(PtAuPt)HN/GC的制备及对甲酸氧化的电催化性能

以Se溶胶为模板,合成了多层核壳结构的Se@Pt@Au@Pt实心纳米粒子;采用化学与电化学相结合的除硒方法制得了(PtAuPt)HN/GC,并表征了(PtAuPt-Se)HN的表面形貌、结构与组成;以甲酸为探针分子,比较了(PtAuPt)HN/GC和Pt/C/GC对甲酸氧化的电催化行为,发现(PtAuPt)HN/GC催化甲酸氧化只有1个氧化峰,峰电位和峰电流分别约为0.35V和1.22mA/cm2,而Pt/C/GC则有2个氧化峰,在0.35V时所对应的电流密度仅约为0.30mA/cm2,前者在该电位时的电流密度是后者的4倍;在0.30mA/cm2的电流密度下,(PtAuPt)HN/GC对应的电极电位为0.01V,比Pt/C/GC负移了340mV;在600s时的计时电流分别为0.06和0.02mA/cm2.(PtAuPt)HN对甲酸氧化的电催化活性不但比Pt/C高,而且具有一定的抗CO中毒性能.     

碳载Pt/Sb_(ad)电极上乙醇电催化氧化特征和原位FTIR反射光谱研究

用电化学循环伏安法和原位 FTIR反射光谱法研究了 Sb在碳载纳米 Pt膜电极 (nm -Pt/ GC)表面不可逆吸附的电化学特性及酸性介质中乙醇的吸附和电催化氧化特性 .结果指出 ,当扫描电位的上限 Eu≤0 .5 0 V(SCE)时 ,Sbad可以稳定地吸附在 nm-Pt/ GC电极表面 .与未修饰的 nm-Pt/ GC电极上结果相比 ,Sbad修饰的 nm-Pt/ GC/ Sbad/ (nm-Pt/ GC)的催化活性显著增加 .测得当覆盖度θsb=0 .1 3 7时 ,修饰电极对乙醇的电催化活性最高 ,乙醇氧化的峰电位负移了 0 .1 5 V,峰电流增大了 1倍 .原位 FTIR反射光谱的结果从分子水平揭示了 Sb修饰对乙醇氧化反应途径的选择功能 .     

甲酸在Aucore@Ptshell/Pt电极上电催化氧化的原位SERS

用化学还原法合成了Aucore@Ptshell纳米粒子, 并用扫描电子显微镜(SEM)及X射线衍射(XRD)等技术对纳米粒子进行表征; 采用电化学原位表面增强拉曼光谱(SERS)技术对甲酸的电催化氧化过程进行了研究, 成功地获得了甲酸在Aucore@Ptshell/Pt电极上解离吸附的原位SERS. 结果显示, 在开路电位时, 甲酸能在Aucore@Ptshell/Pt电极表面自发氧化, 解离生成强吸附中间体COad和弱吸附中间体HCOOad, 在电位为+0.10 V时检测到氧化产物CO2的谱峰. 研究结果表明, Aucore@Ptshell/Pt电极对甲酸的氧化具有较高的催化活性和较强的SERS效应, 甲酸在Aucore@Ptshell/Pt电极上的电催化氧化过程遵循双途径机理.     

不同介质对Pt/GC电极制备及其性能的影响

应用循环伏安法(CV),扫描电子显微镜(SEM)和电化学原位红外反射光谱(in situFTIRS)研究了不同介质对碳载铂纳米薄膜电极(Pt/GC)的表面结构以及该薄膜电极对甲酸电催化氧化性能的影响.结果表明,使用不同介质的镀铂溶液,均可电沉积出分布较为均匀的Pt粒子,但其尺寸与形貌却相差很大.当以H2SO4作介质,由循环伏安法于玻碳电极上电沉积Pt得到的(Pt/GC1)电极,其Pt粒子粒径约100~200 nm;而在HClO4介质得到的(Pt/GC2)电极,则含有两种Pt微晶:其一是立方体形,粒径约200 nm,其二为菜花状,粒径约400 nm.电化学循环伏安和原位红外反射光谱测试指明,不同介质制备的Pt/GC电极对甲酸的电催化氧化均表现出与本体铂电极(Pt)相类似的特性,即可通过活性中间体或毒性中间体将甲酸氧化至CO2,但不同结构的Pt/GC电极具有不同的电催化活性.进一步以Sb或Pb修饰Pt/GC电极,不仅可以有效地抑制毒性中间体CO的生成,而且还能显著提高其电催化活性.比较本文研究的7种电极,其电催化活性顺序依次为:Sb-Pt/GC2>Pb-Pt/GC2>Pb-Pt/GC1>Sb-Pt/GC1>Pt/GC2>Pt/GC1>Pt.     

