Phase relations, crystal chemistry, and dielectric properties in sections of the La2O3-CaO-MgO-TiO2 system

Subsolidus phase equilibria and crystal chemistry were studied for the La₂O₃-MgO-TiO₂ system and for the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃ in the quaternary La₂O₃-CaO-MgO-TiO₂ system. Dielectric properties (relative permittivity and temperature coefficient of resonant frequency, τ_f) were measured at 5-10 GHz and mapped onto the phase equilibria relations to reveal the compositions of temperature-stable (τ_f=0) compounds and mixtures. Phase equilibria relations were obtained by X-ray powder diffraction analysis of approximately 80 specimens prepared by solid-state reactions in air at ∼1450°C. Six ternary phases were found to form in the La₂O₃-MgO-TiO₂ system, including the three previously reported compounds LaMg_1/2Ti_1/2O₃, La₅Mg_0.5Ti_3.5O₁₅, and “La₆MgTi₄O₁₈”; and the new phases La₁₀MgTi₉O₃₄, La₉Mg_0.5Ti_8.5O₃₁, and a perovskite-type solid solution (1−x)LaMg_1/2Ti_1/2O₃-xLa_2/3TiO₃ (0?x?0.5). The phase previously reported as “La₆MgTi₄O₁₈” was found to form off-composition, apparently as a point compound, at La₆Mg_0.913Ti_4.04O₁₈. Indexed experimental X-ray powder diffraction patterns are given for LaMg_1/2Ti_1/2O₃, La₅Mg_0.5Ti_3.5O₁₅, La₆Mg_0.913Ti_4.04O₁₈, La₁₀MgTi₉O₃₄, and La₉Mg_0.5Ti_8.5O₃₁. LaMg_1/2Ti_1/2O₃ exhibits a slightly distorted perovskite structure with ordered B-cations (P2₁/n; a=5.5608(2) Å, b=5.5749(3) Å, c=7.8610(5) Å, β=90.034(4)°). La₅Mg_0.5Ti_3.5O₁₅ (Pm1; a=5.5639(1), c=10.9928(5) Å) and La₆Mg_0.913Ti_4.04O₁₈ (R3m; a=5.5665(1), c=39.7354(9) Å) are n=5 and n=6 members, respectively, of the (111) perovskite-slab series A_nB_n−1O_3n. The new phases La₁₀MgTi₉O₃₄ (a=5.5411(2), b=31.3039(9), c=3.9167(1) Å) and La₉Mg_0.5Ti_8.5O₃₁ (a=5.5431(2), b=57.055(1), c=3.9123(1) Å) are n=5 and n=4.5 members, respectively, of the (110) perovskite-slab series A_nB_nO_3n+2, which exhibit orthorhombic subcells; electron diffraction revealed monoclinic superlattices with doubled c-parameters for both compounds. Extensive perovskite-type solid solutions form in the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃. The La₂O₃-MgO-TiO₂ system contains two regions of temperature-stable (τ_f=0) compositions. The quaternary La₂O₃-CaO-MgO-TiO₂ system contains an extensive single-phase perovskite-type volume through which passes a surface of temperature-stable compositions with permittivities projected to be in the 40-50 range. Traces of this surface occur as lines of τ_f=0 perovskite-type phases in the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃.     

Synthesis and properties of the double perovskites La2NiVO6, La2CoVO6, and La2CoTiO6

The double perovskites La₂CoVO₆, La₂CoTiO₆, and La₂NiVO₆, are described. Rietveld fitting of neutron and powder X-ray diffraction data show La₂NiVO₆ and La₂CoVO₆ to have a disordered arrangement of B-cations whereas La₂CoTiO₆ shows ordering of the B-cations (with ∼5% Co/Ti inversion). Curie-Weiss fits to the linear region of the 1/χ plots reveal Weiss temperatures of −107, −34.8, and 16.3 K for La₂CoVO₆, La₂CoTiO₆, and La₂NiVO₆, respectively, and magnetic transitions are observed. La₂CoTiO₆ prepared by our method differs from material prepared by lower-temperature routes. A simple antiferromagnetic spin model is consistent with the data for La₂CoTiO₆. These compounds are semiconductors with bandgaps of 0.41 (La₂CoVO₆), 1.02 (La₂CoTiO₆) and 0.45 eV (La₂NiVO₆).     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

