硅源对蒸氨法制备Cu/SiO2催化剂催化甲醇裂解制氢的影响

采用蒸氨法制备Cu/SiO₂催化剂,分别考察气相二氧化硅（SiO₂-aer）、硅胶（SiO₂-gel）和碱性硅溶胶（SiO₂-sol）对Cu/SiO₂催化剂催化甲醇裂解制氢性能的影响,并采用N₂吸附-脱附、N₂O化学吸附、电感耦合等离子体原子发射光谱法（ICP-AES）、X射线衍射（XRD）、H₂程序升温还原（H₂-TPR）、透射电子显微镜（TEM）和X射线光电子能谱（XPS）等方法对催化剂进行表征。结果表明,硅源对Cu/SiO₂催化剂的活性具有较大影响。以碱性硅溶胶作为硅源制得的Cu/SiO₂-sol催化剂比表面积较大,活性中心粒径较小且分散均匀,这些使得其制氢性能优于其他两种硅源为载体所制备的催化剂。在反应温度280 ℃,反应压力1 MPa,甲醇质量空速0.6 h^-1的条件下,相较于Cu/SiO₂-aer和Cu/SiO₂-gel催化剂,Cu/SiO₂-sol催化剂的甲醇转化率分别提高10％和7％,气相副产物CH₄和CO₂浓度也有所降低,该催化剂上的甲醇转化率和气体收率分别达到98.4%和96.7%。     

介质阻挡放电等离子体甲烷/水蒸气重整制氢

采用自制的介质阻挡放电实验系统,进行了甲烷/水蒸气大气压下重整制氢实验研究。考察了水碳比（水蒸气/甲烷物质的量比）、气体总流量、放电电压和放电频率对甲烷转化率及氢气等主要产物产率的影响。结果表明,甲烷转化率和氢气产率随着水碳比和放电电压的增加而增大,随着气体总流量和放电频率的增加呈现先增大后减小的变化规律。在放电电压18.6 kV、放电频率9.8 kHz、水碳比3.4、反应气体总流量79 mL/min时,获最大氢气产率（14.38%）。此外,利用发射光谱对放电过程中的活性基团进行了原位诊断,得到了CH·、OH·、H₂及H_α活性粒子的光谱信号强度随实验参数的变化规律,并结合放电机理推测了氢气的生成路径。     

等离子体技术对CO2甲烷化用Ni/SiO2催化剂的改性作用

采用浸渍法制备了Ni/SiO₂催化剂,应用等离子体技术对催化剂进行改性处理。以CO₂甲烷化为模型反应对催化剂进行活性评价,通过H₂程序升温还原(H₂-TPR)和CO₂程序升温脱附(CO₂-TPD)技术对催化剂进行表征。研究了等离子体技术强化处理对催化剂吸附性能和还原性能的影响。结果表明,与常规焙烧的催化剂相比,等离子体技术改性处理提高了催化剂活性组分的分散度,增加反应活性位并调变了活性位对吸附物种的吸附强度,改进了催化剂的还原性能,CO₂甲烷化反应活性和甲烷的时空产率显著提高。     

载体对烯烃歧化制丙烯的影响

以SiO₂（SBA-15、MCM-48和SiO₂）和TiO₂-SiO₂（MTS-9）介孔分子筛为载体负载8%WO₃合成钨基催化剂,研究载体对丁烯歧化制丙烯性能的影响以及载体对丁烯转化率和丙烯选择性的影响。以SBA-15、MCM-48和SiO₂为载体时,催化剂的丁烯转化率在30%~37%;以MTS-9为催化剂载体时,丁烯的转化率高达到37%~42%。对所有使用的催化剂进行多种技术表征。结果表明,活性组分在各种载体上的分散度不同,载体MTS-9具有更好的分散能力,表面活性物种数量最多,催化剂WO₃/MTS-9的歧化性能最佳。     

