[Zn(en)3]SO4配合物大尺寸单晶的水热法生长和表征

Large size single crystals of [Zn(en)₃]SO₄ have been successfully grown by a hydrothermal process at 160℃ for 24h， using CuSO₄·5H₂O， ethylene diamine and reductive Zn powder as reactants. The diameters of the single crystals are range from 0.5mm to 1mm， and lengths reach up to 20mm. The single crystals were characterized by XRD analysis， FTIR and UV-Vis spectrum absorption measurements. The single crystal was confirmed to be [Zn(en)₃]SO₄ by performing powder diffraction of the single crystal. X-ray diffraction of the single crystals shows (100)-face to be cleavage face. The diffraction peaks are sharp and rocking curve for 200 diffraction has a narrow FWHM (the full width at half maximum)， which indicate the single crystal of [Zn(en)₃]SO₄ is perfect with less lattice distortion and defects. The single crystal appears transparent，and has constant weak absorption in UV-Vis spectrum region，which could be used as a novel optical crystal material.     

不同稀土改性SO42-/ZrO2催化剂的结构与性能表征

Solid superacid catalyst SO₄^2-/ZrO₂ was modified by different rare earth compounds and applied to the esterification of acetic acid and n-butanol. The effects of rare earth elements loading on the catalytic properties were studied and the correlation between the structure and properties was investigated by means of XRD, IR, UV, DTA and TG. The results show that the (NH₄)₂Ce(NO₃)₆ modification can enhance catalytic activity more and exhibit better stability than the other two compounds La(NO₃)₃ and Ce(NO₃)₃. Meanwhile,(NH₄)₂Ce(NO₃)₆ modification can restrain the loss of SO₄^2- efficiently. The optimum calcination temperature and molar ratio of Ce(NH)∶Zr for SO₄^2-/ZrO₂ catalyst modified by (NH₄)₂Ce(NO₃)₆ are 450 ℃ and 2, respectively.     

Li4Ti5O12溶胶-凝胶法合成及其机理研究

The precursors of Li₄Ti₅O₁₂ were prepared from tetrabutyl titanate and lithium acetate by sol-gel process. The Li₄Ti₅O₁₂ samples were synthesized by calcining the gel precursors at 400～900 ℃ in air for 6～20 h. Its reaction mechanism was investigated by infrared spectroscopy(IR), thermogravimetry(TG) and X-ray diffraction(XRD). The effects of sinter-temperature, calcination-time and thermal-treatment for the products were discussed. The samples were characterized by X-ray diffraction(XRD), scanning electron microscopy(SEM). The results showed that the single-phase products were obtained by calcining the gel precursors at 800 ℃ in air for 20 h, the sinter-temperature was lower than that of solid-state method, the particles were narrowly distributed, well crystallized with a size range from 0.3μm to 0.5 μm.     

热处理对SILAR法制备CuInSe2薄膜性能的影响

CuInSe₂ ternary films were prepared by successive ionic layer absorption and reaction (SILAR) method. The films were deposited on glass substrates at room temperature and subject to heat-treatment under Ar atmosphere at various calcination temperatures, and then characterized by using X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), optical absorption spectroscopy. XRD results showed that chalcopyrite structure CuInSe₂ with high degree of preferred orientation towards (112) reflection could be obtained by post-heat treatment. The compositions of films calcined at 300～400 ℃ were close to the standard stoichiometry and Cl impurity decreased after calcination. The direct band gap increased from 0.94 eV to 0.98 eV with the increase of calcination temperature.     

柠檬酸溶胶凝胶法制备LiCoO2电极材料及其表征

LiCoO₂ precursors of the cathode material for lithium-ion batteries were prepared from lithium hydroxide， basic cobalt carbonate and citric acid by a sol-gel method. The LiCoO₂ samples were obtained by sintering the gel pre-cursors at different temperatures and for different times. The thermal decomposition behavior of the gel precursors was examined by means of thermo-gravimetric analysis and differential thermal analysis using a PCT-IA thermal analyzer system. Their structures and morphologies were characterized by powder XRD and SEM techniques. It was found that using citric acid realized that the formation of LiCoO₂ crystal can be clearly differentiated to the nucle-ation and growth processes of the crystals; furthermore， the crystal size can be controlled. Electrochemical tests using the LAND BT1-10 test system showed the electrochemical performance of the material is affected by its in-tegrity and stability.     

