负载金属对WO3-TiO2光催化剂结构与催化性能的影响

用溶胶-凝胶和浸渍-还原相结合的方法制得M/WO₃-TiO₂ (M＝Pd, Cu, Ni, Ag)光催化剂. 利用X射线衍射(XRD)、程序升温还原(TPR)、红外(IR)、程序升温脱附(TPD)、紫外-可见漫反射光谱(UV-Vis-DRS)和光反应器等技术研究了复合半导体负载金属的物相结构、光吸收性能和光催化反应性能. 结果表明: 金属负载在复合半导体上延迟了TiO₂由锐钛矿向金红石相转化, 增强W与载体TiO₂的相互作用, 使TiO₂光吸收限发生蓝移, 对可见光部分的吸收明显增加; 固体材料吸光性能强弱顺序Pd/WO₃-TiO₂＞Cu/WO₃-TiO₂＞Ag/WO₃-TiO₂＞Ni/WO₃-TiO₂; 金属Pd对CO₂吸附能力过强, 卧式吸附态脱附温度高, 光催化效率不高; 金属Cu对CO₂吸附能力适中, CO₂与C₃H₆脱附温度较接近, 实现了“光-表面-热”协同作用, 光量子效率最高, 达到19.7%.     

复合半导体负载金属材料光催化性能研究

CO₂和烃类光催化直接合成烃类氧化物在合成化学、碳资源利用和环境保护等方面均有重大意义。用溶胶-凝胶和浸渍-还原相结合的方法制得M/V₂O₅-TiO₂(M=Pd、Cu、Ni和Ag)光催化剂。利用XRD、TPR、IR、TPD、UV-Vis DRS和光反应器等技术研究了负载金属复合半导体的物相结构、吸附性能、光吸收性能和光催化反应性能。结果表明：金属负载在复合半导体上延迟了TiO₂由锐钛矿向金红石相的转化,增强了V与载体TiO₂的相互作用,使TiO₂光吸收限发生蓝移,对可见光部分的吸收明显增加,拓宽了催化剂的光响应范围;材料吸光性能强弱顺序Pd/V₂O₅-TiO₂ >Cu/V₂O₅-TiO₂ >Ag/V₂O₅-TiO₂>Ni/V₂O₅-TiO₂;材料的吸附性能及反应物的吸附态是反应发生的关键,CO₂在Ag/V₂O₅-TiO₂表面无法形成卧式吸附态,没有目的产物甲基丙烯酸(MAA)生成,光量子效率低;光吸收性能较好的Pd/V₂O₅-TiO₂对CO₂吸附能力过强,卧式吸附态脱附温度高,光催化效率不高;Cu/V₂O₅-TiO₂对CO₂吸附能力适中,CO₂与C₃H₆脱附温度较接近,实现了“光-表面-热”的协同作用,光量子效率最高,达15.1%。     

纳米复合材料Ag/MxOy-TiO2(MxOy=ZnO、Al2O3和Fe2O3)的制备及其微波辅助光催化降解甲基橙

采用溶胶-凝胶-程序升温溶剂热一步法,利用表面活性剂EO₂₀PO₇₀EO₂₀(P123)作为模板剂,分别制备了三元纳米复合材料Ag/ZnO-TiO₂、Ag/Al₂O₃-TiO₂和Ag/Fe₂O₃-TiO₂。通过XRD、氮气吸附-脱附测定、TEM以及扫描电子显微镜配合X-射线能量色散谱仪(SEM-EDS)等对合成的3种催化剂进行了对比表征分析。结果表明,复合材料Ag/M_xO_y-TiO₂中Ag以单质形式存在并较好地分布在M_xO_y-TiO₂表面上。所合成产物颗粒尺寸较小(约10 nm左右),形貌较好。其中,Ag/ZnO-TiO₂的比表面积与Ag/Al₂O₃-TiO₂十分相近,略大于Ag/Fe₂O₃-TiO₂。光催化活性研究中,以甲基橙为模型分子且辅以微波场作用。结果显示,上述三元复合材料的活性均明显高于未掺杂银的二元复合材料,其中Ag/ZnO-TiO₂的光催化活性最好,在90 min内对甲基橙的降解率高达86%。     

