2-(4-甲氧基苯基)-4,6-双(三氯甲基)-S-三嗪光引发剂的合成及其光聚合动力学性能研究

以对甲氧基苯甲腈和三氯乙腈为原料合成了光引发剂2-(4-甲氧基苯基)-4,6-双(三氯甲基)-S-三嗪(MBTT),通过傅里叶红外光谱仪、核磁共振仪和紫外吸收光谱对所合成的产物结构进行了表征.并利用实时红外(RT-IR)对该引发剂进行了光聚合反应动力学研究,考察了单体、引发剂浓度和光强对引发速率及单体转化率的影响.结果表明,MBTT是一种高效的紫外光引发剂,在引发剂用量为0.1%时光聚合的单体转化率就能达到90%;随着光强的增大,单体的双键转化率和最大反应速率都增大,诱导期缩短;双丙烯酸酯类单体的双键转化率比三丙烯酸酯类单体的双键转化率要高.     

2,2′-二邻甲氧基苯基-4,4′,5,5′-四苯基-1,2′-二咪唑复合光引发体系的光聚合动力学研究

本文研究了对2,2′-二邻甲氧基苯基-4,4′,5,5′-四苯基-1,2′-二咪唑(BMOIM)复合光引发体系引发聚合动力学过程.采用紫外光谱仪对引发剂、供氢体、增感剂在紫外区的吸收谱图进行了表征.利用实时红外光谱仪对复合光引发体系引发聚合动力学过程进行实时监测,考察了不同光强、引发剂浓度以及不同官能度单体对反应速率及最终双键转化率的影响.结果表明,在引发剂浓度为0.6%(质量分数)时,20s内双键转换率达到96%,随着引发剂浓度的提高,聚合速率增大.聚合速率以及最终双键转化率随着光强增大而增大;双官能团单体的最终双键转化率比三官能团单体的最终双键转化率要高.     

基于α-羟烷基苯酮(HAPK)可聚合大分子光引发剂的合成及其引发三丙二醇双丙烯酸酯(TPGDA)光聚合动力学的研究

以α-羟烷基苯酮(HAPK)、甲苯-2,4-二异氰酸酯(TDI)、聚乙二醇600(PEG600)和丙烯酸-β-羟乙酯(HEA)为原料,通过3步反应,合成了一种可聚合大分子光引发剂:HAPK-TDI-PEG600-TDI-HEA(HTPTH).用IR对反应过程进行了监测.通过Photo-DSC研究了HTPTH引发三丙二醇双丙烯酸酯(TPG-DA)光聚合动力学,考察了光强、引发剂浓度对TPGDA光聚合动力学的影响.结果表明,随着引发剂浓度和光强的增大,最大反应速率对应的转化率、单体最终转化率、最大反应速率都增大,达到最大反应速率所需的时间减小.     

含氟光引发剂的合成及其性能研究

以2-羟基-4'-(2-羟乙氧基)-2-甲基苯丙酮(Irgacure 2959)和全氟辛酰氯(PFOC)为原料合成了光引发剂全氟辛酸-2-[4-(2-羟基-2-甲基丙酰)苯氧基]乙酯(2959-F),利用红外光谱(FT-IR)和核磁共振(¹⁹F NMR)对2959-F进行了结构表征;通过紫外吸收光谱测定了2959-F的紫外吸收谱;通过实时红外光谱(RT-IR)对合成的含氟光引发剂进行了光聚合反应动力学研究,考察了光强和引发剂浓度对单体的双键转化率和聚合速率影响,并研究了光引发剂2959-F的抗氧阻聚性能.结果表明:随着光强的增大,单体的双键转化率和聚合速率增加;在一定范围内,引发剂的浓度越高,双键转化率越高,聚合速率越快.2959-F具有较高的双键转化率和较快的聚合速率,并且具有较好的抗氧阻聚性.     

多官能单体TMPTA在LDPE表面光接枝聚合研究

以二苯甲酮(BP)为光引发剂、丙酮和水的混合物为溶剂,研究了室温下多官能单体三羟甲基丙烷三丙烯酸酯(TMPTA)在低密度聚乙烯(LDPE)表面的光接枝聚合(λ>300nm).研究表明,多官能单体的接枝速率较快,接枝聚合易产生交联结构,聚合后仍残留双键;延长聚合反应时间、增加单体用量有利于单体接枝转化率的提高;随引发剂用量增加,单体接枝转化率出现一峰值;在研究范围内,混合溶剂中水含量增加可使单体接枝转化率明显提高.扫描电镜观察到接枝膜表面形成了许多小球,表面粗糙度增加,疏水性提高.     

