KCl对Cu-K-La/γ-Al2O3催化剂上HCl氧化反应性能的影响

采用等体积浸渍法制备了Cu-K-La/γ-Al₂O₃催化剂,考察了KCl对该催化剂催化HCl氧化制Cl₂反应性能的影响. 当KCl的负载量为5 wt%时,Cu-K-La/γ-Al₂O₃催化剂表现出较好的催化活性和稳定性,可在较大的原料气空速变化范围内使用. 在0.1 MPa,360 ℃,空速450 L/（kg-cat·h）和HCl/O₂摩尔比为2：1的反应条件下,Cu-K-La/γ-Al₂O₃催化剂上HCl转化率在100 h内保持85%以上. 表征结果表明,Cu,K和La物种均高度分散于γ-Al₂O₃载体表面;一定量KCl的加入可降低Cu²⁺ → Cu⁺的还原温度,从而提高Cu²⁺活性中心的催化活性.     

镍基催化剂上稻草水蒸气重整制富氢合成气

采用浸渍法制备了SiO₂, γ-Al₂O₃, CaO和TiO₂负载的Ni催化剂, 以及不同MgO含量的MgO-7.5%Ni/γ-Al₂O₃催化剂,利用X射线衍射和N₂吸附-脱附技术表征了催化剂的结构,在固定床反应器上评价了它们在稻草水蒸气催化重整制合成气反应中的催化性能,考察了反应条件对催化剂性能的影响.结果表明, 以γ-Al₂O₃为载体时Ni催化剂活性最高,其中7.5%Ni/γ-Al₂O₃催化剂的H₂收率可达1071.3ml/g,H₂:CO的体积比为1.4:1;同时,MgO的添加进一步提高了该催化剂的性能,当MgO含量为1.0%时,H₂收率可达1194.6ml/g,H₂:CO体积比可达3.9:1.可见MgO的加入促进了Ni基催化剂上稻草水蒸气催化重整制合成气反应的进行,同时使得合成气中CO发生水-汽转换反应,从而大大提高了合成气中H₂含量.     

Ni/SiO2-Al2O3催化乙酰丙酸加氢制γ-戊内酯

采用溶胶-凝胶法制备了一系列不同Al₂O₃含量的SiO₂-Al₂O₃复合氧化物,以该系列复合氧化物为载体,采用等体积浸渍法制备了Ni负载量15%（重量百分比）的催化剂,用于催化乙酰丙酸加氢制γ-戊内酯.采用N₂物理吸附、X射线衍射（XRD）、H₂程序升温还原（H₂-TPR）、H₂程序升温脱附（H₂-TPD）、NH₃程序升温脱附（NH₃-TPD）和吡啶吸附红外（Py-IR）等手段对催化剂进行了表征.结果表明,不同载体催化剂的活性组分分散度及表面酸性质存在明显差异,显著影响了催化剂吸附、活化H₂与C=O键的能力,进而影响了催化剂的乙酰丙酸加氢活性.其中,Ni/SiO₂-Al₂O₃催化剂上的L酸中心能够促进C=O键的吸附、活化,与金属Ni上的H₂吸附活性位协同作用,大大提高了乙酰丙酸加氢活性.因此,具有最多L酸中心和丰富H₂吸附活性位的Ni/SiO₂-8Al₂O₃催化剂表现出最高的乙酰丙酸加氢活性,在180℃、4 MPa氢气压力下,乙酰丙酸转化率达到90.5%,目标产物γ-戊内酯选择性为100%.     

Pd/MnOx+Pd/γ-Al2O3整体式催化剂降解地表臭氧

用高锰酸钾与硝酸锰氧化还原反应制备了高活性的氧化锰(MnO_x)催化组分,用胶溶法制备了高比表面积的γ-Al₂O₃载体,分别用等体积浸渍法制备了Pd/MnO_x和Pd/γ-Al₂O₃催化剂,然后将两者机械混合涂覆于堇青石上制得Pd/MnO_x+Pd/γ-Al₂O₃整体式催化剂。采用X射线衍射(XRD)、X射线光电子能谱(XPS)、程序升温还原(H₂-TPR)和低温N₂吸附-脱附对催化剂进行了表征。考察了在300至700℃焙烧MnO_x对催化剂降解地表O₃活性的影响。结果表明,Pd和MnO_x之间存在协同作用;MnO_x焙烧温度对催化剂活性有一定的影响,其中以600℃焙烧时催化剂的活性最高,O₃的起始(12℃)转化率达到88%,完全转化温度为18℃。MnO_x的物相和催化剂表面的吸附氧物种对催化活性影响较大,适当比例的MnO₂和Mn₂O₃共存有利于O₃分解,表面吸附氧为O₃分解的活性氧物种。     