Au@Pt纳米粒子催化O2还原反应的电化学研究

以100 nm的Au粒子为核,抗坏血酸为还原剂,H2PtCl6·6H2O为前驱体,合成了Pt包Au核壳结构纳米粒子( Au@ Pt)及其修饰的玻碳(GC)电极(Au@ Pt/GC).采用旋转圆盘电极等常规电化学方法,比较了Au@ Pt/GC和商用碳载铂(Pt/C)修饰的玻碳电极(Pt/C/GC)催化O2还原反应活性及耐甲醇性能,发现Au@ Pt纳米粒子在铂用量很低的情况下,其催化O2还原反应活性仍与商用Pt/C相当,而且还具有优良的耐甲醇性能;其催化O2还原反应机理按O2直接还原成H2O的四电子历程进行.     

Pt-CNTs 修饰玻碳电极(Pt-CNTs/GC)电氧化活性的研究

采用透射电镜(TEM)和选区电子衍射(SAED)技术, 分别表征了Pt-CNTs/GC电极的表面形貌和所负载铂纳米原子簇的结构. 以CO和CH3OH为探针分子, 用循环伏安和计时电流等常规电化学方法检测了CO和CH3OH在Pt-CNTs/GC电极上的氧化行为. 研究结果表明, CO在Pt-CNTs/GC电极上有3个氧化电流峰(Ⅰ, Ⅱ, Ⅲ), 其中峰Ⅰ为CO桥式吸附的氧化峰, 而峰Ⅱ和Ⅲ则分别为CO线形吸附在碳纳米管负载的不同粒径的Pt纳米原子簇以及Pt原子薄膜上所分裂的氧化峰; CH3OH在Pt-CNTs/GC电极上也能自发解离吸附强吸附中间体CO; Pt-CNTs/GC电极对CH3OH的氧化峰电流不总是随CNTs上载铂量的增加而增大, 表明在制备直接甲醇燃料电池阳极时, 应选择合适的载铂量.     

亚硒酸钠在L-半胱氨酸自组装类生物膜修饰电极上的电化学行为

利用L-半胱氨酸自组装膜修饰金电极(L-Cys,Au/SAMs), 在0.05mol/L H_2SO_4 底液中研究了 Na_2SeO_3 的电化学特性.在0.00～1.30 V (vs. SCE) 电位范围内对微量Na_2SeO_3进行循环伏安扫描,发现L-Cys, Au/SAMs修饰电极在峰电位0.89 V处有灵敏的Se的氧化溶出峰.通过比较裸金电极和修饰电极在Na_2SeO_3 溶液中的电化学特性发现,修饰电极通过巯基中的S与Na_2SeO_3发生氧化还原作用生成Se,且修饰电极对沉积在电极表面的Se的氧化过程具有催化作用.根据Na_2SeO_3在单分子膜上的电化学行为,提出了单分子膜中硫(Au-S)与Se(Ⅳ)作用生成Se的反应机理、Se电化学催化氧化机理及巯基化合物通过生成纳米硒生物吸收Se的类生物膜模型.     

