AMPS/MMA二元共聚微球的超声无皂乳液制备与表征 |
| |
引用本文: | 王艳丽,谭德新,徐国财,闵凡飞.AMPS/MMA二元共聚微球的超声无皂乳液制备与表征[J].应用化学,2009,26(7):866-868. |
| |
作者姓名: | 王艳丽 谭德新 徐国财 闵凡飞 |
| |
作者单位: | 安徽理工大学 |
| |
摘 要: | 将超声辐射无皂乳液聚合作用于含有2-丙烯酰胺基-2-甲基丙磺酸(AMPS)和甲基丙烯酸甲酯(MMA)的水溶液中,在不加任何引发剂和乳化剂的条件下合成AMPS/MMA二元共聚高分子微球,考察了超声反应时间对单体转化率的影响,用FTIR、TGA-DSC、TEM和粒度分析仪等技术进行了表征,并初步探讨了聚合反应机理。结果表明,合成得到的高分子微球粒径在0.77μm左右,分散均匀,且具有较好的热稳定性
|
收稿时间: | 2008-07-04 |
修稿时间: | 2008-11-27 |
Preparation and Characterization of AMPS/MMA Copolymer Microspheres via Ultrasonic Emulsifier-free Emulsion Polymerization |
| |
Abstract: | AMPS(2-acrylamido-2-methylpropanesulfonicacid)/MMA(methyl methacrylate) copolymer microspheres were prepared with the solution containing MMA and AMPS without initiator and emulsifier by ultrasonic irradiation emulsifier-free emulsion polymerization. The effect of ultrasonic time on monomer conversion was investigated, the samples were characterized by FTIR, TGA, DSC, TEM and Zeta-sizer and the initiation mechanism of copolymerization was studied as well. The results show that the microspheres possessed a good dispersity, a uniform size with the diameter of 0.77μm and an excellent thermal stability. |
| |
Keywords: | |
|
| 点击此处可从《应用化学》浏览原始摘要信息 |
| 点击此处可从《应用化学》下载免费的PDF全文 |
|