Bi2WO6/TiO2纳米管异质结构复合材料的多模式下的光催化活性比较

以TiO₂纳米管为模板,采用多组分自组装结合水热法制备Bi₂WO₆/TiO₂纳米管异质结构复合材料。通过多种技术如X射线衍射（XRD）,X射线光电子能谱（XPS）,N₂吸附脱附,扫描电镜（SEM）,高分辨透射电镜（HRTEM）和紫外可见漫反射吸收光谱（UV-Vis DRS）考察所制备样品的组成、结构、形貌、光吸收和电子性质。Bi₂WO₆纳米片或纳米粒子分布在TiO₂纳米管上,形成异质结构。随后,通过在紫外、可见和微波辅助光催化模式下降解染料罗丹明B（RhB）来评价复合催化剂的光催化活性。与TiO₂纳米管和Bi₂WO₆相比,Bi₂WO₆/TiO₂-35纳米管在多模式下表现出更优异的光催化活性。与紫外和可见降解模式相比,Bi₂WO₆/TiO₂-35纳米管在微波辅助光催化模式下对RhB的降解效率最高。这种增强的光催化活性源于适量Bi₂WO₆的引入、纳米管独特的形貌特征和降解模式所引起的增强的量子效率。降解过程中的活性物种被证明是h⁺,·OH和·O₂^-自由基。而且,在微波辅助光催化模式下,可产生更多的·OH和·O₂^-自由基。     

Bi2WO6/TiO2纳米管异质结构复合材料的多模式下的光催化活性比较

以TiO₂纳米管为模板,采用多组分自组装结合水热法制备Bi₂WO₆/TiO₂纳米管异质结构复合材料。通过多种技术如X射线衍射（XRD）,X射线光电子能谱（XPS）,N₂吸附-脱附,扫描电镜（SEM）,高分辨透射电镜（HRTEM）和紫外可见漫反射吸收光谱（UV-Vis DRS）考察所制备样品的组成、结构、形貌、光吸收和电子性质。Bi₂WO₆纳米片或纳米粒子分布在TiO₂纳米管上,形成异质结构。随后,通过在紫外、可见和微波辅助光催化模式下降解染料罗丹明B（RhB）来评价复合催化剂的光催化活性。与TiO₂纳米管和Bi₂WO₆相比,Bi₂WO₆/TiO₂-35纳米管在多模式下表现出更优异的光催化活性。与紫外和可见降解模式相比,Bi₂WO₆/TiO₂-35纳米管在微波辅助光催化模式下对RhB的降解效率最高。这种增强的光催化活性源于适量Bi₂WO₆的引入、纳米管独特的形貌特征和降解模式所引起的增强的量子效率。降解过程中的活性物种被证明是h⁺,·OH和·O₂^-自由基。而且,在微波辅助光催化模式下,可产生更多的·OH和·O₂^-自由基。     

TiO2负载型催化剂及光催化还原CO2反应的表面光电压谱研究

The study of mechanism of modified TiO₂ photocatalysts for photoreduction of CO₂ with surface photovoltage spectrum(SPS) was reported for the first time．The results showed that a new surface photovoltaic response band appears in the SPS curve of Pd/TiO₂ or Pd/RuO₂/TiO₂ in near IR region,moreover,the stronger SPS response intensity in near IR is,the higher the catalytic activities of photoreduction of CO₂．The surface state plays a role in the process of photocatalysis．     

用分子轨道理论研究NO气体在TiO2表面吸附

根据一氧化氮(NO)气体在二氧化钛(TiO₂)表面吸附和脱附的实验结果, 揭示了气体脱附量的变化规律. 利用MOPAC 和GAUSSIAN分子轨道理论计算了在TiO₂(110)表面上吸附NO分子的原子簇模型, 电荷分布以及原子簇的能级, 推断了NO在TiO₂(110)表面吸附的稳定性.     

FeO(OH)-TiO2/CoPi复合光阳极的制备及其光电催化氧化水性能

采用溶胶-凝胶法制备了TiO₂ 纳米晶, 并通过浸渍技术在其表面引入了FeO(OH). 采用紫外-可见(UV-Vis)吸收光谱确定了引入FeO(OH)的最佳Fe³⁺浓度. 通过电化学法在FeO(OH)-TiO₂光阳极上沉积了催化水分解制备氧气的钴基催化剂(CoPi), 得到了FeO(OH)-TiO₂/CoPi 复合光阳极. 利用透射电镜(TEM), 高分辨透射电镜(HRTEM), X射线衍射(XRD), 扫描电镜(SEM)对TiO₂纳米晶, FeO(OH)-TiO₂以及FeO(OH)-TiO₂/CoPi复合光阳极进行了表征, 采用电化学和光电化学技术研究了中性条件下FeO(OH)-TiO₂/CoPi 复合光阳极的光电催化分解水性能. 结果表明, TiO₂纳米晶为梭形的锐钛矿, 其表面修饰的FeO(OH)为针铁矿型, 且当前驱体溶液中Fe³⁺与TiO₂的质量比为0.05%时得到的FeO(OH)-TiO₂具有最佳的光吸收效果. 形成FeO(OH)-TiO₂/CoPi复合光阳极后, 在光照条件下CoPi 电催化分解水制备氧气的过电位显著降低. TiO₂表面FeO(OH)的引入增加了光阳极对可见光的吸收能力, 同时光阳极表面沉积的CoPi有效地利用了FeO(OH)-TiO₂产生的光生空穴, 将水氧化形成氧气, 从而在光照条件下显著提高了CoPi催化氧化水的效率.     