铂催化氧还原反应过程中磷酸的影响及抑制磷酸吸附策略

与低温(<100oC)质子交换膜燃料电池相比,磷酸掺杂PBI膜燃料电池可工作于100–200 oC,工作温度的提高有利于提高电极反应动力学速率、增加Pt催化剂对CO等毒物的耐受性,以及简化电池水管理等.然而,磷酸在Pt催化剂表面吸附较强,这将造成Pt一定程度的毒化.基于“第三体效应”,即在Pt表面预吸附某些小分子,可在一定程度上抑制磷酸吸附,然而预吸附分子同时也将占据Pt表面部分活性位点,因而Pt的催化性能最终由两个因素决定：磷酸抑制程度和预吸附分子在Pt表面的覆盖度.
　　本文系统考察了Pt表面预吸附分子覆盖度和预吸附分子链长对其催化氧还原反应(ORR)活性的影响.首先,通过控制预吸附了胺类分子的Pt电极的电位,得到表面具有不同覆盖度的Pt电极,考察了0.1 mol/L H3PO4电解液中Pt电极对ORR的催化活性随预吸附分子覆盖度的变化规律;为分离磷酸吸附和修饰分子吸附本身对Pt催化活性的影响,对比了0.1 mol/L HClO4电解液中Pt电极对ORR的催化活性随预吸附分子覆盖度的变化规律.进一步对比研究了不同链长胺分子——正丁胺(BA)、正辛胺(OA)及十二胺(DA)等作为修饰分子对Pt/C催化剂电催化ORR活性的影响.结果表明,随修饰分子在Pt表面覆盖度提高,在0.1 mol/L HClO4溶液中,由于预吸附分子占据Pt部分活性位,修饰后光滑Pt电极表面的本征活性单调下降;而在0.1 mol/L H3PO4中,修饰后光滑Pt电极表面的ORR活性呈现先升高后降低的趋势,当预吸附分子覆盖度约为20%时,其ORR活性最高,为未修饰的光滑Pt电极表面的1.67倍.这表明预吸附分子有效抑制了磷酸的吸附,且当预吸附分子覆盖度约为20%时,预吸附分子对Pt表面的占据与其抑制磷酸吸附的作用达到最佳平衡点.然而,当修饰分子BA, OA和DA在Pt表面覆盖度分别为38.6%,26.1%和26.1%时, Pt/C在0.1 mol/L H3PO4中的ORR催化活性接近,分别为未经修饰Pt/C电催化剂的1.7,1.8和2.0倍,这表明预吸附分子链长对ORR催化活性影响较小,表面预吸附分子抑制磷酸吸附的策略对Pt/C催化剂也同样适用.同时, Pt/C电极经BA, OA和DA修饰后,其在0.1 mol/L HClO4中的比表面活性分别为未经修饰Pt/C电催化剂的1.0,1.1和1.3倍,与修饰后光滑Pt电极表面本征ORR活性变化规律不一致.然而,与Pt在HClO4电解质中的ORR活性相比, ORR的半波电位仍有大约123 mV的差距,今后还需继续从催化剂的角度,如调控Pt表面的吸附特性,或从创新电解质的角度,如有机磷酸电解质等出发解决磷酸毒化的问题.     

