MoS_2/g-C_3N_4复合材料的制备及可见光催化性能

首先在N-甲基吡咯烷酮溶液中超声剥离得到少层的MoS_2,将其与石墨相氮化碳(g-C_3N_4)复合,制得MoS_2/g-C_3N_4复合材料。采用X射线衍射(XRD),扫描电镜(SEM),X射线光电子能谱(XPS),傅里叶变换红外光谱(FTIR),Raman光谱,紫外-可见漫反射吸收光谱(DRS)和光致荧光(PL)技术对复合材料进行表征。可见光下考察MoS_2/g-C_3N_4复合材料光催化降解罗丹明B(Rh B)的活性,结果表明:将少量MoS_2与g-C_3N_4复合可明显提高光催化活性,且1%(w/w)MoS_2/g-C_3N_4复合物的光催化活性最高,可能的原因是MoS_2和g-C_3N_4匹配的能带结构,增大了界面间电荷的传输,降低了光生电子-空穴的复合,进而提高了光催化活性。     

Ag3PO4/Ag2S/g-C3N4复合光催化剂的制备与性能

通过沉积法和离子交换法成功地制备了Ag_3PO_4/Ag_2S/g-C_3N_4复合型光催化剂。利用X射线多晶粉末衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、N_2吸附-脱附等温线、紫外-可见漫反射光谱、荧光光谱等手段对样品进行了表征。通过降解罗丹明B考察其可见光催化活性及稳定性,研究了硫化钠与磷酸银物质的量的比值(n_(Na_2S)/n_(Ag_3PO_4))、g-C_3N_4添加量对所制备复合光催化材料性能的影响,同时对光催化机理进行了探讨。结果表明,随着n_(Na2S)/n_(Ag3PO4)的增加,所得复合催化材料活性先增加后降低;当n_(Na2S)/n_(Ag_3PO_4)为1.5%、g-C_3N_4与Ag_3PO_4的质量比为3∶7时制备的催化剂ASC1.5的光催化活性最好,在可见光照射下,40 min内可将罗丹明B完全降解,且5次循环使用后仍保持较高的催化活性。和Ag_3PO_4相比,Ag_3PO_4/Ag_2S/g-C_3N_4复合型光催化材料的活性与稳定性都得到明显提高,这主要归因于复合催化剂比表面积和孔结构的增加,载流子分离效率的提高。光催化机理研究表明,空穴(h~+)、超氧阴离子自由基(·O~(2-))和羟基自由基(·OH)都是光催化过程中的主要活性物种。三者作用大小依次为:h~+·O~(2-)·OH。     

一锅法制备Co3O4/g-C3N4复合光催化剂及其光催化性能

以三聚氰胺和六水合氯化钴为原料,一锅法制备Co_3O_4负载的多孔石墨相氮化碳(Co_3O_4/g-C_3N_4)复合光催化材料。采用X射线衍射(XRD)、傅里叶变换红外(FT-IR)光谱、X射线光电子能谱(XPS)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、紫外-可见漫反射光谱(UV-Vis DRS)、光致发光光谱(PL)等手段对其结构和光学特性进行表征。以盐酸四环素(TC)为目标污染物,评价了不同负载量Co_3O_4/g-C_3N_4复合光催化剂的可见光催化性能。结果表明,所制备的Co_3O_4/g-C_3N_4复合光催化剂为多孔结构,其比表面积较大,并在可见光区域具有显著的吸收。利用原位生成的Co_3O_4纳米粒子在氮化碳表面形成异质结构,可有效转移光生载流子,降低光生电子-空穴的再结合率,从而提高光催化活性。并且存在最佳Co_3O_4复合量,当六水合氯化钴加入量为三聚氰胺的8%(w/w)时,所制备的复合光催化剂CoCN-8具有最佳的光催化性能。在可见光的照射下,60 min内可降解85%的TC,而同样条件下,纯g-C_3N_4仅降解23%的TC。     

