镧助剂对Fe/ZrO2催化剂结构及F-T反应性能的影响

用ＸＲＤ，Ｍｏｓｓｂａｕｅｒ谱，ＴＰＲ，ＣＯ－ＴＰＤ和ＣＯ加氢反应性能测试等手段研究了镧助剂对Ｆｅ／ＺｒＯ２催化剂结构及Ｆ－Ｔ合成催化剂性能的影响。结果表明，不同的制备方法明显影响催化剂的结构及反应的性能，镧助剂以Ｌａ２Ｏ３形式存在时，催化剂上甲烷选择降低，烯烃选择性提高；镧助剂以ＬａＦｅＯ３形式存在时，催化剂的催化活性大大提高，但同时甲烷选择性上升，烯烃选择性下降。     

CO／H2合成甲醇CuO—ZnO—ZrO2催化剂的研究

通过活性测定，ＸＲＤ、ＴＧ－ＤＴＡ表征，考察了共沉淀法制备的铜锌锆合成甲醇催化剂中ＺｒＯ２对物相结构、催化活性及热稳定性的影响。结果表明，ＺｒＯ２能显著提高ＣＯ／Ｈ２合成甲醇的催化活性和热稳定性。催化剂母体、氧化态和还原态的物相并未发生变化，仍分别为：Ｃｕ２（ＯＨ）３ＮＯ３，（Ｃｕ，Ｚｎ）５（ＣＯ３）２（ＯＨ）６，（Ｃｕ，Ｚｎ）２ＣＯ３（ＯＨ）２，Ｚｎ５（ＣＯ３）２（ＯＨ）６；ＣｕＯ、ＺｎＯ；Ｃｕ     

锰助剂对Fe／ZrO2催化剂F—T反应催化性能的影响

应用ＸＲＤ，ＸＰＳ，Ｍｏｓｓｂａｕｅｒ谱，ＴＰＲ，ＣＯ化学吸附ＣＯ－ＴＰＤ，ＣＯ＋Ｈ２反应性能测试等手段研究了锰助剂对Ｆ－Ｔ合成制低碳烯烃Ｍｎ－Ｆｅ／ＺｒＯ２催化剂结构及催化性能的影响。结果表明，与Ｆｅ／Ｚｒ催化相比，加锰助剂后的催化剂Ｆ－Ｔ反应催化活性上升，甲烷选择性降低，低碳烯烃选择性增加。     

氧化铈对F-T反应铁锆催化剂的助催化作用

应用ＸＲＤ、ＸＰＳ、Ｍｏｓｓｂａｕｅｒ谱、ＴＰＲ、ＣＯ－ＴＰＤ、ＣＯ＋Ｈ２反应性能测量试等手段研究了ＣｅＯ２对Ｆ－Ｔ合成制低碳烯烃Ｃｅ－Ｆｅ／ＺｒＯ２催化剂催化性能的影响。结果表明，与Ｆｅ／Ｚｒ催化剂相比，加铈助剂后的催化剂Ｆ－Ｔ反应催化活性明显上升。     

合成醇用负载型铜基催化剂的表征

采用ＸＲＤ，ＴＧ－ＤＴＡ－ＤＳＣ，ＣＯ－ＴＰＤ和Ｈ２－ＴＰＤ等技术，对三种负载型铜基催化剂的表征载基合成醇用催化剂进行了表征。结果表明，Ｆｅ组分的存在有利于ＣｕＯ晶相的形成，     

预处理条件对用于CO_2加氢的超细CuO－ZnO－SiO_2催化剂性能的影响

采用ＸＲＤ、ＢＥＴ、ＴＰＲ手段，研究了焙烧和还原温度对超细ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂的性质及其ＣＯ２加氢反应催化活性的影响．胶体在５７３－７７３Ｋ范围内焙烧生成ＣｕＯ、Ｃｕ２Ｏ、ＺｎＯ晶相，随着焙烧温度继续升高，ＣｕＯ和ＺｎＯ晶粒逐渐变大，但催化剂的比表面积和孔容变化很小．在９７３Ｋ焙烧后出现Ｚｎ２ＳｉＯ４晶相，使催化剂比表积和孔容变小，导致催化剂活性降低．焙烧温度对催化剂活性的影响大于对ＣＯ２加氢产物分布的影响．在５４８－６４８Ｋ范围内，催化剂还原温度对其催化活性影响不大．７０３Ｋ高温还原后，可能由于Ｃｕ０晶粒的出现，使得催化剂的活性下降．ＴＰＲ研究结果进一步表明，焙烧温度影响ＣｕＯ同ＺｎＯ、ＳｉＯ２之间的相互作用和催化剂的还原行为．     