Pt/ZrO2-Al2O3催化剂催化氧化C3H6和CO性能

采用共沉淀法合成了ZrO₂与Al₂O₃的不同质量比的ZrO₂-Al₂O₃复合氧化物,并以此为载体通过等体积浸渍法制备了1.5% Pt/ZrO₂-Al₂O₃（w/w）催化剂。以C₃H₆和CO为反应物的催化性能评价显示,在系列催化剂中以Pt/Zr（0.4）-Al₂O₃催化剂催化氧化活性最为优异,其C₃H₆和CO的起燃温度（T₅₀）小于125℃,完全转化温度（T₉₀）小于150℃。采用XRD、低温N₂吸附、H2-TPR、CO脉冲吸附等分析表征技术探索了催化剂物相结构、比表面积、颗粒尺寸等对催化活性的影响规律。结果发现,ZrO₂-Al₂O₃复合氧化物具有Al₂O₃材料的介孔织构和大比表面积特性,且产生了Al_xZr_1-xO_y固溶体新物相。适当的ZrO₂与Al₂O₃的质量比,是改善Pt与ZrO₂-Al₂O₃的相互作用强度,促进贵金属Pt的分散,提升Pt/ZrO₂-Al₂O₃催化剂的低温氧化活性的关键。     

K2CO3含量对Ni-Cu-Mn-K/Al2O3水煤气变换催化剂结构和性能的影响

以γ-Al₂O₃为载体，采用等体积浸渍法，制备了不同K₂CO₃含量的Ni-Cu-Mn-K/Al₂O₃水煤气变换催化剂，采用低温N₂吸附、XRD、TPD和TPR，考察了K₂CO₃含量对催化剂结构和性能的影响。结果表明:K₂CO₃的加入使催化剂的还原温度有所提高，适量的K₂CO₃能增加活性组分的电子密度，从而增强其给电子活化CO的能力，提高催化剂的活性。但过量的K₂CO₃使得催化剂比表面积和孔容降低，且导致催化剂对CO吸附过强，催化活性降低。当Ni-Cu-Mn-K/γ-Al₂O₃催化剂中K₂CO₃的添加量为7.5%时，且催化剂经530 ℃耐热15 h后，在350 ℃时水煤气变换反应中CO转化率达62.29%。     

Pt/ZrO2-Al2O3催化剂催化氧化C3H6和CO性能

采用共沉淀法合成了ZrO₂与Al₂O₃的不同质量比的ZrO₂-Al₂O₃复合氧化物,并以此为载体通过等体积浸渍法制备了1.5% Pt/ZrO₂-Al₂O₃（w/w）催化剂。以C₃H₆和CO为反应物的催化性能评价显示,在系列催化剂中以Pt/Zr（0.4）-Al催化剂催化氧化活性最为优异,其C₃H₆和CO的起燃温度（T₅₀）小于125℃,完全转化温度（T₉₀）小于150℃。采用XRD、低温N₂吸附、H₂-TPR、CO脉冲吸附等分析表征技术探索了催化剂物相结构、比表面积、颗粒尺寸等对催化活性的影响规律。结果发现,ZrO₂-Al₂O₃复合氧化物具有Al₂O₃材料的介孔织构和大比表面积特性,且产生了Al_xZr_1-xO_y固溶体新物相。适当的ZrO₂与Al₂O₃的质量比,是改善Pt与ZrO₂-Al₂O₃的相互作用强度,促进贵金属Pt的分散,提升Pt/ZrO₂-Al₂O₃催化剂的低温氧化活性的关键。     

选择氧化物载体调变乙醇重整和1,3-丁二烯加氢反应双金属催化剂

研究了不同载体负载的Pt-Ni双金属和单金属催化剂上乙醇重整和1,3-丁二烯加氢反应性能, 以考察氧化物载体对双金属结构和催化活性的影响. 所用的氧化物载体包括γ-Al₂O₃, SiO₂, TiO₂, CeO₂以及高比表面积(HSA)和低比表面积(LSA)ZrO₂. 采用共浸渍法制备催化剂, 用CO化学吸附、透射电镜和扩展X射线吸收精细结构光谱进行催化剂表征, 采用傅里叶变换红外间歇反应器进行化学反应评价. 对于乙醇重整反应, Pt-Ni双金属催化剂优于单金属催化剂, Pt-Ni双金属催化剂活性顺序为TiO₂ > SiO₂ > γ-Al₂O₃ ≈ LSA-ZrO₂ > CeO₂ > HSA-ZrO₂. 对于1,3-丁二烯加氢反应, 在SiO₂, TiO₂和HSA-ZrO₂载体上双金属催化剂优于单金属催化剂, Pt-Ni双金属催化剂活性顺序为SiO₂ > CeO₂ > γ-Al₂O₃ > LSA-ZrO₂ > HSA-ZrO₂ ≈ TiO₂.     