Structural change of layered perovskite La2Ti2O7 at high pressures

The perovskite-related layered structure of La₂Ti₂O₇ has been studied at pressures up to 30 GPa using synchrotron radiation powder X-ray diffraction (XRD) and Raman scattering. The XRD results indicate a pronounced anisotropy for the compressibility of the monoclinic unit cell. The ratio of the relative compressibilities along the [100], [010] and [001] directions is ∼1:3:5. The greatest compressibility is along the [001] direction, perpendicular to the interlayer. A pressure-induced phase transition occurs at 16.7 GPa. Both Raman and XRD measurements reveal that the pressure-induced phase transition is reversible. The high-pressure phase has a close structural relation to the low-pressure monoclinic phase and the phase transition may be due to the tilting of TiO₆ octahedra at high pressures.     

Effect of sintering on the ionic conductivity of garnet-related structure Li5La3Nb2O12 and In- and K-doped Li5La3Nb2O12

Garnet-structure related metal oxides with the nominal chemical composition of Li₅La₃Nb₂O₁₂, In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ and K-substituted Li_5.5La_2.75K_0.25Nb₂O₁₂ were prepared by solid-state reactions at 900, 950, and 1000 °C using appropriate amounts of corresponding metal oxides, nitrates and carbonates. The powder XRD data reveal that the In- and K-doped compounds are isostructural with the parent compound Li₅La₃Nb₂O₁₂. The variation in the cubic lattice parameter was found to change with the size of the dopant ions, for example, substitution of larger In³⁺(r_CN6: 0.79 Å) for smaller Nb⁵⁺ (r_CN6: 0.64 Å) shows an increase in the lattice parameter from 12.8005(9) to 12.826(1) Å at 1000 °C. Samples prepared at higher temperatures (950, 1000 °C) show mainly bulk lithium ion conductivity in contrast to those synthesized at lower temperatures (900 °C). The activation energies for the ionic conductivities are comparable for all samples. Partial substitution of K⁺ for La³⁺ and In³⁺ for Nb⁵⁺ in Li₅La₃Nb₂O₁₂ exhibits slightly higher ionic conductivity than that of the parent compound over the investigated temperature regime 25-300 °C. Among the compounds investigated, the In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ exhibits the highest bulk lithium ion conductivity of 1.8×10⁻⁴ S/cm at 50 °C with an activation energy of 0.51 eV. The diffusivity (“component diffusion coefficient”) obtained from the AC conductivity and powder XRD data falls in the range 10⁻¹⁰-10⁻⁷ cm²/s over the temperature regime 50-200 °C, which is extraordinarily high and comparable with liquids. Substitution of Al, Co, and Ni for Nb in Li₅La₃Nb₂O₁₂ was found to be unsuccessful under the investigated conditions.     

A Structural Investigation of La2(GeO4)O and Alkaline-Earth-Doped La9.33(GeO4)6O2

The structures of the oxyorthogermanate La₂(GeO₄)O and the apatite-structured La_9.33(GeO₄)₆O₂ have been refined from powder neutron diffraction data. La₂(GeO₄)O crystallizes in a monoclinic unit cell (P2₁/c) and is cation stoichiometric in contrast to previous reports. La_9.33(GeO₄)₆O₂ crystallizes in a hexagonal unit cell (P6₃/m) and the powder diffraction data show anisotropic peak broadening that is observed in electron diffraction patterns as incommensurate diffuse spots at hkq reciprocal planes (with q=1.6-1.7) and can be attributed to a correlated disorder in the “apatite channels”. This compound was doped up to a nominal composition close to M₂La₈(GeO₄)₆O₂ with M=Ca, Sr, Ba. The dopant ions preferentially occupy the 4f sites as the number of La vacancies decreases. The measured ionic conductivity of La_9.33(GeO₄)₆O₂ is about 3 orders of magnitude larger than for La₂(GeO₄)O at high temperatures and decreases with increasing dopant content from the highest value of about 0.16 S cm⁻¹ at 1160 K.     