g-C3N4-BiOBr复合材料制备及可见光催化性能

利用原位沉积法将Bi OBr纳米片生长到g-C_3N_4表面,制得g-C_3N_4-Bi OBr p-n型异质结复合光催化剂。采用X射线衍射(XRD)、红外光谱(FTIR)、场发射扫描电子显微镜(FE-SEM)、透射电子显微镜(TEM)、紫外可见漫反射(UV-Vis-DRS)和荧光光谱(PL)等测试对光催化剂结构和性能进行表征。通过可见光辐照降解甲基橙水溶液检测评估复合光催化剂光催化活性。研究结果表明:复合光催化剂由Bi OBr和g-C_3N_4两相组成,Bi OBr纳米片在片状g-C_3N_4表面快速形核生长形成面-面复合结构。相比于纯相g-C_3N_4和Bi OBr,g-C_3N_4-Bi OBr复合材料具有更强可见光吸收能力,吸收带边红移。在可见光辐照100 min后,性能最佳的2:8 gC_3N_4-Bi OBr复合光催化剂光催化活性分别是纯相g-C_3N_4和Bi OBr的1.8和1.2倍,经过4次循环实验后,其降解率仍达84%,说明复合结构光催化剂催化性能和稳定性增强。复合光催化剂的荧光强度显著降低,说明光生载流子复合得到了有效抑制。复合光催化剂催化性能的提高归因于p-n型异质结促进电荷有效分离、抑制电子-空穴复合和吸收光波长范围的扩展,相比单一成分材料具有更好的催化活性和稳定性。自由基捕获实验证明,可见光降解甲基橙光催化过程中的主要活性成分为空穴,并据此提出了可能的光催化机理。     

中空花状可见光响应催化剂g-C3N4@BiOCl的制备及其光催化活性

以g-C₃N₄/H₂SO₄溶液和硝酸铋为前驱体,采用自组装法制备了中空花状且具有可见光响应能力的异质结光催化剂g-C₃N₄@BiOCl。利用X射线衍射、电子扫描显微镜、高分辨透射电镜、X射线能谱、紫外可见漫反射光谱及X射线光电子能谱等表征手段确证了催化剂的结构。该催化剂能够有效地实现光生电子-空穴的分离,表现出优异的可见光催化活性。通过对50 mg·L^-1罗丹明B的降解实验验证了g-C₃N₄@BiOCl的光催化活性,在可见光条件下（λ≥420 nm）的降解效率优良,12 min即可达到99%。     

g-C_3N_4/CaTi_2O_5复合材料制备及其光催化性能

利用类石墨氮化碳(g-C_3N_4)和亚稳相钙钛氧化物(CaTi_2O_5)固相法制备C_3N_4/CaTi_2O_5复合材料。利用X射线衍射(XRD)、金相显微镜、扫描电子显微镜(SEM)及附带能谱分析仪(EDS)和N2吸附-脱附对样品的显微结构和比表面积进行检测分析,并用紫外-可见吸收光度计(UV-Vis)测试了样品的光吸收性能,研究C_3N_4与CaTi_2O_5物质的量之比(nC_3N_4/nCaTi_2O_5)对C_3N_4/CaTi_2O_5复合样品的物相结构和微观形貌的影响,同时考察C_3N_4/CaTi_2O_5复合样品在可见光照射下光催化降解罗丹明染料效果。实验结果表明:相比纯C_3N_4和CaTi_2O_5样品,C_3N_4/CaTi_2O_5复合样品在可见光下具有较高的光催化性能,随着nC_3N_4/nCaTi_2O_5增加,样品的光催化降解率随之增加而后降低,当nC_3N_4/nCaTi_2O_5=1∶1时,样品的光催化降解率达到最大值99.5%,并且循环重复利用5次后,样品的光催化剂降解率仍几乎保持不变。复合样品光催化性能提高主要归因于复合能级结构有效地抑制了电子和空穴复合所致。     