氧空位修饰的暴露TiO2{001}的Ru/TiO2增强光热协同CO2甲烷化活性和稳定性

利用太阳能在温和条件下实现CO₂还原反应,不仅可以缓解过度消耗化石能源造成的能源危机,还可以改善诸如温室效应和海洋酸化等环境问题.光热协同催化可以有效降低催化反应温度,具有较大的应用前景.本文利用Ru与暴露TiO₂{001}晶面的TiO₂载体产生的金属-载体相互作用,经过高温氢气煅烧后,获得具有丰富表面氧空位的Ru/TiO₂催化剂.活性测试结果表明,具有丰富表面氧空位的Ru/TiO₂表现出优异的CO₂甲烷化活性,反应过程中甲烷的TOF值在300°C时可以达到22 h-1,但该催化剂却表现出较差的稳定性,在反应10小时后,甲烷的TOF值逐渐降低到19 h-1.将紫外光引入到Ru/TiO₂热催化甲烷化体系中,甲烷的TOF值增加到30 h-1,且兼具高稳定性.热催化反应过程中逐渐消失的表面氧空位和部分氧化的Ru是活性降低的主要原因.在光热协同反应中,光生电子的产生稳定了Ru表面的电子密度,同时也再生了催化剂上表面氧空位,这有效地提高了反应的活性和稳定性.程序升温原位红外和X射线光电子能谱实验结果表明,当催化剂表面具有丰富的表面氧空位时,CO₂可以有效地在Ru纳米粒子上解离成CO中间体,随后吸附在Ru上的CO中间体解离成表面碳物种,并加氢产生甲烷.在热催化反应过程中,Ru纳米粒子逐渐被氧化成Ru Ox物种,且表面氧空位被CO中间物种覆盖,降低了催化反应的稳定性.当紫外光引入到上述反应中,催化剂的表面氧空位可有效提高光生载流子的分离能力.TiO₂载体产生的光电子转移至Ru表面,稳定了金属Ru纳米粒子的价态.另外,载体产生的光生空穴加速了H₂质子化,提高了催化剂对氢气的活化迁移能力,促进了CO中间体的加氢甲烷化反应,进而再生表面氧空位.因此在紫外光照下,兼顾提高了热催化CO₂甲烷化的活性和稳定性.值得注意的是,当Ru负载于暴露少量TiO₂{001}晶面的TiO₂载体上时,产生了强金属-载体相互作用并抑制了H₂在催化剂上的吸附活化,不利于产生表面氧空位.因此暴露少量TiO₂{001}晶面的Ru/TiO₂催化剂也不利于光生载流的产生和分离,这导致热催化或光热协同催化反应活性较低.     

MoO3纳米带修饰MCM-22催化甲烷无氧芳构化反应

利用天然气生产芳烃是一个有吸引力的课题，这个过程需要具有高性能活性位点的催化剂，以活化稳定的碳氢键．在甲烷直接转化方法中，将甲烷无氧脱氢芳构化(MDA)转化为高附加值芳烃(如苯、甲苯和萘)是甲烷增值的有效途径．本研究采用MoO₃纳米带作为Mo源，微孔分子筛MCM-22作为载体制备双功能Mo基催化剂，结果表明MoO₃纳米带高度分散在分子筛内部，与分子筛中Br?nsted酸中心结合形成有效活性中心，改善了甲烷无氧脱氢芳构化反应的催化活性，提高了催化剂的稳定性．在甲烷无氧脱氢芳构化反应测试中，当MoO₃纳米带的负载量质量分数为6%时，N-Mo-HMCM-22催化剂催化的甲烷转化率达到14.1%，苯产率可达8.2%．本研究为合成高性能、稳定的MDA催化剂提供了一种更为简易的策略．     

CO2重整CH4纳米ZrO2负载Ni催化剂的研究(Ⅰ)——与常规载体上Ni催化剂的比较

在Ni负载量相近(约5%)时,比较了由超临界干燥得到的纳米ZrO₂-AS为载体制备的Ni/ZrO₂-AS与几种常规载体(γ-Al₂O₃,TiO₂,SiO₂和ZrO₂-CP)负载的Ni催化剂对CO₂重整CH₄制合成气反应的催化性能.研究结果表明,γ-Al₂O₃,TiO₂,SiO₂和ZrO₂-CP负载Ni催化剂表现出明显的失活过程,而Ni/ZrO₂-AS催化剂在反应200h后活性未下降.“纯ZrO₂-AS”载体本身不仅能催化生成合成气的反应,而且活性稳定.TPO测定结果表明,负载在这种活性ZrO₂-AS载体上的Ni催化剂具有良好的抗积炭能力.     