Effect of La2O3 on Catalytic Performance of Au/TiO2 for CO Oxidation

Pure TiO₂ and La-doped TiO₂ were prepared by the sol-gel method. Au was supported on TiO₂ by the deposition-precipitation (DP) method, and its catalytic activity for CO oxidation was tested. The results showed that doping La in Au/TiO₂ could improve its catalytic activity obviously for CO oxidation. The analyses of X-ray diffraction (XRD), temperature-programmed desorption (TPD), and Brunauer-Emmett-Teller (BET) surface area further showed that the presence of La in TiO₂ not only increased its surface area and restrained the growth of TiO₂ crystallites, but could also enhance the microstrain of TiO₂. In terms of O₂-TPD, a new adsorbed species O⁻ appeared on the surface of La-doped TiO₂. The results of in-situ Fourier transform-infrared (FT-IR) spectroscopy illustrated that the high activity of Au/La₂O₃-TiO₂ was attributed to the presence of La promoting the reactivity of CO adsorbed on the Au site and the formation of the second active site on the surface of TiO₂     

La3Ru8B6 and Y3Os8B6, new members of a homologous series R(A)nM3n−1B2n

Two new compounds, La₃Ru₈B₆ and Y₃Os₈B₆, were synthesized by arc melting the elements. Their structural characterization was carried out at room temperature on as-cast samples by using X-ray diffractometry. According to X-ray single-crystal diffraction results these borides crystallize in Fmmm space group (no. 69), Z=4, a=5.5607(1) Å, b=9.8035(3) Å, c=17.5524(4) Å, ρ=8.956 Mg/m³, μ=25.23 mm⁻¹ for La₃Ru₈B₆ and a=5.4792(2) Å, b=9.5139(4) Å, c=17.6972(8) Å, ρ=13.343 Mg/m³, μ=128.23 mm⁻¹ for Y₃Os₈B₆. The crystal structure of La₃Ru₈B₆ was confirmed from Rietveld refinement of X-ray powder diffraction data. Both La₃Ru₈B₆ and Y₃Os₈B₆ compounds are isotypic with the Ca₃Rh₈B₆ compound and their structures are built up from CeCo₃B₂-type and CeAl₂Ga₂-type structural fragments taken in ratio 2:1. They are the members of structural series R(A)_nM_3n−1B_2n with n=3 (R is the rare earth metal, A the alkaline earth metal, and M the transition metal). Structural and atomic parameters were also obtained for La_0.94Ru₃B₂ compound from Rietveld refinement (CeCo₃B₂-type structure, P6/mmm space group (no. 191), a=5.5835(9) Å, c=3.0278(6) Å).     

High-pressure transitions in MgAl2O4 and a new high-pressure phase of Mg2Al2O5

Phase transitions in MgAl₂O₄ were examined at 21-27 GPa and 1400-2500 °C using a multianvil apparatus. A mixture of MgO and Al₂O₃ corundum that are high-pressure dissociation products of MgAl₂O₄ spinel combines into calcium-ferrite type MgAl₂O₄ at 26-27 GPa and 1400-2000 °C. At temperature above 2000 °C at pressure below 25.5 GPa, a mixture of Al₂O₃ corundum and a new phase with Mg₂Al₂O₅ composition is stable. The transition boundary between the two fields has a strongly negative pressure-temperature slope. Structure analysis and Rietveld refinement on the basis of the powder X-ray diffraction profile of the Mg₂Al₂O₅ phase indicated that the phase represented a new structure type with orthorhombic symmetry (Pbam), and the lattice parameters were determined as a=9.3710(6) Å, b=12.1952(6) Å, c=2.7916(2) Å, V=319.03(3) Å³, Z=4. The structure consists of edge-sharing and corner-sharing (Mg, Al)O₆ octahedra, and contains chains of edge-sharing octahedra running along the c-axis. A part of Mg atoms are accommodated in six-coordinated trigonal prism sites in tunnels surrounded by the chains of edge-sharing (Mg, Al)O₆ octahedra. The structure is related with that of ludwigite (Mg, Fe²⁺)₂(Fe³⁺, Al)(BO₃)O₂. The molar volume of the Mg₂Al₂O₅ phase is smaller by 0.18% than sum of molar volumes of 2MgO and Al₂O₃ corundum. High-pressure dissociation to the mixture of corundum-type phase and the phase with ludwigite-related structure has been found only in MgAl₂O₄ among various A²⁺B³⁺₂O₄ compounds.     