g-C3N4纳米管的制备及其光催化降解性能

以三聚氰胺和碳酸氢铵混合物为原料,采用简便热解法制备g-C_3N_4纳米管。热解过程中碳酸氢铵分解释放出大量的NH3,能够诱导纳米管的形成。利用X射线衍射(XRD)、扫描电子显微镜(SEM)、红外光谱(IR)、N_2吸附-脱附、紫外-可见漫反射光谱以及紫外可见光谱(UV)等分析测试方法对该光催化剂的微观形貌结构和催化性能进行了表征。以罗丹明光催化降解为模型反应研究了g-C_3N_4纳米管的光催化活性。g-C_3N_4纳米管的表面积明显增大,且能够有效地促进光生电子转移,在可见光下具有较强的光催化性能,降解率在60和120 min时分别能达到95%和99.4%,且循环重复利用5次后降解率不低于92%。     

g-C_3N_4/BiOBr异质结光催化剂的制备与可见光催化活性

以三聚氰胺作为合成g-C_3N_4纳米片的前躯体,以Bi(NO3)3·5H2O和KBr作为合成BiOBr的原料,采用水热法构建g-C_3N_4/Bi OBr二维异质结可见光催化剂,有效的晶面复合和合适的能带组合有助于增强g-C_3N_4和BiOBr的可见光催化活性。利用X射线衍射(XRD)、透射电镜(TEM)、X射线光电子能谱(XPS)、光致发光光谱(PL)和紫外-可见漫反射光谱(UVvis DRS)等方法表征其结构、光学性质以及组成结构。在可见光(λ420 nm)下以光催化降解RhB来评价合成催化剂的光催化活性,结果表明,g-C_3N_4/BiOBr光催化降解罗丹明B(Rh B)的效率高于单体g-C_3N_4和BiOBr,并对g-C_3N_4/BiOBr增强可见光催化RhB机理进行解释。     

氮缺陷石墨相氮化碳的制备及其光催化降解环境有机污染物性能（英文）

通过在三聚氰胺热分解过程中加入NaHCO_3制备出具有氮缺陷的石墨相氮化碳(g-C_3N_4),利用X射线衍射(XRD)、傅里叶变换红外光谱(FT-IR)、N2吸附-脱附、X射线光电子能谱(XPS)、紫外-可见漫反射光谱(UV-vis DRS)和固体荧光光谱(PL)等方法对其进行表征,并在可见光(λ420 nm)照射下,以水相中罗丹明B(Rh B)的降解为模型反应,研究了该氮缺陷g-C_3N_4对有机污染物降解的光催化活性。结果表明,引入氮缺陷可以提高g-C_3N_4对可见光的吸收以及电子-空穴对的分离效率,进而提高g-C_3N_4的可见光催化活性。催化剂CNK0.005、CNK0.01和CNK0.05在30 min内对Rh B的降解率分别为79.8%、100.0%和87.6%;而在相同条件下,没有氮缺陷的g-C_3N_4对RhB的降解率仅为59.8%。     

碳纳米管改性g-C3N4提升可见光催化降解性能

以尿素为原料,引入少量的多壁碳纳米管(CNT)改性,采用简便方法制备CNT/g-C_3N_4催化剂。利用扫描电镜(SEM)、透射电镜(TEM)、傅里叶红外光谱仪(FT-IR)、X射线衍射(XRD)、X射线光电子能谱(XPS)、紫外-可见-近红外分光光度计(UV-Vis-NIR Spectrophotometer)、荧光光谱(PL)等手段对CNT/g-C_3N_4催化剂进行表征。结果表明,g-C_3N_4与CNT之间的协同作用,影响了gC_3N_4的能带结构,增强了其对可见光的吸收,改善了光生载流子的分布,提高了电子-空穴对的分离效率。并以罗丹明B(RhB)水溶液模拟废水,在可见光下考察催化剂的光催化降解性能,发现当CNT掺杂量为0.1%(w/w)时效果最佳,降解速率常数是体相g-C_3N_4的3.1倍,且研究发现超氧自由基是该体系下的主要活性物种。     