SiO2和Al2O3负载的Ni基催化剂在甲烷干重整中的催化性能差异

CH₄与CO₂干重整反应对于环境保护和天然气资源的合理利用具有重要意义。SiO₂和Al₂O₃是适用于甲烷干重整反应的两种典型的催化剂载体。为了阐明这两种载体对催化剂性能的影响,本研究采用等体积浸渍法制备了Ni/Al₂O₃和Ni/SiO₂催化剂,并利用BET、TEM、H₂-TPR、XRD、TG和Raman等技术对还原和反应后的催化剂进行了表征。结果表明,由于载体的性质不同,Ni基催化剂在甲烷干重整中的催化性能也不同。Ni/SiO₂催化剂的初始活性较高,但由于其金属-载体相互作用较弱,催化稳定性较差,在800℃下反应15h其催化活性急剧下降;较弱的金属-载体相互作用使得Ni/SiO₂催化剂上的Ni颗粒较大,有利于积炭前驱物种的生成,导致催化剂快速失活。而对于Ni/Al₂O₃催化剂,金属-载体相互作用较强,Ni颗粒较小,但由于Ni与Al₂O₃生成了NiAl_xO_y物种,有效活性位减少,其催化活性相对较低,但催化稳定性较好,干重整反应进行50h其活性保持稳定;Ni与Al₂O₃之间较强的相互作用有利于形成小且稳定的Ni粒子,能减少积炭,因而具有优异的催化稳定性。     

TiOx/SiO2复合载体上高分散Au催化剂的CO氧化性能

负载型Au催化剂中金与载体间存在相互作用,载体性质能够影响Au纳米颗粒分散度及稳定性.本文通过表面溶胶-凝胶(SSG)法制备了TiO_x/SiO₂复合载体,以期增加氧化物载体表面配位不饱和度从而使其具有较高的金属分散性,并利用低能离子散射(LEIS)谱、X射线光电子能谱(XPS)、X射线衍射(XRD)、透射电子显微镜(TEM)及N₂物理吸附(BET)等手段对载体及催化剂进行表征分析.实验表明TiO_x/SiO₂复合载体表面TiO_x分散性良好,没有形成明显的TiO₂晶相,且与SiO₂间形成Ti―O―Si键.与Au/TiO₂相比, Au/TiO_x/SiO₂催化剂中Au纳米颗粒的分散性更好,因而CO氧化活性显著提高. TiO_x/SiO₂复合载体上的TiO₂膜是Au的主要表面键合位,导致Au与载体间相互作用增强,从而使得Au纳米颗粒抗烧结能力提高,同时催化剂反应稳定性得到改善.     

载体效应对Ru基催化剂费托合成制烯烃的性能影响（英文）

本研究考察了不同载体(CeO₂、ZrO₂、MnO₂、SiO₂和活性炭)对负载型Ru基费托合成制烯烃(FTO)催化剂结构和催化性能的影响。结果表明,载体的本征属性和金属-载体相互作用(MSI)对催化性能有很大影响。在同一反应条件下的催化活性关系为：Ru/SiO₂> Ru/ZrO₂> Ru/MnO₂> Ru/AC> Ru/CeO₂。对于烯烃选择性,Ru/SiO₂和Ru/MnO₂得到的总烯烃选择性最高,超过70%,而Ru/ZrO₂催化剂的烯烃选择性低至29.9%。由于金属Ru与SiO₂的金属载体相互作用较弱,反应后的Ru/SiO₂催化剂得到适中的Ru纳米颗粒尺寸(～5 nm)且反应活性也最高。对于Ru/AC和Ru/MnO₂,其Ru纳米颗粒尺寸仅为1-3 nm,表现出...     

碱改性ZSM-11分子筛及其催化裂化增产烯烃性能

通过晶种辅助法合成ZSM-11分子筛,并对其进行碱处理从而制备了改性样品ZSM-11-AT.采用XRD、 N₂吸附和脱附、 XRF、 TEM、 NH₃-TPD和Py-IR等表征手段对样品ZSM-5、 ZSM-11和ZSM-11-AT的物化性质进行了表征和对比分析,发现改性样品ZSM-11-AT的比表面积、孔隙结构和酸性质均得到了改善.采用固定床反应装置对样品的催化裂化性能进行了评价,对样品ZSM-5、 ZSM-11和ZSM-11-AT的反应物转化率和产物分布进行了对比研究.结果表明, ZSM-11和ZSM-11-AT在烯烃乙烯和丙烯产率方面优于ZSM-5.与ZSM-11相比, ZSM-11-AT的催化性能得到了进一步的提高.     