铂催化氧还原反应过程中磷酸的影响及抑制磷酸吸附策略（英文）

与低温(100 oC)质子交换膜燃料电池相比,磷酸掺杂PBI膜燃料电池可工作于100–200 oC,工作温度的提高有利于提高电极反应动力学速率、增加Pt催化剂对CO等毒物的耐受性,以及简化电池水管理等.然而,磷酸在Pt催化剂表面吸附较强,这将造成Pt一定程度的毒化.基于"第三体效应",即在Pt表面预吸附某些小分子,可在一定程度上抑制磷酸吸附,然而预吸附分子同时也将占据Pt表面部分活性位点,因而Pt的催化性能最终由两个因素决定:磷酸抑制程度和预吸附分子在Pt表面的覆盖度.本文系统考察了Pt表面预吸附分子覆盖度和预吸附分子链长对其催化氧还原反应(ORR)活性的影响.首先,通过控制预吸附了胺类分子的Pt电极的电位,得到表面具有不同覆盖度的Pt电极,考察了0.1 mol/L H_3PO_4电解液中Pt电极对ORR的催化活性随预吸附分子覆盖度的变化规律;为分离磷酸吸附和修饰分子吸附本身对Pt催化活性的影响,对比了0.1 mol/L HClO_4电解液中Pt电极对ORR的催化活性随预吸附分子覆盖度的变化规律.进一步对比研究了不同链长胺分子——正丁胺(BA)、正辛胺(OA)及十二胺(DA)等作为修饰分子对Pt/C催化剂电催化ORR活性的影响.结果表明,随修饰分子在Pt表面覆盖度提高,在0.1 mol/L HClO_4溶液中,由于预吸附分子占据Pt部分活性位,修饰后光滑Pt电极表面的本征活性单调下降;而在0.1 mol/L H_3PO_4中,修饰后光滑Pt电极表面的ORR活性呈现先升高后降低的趋势,当预吸附分子覆盖度约为20%时,其ORR活性最高,为未修饰的光滑Pt电极表面的1.67倍.这表明预吸附分子有效抑制了磷酸的吸附,且当预吸附分子覆盖度约为20%时,预吸附分子对Pt表面的占据与其抑制磷酸吸附的作用达到最佳平衡点.然而,当修饰分子BA,OA和DA在Pt表面覆盖度分别为38.6%,26.1%和26.1%时,Pt/C在0.1 mol/L H_3PO_4中的ORR催化活性接近,分别为未经修饰Pt/C电催化剂的1.7,1.8和2.0倍,这表明预吸附分子链长对ORR催化活性影响较小,表面预吸附分子抑制磷酸吸附的策略对Pt/C催化剂也同样适用.同时,Pt/C电极经BA,OA和DA修饰后,其在0.1 mol/L HClO_4中的比表面活性分别为未经修饰Pt/C电催化剂的1.0,1.1和1.3倍,与修饰后光滑Pt电极表面本征ORR活性变化规律不一致.然而,与Pt在HClO_4电解质中的ORR活性相比,ORR的半波电位仍有大约123 m V的差距,今后还需继续从催化剂的角度,如调控Pt表面的吸附特性,或从创新电解质的角度,如有机磷酸电解质等出发解决磷酸毒化的问题.     

甲酸在Pt-Ru/GC电极上氧化的SERS研究

采用循环伏安(CV)法、计时电流法和电化学原位表面增强拉曼散射光谱(SERS)技术研究了甲酸在Pt-Ru/GC电极上的氧化行为, 发现甲酸在Pt-Ru/GC电极上与在粗糙Pt电极上一样, 也能自发解离出强吸附中间体CO和活性中间体—COO－. 从分子水平证实钌的加入有利于提高电极对甲酸的电催化氧化活性, 当镀液中Pt：Ru的摩尔比从10∶1变化到1∶1, CO的氧化峰电位从0.41 V负移至0.35 V, 约负移了60 mV. Pt-Ru/GC(1∶1)电极与粗糙Pt电极相比, CO在电极表面氧化完毕的电位亦负移了约200 mV. 该研究结果表明, 电化学原位表面增强拉曼散射光谱技术可望成为研究电催化反应机理的普适谱学工具.     

Three-dimensional porous Au nanocoral structure decorated with Pt submonolayer via galvanic displacement of copper adatoms for electrooxidation of formic acid

Three-dimensional (3D) porous Au nanocoral network (GNN) structure was fabricated on glassy carbon (GC) electrode by one-step, template-free electrodeposition and decorated with ultrathin Pt film by combining the underpotential deposition (UPD) of copper adatoms and the galvanic displacement (GD) between PtCl₆^2- and Cu. The thickness of Pt atomic layers can be controlled precisely by repeating the UPD–GD process. Scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM) were employed to characterize the morphology of GNN and Pt_n/GNN (n, the cycles of repeating the UPD–GD process). Cyclic voltammometric and chronoamperometric tests indicate that all Pt_n/GNN samples effectively support the direct oxidation of formic acid and show higher electrocatalytic performance than the commercial Pt/C catalyst (Pt, 20 wt %, Johnson Matthey Co.), where Pt₁/GNN completely eliminates the indirect oxidation of formic acid, exhibiting the best electrocatalytic activity and stability among all Pt_n/GNN samples due to the optimal coverage and distribution of Pt atoms on GNN.     