乙烯基单体光聚合动力学与光固化流变行为

概述了光引发体系、光照强度、单体平均官能度、液晶含量、反应温度、助剂等对乙烯基单体/液晶混合物光聚合动力学及光固化流变行为的影响.在染料和胺组成的二元Ⅱ型(夺氢型)光引发体系中,引入适当的第三组分能显著提高反应速率和转化率;增加光照强度和升高温度也能显著提高反应速率和转化率.随着单体平均官能度的增加,体系的反应速率和转化率呈现先增加后降低的趋势.对于I型(裂解型)光引发剂,液晶含量增加,单体反应速率降低,但转化率基本不变;但对于Ⅱ型光引发剂,液晶含量增加能大幅提高单体反应速率和转化率.加入使体系黏度降低的助剂也能提高体系的反应速率和转化率.在体系相同、温度固定的条件下,反应速率越高,凝胶化时间越短;相同体系,温度升高,凝胶化时间提前;相同温度下,单体官能度愈高,体系凝胶时间亦愈短.     

可聚合二苯甲酮类光引发剂的合成及其光聚合性能研究

以4-(2,3-环氧丙氧基)二苯甲酮(EBP)和丙烯酸为原料,通过开环反应合成了含有不饱和双键的可聚合光引发剂4-(丙烯酸-2-羟基丙酯-3-氧基)二苯甲酮(AEBP).采用红外光谱(FT-IR)、核磁共振氢谱(¹HNMR)对其结构进行表征,利用紫外吸收光谱对AEBP的紫外吸收波长进行表征,通过实时红外(RT-IR)研究了AEBP引发丙烯酸酯单体的光聚合动力学.采用萃取法对比了BP与AEBP引发固化体系后的迁移性.结果表明,随AEBP浓度增加,单体最终转化率增加;当助引发剂N,N-二甲氨基苯甲酸-乙酯(EDAB)浓度为1.2%时,单体最终双键转化率最高;AEBP对双官能度单体的引发效率较之三官能度单体的好;聚合速率随光照强度的增强而变快;固化后AEBP的迁移性比传统的BP大大降低.     

可聚合型光引发剂4-丙烯酰氧基二苯甲酮的光聚合性能研究

以实时红外光谱(RT-IR)法研究了合成的4-丙烯酰氧基二苯甲酮(4-ABP)的光聚合动力学性质,考察了不同单体、不同引发剂和助引发剂浓度、不同光强对聚合性能的影响.以萃取法对比研究了4-ABP和二苯甲酮(BP)在固化膜中的的残留量.结果表明,4-ABP是一种非常有效的光引发剂.随着引发剂浓度和光强的增大,单体转化率、最大反应速率都增大,诱导期缩短.萃取实验表明4-ABP在固化膜中的残留量远低于BP.     

丙烯酸β-羟丙酯与聚氯乙烯膜的紫外光接枝改性

采用液相接枝方法 ,在紫外线辐照下 ,合成了一系列丙烯酸 β-羟丙酯 (β -HPAT) /聚氯乙烯接枝膜。讨论了引发剂浓度、单体浓度、光照时间、光照强度对接枝率的影响。结果表明 ,引发剂浓度为 6 .5 1× 10 -3 mol/L ,单体浓度 2 .0mol/L ,光照时间为 2 .0h ,且光照强度越强时 ,接枝率最大。接枝膜的结构特征通过FT -IR光谱进行了确证 ,最后 ,对接枝膜进行TGA分析 ,结果表明聚氯乙烯经过表面改性后 ,表面极性增大 ,热稳定性大大提高。     

分散聚合法制备PVP微球的研究

以N-乙烯基吡咯烷酮(NVP)为初始单体,乙酸乙酯为分散介质,采用分散聚合法制备了分散性能良好、粒径为3～4μm的聚乙烯基吡咯烷酮(PVP)微球.考察了单体、分散剂及引发剂浓度对PVP微球的粒径、单体转化率及分子量的影响,并对PVP的结构和性能进行研究.结果表明,单体浓度增加,PVP微球粒径和分子量增大,单体转化率升高;分散剂浓度增加,PVP微球粒径变小,分子量增大,单体转化率升高;引发剂浓度增加,PVP微球粒径变大,分子量减小,单体转化率升高.与溶液聚合法相比,分散聚合法制备的PVP分子量较小且具有一定的结晶性.     