不同模板剂合成具有介微结构的ZSM-5分子筛及其甲醇制丙烯性能

分别采用四丙基氢氧化铵(TPAOH),十六烷基三甲基溴化铵(CTAB)和N-十八烷基-N'-己基-四甲基-1, 6-己二铵(C_18-6-6Br₂)作为模板剂,合成了具有不同介微结构的纳米ZSM-5分子筛(NZ),介孔ZSM-5分子筛(MZ)和纳米薄层ZSM-5分子筛(NSZ).对合成的样品进行X射线衍射(XRD),扫描电子显微镜(SEM), N₂吸附-脱附和氨程序升温脱附(NH₃-TPD)表征,并与传统微孔ZSM-5分子筛(CZ)对比.结果表明,样品的介孔孔容和外表面积大小的顺序为NSZ > MZ > NZ > CZ,强/弱酸之比的顺序为CZ > MZ > NZ > NSZ.在甲醇制丙烯(MTP)反应中,催化剂的介微结构特征影响MTP反应的产物选择性及稳定性,丙烯和总低碳烯烃选择性随着介孔孔容的增加而增加, NSZ样品具有最高的丙烯选择性(47.5%)及总低碳烯烃选择性(78.4%).此外,介孔的引入能适当延长催化剂的寿命,具有适宜酸性质的NZ样品的催化寿命最长(200 h).     

固体酸催化剂对LDPE与PS混合物催化裂解行为的研究

研究ZSM—G5和USY，及新型改性催化剂DeLaZSM-5对LDPE与PS混合聚烯烃的催化裂解行为，与热裂解相比，ZSM-5与DeLaZSM-5使裂解速率增加、残渣收率降低、产品分布变窄，而USY使裂解活性降低，其中De-LaZSM-5对LDPE／PS混合物具有最高的催化裂解活性。     

Catalytic Oxidation of CO and Benzene over Metal Nanoparticles Loaded on Hierarchical MFI Zeolite

In order to obtain highly active catalytic materials for oxidation of carbon monoxide and volatile organic compounds (VOCs), monometallic platinum, copper, and palladium catalysts were prepared by using of two types of ZSM-5 zeolite as supports—parent ZSM-5 and the same one treated by HF and NH₄F buffer solution. The catalyst samples, obtained by loading of platinum, palladium, and copper on ZSM-5 zeolite treated using HF and NH₄F buffer solution, were more active in the reaction of CO and benzene oxidation compared with catalyst samples containing untreated zeolite. The presence of secondary mesoporosity played a positive role in increasing the catalytic activity due to improved reactant diffusion. The only exception was the copper catalysts in the reaction of CO oxidation, in which case the catalyst, based on untreated ZSM-5 zeolite, was more active. In this specific case, the key role is played by the oxidative state of copper species loaded on the ZSM-5 zeolites.     

Synthesis of nano/micro scale ZSM-5 from kaolin and its catalytic performance

Nano/micro scale ZSM-5 zeolites were synthesized by using natural kaolin as raw material. The effect of particle size on the catalytic performance of ZSM-5 zeolite for the methanol to olefins conversion was evaluated in a fixed-bed reactor. The results indicated the crystal size had a significant effect on the catalytic stability and the products distribution. ZSM-5 with nanosize showed better tolerance to coke formation, longer catalytic lifetime, and higher selectivity to propylene. The selectivity to propylene on nanosized ZSM-5 was on average 4.5% higher than on the submicron sample and 10% higher than on microsized ZSM-5. After the reaction was conducted for 20 h the ZSM-5 catalyst synthesized from kaolin showed longer lifetime and higher propylene selectivity than the sample synthesized with chemical materials The reason can be explained by the occurence of such elements as Fe, P, and especially Ti.     

Study on Methylation of Naphthalene with Methanol over ZSM-5 (core)/SAPO-11(shell) Composite Molecular Sieve

ZSM-5 (core)/SAPO-11 (shell) composite molecular sieve was synthesized by the hydrothermal method in order to combine the advantages of ZSM-5 and SAPO-11 for the methylation of naphthalene with methanol. For comparison, the mechanical mixture was prepared through the blending of ZSM-5 and SAPO-11. The characterization results indicated that ZSM-5/SAPO-11 composite molecular sieve exhibited a core–shell structure, with the ZSM-5 phase as the core and the SAPO-11 phase as the shell. The pore size of the composite was between that of ZSM-5 and SAPO-11. The composite had fewer acid sites than ZSM-5 and mechanical mixture while more acid sites than SAPO-11. The experimental results indicated that the composite exhibited high catalytic performances for the methylation of naphthalene with methanol.     