NO气体在TiO2表面的吸附行为

采用TPD (Temperature Programmed Desorption)试验方法测定了NO在TiO₂表面吸附后的脱附谱, 揭示了气体脱附量的变化规律. 结果表明, NO在TiO₂表面吸附后可在两个峰值温度450和980 K脱附出N₂气体, 其活化能分别是0.48 和2.5 eV. TiO₂表面经预覆氧处理后, N₂的脱附量降低. N₂的脱附量随NO气体暴露量增加而增加, 但当气体覆盖度超过一定值后, 脱附量趋于定值. 脱附峰值温度随气体暴露量的增加而降低.     

NO气体在TiO2表面的吸附行为

采用TPD (Temperature Programmed Desorption)试验方法测定了NO在TiO₂表面吸附后的脱附谱, 揭示了气体脱附量的变化规律. 结果表明, NO在TiO₂表面吸附后可在两个峰值温度450和980 K脱附出N₂气体, 其活化能分别是0.48 和2.5 eV. TiO₂表面经预覆氧处理后, N₂的脱附量降低. N₂的脱附量随NO气体暴露量增加而增加, 但当气体覆盖度超过一定值后, 脱附量趋于定值. 脱附峰值温度随气体暴露量的增加而降低.     

负载金属对MoO3-TiO2光催化剂结构与催化性能的影响

用溶胶-凝胶和浸渍-还原相结合的方法制得M/MoO3-TiO2 (M=Pd, Cu, Ni和Ag)光催化剂。利用X-射线衍射(XRD)、程序升温还原(TPR)、红外光谱(IR)、程序升温脱附(TPD)、紫外-可见漫反射光谱(UV-VisDRS)和光反应等技术，研究了负载金属复合半导体的物相结构、吸附性能、吸光性能和光催化反应性能。结果表明，金属M(M=Pd, Cu)负载在复合半导体上，延迟了TiO2由锐钛矿向金红石相的转化，增强了Mo与载体TiO2的相互作用，促进Mo物种由四面体配位向八面体配位转化，使TiO2光吸收限发生蓝移，对可见光部分的吸收明显增加，拓宽了催化剂的光响应范围；固体材料吸光性能强弱顺序Pd/MoO3-TiO2 >Cu/MoO3-TiO2>Ag/MoO3-TiO2>Ni/MoO3-TiO2；Pd对CO2吸附能力过强，卧式吸附态脱附温度高，光催化效率不高；金属Cu对CO2吸附能力适中，CO2与C3H6脱附温度较接近，实现了光-表面-热的协同作用，光量子效率最高。     

Preparation and Characterisation of Nano-Structured WO<Subscript>3</Subscript>-TiO<Subscript>2</Subscript> Layers for Photoelectrochromic Devices

Nano-structured WO₃-TiO₂ layers were prepared by the sol-gel route. To obtain transparent, porous and crack free layers up to 0.8 μ m with a single dipping cycle a templating strategy was used. As a template three-dimensionally network based on organically modified silane was introduced to the WO₃ and TiO₂ sols. The WO₃ layers were dip-coated onto the conductive glass substrate (TCO) and the TiO₂ layers on the top of the WO₃ layer. The morphology and the structure of the layers were determined by Scanning Electron Microscopy (SEM), High Resolution Transmission Electron Microscopy (HR-TEM), Energy Dispersive X-Ray Spectroscopy (EDXS), Auger and Infrared spectroscopy. SEM image of the WO₃-TiO₂ layer confirmed the nano-porosity of the layers and give the size of the particles of about 10 nm for TiO₂ and 30 nm for WO₃ layer. Further analysis indicated that the titanium sol penetrates the WO₃ layer. Particles in the WO₃ layer consist of a crystalline monoclinic WO₃ core surrounded by a 5–10 nm amorphous phase consisting of WO₃, TiO₂ and SiO₂. The WO₃-TiO₂ layers were used to assemble all solid state photoelectrochromic (PE) devices. Under 1 sun irradiation (1000 W/m²) the visible transmittance of the PE device changes from 62% to 1.6%. The colouring and bleaching processes last about 10 minutes.     