Phase stability and ionic conductivity in substituted La2W2O9

Different substitutions, i.e. Sr²⁺, Ba²⁺, K⁺, Nb⁵⁺ and V⁵⁺, have been performed in the triclinic α-La₂W₂O₉ structure in order to stabilise the high temperature and better ionic conductor cubic β-phase. This approach has been used to try to obtain a new series of ionic conductors with LAMOX-type structure without molybdenum and presumably better redox stability compared to β-La₂Mo₂O₉. Nanocrystalline materials obtained by a freeze-drying precursor method at 600 °C exhibit mainly the β-La₂W₂O₉ structure, however, the triclinic α-form is stabilised as the firing temperature increases and the crystallite size grows. Only high levels of Ba²⁺ and V⁵⁺ substitutions retained the cubic form at room temperature after firing above 1100 °C. However, these phases are metastable above 700 °C, exhibiting an irreversible transformation to the low temperature triclinic α-phase. The synthesis, structure, phase stability, kinetic of phase transformation and electrical conductivity of these materials have been studied in the present report.     

The direct decomposition of NO over the La2CuO4 nanofiber catalyst

The NO catalytic direct decomposition was studied over La₂CuO₄ nanofibers, which were synthesized by using single walled carbon nanotubes (CNTs) as templates under hydrothermal condition. The composition and BET specific surface area of the La₂CuO₄ nanofiber were La₂Cu_0.88²⁺Cu_0.12⁺O_3.94 and 105.0 m²/g, respectively. 100% NO conversion (turnover frequency-(TOF): 0.17 g_NO/g_catalyst s) was obtained over such nanofiber catalyst at temperatures above 300 °C with the products being only N₂ and O₂. In 60 h on stream testing, either at 300 °C or at 800 °C, the nanofiber catalyst still showed high NO conversion efficiency (at 300 °C, 98%, TOF: 0.17 g_NO/g_catalyst s; at 800 °C, 96%, TOF: 0.16 g_NO/g_catalyst s). The O₂ and NO temperature programmed desorption (TPD) results indicated that the desorption of oxygen over the nanofibers occurred at 80-190 and 720-900 °C; while NO desorption happened at temperatures of 210-330 °C. NO and O₂ did not competitively adsorb on the nanofiber catalyst. For outstanding the advantage of the nanostate catalyst, the usual La₂CuO₄ bulk powder was also prepared and studied for comparison.     

Ce掺杂K2La2Ti3O10催化剂的可见光高效催化制氢的研究

采用高温固相法合成了铈掺杂的K₂La₂Ti₃O₁₀催化剂, 利用X射线衍射(XRD)、紫外-可见漫反射(UV-vis DRS)、透射电镜(TEM)和X射线光电子能谱(XPS)对催化剂进行了表征. 考察了催化剂的可见光催化分解甲醇水溶液制氢的活性, 并对可见光催化机理进行了分析. 研究表明, 铈的掺杂没有改变K₂La₂Ti₃O₁₀的微晶结构, 并使催化剂粒径有所减小. 紫外可见漫反射分析表明禁带宽度为2.3 eV左右, 对可见光具有较高吸收. XPS表明La和Ti为＋3和＋4价, 而Ce则是＋3和＋4的混合价态. 担载2 wt% Pt后, 在可见光下光催化活性大大提高, 当铈的掺杂量为0.5 mol%(即Ce取代La的摩尔百分量)时, 光催化活性达到最大, 产氢速率为0.05 mmol/h; 光照5 h后产氢量为0.22 mmol, 而纯K₂La₂Ti₃O₁₀的产氢量只有0.037 mmol.     

Synthesis and nonlinear optical properties of BaTi(BO3)2 and Ba3Ti3O6(BO3)2 crystals in glasses with high TiO2 contents