Ni2+在γ-Al2O3上的分散状态及负载型Ni/γ-Al2O3催化剂的α-蒎烯加氢活性

用X-射线衍射(XRD)、紫外-可见漫散射光谱(UV-Vis DRS)、程序升温还原(TPR)、CO化学吸附和微反测试等方法研究了Ni²⁺在γ-Al₂O₃上的分散状态和负载型Ni/γ-Al₂O₃催化剂的α-蒎烯加氢催化活性。结果表明，当Ni²⁺负载量远低于其在γ-Al₂O₃载体表面分散容量时，Ni²⁺优先嵌入载体表面四面体空位，随着Ni²⁺负载量的增加，嵌入载体表面八面体空位Ni²⁺的比例增大。由于八面体Ni²⁺易被还原为金属态Ni⁰，NiO/γ-Al₂O₃样品的还原度随Ni²⁺负载量的增加而大幅度地增加，经氢还原所得Ni/γ-Al₂O₃催化剂的CO吸附量和α-蒎烯加氢催化活性大幅度增加。对La₂O₃助剂的作用进行了研究，结果表明分散在γ-Al₂O₃上的La³⁺物种可阻止Ni²⁺嵌入γ-Al₂O₃表面四面体空位，增大了八面体Ni²⁺物种所占比例，提高了催化剂的还原度，故Ni-La₂O₃/γ-Al₂O₃催化剂催化活性高于Ni/γ-Al₂O₃催化剂。     

面向异丁烷脱氢介孔γ-Al2O3基催化剂的合成及其高催化性能

采用溶剂蒸发自组装法调控载体形貌及孔道结构,成功制备了有序介孔氧化铝载体。以铬氧物种为活性组分,碱金属钾为助剂,采用浸渍法制备负载型催化剂,用于异丁烷催化脱氢反应,研究了反应温度、原料流速、催化剂粒径等因素对催化性能的影响。采用X射线粉末衍射、透射电子显微镜、N₂物理吸附、氢气程序升温还原及热重等表征方法探讨了载体形貌、孔道结构与催化性能的构效关系,结果表明,低温下有利于控制异丙醇铝的水解和缩合及介孔γ-Al₂O₃的研制。与常规的γ-Al₂O₃相比,所制备的介孔γ-Al₂O₃的有更大的比表面积和良好的有序性,在600℃、101.325kPa、GHSV=1 000 h^-1的条件下,10%（w/w）Cr₂O₃/γ-Al₂O₃催化剂性能最佳,异丁烷的转化率达63.1%,异丁烯的选择性达到85.5%。与传统的催化剂相比,介孔Cr₂O₃/γ-Al₂O₃催化剂具有大的比表面积,高度分散的活性组分,优良的催化性能和良好的抗积碳能力。     

柠檬酸添加方式对Mo-Ni-P/Al_2O_3催化剂加氢活性的影响

以Mo、Ni为活性组分,Al_2O_3为载体,采用不同柠檬酸添加方法制备了Mo-Ni-P/Al_2O_3催化剂.通过氢气程序升温还原(H2-TPR)、X射线衍射(XRD),透射扫描电镜(TEM)、XPS等表征方法研究催化剂的物化性质.结果表明:催化剂经柠檬酸的后处理,改善了载体氧化铝表面羟基基团的分布,促使Mo物种以八面体配位多核聚钼酸的形态存在,有效地减弱了载体与活性金属之间的强相互作用,提高了Mo物种的分散度与硫化度,使得催化剂形成更多"Mo-Ni-S"加氢活性相,提高了催化剂的加氢活性.与其他处理方法相比,柠檬酸后处理的催化剂对VGO具有更高的加氢脱硫、脱氮与芳烃饱和性能.     

