钛基PbO2+nano-WO3电极材料的复合共沉积及析氧活性

利用复合共沉积法,在涂有中间层SnO2-Sb2O5的Ti基体上制备了PbO2+nano-WO3复合电极材料.采用X射线衍射(XRD)、X射线光电子能谱(XPS)、扫描电子显微镜(SEM)和双电层电容法等对复合电极表面的组成、结构、形貌及有效电化学面积进行测试.结果表明,随着纳米WO3掺杂量逐渐增大,复合电极的表面粗糙度和孔隙率逐渐变大,电化学有效面积也随之增大;利用线性扫描及Tafel曲线等电化学测试方法研究了nano-WO3的掺杂对复合电极析氧活性的影响,结果表明,掺杂nano-WO3的复合电极较纯PbO2电极的析氧活性大幅提高,其起始析氧电位发生负移,析氧过电位下降,最大可降低近300 m V.     

阳极电沉积条件对Ti/SnO2-Sb2O5/PbO2+Nano-Co3O4复合电极组成、形貌和结构的影响

本文在涂有中间层SnO2-Sb2O5的Ti基体上,采用阳极复合电沉积法制备了Ti/SnO2-Sb2O5/PbO2+Nano-Co3O4复合电极材料,借助于X射线衍射（XRD）、X射线光电子能谱（XPS）、扫描电镜（SEM）等分析方法研究了制备条件对该复合电极材料的组成、结构和形貌的影响。结果表明,纳米Co3O4的掺杂可提高PbO2电极表面的粗糙度和空隙率;沉积电位、镀液中Co3O4粒子浓度及有机溶剂的添加均对镀层中Co3O4的嵌入量有很大影响。     

模板法制备的掺镧氧化镍多孔空心微球及电化学电容性能

采用模板法在水热条件下合成了掺La的NiO多孔空心球。采用X射线衍射(XRD)、X射线光电子能谱(XPS)、扫描电镜(SEM)、透射电子显微镜(TEM)和X射线能谱(EDS)对其结构和形貌进行了表征。采用循环伏安、恒流充放电技术对其电化学性能进行了测试,研究结果表明,La掺杂对NiO空心球的粒径、壳层厚度和电化学性能均有显著影响,当La掺杂量为1.30mol%时,掺杂后NiO的单电极比电容达到205 F.g-1,比未掺杂的提高了50%,并且表现出良好的循环稳定性和可逆性。     

不同掺杂元素的钛基PbO2电极对苯酚电催化氧化性能的影响

本文在SnO2-Sb2O5氧化物为中间层的钛基体上,采用电沉积法制备了无掺杂的Ti/PbO2、掺杂F的Ti/PbO2(Ti/PbO2+F)和掺杂Co3O4纳米粒子的Ti/PbO2电极(Ti/PbO2+Nano-Co3O4).用X射线衍射(XRD)和扫描电镜(SEM)分析和观察了电极材料的组成、结构和形貌,并通过电化学方法研究了这三种电极对苯酚的电催化氧化性能.结果表明,Ti/PbO2+F电极的析氧电位较Ti/PbO2电极的发生明显正移,但其苯酚的氧化峰和析氧峰并不能分开;而Ti/PbO2+Nano-Co3O4电极虽然其析氧电位负移,但对苯酚的氧化峰出现在析氧峰之前.这一结果表明,体系存在着某种反应特别快的瞬态中间体,即在水分子被解离之前已与苯酚发生了反应,从而更有利于苯酚的转化和降解.     

不锈钢基/β-PbO2-TiO2-Co3O4复合镀层制备及其性能表征

使用直流复合电沉积方法制备不锈钢基β-PbO2、TiO2掺杂β-PbO2、Co3O4掺杂β-PbO2、TiO2和Co3O4共掺杂β-PbO2复合镀层材料.采用SEM、EDS、XRD和电化学测试等对复合电极进行形貌、成分、组成和催化活性表征,并且将不锈钢基/β-PbO2-TiO2-Co3O4电极应用到锌电积实验中.结果表明,添加Co3O4能提高PbO2电极的催化活性;添加TiO2可以起到细化晶粒,增大比表面积的作用;不锈钢基β-PbO2-TiO2-Co3O4复合镀层阳极与Pb-Ag合金阳极相比,锌电积槽电压降低为2.97V,电流效率提高到91.2％,使用寿命延长.     

电沉积Ni/LaNiO3复合电极及其在碱性介质中的析氧性能

采用溶胶-凝胶法制备了钙钛矿型复合氧化物LaNiO3,然后将其加入瓦特镀镍液中进行复合电沉积,研究了镀液pH值和阴极电流密度对Ni/LaNiO3复合镀层组成的影响。运用扫描电镜(SEM)、能谱分析(EDS)和X射线衍射(XRD)等对复合镀层进行表征,结果表明:最佳电沉积工艺条件是镀液pH=5.8和阴极电流密度jk=90 mA.cm-2,所得的Ni/LaNiO3复合镀层中LaNiO3的质量含量约为60%。用循环伏安、稳态极化、恒电位阶跃、电化学阻抗谱等电化学技术评价了Ni/LaNiO3复合电极的析氧性能。结果表明:在5 mol.L-1的KOH溶液中,Ni/LaNiO3复合电极的起始析氧电位较镍电极负,表观活化自由能比镍电极降低约2/3,比表面积约为镍电极的55倍,析氧电催化性能得到大幅度提高。     