Synthesis, characterization, and adsorption properties of nanocrystalline ZSM-5

Nanocrystalline ZSM-5 with a Si/Al ratio of 20 was synthesized using clear solutions and a hydrothermal synthesis procedure. The resulting ZSM-5 materials were characterized by powder X-ray diffraction, scanning electron microscopy (SEM), nitrogen adsorption isotherms, solid-state nuclear magnetic resonance, and toluene adsorption. A commercial ZSM-5 sample was similarly characterized for comparison with the synthesized materials. The particle sizes of the synthesized ZSM-5 samples were calculated using the measured external surface areas and were determined to be 15 and 60 nm. SEM images indicated that the ZSM-5 samples consist of agglomerated and possibly intergrown particles. Toluene adsorption measurements showed that the ZSM-5 sample with a particle size of 15 nm adsorbed approximately 50% more toluene than the other ZSM-5 samples, most likely due to the adsorption of toluene on the external surface. For the toluene adsorbed on the internal zeolite surface, approximately one toluene molecule was adsorbed per channel intersection for each of the ZSM-5 samples.     

HZSM-5/SAPO-11复合分子筛的制备、 表征及在异丁烷芳构化反应中的催化性能

将经聚二烯丙基二甲基氯化铵(PDDA)预处理的HZSM-5分子筛置于SAPO-11分子筛的合成母液中, 在水热体系中原位制备了一系列HZSM-5/SAPO-11复合分子筛, 并对分子筛的结构、 形貌及酸性进行了表征, 考察了其在异丁烷芳构化反应中的催化性能. 结果表明, 所得复合分子筛由HZSM-5表面包覆约20 nm的SAPO-11微晶组成, 且通过调变SAPO-11的Si含量可以有效调变复合分子筛的酸性, 提高芳构化强弱酸协同催化作用, 有效抑制裂解副反应. 结合异丁烷芳构化转化率及液体收率结果可知, 当SAPO-11合成溶胶中硅铝摩尔比为0.6时, HZSM-5/SAPO-11复合分子筛的芳构化活性及稳定性最佳.     

ZSM-5/Y复合分子筛的酸性及其重油催化裂化性能

 ZSM-5/Y是本研究组合成的一种新型复合分子筛材料. 用“两次交换,两次焙烧”和磷 酸氢二铵浸渍方法对该复合分子筛材料进行了改性,采用红外光谱表征了复合分子筛的酸性,研究了磷改性对复合分子筛样品羟基区谱学性质的影响,并与相应的机械混合分子筛样品进 行了对比. 红外光谱数据表明,磷改性后复合分子筛的B酸(主要是中强酸)增加,而机械混合分子筛在各个酸强度区域的B酸量和L酸量都减少. 以新疆重油为原料考察了改性后复合分子 筛样品和机械混合分子筛样品的催化裂化性能. 与相应的机械混合分子筛催化剂相比,磷改 性复合分子筛催化剂具有较高的柴油选择性,其柴油产率增加了4.1个百分点,柴汽比增加了0.11,总轻油产率与机械混合分子筛相当. 用气体产物中的CMR(裂化机理比)和C3/C4比 值分析了复合分子筛的催化性能与其聚集体结构的关系.     

不同硅铝比ZSM-5分子筛作为助催化剂在渣油裂化中的应用

采用不同方法表征了硅铝比(SiO2/Al2O3)为33、266和487的质子型ZSM-5分子筛,并研究了ZSM-5分子筛作为助催化剂在渣油裂解中的应用。与USY分子筛基催化剂混合后,在固定流化床上,评价了ZSM-5分子筛助催化剂的催化裂化性能。研究发现,提高ZSM-5分子筛硅铝比,可以有效抑制混合催化剂对汽油烯烃的裂解,从而避免了汽油烷烃的大量损失。加入ZSM-5助催化剂后,伴随着液化气(LPG)产率的增加,异丁烷和异戊烷产率增加,这可能是由USY基催化剂和ZSM-5助催化剂的综合效应引起的。汽油烷烃和芳烃含量的变化,引起了汽油辛烷值的增加。高硅铝比ZSM-5分子筛(硅铝比为266和487)不仅可以显著改善汽油的辛烷值,而且有效避免了汽油的大量损失。催化汽油辛烷值的改善主要是由于高硅铝比ZSM-5分子筛具有适宜的芳构化和异构化活性,这些变化主要源于高硅铝比ZSM-5分子筛小的孔道直径和适宜的酸性。