Detection of nitrogen dioxide using mixed tungsten oxide-based thick film semiconductor sensor

The thick film semiconductor sensor for NO₂ gas detection was fabricated by screen-printing method using a mixed WO₃-based as sensing material. The sensing characteristics, such as response time, response linearity, sensitivity, working range, cross sensitivity, and long-term stability were further studied by using a WO₃-based mixed with different metal oxides (SnO₂, TiO₂ and In₂O₃) and doped with noble metals (Au, Pd and Pt) as sensing materials was observed. The highest sensitivity for low concentrations (<16 mg l⁻¹) was observed using WO₃-based mixed with In₂O₃ or TiO₂. The NO₂ gas sensor showing the fastest response and recovery time (both within 2 min), good linearity (Y=0.606X+0.788 R²=0.991) for gas concentrations from 3 to 310 mg l⁻¹, low resistance (3 MΩ), high sensitivity, undesirable cross sensitivity effect and good long-term stability (at least 120 days) using WO₃-SnO₂-Au as sensing material.     

Influence of CeO2 addition on the physicochemical and catalytic properties of Pd/TiO2 catalysts in CO oxidation

The influence of CeO₂ addition on the formation of the microstructure, electronic state, and catalytic properties of Pd/TiO₂ supported catalysts in CO oxidation were investigated. It was shown that, when Pd is supported on titanium dioxide modified with cerium dioxide, annealing at 500°C results in the formation of Pd/(CeO₂-TiO₂) catalysts with a nanocrystalline structure composed of incoherently intergrown fine anatase crystals and interblock boundaries in which palladium and cerium are stabilized. The higher catalytic activity of Pd/(CeO₂-TiO₂) catalysts compared to Pd/TiO₂ catalysts is explained by the smaller size of Pd particles and the higher proportion of palladium in the Pd^δ+ state.     

Comparison of CO2 Reduction Performance with NH3 and H2O between Cu/TiO2 and Pd/TiO2

The aim of this study is to clarify the effect of doped metal type on CO₂ reduction characteristics of TiO₂ with NH₃ and H₂O. Cu and Pd have been selected as dopants for TiO₂. In addition, the impact of molar ratio of CO₂ to reductants NH₃ and H₂O has been investigated. A TiO₂ photocatalyst was prepared by a sol-gel and dip-coating process, and then doped with Cu or Pd fine particles by using the pulse arc plasma gun method. The prepared Cu/TiO₂ film and Pd/TiO₂ film were characterized by SEM, EPMA, TEM, STEM, EDX, EDS and EELS. This study also has investigated the performance of CO₂ reduction under the illumination condition of Xe lamp with or without ultraviolet (UV) light. As a result, it is revealed that the CO₂ reduction performance with Cu/TiO₂ under the illumination condition of Xe lamp with UV light is the highest when the molar ratio of CO₂/NH₃/H₂O = 1:1:1 while that without UV light is the highest when the molar ratio of CO₂/NH₃/H₂O = 1:0.5:0.5. It is revealed that the CO₂ reduction performance of Pd/TiO₂ is the highest for the molar ratio of CO₂/NH₃/H₂O = 1:1:1 no matter the used Xe lamp was with or without UV light. The molar quantity of CO per unit weight of photocatalyst for Cu/TiO₂ produced under the illumination condition of Xe lamp with UV light was 10.2 μmol/g, while that for Pd/TiO₂ was 5.5 μmol/g. Meanwhile, the molar quantity of CO per unit weight of photocatalyst for Cu/TiO₂ produced under the illumination condition of Xe lamp without UV light was 2.5 μmol/g, while that for Pd/TiO₂ was 3.5 μmol/g. This study has concluded that Cu/TiO₂ is superior to Pd/TiO₂ from the viewpoint of the molar quantity of CO per unit weight of photocatalyst as well as the quantum efficiency.     