Highly active CoMo HDS catalyst for the production of clean diesel fuels

HY–Al₂O₃-supported CoMo catalysts with a chelating agent and phosphorus for the hydrodesulfurization (HDS) of diesel fractions were prepared. The activity measurements with the prepared catalysts were carried out with straight-run light gas oil feedstocks in a pilot plant under industrial hydrotreating conditions. As a result, Cosmo Oil Co., Ltd. developed a new CoMoP/HY–Al₂O₃ catalyst, C-606A, which had three times higher HDS activity than the conventional CoMoP/Al₂O₃ catalyst. Commercial operations to produce ultra-low sulfur diesel (ULSD) with C-606A have successfully demonstrated its high performance and high stability. This catalyst has an extremely high activity, which enables to achieve <10-ppm sulfur in products in diesel hydrotreater designed to produce 500-ppm sulfur diesel fuels. Mo K-edge EXAFS, TEM and FT-IR of adsorbed NO were performed to investigate the nature of the active sites on the developed catalysts. The results showed that the new catalyst has multiple layers of MoS₂ slabs and the edges of MoS₂ are mainly occupied by Co–Mo–S phases. XPS and FT-IR were used to investigate the sulfiding behavior of Co and Mo in the formation process of the active sites during sulfidation. The results showed that addition of carboxylic acid to the impregnation solution postponed the sulfidation of Co at low temperatures, thereby increasing formation of the Co–Mo–S phase.     

Influence of Pd-Ce interaction and chlorine ion on hydrodesulfurization reaction: The activity and sulfur tolerance of the Pd-Ceo2/Al2O3 catalyst

CeO₂ promoted palladium catalysts supported on Al₂O₃ were prepared using the impregnation (IM) and the deposition-precipitation (DP) methods. The activities and sulfur tolerance of the catalysts for hydrodesulfurization (HDS) were detected with thiophene HDS as probe reaction. H₂ adsorption, XRD, FTIR, NH₃-TPD, XPS were used to characterize the catalysts. The Pd-CeO₂/Al₂O₃ (IM) catalyst was highly active for the HDS reaction, and it had much stronger sulfur tolerance than the Pd/Al₂O₃ catalyst. Pd-CeO₂/Al₂O₃ (DP) showed excellent sulfur tolerance while its initial activity decreased. It was observed that with the chlorine bridge, the interfacial structure of Pd-Cl⁻¹-Ce³⁺ was responsible for the high activity of the Pd-CeO₂/Al₂O₃ (IM) catalyst, at the same time the interaction of Pd with Ce was weakened by Cl₋₁ ions. The enhanced sulfur tolerance over the Pd-CeO₂/Al₂O₃ (IM) catalyst was attributed to the weakened Pd-S bond caused by the competitive adsorption of H₂S on Ce³⁺ ions. As to the Pd-CeO₂/Al₂O₃ (DP) catalyst, a strong interaction of Pd with Ce put Pd at an electron-deficient state, the creation of sulfided palladium was therefore inhibited.     

Decomposition of molybdate–hexamethylenetetramine complex: One single source route for different catalytic materials

Decomposition of ammonium heptamolybdate–hexamethylentetramine (HMTA) complex (HMTA)₂(NH₄)₄Mo₇O₂₄·2H₂O was studied as a function of treatment conditions in the range 300–1173 K. The evolution of solid products during decomposition was studied by thermal analysis and in situ EXAFS. Depending on the nature of the gas used for treatment, single phases of highly dispersed nitrides Mo₂N, carbide Mo₂C, or oxide MoO₂ can be obtained. The nature of the products obtained was explained by qualitative thermodynamical considerations. Morphology of the solids considerably depends on such preparation parameters as temperature and mass velocity of the gas flow. For the nitride-based materials, catalytic activity was evaluated in the model thiophene HDS reaction. It was demonstrated that NH₃-treated samples showed better catalytic activity than N₂-treated ones due to cleaner surface and better morphology. Transmission microscopy, XRD and XPS studies showed that MoS₂ is formed on the surface during HDS reaction or sulfidation with H₂S. Optimized nitride-derived catalysts showed mass activity several times higher than unsupported MoS₂ or MoS₂/Al₂O₃ reference catalyst.     