制备高碳醇用Cu－Fe系催化剂的活性相

用共沉淀法制备了Ｃｕ－Ｆｅ系催化剂，它是由脂肪酸甲酯加氢制备高碳醇的新催化体系．催化剂经焙烧后的物相为ＣｕＯ，γ－Ｆｅ２Ｏ３和ＭｇＯ，形成了活性相的结构前驱．在反应条件下，ＣｕＯ首先被还原为金属态的Ｃｕ０，然后γ－Ｆｅ２Ｏ３被还原为Ｆｅ３Ｏ４；Ｃｕ０和Ｆｅ３Ｏ４共同参与催化该反应．本文用ＸＲＤ，ＴＧ－ＤＴＡ和Ｍｏｓｓｂａｕｅｒ谱等手段，结合催化剂的活性测定，确定了催化剂的活性相为Ｃｕ０和Ｆｅ３Ｏ４；ＭｇＯ可改变催化剂的电子结构和几何构型，起到重要的助催化作用     

助剂对超细CuO－ZnO－SiO_2催化剂性质和CO_2加氢反应性能的影响

研究了９种助剂对用于ＣＯ２加氢反应的超细ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂性能的影响，并进行了ＸＲＤ和ＴＰＲ表征．结果表明，助剂影响超细催化剂的性质和催化性能，ＴｉＯ２、ＣｅＯ２、ＭｇＯ和Ｌａ２Ｏ３是ＣＯ２加氢合成甲醇的超细ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂体系的优良助剂．在含有不同助剂的ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂体系内存在ＣｕＯ和ＺｎＯ晶相，但除ＣｅＯ２以外，其它的助剂都可能以微晶或无定型的形式存在．ＴＰＲ研究表明，添加的助剂除ＣｅＯ２以外，都使超细ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂的还原温度提高，而且助剂对ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂活性的影响，按照助剂对ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂还原温度的影响进行了探讨     

Rh—Mo—K／Al2O3催化剂的CO加氢合成低碳醇性能

本文研究了硫化态和还原态Ｒｈ－Ｍｏ－Ｋ／Ａｌ２Ｏ３催化剂上ＣＯ加氢合成低碳醇的反应性能，考察了不同铑负载量、钾助剂、合成气组成和反应条件（温度、压力和空速）对合成醇性能的影响及催化剂的反应稳定性。发现硫化样品较之还原态样品具有更好的合成醇选择性，催化剂中添加铑后，生成醇活性和选择性大幅度提高。选择合适的反应温度、提高反应压力和空速、适当增加合成气Ｈ２／ＣＯ的比例可以获得较好的合成醇反应性能。     

助剂钾对二氧化碳加氢反应活性及产物分布的影响

报导助剂Ｋ对Ａｌ２Ｏ３，ＴｉＯ２，ＺｒＯ２担载Ｆｅ催化剂，用于ＣＯ２加氢合成Ｃ２＋烃的催化活性及产物分布的影响。与不含Ｋ的催化剂相比，Ｋ的存在导致Ｆｅ／Ｋ－Ａｌ２Ｏ３的催化活性及Ｃ＾２＋烃选择性明显提高，但使Ｆｅ／Ｋ－ＴｉＯ２的催化活性及Ｃ２＋烃选择性显著下降，而对Ｆｅ／Ｋ－ＺｒＯ２，这种影响并不显著。Ｋ的明显有利于低碳烯烃的生存。     

铬掺杂对V2O5/TiO2催化氧化3-甲基吡啶合成烟酸性能的影响

为进一步提高V2O5/TiO2催化剂对气相一步催化合成烟酸反应的活性和选择性.通过浸渍法制备一系列掺杂过渡金属铬的V2O5/TiO2催化剂,并对催化剂进行了BET、XRD、H2-TPR、NH3-TPD表征.结果表明,掺杂Cr后催化剂产生了新晶相CrVO4,减小了V2O5晶粒尺寸,并提高了催化剂的酸性,可较大地提高催化剂...     