Implanting Atomic Dispersed Ru in PtNi Colloidal Nanocrystal Clusters for Efficient Catalytic Performance in Electro-oxidation of Liquid Fuels

Although PtRu alloy nanocatalysts have been certified to possess excellent electrocatalytic performance and CO-poisoning tolerance toward formic acid and methanol electro-oxidation, the unaffordable usages of ruthenium (Ru) and platinum (Pt) have greatly limited their widespread adoption. Here, a facile one-pot method is reported for implanting atomic dispersed Ru in PtNi colloidal nanocrystal clusters with different Ru/Pt/Ni molar ratios, greatly reducing the dosages of Pt and Ru, and further improving the catalytic performances for the electro-oxidation of formic acid and methanol. Through simple control of the amount of Ni(acac)₂ precursor, trimetallic Ru_0.3Pt_70.5Ni_29.2, Ru_0.6Pt_55.9Ni_43.5, Ru_0.2Pt_77.3Ni_22.5, and Ru_0.9Pt_27.3Ni_71.8 colloidal nanocrystal clusters (CNCs) are obtained. In particular, the Ru_0.3Pt_70.5Ni_29.2 CNCs exhibit excellent specific activities for formic acid and methanol electro-oxidation, that is, 14.2 and 15.3 times higher, respectively, than those of the Pt/C catalyst. Moreover, the Ru_0.3Pt_70.5Ni_29.2 CNCs also possess better anti-CO-poisoning properties and diffusion ability than the other RuPtNi CNCs. The excellent formic acid and methanol electro-oxidation activities of RuPtNi CNCs are ascribed to the optimal ligand effects derived from the Pt, Ni, and atomic dispersed Ru atoms, which can improve the OH adsorption ability and further the anti-CO-poisoning capability. This research opens a new door for increasing the electro-oxidation properties of liquid fuels by using lower dosages of noble metals in Pt-based catalysts.     

Pt纳米空球壳厚的可控制备及对甲酸的电催化氧化

本文以约120nm的α-Se球为模板,抗坏血酸为还原剂,H2PtCl6为前驱体,通过改变氯铂酸的用量可控合成了不同壳厚的纳米铂空球（Pthollow）及其修饰玻碳（GC）电极（Pthollow／GC）;采用扫描电子显微镜（SEM）、高分辨透射电子显微镜（HR-TEM）、能量色散X射线（EDX）谱、X射线衍射（X-ray diffraction,XRD）谱和选区电子衍射（SAED）图等表征其形貌、组成与结构;以甲酸为探针分子,采用循环伏安和计时电流法研究了甲酸在Pthollow／GC电极上的电催化氧化行为．结果表明,所制备的Pthollow分散性好、粒径比较均匀,其多孔球壳是由多维多级的铂原子团簇所构建,呈现多晶铂的结构与性质;当RPt/Se=1．2时,所合成Pthollow。对甲酸的电催化氧化活性最高,且明显优于电沉积铂（Ptnano）修饰GC电极（Ptnano／GC）,为直接甲酸燃料电池（DFAFC）阳极材料的优化制备提供了一定的实验与理论依据,有潜在的应用推广价值．     

Composition-Controllable AuPt Alloy Catalysts for Electrooxidation of Formic Acid

AuPt alloy catalysts with various compositions have been successfully prepared simply by one-step co-reduction of Au and Pt precursors involving sodium citrate as stabilizer and reductant. XRD, TEM and EDX element mapping analysis confirmed that the resulting AuPt nanoparticles are single-phase alloys rather than random mixtures of tiny Au and Pt particles. Compared with Pt/C, alloying Au with Pt can effectively alter the kinetic process of formic acid oxidation, reducing the generation of CO-like intermediates. Au₈₁Pt₁₉ displays superior electrocatalytic activity and durability, ~11 times in the mass activity better than commercial Pt/C and may be of practical significance for the commercialization of direct formic acid fuel cell.