一维Y2O3∶Eu3+纳米发光材料的制备与表征

One-dimensional Y₂O₃∶Eu³⁺ luminescence nanomaterials were prepared by hydrothermal method without template, and their properties were characterized. XRD patterns show that the precursors are hexagonal phase Y(OH)₃ crystals, and the samples are cubic Y₂O₃ after heat-treatment. SEM images indicate that the one-dimensional material with a diameter of 100 nm and length of micrometer scale can be obtained by this hydrothermal method. Photoluminescence properties show that the position and intensity of the precursors are different with that of the heat-treated samples resulted from the different hosts.     

Ceramic Filter Balls Loaded with α-Fe2O3 and Their Application to NH3-N Wastewater Treatment

Hydrolysis reaction of Fe(NO₃)₃ at a high temperature in the presence of urea as the homogeneous precipitant was studied. With the prepared ceramic filter balls loaded with α-Fe₂O₃ after high temperature calcination, the loading of α-Fe₂O₃ on the porous ceramic filter balls from Fe(NO₃)₃ solutions of different concentrations and mechanical stability of the loaded α-Fe₂O₃ were studied. The product was characterized using XRD and SEM. Adsorption experiments were conducted to evaluate the performance of the product in adsorbing NH₃-N. It turned out that the specific surface area of the ceramic filter balls loaded with α-Fe₂O₃ had increased to 36.5387 m²/g from original 4.6127 m²/g. When the concentration of Fe(NO₃)₃ was 0.40 mol/L, the loading of α-Fe₂O₃ on the ceramic filter balls accounted for 8.4% of the total mass of the adsorbent and α-Fe₂O₃ was adsorbed on the filter balls very well. The adsorption isotherm of NH₃-N on the ceramic filter ball adsorbent loaded with α-Fe₂O₃ was of Langmuir type. The saturated adsorption capacity was 3.33 mg/L, and the adsorption constant K was 0.1873. NH₃-N was adsorbed by α-Fe₂O₃ more easily, which was a kind of specific adsorption.     

草酸盐共沉淀法制备Y1.84La0.16O3纳米粉体

Nanopowder of Y_1.84La_0.16O₃ was prepared by oxalate co-precipitation method. The powder was characterized by TG-DTA, XRD and TEM. The results show that the precursor is Re₂(NO₃)₂(C₂O₄)₂·2H₂O (Re=Y, La), and the Y_1.84La_0.16O₃ nanopowders produced by calcining the precursor at 1 000 ℃ for 4 h are 20～40 nm spherical particles and well dispersed. The powders were with high sintering activity and could be fabricated to transparent ceramic without additive at 1 450～1 550 ℃ in H₂ atmosphere for 3 hours. The total transmission of the transparent ceramic could reach 80%.     

离子层气相反应法(ILGAR)制备CuInS2薄膜的研究

CuInS₂ thin films have been prepared by ion layer gas reaction (ILGAR) using C₂H₅OH as solvent, CuCl and InCl₃ as reagents and H₂S gas as sulfuration source. The effects of cationic concentrations and numbers of cycle on the properties of CuInS₂ film were investigated. The chemical composition, crystalline structure, surface topography, deposited rate, optical and electronic properties of the films were characterized by X-ray diffractrometry (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), ultraviolet-visible spectrometry (UV-Vis) and Hall System. The results show that the crystalline of CuInS₂ thin films and the deposition rate have been improved with the increase of cationic concentration, while CuxS segregation phases appear with further increasing cationic concentration. The deposition rate is close to constant as cationic concentration is fixed. CuInS₂ thin film derived form lower cationic concentration is uniform, compact and good in adhesion to the substrates. The absorption coefficient of CuInS₂ thin films is larger than 10⁴ cm^-1, and the band gap E_g is in the range of 1.30～1.40 eV. The dark resisitivity of the thin film decreases from 50 to 10 Ω·cm and the carrier concentration ranges are over 10¹⁶ cm^-3.     

(ZrO2)1-x(Yb2O3)x纳米晶的水热法合成及其烧结体的电性能

(ZrO₂)_1-x(Yb₂O₃)_x (x=0.07, 0.09, 0.11) nanocrystallites were hydrothermally prepared in basic media by using co-precipitated Zr(OH)₄ and Yb(OH)₃ as precursor. The nanocrystallites have small particle sizes of 5.8~7.5 nm, narrow size distribution, less agglomeration and high sinterability. The oxide-ionic conduction properties of the prepared ceramics were investigated by means of AC impedance spectroscope, oxygen concentration cell at 600~1 000 ℃. The results show that the ceramic with x=0.09 is superior to the ceramics with x=0.07 and 0.11 in oxide-ionic conduction.     