NiMo催化剂载体中纳米HY分子筛和氧化铝混合方式对柴油加氢脱硫性能的影响

以纳米HY分子筛-氧化铝混合物为载体,根据两者混合方式的不同（溶胶凝胶法和机械混合法）制备了两种NiMo加氢脱硫催化剂,并对其进行了XRD、BET、TPD、H₂-TPR、HRTEM和FT-IR等表征。与溶胶凝胶法催化剂相比,机械混合法催化剂表现出了较好的纹理结构和更高酸量,其金属相更易还原,边角位Mo原子的分散度更高,表现出了更高的加氢脱硫性能。但溶胶凝胶法催化剂的type-Ⅱ Ni-Mo-S活性相前驱物比例更高,MoS₂晶片长度更大,堆垛程度更高,活性组分分散度较差。虽然溶胶凝胶法有利于提高type-Ⅱ Ni-Mo-S活性相前驱物比例,但是该方法导致的较差孔结构抑制了这种优势,并且降低了活性组分分散度,减弱了催化活性。     

Comparison of the quantity and reactivity of carbon deposit arising on Mo/Al2O3 and Mo/ZrO2 catalysts

The quantity and reactivity of carbon deposit arising on Mo/Al₂O₃ and Mo/ZrO₂ catalysts in propane decomposition was investigated. Results showed that the Mo/ZrO₂ catalyst is more resistant to carbon deposit formation process. The coke formed on the surface of this catalyst is more reactive in oxygen atmosphere than the carbon deposit formed under the same conditions on Mo/Al₂O₃. This revised version was published online in June 2006 with corrections to the Cover Date.     

超声改性的CuO/Al2O3-MgO催化剂结构 及其超低浓度甲烷催化燃烧性能

采用普通浸渍和超声改性的方法分别制备了CuO/Al₂O₃-MgO催化剂,用于超低浓度甲烷的催化燃烧,并利用SEM、XRD、XPS、H₂-TPR等技术对催化剂进行表征,研究了超声改性作用对催化剂的结构和性能的影响.结果表明,与普通浸渍法制备的催化剂相比,在超声改性的CuO/Al₂O₃-MgO催化剂上,甲烷的转化率得到提高,燃烧特征温度降低.随着超声时间的延长和超声功率的增加,催化剂的催化活性均呈现先增大后减小的趋势;催化剂制备的最佳超声工况为功率150 W、时间20 min.超声改性可使催化剂的比表面积和孔容积增大,表面催化活性较高的Cu⁺浓度增加,活性组分CuO由晶相向非晶相转变、分散度增大,晶粒粒径变小、分布更均匀;这使得甲烷催化燃烧的表观活化能下降、催化剂活性得到增强.     

Influence of the activation temperature on structural and textural properties of NiMo/Al2O3 hydrodesulfurization catalysts

Investigations of a commercial NiMo/Al₂O₃ hydrodesulfurization (HDS) catalyst are directed towards optimization of the activation procedure of HDS catalyst concerning active phase formation and thermal stability. Structural and textural data obtained with XRD, IR-FTIR, XPS and LTNA reveal that the optimal temperature for the formation of active species on the catalyst surface and an appropriate pore structure is 300°C.     

Improvement of HDS catalysts through the modification of the oxidic precursor with 1,5-pentanediol: Gas phase sulfidation and thiophene conversion

The performance, in thiophene HDS, of a CoMo/Al₂O₃ catalyst was successfully improved through chemical modification of its oxidic precursor by impregnation with 1,5-pentanediol solution. The gas phase activation with a H₂/H₂S mixture was followed by thermogravimetric analysis coupled with a rapid chromatograph; the catalysts were characterized at different steps of the activation using X-ray photoelectron spectroscopy (XPS). It appeared that the addition of the organic agent retards the sulfidation of the supported metals, leading to a simultaneous sulfidation of Co and Mo atoms. This induces the formation of smaller MoS₂ slabs and thus an increase in the number of active CoMoS sites, directly correlated with the better HDS performance of the modified solid. The role of 1,5-pentanediol is likely to inhibit, at low temperature, the adsorption of H₂S on the solid and thus the sulfidation of the supported metals.     

Preparation of MoO3/g-Al2O3 catalyst by the reaction of a-boehmite with MoO3/H2O slurry - dual role of MoO3 as active phase and texture stabilizer during calcination

Summary Catalyst MoO₃/g-Al₂O₃ was prepared by the reaction of a-boehmite with molybdic acid in slurry MoO₃/H₂O followed by calcination. The deposited MoO₃ functioned as thermal stabilizer and inhibited sintering of Al₂O₃ phase during calcination. After calcination at 550 and 650^oC the surface area of Al₂O₃ obtained from a-boehmite was 207 and 172 m² g^-1, respectively, and of MoO₃/Al₂O₃ obtained from MoO₃/a-boehmite was 323 and 285 m² g^-1, respectively. On the other hand, molybdic acid did not work as peptization agent and the mechanical strength of MoO₃/Al₂O₃ was not higher than of Al₂O₃. The catalyst was sulfided and its activity in thiophene hydrodesulfurization was tested; it exhibited about the same activity as reference industrial MoO₃/Al₂O₃ catalyst.