     

Titanium-supported nanoporous bimetallic Pt–Ir electrocatalysts for formic acid oxidation

Novel titanium-supported nanoporous network bimetallic Pt–Ir/Ti electrocatalysts (S1:Pt₅₉Ir₄₁/Ti, S2:Pt₄₄Ir₅₆/Ti, S3:Pt₂₂Ir₇₈/Ti) have been successfully fabricated by the hydrothermal process. The nanoparticles of Pt and Ir were deposited on the titanium substrates in the presence of formaldehyde as a reduction agent. The electrocatalytic activity of these electrocatalysts towards formic acid oxidation in 0.5 M H₂SO₄ + 0.5 M HCOOH solutions was investigated using cyclic voltammograms (CVs), linear sweep voltammograms (LSVs), chrono amperometry and electrochemical impedance spectroscopy (EIS). The CVs of S1, S2 and S3 exhibit two anodic peaks in the forward scan and one anodic peak in the reverse scan which are similar to the pure Pt. Their LSVs show that the three samples present significantly high current densities of formic acid oxidation compared to the Pt electrode. It is observed from the chrono amperometric measurements at potential 600 mV that the sample S2 delivers a steady-state current density that is 545 times larger than that for the pure Pt electrode. EIS analysis shows that the impedances on both the imaginary and real axes of S1, S2 and S3 are much lower than those of the pure Pt. Among the three samples (S1, S2 and S3), S2 exhibits the highest electrocatalytic activity towards the formic acid oxidation.     

磷钨酸对甲酸在碳载Pt催化剂上电氧化的促进作用

用X射线能谱(EDS)、X射线衍射(XRD)和电化学等测试技术研究了电解液中的磷钨酸(PWA)对甲酸在碳载Pt(Pt/C)催化剂电极上氧化的促进作用。 结果表明,PWA不但能提高甲酸在Pt/C催化剂电极上氧化的电催化活性,而且也能提高其电催化稳定性。 这种促进作用与电解液中PWA的浓度有关,当电解液中PWA的质量浓度为0.10 g/L时,这种促进作用最佳。 这主要是由于电解液中PWA质量浓度＞0.10 g/L时,吸附到电极表面的PWA的量太多,占据了Pt/C催化剂电极中Pt表面的部分活性位点,从而降低了催化剂的电催化性能。     

Carbon-supported ultrafine Pt nanoparticles modified with trace amounts of cobalt as enhanced oxygen reduction reaction catalysts for proton exchange membrane fuel cells

To accelerate the kinetics of the oxygen reduction reaction (ORR) in proton exchange membrane fuel cells, ultrafine Pt nanoparticles modified with trace amounts of cobalt were fabricated and decorated on carbon black through a strategy involving modified glycol reduction and chemical etching. The obtained Pt₃₆Co/C catalyst exhibits a much larger electrochemical surface area (ECSA) and an improved ORR electrocatalytic activity compared to commercial Pt/C. Moreover, an electrode prepared with Pt₃₆Co/C was further evaluated under H₂-air single cell test conditions, and exhibited a maximum specific power density of 10.27 W mg_Pt^?1, which is 1.61 times higher than that of a conventional Pt/C electrode and also competitive with most state-of-the-art Pt-based architectures. In addition, the changes in ECSA, power density, and reacting resistance during the accelerated degradation process further demonstrate the enhanced durability of the Pt₃₆Co/C electrode. The superior performance observed in this work can be attributed to the synergy between the ultrasmall size and homogeneous distribution of catalyst nanoparticles, bimetallic ligand and electronic effects, and the dissolution of unstable Co with the rearrangement of surface structure brought about by acid etching. Furthermore, the accessible raw materials and simplified operating procedures involved in the fabrication process would result in great cost-effectiveness for practical applications of PEMFCs.     

Mass-transport-limited oxidation of formic acid on a PdMLPt(100) electrode in perchloric acid

In this communication, we study the electrocatalytic formic acid oxidation process on an epitaxially grown Pd monolayer on a Pt(100) single crystal in perchloric acid. The formic acid oxidation activity on this Pd_MLPt(100) electrode in perchloric acid is significantly enhanced compared to the same electrode in sulfuric acid and compared to unmodified Pt(100), with a low onset potential of around 0.14 V_RHE. The absence of hysteresis between the positive and negative scan during formic acid oxidation indicates the remarkable resistance to CO poisoning of the Pd monolayer surface. Most importantly, we report, for the first time, a mass-transport-limited formic acid oxidation rate on the Pd_MLPt(100) rotating electrode in perchlorate acid, setting a catalytic benchmark for future electrocatalysts for formic acid oxidation.