Cr2(WO4)3和Cr2(MoO4)3的负热膨胀特性研究

用液相反应-前驱物烧结法制备了Cr₂(WO₄)₃和Cr₂(MoO₄)₃粉体。298～1 073 K的原位粉末X射线衍射数据表明Cr₂(WO₄)₃和Cr₂(MoO₄)₃的晶胞体积随温度的升高而增大, 本征线热膨胀系数分别为(1.274±0.003)×10^-6 K^-1和(1.612±0.003)×10^-6 K^-1。用热膨胀仪研究了Cr₂(WO₄)₃和Cr₂(MoO₄)₃在静态空气中298～1 073 K范围内热膨胀行为，即开始表现为正热膨胀，随后在相转变点达到最大值，最后表现为负热膨胀，其负热膨胀系数分别为(-7.033±0.014)×10^-6 K^-1和(-9.282±0.019)×10^-6 K^-1。     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

Eu0.5RE0.5Fe0.5Mn0.5O3的57Fe Msosbauer谱研究

利用固相反应合成了Eu0.5RE0.5Fe0.5Mn0.5O3(RE=La,Pr,Nd,Sm,Eu,Gd,Tb,Dy,Ho,Er,Tm,Yb,Y)等化合物。测量了其XRD谱及57FeMssbauer谱。实验发现,随着RE原子序数的增加,样品的晶胞体积减小,Fe在化合物中处于Fe3+的高自旋状态,57Fe的四极裂矩与样品的畸变参数D成线性关系。     

可见光响应的Co3(PO4)2/Ag3PO4纳米复合光催化剂的制备及表征

采用简单的化学偏聚法合成出Ag₃PO₄纳米颗粒、磷酸钴（Co₃（PO₄）₂,CoP）纳米片以及它们两者的纳米复合结构（CoP/Ag₃PO₄）,同时还比较了它们的可见光催化活性. 采用场发射扫描电镜（FESEM）、X 射线衍射（XRD）、紫外-可见（UV-Vis）吸收光谱以及光致发光谱等手段对其形貌、结构、光学以及可见光催化性能等进行表征. 结果表明,CoP/Ag₃PO₄复合纳米结构的可见光降解甲基橙（MO）的速率和循环稳定性均明显优于其它两种物质. 这表明CoP应该起着共催化剂的作用,它能够抑制光生电子与空穴之间的复合,并且提供大量高活性的光生空穴. 此外,我们还发现CoP/Ag₃PO₄降解另一种阳离子型染料——罗丹明B（RhB）的能力则远不如纯Ag₃PO₄,这可能是与光催化剂的表面性质发生改变有关,造成更低的RhB吸附能力. 本文提供了一种廉价制备高效可见光催化剂的新方法.     

g-C3N4/Bi2O2CO32D纳米片复合材料的制备及可见光催化性能研究

采用自组装和化学沉淀法分别制得两种可见光驱动复合材料石墨相氮化碳/碳酸氧铋(g-C_3N_4/Bi_2O_2CO_3).采用X射线衍射光谱(XRD),紫外可见光谱、扫描电镜(SEM)、N_2吸附、电化学阻抗谱(EIS)和X射线光电子能谱(XPS)等分析手段对制备的催化剂进行了表征.结果表明,制备方法对纳米复合材料的晶相、形态及光学性能没有影响,但是影响g-C_3N_4和Bi_2O_2CO_3之间的相互作用力,导致光生电子-空穴对的分离速率存在显著差异.以可见光驱动苯酚和罗丹明B的降解实验为探针反应检测催化剂的光催化性能.实验结果表明自组装法得到的异质结催化剂中相互作用力更强,催化效果最高.O_2-是罗丹明B降解反应的主要活性物种,染料的光敏化、Bi_2O_2CO_3与g-C_3N_4综合效应,导致光生载流子电荷分离效率更高.     

Vibrational spectra of the peroxotantalates (NH4)3[Ta(O2)4], K3[Ta(O2)4], Rb3[Ta(O2)4] and Cs3[Ta(O2)4] and the crystal structure of Rb3[Ta(O2)4]

The compounds (NH₄)₃[Ta(O₂)₄], K₃[Ta(O₂)₄], Rb₃[Ta(O₂)₄] and Cs₃[Ta(O₂)₄] have been prepared and investigated by X-ray powder methods as well as Raman- and IR-spectroscopy. In the case of Rb₃[Ta(O₂)₄] the structure has been solved from single crystal data. It is shown that all these compounds are isotypic and crystallize in the K₃[Cr(O₂)₄] type (SG , No. 121). The infrared- and Raman spectra (recorded on powdered samples) are discussed with respect to the internal vibrations of the peroxo-group and the dodecahedral [Ta(O₂)₄]³⁻ ion. Symmetry coordinates for the [Ta(O₂)₄]³⁻ ion are given from which the vibrational modes of the O-O stretching vibrations of the O₂²⁻ groups, the Ta-O stretching vibrations and the Ta-O bending vibrations are deduced.     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