Fe3+掺杂TiO2/凹凸棒复合光催化剂的制备和光催化活性

用酸催化溶胶-凝胶法制备了Fe³⁺掺杂TiO₂/凹凸棒（Fe³⁺-TiO₂/ATP）复合光催化剂,对其结构、微观形貌、光吸收性能和可见光下的光催化性能进行了表征。XRD和TEM测试结果表明,Fe³⁺-TiO₂/ATP具有较好的热稳定性,经450 ℃热处理后的ATP晶体结构基本保持不变,锐钛矿TiO2均匀的分布在ATP表面,TiO2颗粒之间无团聚,且平均粒径小于纯TiO₂。UV-Vis-DRS测试结果表明,Fe³⁺的掺杂可明显增强复合光催化剂对可见光的吸收,光响应范围拓展到了整个紫外-可见光区。在可见光下,Fe³⁺-TiO₂/ATP复合光催化剂对亚甲基蓝具有很好的催化降解活性。Fe³⁺-TiO₂/ATP的反应速率常数分别为TiO₂/ATP、P25和纯TiO2的1.37、4.83和6.51倍。复合光催化剂的沉降性能优于纯TiO2和P25,易于分离。     

Construction of SiO2-TiO2/g-C3N4 composite photocatalyst for hydrogen production and pollutant degradation: Insight into the effect of SiO2

Using low-cost precipitated silica (SiO₂) as the carrier, a ternary SiO₂-TiO₂/g-C₃N₄ composite photocatalyst was prepared via the sol-gel method associated with a wet-grinding process. The as-prepared composite exhibits photocatalytic hydrogen production and pollutant degradation performance under solar-like irradiation. The effect of SiO₂ carrier on the properties of the heterostructure between TiO₂ and g-C₃N₄ (CN) was systematically studied. It is found that SiO₂ has important effects on promoting the interaction between TiO₂ and CN. The particle size of TiO₂ and CN was obviously reduced during the calcination process due to the effects of SiO₂. Especially, the TiO₂ particles exhibit monodispersed state with particle size below 10 nm (quantum dots), resulting in the improvement of the contact area and the interaction between TiO₂ and CN, and leading to the formation of efficient TiO₂/CN Z-scheme heterostructure in SiO₂-TiO₂/CN. Besides, the introduction of SiO₂ can increase the specific surface area and light absorption of SiO₂-TiO₂/CN, further promoting the photocatalytic reaction. As expected, the optimum SiO₂-TiO₂/CN composite exhibits 12.3, 3.1 and 2.9 times higher photocatalytic hydrogen production rate than that of SiO₂-TiO₂, CN and TiO₂/CN under solar-like irradiation, while the photocatalytic active component in SiO₂-TiO₂/CN is only about 60 wt%. Moreover, the rhodamine B degradation rate of SiO₂-TiO₂/CN is also higher than that of SiO₂-TiO₂, CN and TiO₂/CN.     

Influence of NH<Subscript>3</Subscript>-treating temperature on visible light photocatalytic activity of N-doped P<Subscript>25</Subscript>-TiO<Subscript>2</Subscript>

The influence of NH₃-treating temperature on the visible light photocatalytic activity of N-doped P₂₅-TiO₂ as well as the relationship between the surface composition structure of TiO₂ and its visible light photocatalytic activity were investigated. The results showed that N-doped P₂₅-TiO₂ treated at 600°C had the highest activity. The structure of P₂₅-TiO₂ was converted from anatase to rutile at 700°C. Moreover, no N-doping was detected at the surface of P₂₅-TiO₂. There was no simply linear relationship between the visible light photocatalytic activity and the concentration of doped nitrogen, and visible light absorption. The visible light photocatalytic activity of N-doped P₂₅-TiO₂ was mainly influenced by the synergistic action of the following factors: (i) the formation of the single-electron-trapped oxygen vacancies (denoted as V_o^·); (ii) the doped nitrogen on the surface of TiO₂; (iii) the anatase TiO₂ structure.     

V2O5-TiO2复合半导体光催化材料结构及光响应性能研究

采用溶胶凝胶法制备了V₂O₅-TiO₂复合半导体材料，通过Raman、XRD及UV-Vis DRS等实验方法研究了V₂O₅与TiO₂复合对材料表面组成、晶体结构以及光响应性能的影响。结果表明：钒加入后优先与TiO₂作用形成较为稳定的金红石型TiVO₄晶相，其中V⁴⁺是促进TiO₂发生相变的关键；随着钒加入量的增加，V₂O₅由表面高分散状态逐渐聚集形成晶相，并释放部分Ti⁴⁺使之形成锐钛矿型TiO₂晶相，使得体相中金红石型TiO₂的含量有所下降；复合后形成的TiVO₄晶相显著提高了材料对可见光的吸收率，并使其吸光域红移至460 nm左右。