钒元素在铬铝丙烷氧化脱氢催化剂中的助催化作用

研究了丙烷在以钒元素为助剂的Ｃｒ－Ａｌ－Ｏ催化剂上的氧化脱氢反应性能，利用ＸＲＤ、ＤＲＳ、ＸＰＳ等方法，讨论了钒元素的助催化作用，实验结果表明，钒元素的添加，使得催化剂表面产生Ｏ物种，并且可以改变催经上表面组成，提高催化剂表面Ｃｒ＾３＋的浓度，从而影响催化剂的氧化脱氢活性。     

V2O5／TiO2催化剂的表面结构和酸碱性及氧化还原性

 研究了一系列锐钛矿担载的钒氧化物催化剂的表面性质．X射线衍射和Raman光谱表明，8％V2O5／TiO2催化剂上的V2O5处于单层分散状态．程序升温还原研究表明，单层分散的钒物种较易被还原，而形成多聚态和晶态后钒物种的还原温度升高．NH3吸附量热结果表明，在钒物种达到单层分散前，催化剂的表面酸性随钒担载量的增加而减弱，超过单层分散后，表面酸位的数目和强度基本不变．异丙醇脱氢／脱水反应结果表明，有O2时V2O5／TiO2催化剂显示出很强的氧化还原性，无O2时催化剂的脱水选择性较高．通过异丙醇的脱氢／脱水反应，将V2O5／TiO2催化剂的表面结构与其酸碱性和氧化还原性进行了初步的关联．     

The co-effect of Sb and Nb on the SCR performance of the V2O5/TiO2 catalyst

The effect of the Sb and Nb additives on the V(2)O(5)/TiO(2) catalyst for the selective catalytic reduction (SCR) of NO with NH(3) was investigated. The experimental results show that either Nb or Sb can improve the activity of V(2)O(5)/TiO(2) catalyst. Higher Nb loading led to higher N(2) selectivity. The co-doping of Sb and Nb showed higher improving effect than the single doping of Sb or Nb. The V(2)O(5)/TiO(2) catalyst doped with Sb and Nb had a better H(2)O resistance than the V(2)O(5)/TiO(2) catalyst. The addition of Sb and Nb also enhance the resistance of the V(2)O(5)/TiO(2) catalyst to K(2)O poisoning. The catalysts were characterized by BET, XRD, TEM, and XPS. The results showed that the active components of V, Sb, and Nb were well interacting with each other. The coexistence of Sb and Nb will enhance the redox ability and surface acidity and thus promote the SCR performance.     

TiO_2-Supported Binary Metal Oxide Catalysts for Low-temperature Selective Catalytic Reduction of NO_x with NH_3

Binary metal oxide（MnOx-A/TiO2）catalysts were prepared by adding the second metal to manganese oxides supported on titanium dioxide（TiO2）,where,A indicates Fe2O3,WO3,MoO3,and Cr2O3.Their catalytic activity,N2 selectivity,and SO2 poisonous tolerance were investigated.The catalytic performance at low temperatures decreased in the following order：Mn-W/TiO2〉Mn-Fe/TiO2〉Mn-Cr/TiO2〉Mn-Mo/TiO2,whereas the N2 selectivity decreased in the order：Mn-Fe/TiO2〉Mn-W/TiO2〉Mn-Mo/TiO2〉Mn-Cr/TiO2.In the presence of 0.01%SO2 and 6%H2O,the NOx conversions in the presence of Mn-W/TiO2,Mn-Fe/TiO2,or Mn-Mo/TiO2 maintain 98.5%,95.8%and 94.2%, respectively,after 8 h at 120°C at GHSV 12600 h？ 1 .As effective promoters,WO3 and Fe2O3 can increase N2 selectivity and the resistance to SO2 of MnOx/TiO2 significantly.The Fourier transform infrared（FTIR）spectra of NH3 over WO3 show the presence of Lewis acid sites.The results suggest that WO3 is the best promoter of MnOx/TiO2,and Mn-W/TiO2 is one of the most active catalysts for the low temperature selective catalytic reduction of NO with NH3.     