A Structural Investigation of La2(GeO4)O and Alkaline-Earth-Doped La9.33(GeO4)6O2

The structures of the oxyorthogermanate La₂(GeO₄)O and the apatite-structured La_9.33(GeO₄)₆O₂ have been refined from powder neutron diffraction data. La₂(GeO₄)O crystallizes in a monoclinic unit cell (P2₁/c) and is cation stoichiometric in contrast to previous reports. La_9.33(GeO₄)₆O₂ crystallizes in a hexagonal unit cell (P6₃/m) and the powder diffraction data show anisotropic peak broadening that is observed in electron diffraction patterns as incommensurate diffuse spots at hkq reciprocal planes (with q=1.6-1.7) and can be attributed to a correlated disorder in the “apatite channels”. This compound was doped up to a nominal composition close to M₂La₈(GeO₄)₆O₂ with M=Ca, Sr, Ba. The dopant ions preferentially occupy the 4f sites as the number of La vacancies decreases. The measured ionic conductivity of La_9.33(GeO₄)₆O₂ is about 3 orders of magnitude larger than for La₂(GeO₄)O at high temperatures and decreases with increasing dopant content from the highest value of about 0.16 S cm⁻¹ at 1160 K.     

Ni-P-Zn3(PO4)2(ZnSnO3、ZnSiO3)纳米复合化学镀层性质和组成的研究

研究了温度、时间、浓度等对Ａ３钢片上Ｎi-P-Zn3(PO4)2、Ni-P-ZnSnO3和Ｎi-P-ZiSiO3纳米复合合化学镀层外貌的影响,用扫描电子显微镜（ＳＥＭ）观察外貌、称重法测定厚度;通过１０％ＮaCl溶液、１％Ｈ２Ｓ气体加速腐蚀试验,１０％ＣuSO4溶液点滴试验等多种手段测定其耐腐蚀性能,用Ｘ－射线光电子谱（ＸＰＳ）及俄歇电子能谱（ＳＥＳ）测定其价态组成,结果表明：在最佳施镀条件下,可得光亮、致密、耐腐蚀性强于Ａ３钢、磷化膜及Ｎi-P镀层的纳米复合化学镀层,镀层的原子百分组成约为（％）：Ｎi-P-Zn3(PO4)2:Ni70.00,P12.47,Zn3(PO4)213.93,C3.6;Ni-P-ZnSnO3;Ni77.56,P10.00,ZnSnO39.84,C2.6;Ni-P-NiSiO3,Ni83.00,P10.96,ZnSi5.15,C0.89.     

Sol-gel synthesis of K3InF6 and structural characterization of K2InC10O10H6F9, K3InC12O14H4F18 and K3InC12O12F18

K₃InF₆ is synthesized by a sol-gel route starting from indium and potassium acetates dissolved in isopropanol in the stoichiometry 1:3, with trifluoroacetic acid as fluorinating agent. The crystal structures of the organic precursors were solved by X-ray diffraction methods on single crystals. Three organic compounds were isolated and identified: K₂InC₁₀O₁₀H₆F₉, K₃InC₁₂O₁₄H₄F₁₈ and K₃InC₁₂O₁₂F₁₈. The first one, deficient in potassium in comparison with the initial stoichiometry, is unstable. In its crystal structure, acetate as well as trifluoroacetate anions are coordinated to the indium atom. The two other precursors are obtained, respectively, by quick and slow evaporation of the solution. They correspond to the final organic compounds, which give K₃InF₆ by decomposition at high temperature. The crystal structure of K₃InC₁₂O₁₄H₄F₁₈ is characterized by complex anions [In(CF₃COO)₄(OH_x)₂]^(5−2x)− and isolated [CF₃COOH_2−x]^(x−1)− molecules with x=2 or 1, surrounded by K⁺ cations. The crystal structure of K₃InC₁₂O₁₂F₁₈ is only constituted by complex anions [In(CF₃COO)₆]³⁻ and K⁺ cations. For all these compounds, potassium cations ensure only the electroneutrality of the structure. IR spectra of K₂InC₁₀O₁₀H₆F₉ and K₃InC₁₂O₁₂F₁₈ were also performed at room temperature on pulverized crystals.