Sol-gel synthesis of K3InF6 and structural characterization of K2InC10O10H6F9, K3InC12O14H4F18 and K3InC12O12F18

K₃InF₆ is synthesized by a sol-gel route starting from indium and potassium acetates dissolved in isopropanol in the stoichiometry 1:3, with trifluoroacetic acid as fluorinating agent. The crystal structures of the organic precursors were solved by X-ray diffraction methods on single crystals. Three organic compounds were isolated and identified: K₂InC₁₀O₁₀H₆F₉, K₃InC₁₂O₁₄H₄F₁₈ and K₃InC₁₂O₁₂F₁₈. The first one, deficient in potassium in comparison with the initial stoichiometry, is unstable. In its crystal structure, acetate as well as trifluoroacetate anions are coordinated to the indium atom. The two other precursors are obtained, respectively, by quick and slow evaporation of the solution. They correspond to the final organic compounds, which give K₃InF₆ by decomposition at high temperature. The crystal structure of K₃InC₁₂O₁₄H₄F₁₈ is characterized by complex anions [In(CF₃COO)₄(OH_x)₂]^(5−2x)− and isolated [CF₃COOH_2−x]^(x−1)− molecules with x=2 or 1, surrounded by K⁺ cations. The crystal structure of K₃InC₁₂O₁₂F₁₈ is only constituted by complex anions [In(CF₃COO)₆]³⁻ and K⁺ cations. For all these compounds, potassium cations ensure only the electroneutrality of the structure. IR spectra of K₂InC₁₀O₁₀H₆F₉ and K₃InC₁₂O₁₂F₁₈ were also performed at room temperature on pulverized crystals.     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

Ion-beam irradiation of lanthanum compounds in the systems La2O3-Al2O3 and La2O3-TiO2

Thin crystals of La₂O₃, LaAlO₃, La_2/3TiO₃, La₂TiO₅, and La₂Ti₂O₇ have been irradiated in situ using 1 MeV Kr²⁺ ions at the Intermediate Voltage Electron Microscope-Tandem User Facility (IVEM-Tandem), Argonne National Laboratory (ANL). We observed that La₂O₃ remained crystalline to a fluence greater than 3.1×10¹⁶ ions cm⁻² at a temperature of 50 K. The four binary oxide compounds in the two systems were observed through the crystalline-amorphous transition as a function of ion fluence and temperature. Results from the ion irradiations give critical temperatures for amorphisation (T_c) of 647 K for LaAlO₃, 840 K for La₂Ti₂O₇, 865 K for La_2/3TiO₃, and 1027 K for La₂TiO₅. The T_c values observed in this study, together with previous data for Al₂O₃ and TiO₂, are discussed with reference to the melting points for the La₂O₃-Al₂O₃ and La₂O₃-TiO₂ systems and the different local environments within the four crystal structures. Results suggest that there is an observable inverse correlation between T_c and melting temperature (T_m) in the two systems. More complex relationships exist between T_c and crystal structure, with the stoichiometric perovskite LaAlO₃ being the most resistant to amorphisation.     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

A new 2212-type stair like structure: Bi14Sr21Fe12O61, m=5 member of the generic [Bi2Sr3Fe2O9]m[Bi4Sr6Fe2O16] family

A new oxide, Bi₁₄Sr₂₁Fe₁₂O_61, with a layered structure derived from the 2212 modulated type structure Bi₂Sr₃Fe₂O₉, was isolated. It crystallizes in the I2 space group, with the following parameters: a=16.58(3) Å, b=5.496(1) Å, c=35.27(2) Å and β=90.62°. The single crystal X-ray structure determination, coupled with electron microscopy, shows that this ferrite is the m=5 member of the [Bi₂Sr₃Fe₂O₉]_m[Bi₄Sr₆Fe₂O₁₆] collapsed family. This new collapsed structure can be described as slices of 2212 structure of five bismuth polyhedra thick along , shifted with respect to each other and interconnected by means of [Bi₄Sr₆Fe₂O₁₆] slices. The latter are the place of numerous defects like iron or strontium for bismuth substitution; they can be correlated to intergrowth defects with other members of the family.     