The ternary BaO-TiO₂-B₂O₃ glasses containing a large amount of TiO₂ (20-40 mol%) are prepared, and their optical basicities (Λ), the formation, structural features and second-order optical nonlinearities of BaTi(BO₃)₂ and Ba₃Ti₃O₆(BO₃)₂ crystals are examined to develop new nonlinear optical materials. It is found that the glasses with high TiO₂ contents of 30-40 mol% show large optical basicities of Λ=0.81-0.87, suggesting the high polarizabity of TiO_n polyhedra (n=4-6) in the glasses. BaTi(BO₃)₂ and Ba₃Ti₃O₆(BO₃)₂ crystals are found to be formed as main crystalline phases in the glasses. It is found that BaTi(BO₃)₂ crystals tend to orient at the surface of crystallized glasses. The new XRD pattern for the Ba₃Ti₃O₆(BO₃)₂ phase is proposed through Rietvelt analysis. The second harmonic intensities of crystallized glasses were found to be 0.8 times as large as α-quartz powders, i.e., I^2ω(sample)/I^2ω(α-quartz)=0.8, for the sample with BaTi(BO₃)₂ crystals and to be I^2ω(sample)/I^2ω(α-quartz)=68 for the sample with Ba₃Ti₃O₆(BO₃)₂ crystals. The Raman scattering spectra for these two crystalline phases are measured for the first time and their structural features are discussed.     

La2Ti6O15-CeTi21O38-PbTiO3 ceramics formed in gaseous penetration of La-Ce into PbTiO3 and their electric properties

The gaseous penetration of La-Ce into PbTiO₃ ceramics is reported. The compounds of La₂Ti₆O₁₅ and CeTi₂₁O₃₈ are formed and the new La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃ ceramics are prepared by the penetration of La and Ce in the gaseous state. The new ceramic materials have a significant change in electric properties. The room temperature resistivity decreases from 2.0×10¹⁰ to 0.248 Ω. m, and the grain resistance exhibits an obvious PTCR effect with the change of temperature. However, the grain boundary resistance decreases rapidly with increase in temperature. The change rule of the total resistance is similar to that of the grain boundary, and the PTCR effect disappears and the tendency of transition to a conductive body is manifest. The XPS analysis suggests that the particles that are Pb, Ti, La and Ce in La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃ ceramics all change their valence and lead to decreasing resistivity, and the bound energy peak values of elements in La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃ ceramics are also reported. The La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃ ceramics have a better thermal stability in high temperatures through TG-DTA analysis.     

Crystal structure of BaMg2Si2O7 and Eu luminescence

Crystal structure of BaMg₂Si₂O₇ was determined and refined by a combined powder X-ray and neutron Rietveld method (monoclinic, C2/c, no. 15, Z=8, a=7.24553(8) Å, b=12.71376(14) Å, c=13.74813(15) Å, β=90.2107(8)°, V=1266.44(2) Å³; R_p/R_wp=3.38%/4.77%). The structure contains a single crystallographic type of Ba atom coordinated to eight O atoms with C₁ (1) site symmetry. Under 325-nm excitation Ba_0.98Eu_0.02Mg₂Si₂O₇ exhibits an asymmetric emission band around 402 nm. The asymmetric shape of the emission band is likely associated with a small electron-phonon coupling in BaMg₂Si₂O₇. The integrated intensity of the emission band was observed to remain constant over the temperature range 4.2-300 K.     

Structure and properties of a novel cobaltate La0.30CoO2

The layered cobaltate La_0.30CoO₂ was prepared from Na_xCoO₂ precursor by a solid-state ionic exchange and was characterized by means of X-ray and neutron diffraction, magnetic, thermal and electric transport measurements. The compound consists of hexagonal sheets of edge-sharing CoO₆ octahedra interleaved by lanthanum monolayers. Compared to Na⁺ in the parent system, the La³⁺ ions occupy only one-third of available sites, forming a 2-dimensional superstructure. The deviation from the ideal stoichiometry La_1/3CoO₂ introduces extra hole carriers into the diamagnetic LS Co³⁺ matrix making the sample Pauli paramagnetic. The temperature dependence of the electrical conductivity in La_0.30CoO₂ follows Mott's T^−1/3 law up to about 400 K, which is in contrast with the standard metallic behavior in the Na⁺ homolog possessing the same formal doping. The experiments are complemented by electronic structure calculations for La_0.30CoO₂ and related Na_xCoO₂ systems.     