甲苯气相选择氧化制苯甲醛 Ⅳ.助剂锂、钾、铯对V_2O_5/TiO_2催化剂性能的影响

在Ｖ２Ｏ５／ＴｉＯ２催化剂中分别添加Ｌｉ、Ｋ、Ｃｓ等碱金属离子，利用ＢＥＴ、ＸＲＤ、ＸＰＳ、Ｈ２－ＴＰＲ、Ｏ２－ＴＰＤ－ＭＳ和化学分析方法，研究了催化剂结构和性能的变化．结果表明，催化剂在添加不同碱金属离子后，其结构和表面活性氧发生了很大变化．Ｋ离子可以改善催化剂的活性、提高反应选择性；Ｌｉ离子能提高催化剂活性，但在相当宽的温度范围内使反应选择性下降；在６９３Ｋ以下，Ｃｓ离子对催化剂的活性和选择性均起抑制作用．     

Effect of CeO2 and CaO Promoters on Ignition Performance for Partial Oxidation of Methane over Ni/MgO-Al2O3 Catalyst

The effect of CeO2 and CaO promoters on the ignition performance over Ni/MgO-Al2O3 catalyst for the partial oxidation of methane （POM） to synthesis gas was investigated. It was found that the POM reaction could not be ignited over lwt%Ni/MgO-Al2O3 catalyst without the promoters in the temperature range from 773 K to 1073 K. CeO2 and CaO promoters enhanced the ignition performance and the POM reactivity of lwt%Ni/MgO-Al2O3 catalyst remarkably. Moreover, the improving effect became greater with the increase of the promoter content under the investigated reactiorrconditions. The modification effects of CeO2 and CaO promoters were closely related to the concentration and reducibility of the surface and bulk oxygen species.     

甲苯气相选择氧化制苯甲醛：Ⅱ.锑对V2O5／TiO2催化剂结构及反应性能的影响

Ｖ_２Ｏ_５／ＴｉＯ_２体系引入Ｓｂ后催化剂的活性受到抑制，但苯甲醛选择性有所提高．在Ｓｂ／Ｖ＝０．０８（原子比），反应温度６７３Ｋ，氧浓度７％，空速１４０００ｈ~（－１）时，甲苯转化率为２２．８％，苯甲醛选择性６９．７％，产率为１５．９％．运用ＸＲＤ、ＴＰＲ、ＴＰＤ考察了助剂锑对Ｖ_２Ｏ_５／ＴｉＯ_２催化剂体系的体相结构，表面酸碱性及其还原性能的影响．结果表明，Ｓｂ的引入有利于Ｖ_２Ｏ_５的分散，催化剂表面酸中心数目减少，强度减弱，及Ｖ_２Ｏ_５还原温度提高，而表面高分散的Ｖ_Ｏ_５还原峰随Ｓｂ添加量增加出现极大值，反应过程也能够使Ｖ_２Ｏ_５更分散，有利于甲苯的选择氧化．     

SiO2改性的V2O5-MoO3/ TiO2催化剂抗碱中毒性能研究

以陶瓷为骨架,用溶胶凝胶法和浸渍法制备了V₂O₅-MoO₃/ TiO₂催化剂,并用SiO₂进行改性。采用浸渍法模拟碱K中毒,研究了SiO₂改性前后催化剂中毒脱硝效率的变化,并通过BET、H₂-TPR、NH₃-TPD等技术手段对催化剂进行了表征。结果表明,加入SiO₂后,催化剂的比表面积明显提高。SiO₂改性后新鲜催化剂还原温度向低温方向迁移10 ℃左右,氧化还原能力得到了提高,其表面酸强度和酸量也得到较大的提高。反应评价结果表明,SiO₂改性可以提高催化剂抗碱中毒的性能。     

高能机械球磨法制备V-Ti-O超细微粒催化剂

负载型V2O5/TiO2氧化物催化剂因具有优良的催化性能而广泛地用于烃类选择性氧化[1,2]和氮氧化物选择性催化还原(SCR)[3]. 迄今,所研究的负载型V2O5/TiO2氧化物催化剂大多是采用浸渍法制备的[2,4～6],通过调整催化剂的组成[2,5]、引入适当的助剂组分[2,6]和选择适宜的反应操作条件[2,5]可进一步优化其催化性能.