Raman scattering investigations on lanthanum-doped Bi4Ti3O12-SrBi4Ti4O15 intergrowth ferroelectrics

The ferroelectric ceramics of Bi₄Ti₃O₁₂, SrBi₄Ti₄O₁₅, and lanthanum-doped Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅ were synthesized, and their Raman spectra were investigated. La-doping resulted in the enlargement of remnant polarization of Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅. The structure of the Bi₂O₂ layers and TiO₆ octahedra of the intergrowth was found to be different from those of Bi₄Ti₃O₁₂ and SrBi₄Ti₄O₁₅. La³⁺ ions exhibit pronounced selectivity for the occupation of A site as La content is lower than 0.50, and tend to be incorporated into Bi₂O₂ layers when the La content is higher than 0.50. Lanthanum substitution brings about the structural phase transition in Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅. The variation of ferroelectric property may be attributed to combined contribution from the decreasing of the oxygen vacancies, the relaxation of the lattice distortion, the destroying of the insulation and the space charge compensation effects of the Bi₂O₂ slabs.     

Crystal growth, structural characterization and magnetic properties of Ca3CuRhO6, Ca3Co1.34Rh0.66O6 and Ca3FeRhO6

Single crystals of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ were synthesized by high temperature flux growth in molten K₂CO₃ and structurally characterized by single crystal X-ray diffraction. While Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ crystallize with trigonal (rhombohedral) symmetry in the space group , Z=6: Ca₃Co_1.34Rh_0.66O₆a=9.161(1) Å, c=10.601(2) Å; Ca₃FeRhO₆a=9.1884(3) Å, c=10.7750(4) Å; Ca₃CuRhO₆ adopts a monoclinic distortion of the K₄CdCl₆ structure in the space group C2/c, Z=4: a=9.004(2) Å, b=9.218(2) Å, c=6.453(1) Å, β=91.672(5). All crystals of Ca₃CuRhO₆ examined were twinned by pseudo-merohedry. Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are structurally related and contain infinite one-dimensional chains of alternating face-sharing RhO₆ octahedra and MO₆ trigonal prisms. In the monoclinic modification, the copper atoms are displaced from the center of the trigonal prism toward one of the rectangular faces adopting a pseudo-square planar configuration. The magnetic properties of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are discussed.     

Magnetic diphase nanostructure of ZnFe2O4/γ-Fe2O3

Magnetic diphase nanostructures of ZnFe₂O₄/γ-Fe₂O₃ were synthesized by a solvothermal method. The formation reactions were optimized by tuning the initial molar ratios of Fe/Zn. All samples were characterized by X-ray diffraction, thermogravimetric analysis, infrared spectroscopy, and Raman spectra. It is found that when the initial molar ratio of Fe/Zn is larger than 2, a diphase magnetic nanostructure of ZnFe₂O₄/γ-Fe₂O₃ was formed, in which the presence of ZnFe₂O₄ enhanced the thermal stability of γ-Fe₂O₃. Further increasing the initial molar ratio of Fe/Zn larger than 6 destabilized the diphase nanostructure and yielded traces of secondary phase α-Fe₂O₃. The grain surfaces of diphase nanostructure exhibited a spin-glass-like structure. At room temperature, all diphase nanostructures are superparamagnetic with saturation magnetization being increased with γ-Fe₂O₃ content.