Preparation of Fluorine-Containing Polyacrylate Emulsion by a UV-initiated Polymerization

A fluorine-containing polyacrylate emulsion was synthesized by a UV-initiated emulsion polymerization from methyl methacrylate (MMA) and hexafluorobutly methacrylate (HFMA) in the presence of 2-hydroxy-4-(2-hydroxyethoxy)-2-methyl-propiophenone (Irgacure 2959) as a hydrophilic photoinitiator at room temperature. The latex and films were characterized by Fourier transformed infrared (FT-IR) spectrometry, nuclear magnetic resonance (¹H-NMR, ¹⁹F-NMR) spectrometry, transmission electron microscopy (TEM), recycling gel permeation chromatography (GPC), dynamic light scattering (DLS), and contact angle (CA) analysis, respectively. The effects of photoinitiator and emulsifier concentration on the polymerization were discussed. Compared to the corresponding thermal polymerization, UV-initiated polymerization of the MMA/HFMA emulsion could be accomplished at a much higher speed. The polymerization conversion in UV-initiated polymerization reached 95% within 10 min at an emulsifier concentration of 0.6 wt%, photoinitiator concentration of 0.4 wt%, and monomer concentration of 10 wt%.     

Ultrasonically initiated emulsion polymerization of methyl methacrylate

The ultrasonically initiated emulsion polymerization of methyl methacrylate (MMA) was investigated. Experimental results show that sodium dodecyl sulfonate (SDS) surfactant plays a very important role in obtaining a high polymer yield, because in the absence of SDS, monomer conversion is near zero. Thus, the surfactant serves as an initiator and as interfacial modifier in this system (MMA/H₂O), and the monomer conversion increases significantly with increasing SDS concentration. An increase in the reactor temperature also leads to an increase in the monomer conversion. An appropriate increase in the N₂ purging rate also leads to higher conversion. The conversion of MMA decreases with increasing monomer concentration because of the higher viscosity of the system. With the experimental results, optimized reaction conditions were obtained. Accordingly, a high monomer conversion of about 67% and a high molecular weight of several millions can be obtained in a period of about 30 min. Furthermore, transmission electron micrographs show that the latex particles prepared are nanosized, indicating a promising technique for preparing nanoscale latex particles with a small amount of surfactant. In conclusion, a promising technique for ultrasonically initiated emulsion polymerization has been successfully performed. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3356–3364, 2001     

新型红外光引发剂的激光光聚合研究

目前对紫外区敏感的光聚合体系的研究已经比较成熟 ,并且在工业生产中得到了实际应用 .对可见光区的光聚合体系的研究也已引起了不少研究者的关注 .而有关近红外 /红外区敏感的光聚合体系的报道还很少 .已经商业化的红外半导体激光器具有体积小、价格便宜、操作简便、性能稳定等特点 ,配合计算机布线技术 ,可大大提高生产效率 ,这些优点使得与之匹配的对红外区域敏感的光聚合体系具有广阔的应用前景[1 ] ,尤其是在计算机直接制版 (Ｃｏｍｐｕｔｅｒ ｔｏ ｐｌａｔｅｓ,ＣＴＰｓ)领域[2 ] .Ｃｈａｔｔｅｒｊｅ等曾经研究了用阳离子菁染料与不…     

MMA/DVB emulsion surface graft polymerization initiated by UV light

Methyl methacrylate/1,2-divinylbenzene (MMA/DVB) in an opaque emulsion were successfully grafted onto the surface of polymeric substrate under the irradiation of UV light with benzophenone (BP) as a photoinitiator that was previously coated on the substrate surface. Monomer conversion, grafting efficiency, and grafting yields were determined by the gravimetric method. ATR-IR, AFM, and TEM were used to characterize the surface composition, to observe the topography of the grafted substrates, and to view inter-film colloid particles formed by cross-linking. The results reveal that, with the opaque MMA/DVB emulsion system and CPP film as substrate, the monomer conversion is in the range of 15-55%, the grafting efficiency is about 80%, the grafting yield reaches 5%, and the thickness of the graft layer can be controlled in the range 0.09-1.5 microm. Images of AFM show that the graft layer is piled up by nanoparticles (about 30-50 nm in diameter), which are linked together and tied to the substrate surface with covalent bonds. A possible model of surface graft polymerization including surface initiating, nucleation, and shish kebab growing is put forward to interpreting the above results.     

A one-component photoinitiator based on 4-methylbenzophenone and morpholine

4-Benzoylbenzyl-3-morpholinopropanoate was synthesized, characterized and used as a one-component photoinitiator of Type II. Real-time near-IR spectroscopy was used to study the kinetics of conversion of double bonds of monomers vs. irradiation time. In this initiator, the radicals could be generated through hydrogen abstraction based on intermolecular reaction. Light intensity, concentration of initiator, and the functionality of acrylates affected the polymerization rate and the final monomer conversion.     