Structure and properties of the CaFe2O4-type cobalt oxide CaCo2O4

The calcium cobalt oxide CaCo₂O₄ was synthesized for the first time and characterized from a powder X-ray diffraction study, measuring magnetic susceptibility, specific heat, electrical resistivity, and thermoelectric power. CaCo₂O₄ crystallizes in the CaFe₂O₄ (calcium ferrite)-type structure, consisting of an edge- and corner-shared CoO₆ octahedral network. The structure of CaCo₂O₄ belongs to an orthorhombic system (space group: Pnma) with lattice parameters, a=8.789(2) Å, b=2.9006(7) Å and c=10.282(3) Å. Curie-Weiss-like behavior in magnetic susceptibility with the nearly trivalent cobalt low-spin state (Co³⁺, 3d, S=0), semiconductor-like temperature dependence of resistivity (ρ=3×10⁻¹ Ω cm at 380 K) with dominant hopping conduction at low temperature, metallic-temperature-dependent large thermoelectric power (Seebeck coefficient: S=+147 μV/K at 380 K), and Schottky-type specific heat with a small Sommerfeld constant (γ=4.48(7) mJ/Co mol K²), were observed. These results suggest that the compound possesses a metallic electronic state with a small density of states at the Fermi level. The doped holes are localized at low temperatures due to disorder in the crystal. The carriers probably originate from slight off-stoichiometry of the phase. It was also found that S tends to increase even more beyond 380 K. The large S is possibly attributed to residual spin entropy and orbital degeneracy coupled with charges by strong electron correlation in the cobalt oxides.     

Structural studies on W and Nd substituted La2Mo2O9 materials

The structure of a series of new ionic conductors based in lanthanum molybdate (La₂Mo₂O₉) has been investigated using transmission electron microscopy (TEM), high-resolution X-ray diffraction (XRD) and differential scanning calorimetry (DSC). The superstructure 2a_c×3a_c×4a_c of the low temperature α-polymorph relative to the β-polymorph was confirmed by HRTEM imaging and electron diffraction. Furthermore, the effects of partial cation substitution in the La_2−xNd_xMo₂O₉ and La₂Mo_2−yW_yO₉ series have been also evaluated in the search of new clues to understand the structure and stabilisation of the high temperature and better conductor β-polymorph. The thermal analysis studies show that Nd-substitution does not stabilise completely the β-polymorph at room temperature, although no superstructure ordering was observed by both XRD and HRTEM. On the other hand, W-substitution stabilises the cubic β-polymorph for y>0.25, although, electron diffraction indicates a slight distortion from the cubic symmetry for low W-content. This distortion disappears as the W content increases and the Rietveld refinements gradually render better results.     

Synthesis, structure and physical properties of the new uranium ternary phase U3Co2Ge7

A new ternary compound, U₃Co₂Ge₇, has been synthesized from the corresponding elements by a high temperature reaction using molten tin flux. It crystallizes in the orthorhombic La₃Co₂Sn₇-type (Pearson's symbol oC24, space group Cmmm, No. 65) with lattice parameters determined from single-crystal X-ray diffraction as follows: a=4.145(2) Å; b=24.920(7); c=4.136(2) Å, V=427.2(3) Å³. Structure refinements confirm an ordered structure having two crystallographically inequivalent uranium atoms, occupying sites with dissimilar coordination. U₃Co₂Ge₇ orders ferromagnetically below 40 K and undergoes a consecutive magnetic transition at 20 K. These results have been obtained from temperature- and field-dependent magnetization, resistivity and heat-capacity measurements. The estimated Sommerfeld coefficient γ=87 mJ/mol-U K² suggests U₃Co₂Ge₇ to be a moderately heavy-fermion material.     

Preparation of Pt/K2La2Ti3O10 and its photo-catalytic activity for hydrogen evolution from methanol water solution

A layered perovskite-type oxide K₂La₂Ti₃O₁₀ was prepared with high-temperature solid-state reaction, and characterized with X-ray diffraction (XRD) and ultraviolet-visible diffuse reflectance spectroscopy (UV-Vis DRS). Platinum was loaded onto K₂La₂Ti₃O₁₀ as a co-catalyst with different methods. The dispersion of platinum on K₂La₂Ti₃O₁₀ was determined with HOT method. The photocatalytic activity of Pt/K₂La₂Ti₃O₁₀ was studied. This catalyst showed much higher activity in hydrogen evolution reaction than Ni/K₂La₂Ti₃O₁₀. The effects of different amounts of loaded platinum and several preparation methods were evaluated. The best achieved hydrogen evolution rate was 233.88 μmol·h⁻¹ by Pt(2%)/K₂La₂Ti₃O₁₀. A possible band structure and mechanism were discussed based on the results.