis and universal tensile testing machine, respectively. From the obtained results, it was found that synergistic effect between POSS-rich areas and fumed silica on thermal stability and mechanical property of RTV silicone rubber indeed existed. And the experimental results also exhibited that the thermal stabilities and mechanical properties of the novel RTV silicone rubbers were far better than those of the reference materials (DVPR and MTFR). The striking enhancements in thermal properties and improvements on mechanical properties of novel RTV silicone rubbers were likely attributed to the synergistic effect between POSS-rich domains and fumed silica. Meanwhile, it was found that the mechanical properties of RTV silicone rubbers prepared with a given amount of POSS cross-linker were enhanced with the increment of the loading amount of fumed silica.     

Hysteresis loss as a measure of metal–rubber adhesion

As in the case of reinforcing filler-induced increase in hysteresis in rubbers, placement of aluminum (A1) foil to the surface of a rubber blend of epichlorohydrin rubber and carboxylated nitrile base induces increased hysteresis of the rubber due to adhesion between Al and the rubber blend. Changes in hysteresis loss due to Al foil can be correlated with the peel strength of Al-rubber-Al joints. © 1995 John Wiley & Sons, Inc.     

硅橡胶/氟橡胶并用胶的制备及力学性能

硅橡胶和氟橡胶作为国防、航天等重要领域的耐热材料一直被人们青睐,但其有着各自地优缺点且价格昂贵,本文尝试将这两种橡胶制成并用胶以解决氟橡胶不耐低温和加工性差的问题,以期增大其使用温度范围。采用机械共混法制备硅橡胶/氟橡胶并用胶,研究了硅橡胶和氟橡胶的混炼工艺、并用比、共硫化体系和硫化条件对并用胶力学性能的影响。结果表明,当硅橡胶/氟橡胶的质量比为10∶90,共硫化体系为3~#硫化剂/过氧化二异丙苯(DCP),一段硫化温度为170℃、硫化压力为10MPa、硫化时间为30min,二段硫化温度为200℃、硫化时间为6h时,并用胶的力学性能达到最好。     

Theoretical investigation of polymer molecular structure influence on dielectric properties and mechanical properties

Triboelectric nanogenerator (TENG) technologies have explosive development in the field of energy harvesting and self-powered sensing. As the key element of triboelectric devices, dielectric polymers have obtained much attention in recent years. The dielectric properties of polymer determine the output performance of TENG. In this paper, we take silicone rubber as an example of dielectric polymers, to study the properties of molecular structure influence on the dielectric properties and mechanical properties by the molecular dynamics simulation method. The free volume fraction, dielectric constant, and mechanical properties of silicone rubbers with different branch chains were calculated. The dielectric constant is highly related to the free volume distribution and the dipole moments of silicone rubbers with different amounts of branch chains. For fewer branch chains silicone rubber, the free volume distribution contributes most to the dielectric constant; for more branch chains silicone rubber, the dipole moment dominates the dielectric constant. Therefore, the silicone rubber ratio has a great influence on the dielectric constant of silicone rubber. With the increase of temperature, the dielectric constant of 2-chain silicone rubber increases at first and then decreases, and the maximum value is obtained near 300 K. Therefore, it is necessary to control the temperature when silicone rubber is used as a dielectric material. This work can be a guide for improving the dielectric properties of silicone rubber, and it provides a new approach to the optimal design of high-performance triboelectric nanogenerators.     

Dynamic bulk modulus of various elastomers

The dynamic bulk modulus of elasticity has been measured for 14 different rubbery elastomers: three natural rubbers, five neoprenes, three polyurethanes, and one each of butyl, nitrile, and butadiene types. The measurements ranged in temperature from ?10 to +40°C, at frequencies from 5 to 3000 Hz, but mostly in the range 100–1000 Hz, at 2.5 MPa pressure. Values of the real (storage) part of the modulus fell within 35% of the mean value of 2.9 GPa for all elastomers, whereas loss moduli were a few percent of the storage moduli. Master curves were obtained for two neoprenes, a polyurethane, and a butyl rubber. These were fitted by hyperbolic functions with four adjustable parameters. Effects of room-temperature aging in artificial sea water were also studied. Aging versus time profiles fell into two distinct forms. Natural rubbers were least stable, neoprenes were intermediate, and urethanes proved most stable in bulk modulus.     

New membrane materials for potassium-selective ion-sensitive field-effect transistors

Several polymeric materials were studied as membrane materials for potassium-selective ion-sensitive field-effect transistors (ISFETs) to overcome the problems related with the use of conventional plasticized poly(vinyl chloride) membranes casted on ISFET gate surfaces. Several acrylate materials, such as ACE, Epocryl and derivatives, showed no reproducible results. Three room-temperature vulcanizing (RTV)-type silicone rubbers were tested. The addition-type RTV-2 silicone rubber was not suitable as a membrane material, but the condensation-type RTV-1 and especially the RTV-2 silicone rubber showed good results. ISFETs with a Silopren membrane showed a durability of at least 2 months.     

A thermal oxidative degradation study of triallyl isocyanurate crosslinking moiety in fluorinated rubber by two-dimensional infrared correlation spectroscopy

Thermal degradation of crosslinking moiety in fluorinated rubbers was studied with a new method using spatial-dependent infrared (IR) microscopy and two-dimensional (2D) IR correlation spectroscopy. Upon heating the fluorinated rubber, initially the amount of crosslinker decreased followed by generating another chemical species with carbonyl substituent with IR absorption at around 1730 cm^–1, implying generation of carboxylic acids forming intermolecular hydrogen bonding. Furthermore, projection 2D IR correlation analysis revealed that another chemical species with IR absorption at around 1755 cm^–1 generates, indicating that further degradation progresses upon heating and intermolecular hydrogen bonding were broken. As a result, the multi-step degradation process of the crosslinker in the fluorinated rubber could be detected by combination of spatial-dependent IR microscopy and projection 2D IR correlation spectroscopy.