Kinetic and particle size studies of emulsion polymerization of methyl methacrylate and styrene with using polyamidoamine dendrimer as seed

The emulsion polymerization of methyl methacrylate (MMA) and styrene (St) were investigated with using polyamidoamine (PAMAM) dendrimer as seed, potassium persulfate as initiator and sodium dodecyl sulfate as emulsifier. The effects of 4.0GPAMAM dendrimer concentration, initiator concentration, emulsifier concentration, monomer concentration, and polymerization temperature on the monomer conversion and polymerization rate were investigated. At the same time, the influence of the generation of PAMAM dendrimer on latex particle size was studied also. The results showed that the monomer conversion and polymerization rate increased with increasing initiator concentration, emulsifier concentration, monomer concentration, and polymerization temperature. But polymerization rate increased firstly with an increase in the 4.0GPAMAM dendrimer from 0.03 g to 0.09 g and then decreased with further increase to 0.12 g. When the concentration of 4.0GPAMAM dendrimer less than 1.449 × 10^?4 mol/L, the kinetic equation can be expressed by Rp∝[4.0GPAMAM]^0.772[SDS]^0.562[KPS]^0.589[M]^0.697, and the activation energy (Ea) of emulsion polymerization is 62.56kJ/mol. In additional, the copolymer latex particle size decreased and possessed monodispersity with increasing the generation of PAMAM dendrimer. According to FT-IR spectrum analysis, PAMAM dendrimer is successfully incorporated into the poly(PAMAM-St–MMA) latex particles.     

Emulsion polymerization of methyl methacrylate under pulsed microwave irradiation

Emulsion polymerization of methyl methacrylate (MMA) under pulsed microwave irradiation (PMI) with higher peak pulse power was studied. The effects of various parameters of PMI on the polymerization were analyzed and compared with that under conventional heating (CH) process. The results were summarized, as compared with that under CH, as follows. The amount of initiator used to reach constant conversion reduced by 50% at the same polymerization time; at the same initiator concentration 0.15 and 0.2 wt.%, the polymerization rate increased by 131% and 163%, respectively. The molecular weight of polymer obtained was 1.1-2.0 times larger than that under CH; at the same irradiation energy, the conversion achieved using a lower pulse power was greater than that using a higher pulse power. There seemed to be a factor of the irradiation energy efficiency; in other words, for the monomer conversion, the irradiation energy of low pulse power had a higher efficiency. The conversion achieved using a 3.5 μs pulse width was almost the same as that using a 1.5 μs pulse width. The results indicated that PMI had a significant non-thermal effect on the emulsion polymerization of MMA so as to effectively enhance the polymerization rate. The glass transition temperature (T_g), the polydispersity index (PDI) and the regularity of the polymer obtained using two processes were similar, indicating that the physical properties and microstructure of the polymer were not modified by the use of microwaves.     

Emulsifier‐free,organotellurium‐mediated living radical emulsion polymerization (emulsion TERP): Effect of monomer hydrophilicity

Emulsifier‐free, organotellurium‐mediated living radical emulsion polymerizations (emulsion TERPs) of methyl methacrylate (MMA) and n‐butyl methacrylate (BMA) with dimethyl ditelluride were carried out at two different stirring rates (220 rpm and 1000 rpm). In the emulsion TERP of MMA as a hydrophilic monomer, the molecular weight distribution (MWD) controls with both stirring rates were good with high polymerization rate (100% conversion at 1.5 h). On the other hand, in the emulsion TERP of BMA as a hydrophobic monomer, at 220 rpm the polymerization rate was much slow (～50% conversion at 22 h) and the MWD control was bad, but at 1000 rpm the polymerization was completed within 7 h and MWD control was good. These results suggest that monomer transportation from droplets to polymerizing particles via aqueous medium is important for good MWD control and steady polymerization in the emulsion TERP. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

AMPS/MMA二元共聚微球的超声无皂乳液制备与表征

将超声辐射无皂乳液聚合作用于含有2-丙烯酰胺基-2-甲基丙磺酸（AMPS）和甲基丙烯酸甲酯（MMA）的水溶液中,在不加任何引发剂和乳化剂的条件下合成AMPS/MMA二元共聚高分子微球,考察了超声反应时间对单体转化率的影响,用FTIR、TGA-DSC、TEM和粒度分析仪等技术进行了表征,并初步探讨了聚合反应机理。结果表明,合成得到的高分子微球粒径在0.77μm左右,分散均匀,且具有较好的热稳定性