La掺杂Bi2O3的制备、表征与可见光催化活性

采用浸渍法制备了La掺杂Bi2O3(La-Bi2O3)光催化剂,利用X射线荧光光谱(XRF)、X射线衍射(XRD)、扫描电子显微镜(SEM)、傅立叶变换红外光谱(FT-IR)、X射线光电子能谱(XPS)、紫外-可见吸收光谱(UV-Vis)和光致发光谱(PL)等分析测试手段对样品的La掺杂量、晶体结构和光谱特征等进行了表征,并以2,4-二氯苯酚(2,4-DCP)水溶液的降解作为探针反应,考察了样品的可见光催化性能.结果表明,适量的La掺杂能有效抑制Bi2O3由四方相向单斜相转变,并将光吸收范围拓展到550 nm以上.掺杂的La可取代Bi2O3晶格中部分Bi,形成Bi—O—La键,并生成了少量镧铋复合氧化物(La0.176Bi0.824O1.5),它们的存在能有效抑制光生电子-空穴对的复合,从而提高光催化量子产率.可见光照射下2,4-DCP的光催化降解实验表明,La-Bi2O3具有良好的可见光催化性能,并且当La的掺杂量为3%(摩尔分数)时,催化剂的可见光催化效率最高.     

硫酸盐体系三价铬沉积机理及镀层表征

在新研发的硫酸盐三价铬镀厚铬的镀液体系中, 运用线性扫描伏安法(LSV)和循环伏安法(CV)对三价铬在铜电极表面的电沉积过程进行研究, 并运用X射线荧光测厚仪、扫描电子显微镜(SEM)、X射线能量色散谱(EDS)、X射线衍射仪(XRD)、显微硬度计和Tafel曲线表征铬镀层厚度、形貌、组成、结构、显微硬度及在3.5wt% NaCl溶液中的耐蚀性. 结果表明, 在该体系中三价铬的沉积过程分两步进行(Cr³⁺ + e →Cr²⁺ , Cr²⁺ + 2e → Cr), 第一步得到1个电子, 受电化学过程和扩散过程共同控制, 第二步得到2个电子, 为扩散控制下的不可逆过程; 该镀层为瘤状纳米晶结构, 镀层中含有少量的铁元素(1.10 wt%), 显微硬度达到789.2 Hv, 镀层在3.5wt% NaCl溶液中的腐蚀电位(E_corr)为-0.29 V, 腐蚀电流密度(j_corr)为9.26×10^-5 A·dm^-2.     

La掺杂BiFeO_3对苯酚光催化降解性能的影响（英文）

苯酚是一种稳定、毒性大且难降解的有机物,对人类和生态环境产生很大威胁,因此急需研发出能有效移除工业废水中苯酚污染物的方法.其中,绿色、高效的光催化氧化技术得到研究人员青睐.在半导体光催化剂中,BiFeO_3具有带隙窄(2.2–2.5eV)、化学稳定性好及成本低等优点,被看作是最有潜力的光催化剂.但是,BiFeO_3存在光生电子空穴对复合率高,制备过程中易形成杂质相的缺点,使得其光催化活性很差,限制了BiFeO_3在光催化领域的应用.异种离子的引入能产生杂质能级或裁剪半导体带隙,同时促进光生载流子分离,故可考虑采用离子掺杂改性BiFeO_3的手段来抑制杂质相生成,提高载流子分离,从而提高BiFeO_3的光催化性能.本文以柠檬酸为络合剂,通过一步溶胶凝胶法合成了系列样品Bi_(1-x)La_xFeO_3(摩尔分数x=0,0.10,0.15,0.20).通过X射线衍射(XRD)、扫描电镜(SEM)、能谱(EDS)、透射电镜(TEM)、X射线光电子能谱(XPS)、紫外可见漫反射(UV-VisDRS)及荧光光谱(PL)等手段对不同样品的物相、形貌、表面价态和光学性能进行了表征.并通过活性物种捕获实验和羟基自由基(·OH)产生实验分析了Bi0.85La0.15FeO_3样品在苯酚降解过程中的主要活性物种和降解机理.相对于单相BiFeO_3,La改性BiFeO_3催化剂的光降解苯酚性能均有提高,其中La最佳掺杂量为0.15.在模拟太阳光下照射180min后,Bi0.85La0.15FeO_3的光催化活性达到96%,同时COD去除率达到81.53%,并表现出好的循环使用活性和稳定性.研究发现,该光催化过程中主要的活性物种为·OH.XRD,SEM,TEM和EDS结果表明,La元素掺杂进BiFeO_3结构中,且各元素分布均匀,同时,适量La元素掺杂能有效抑制杂质相Bi25FeO_40的形成,而且La掺杂BiFeO_3样品的颗粒尺寸略有减小,有利于电子空穴转移.XPS显示,La改性BiFeO_3样品的表面有氧空位形成,将有利于有机物的吸附和降解;另外,羟基氧和吸附氧含量增大,有利于活性氧物种形成.UV-VisDRS和PL测试证明,La改性后的样品对可见光的响应增强,样品带隙变窄,产生杂质能级,抑制了光生载流子复合,有利于产生更多载流子来促进活性物种形成,从而提高光催化活性.氧物种捕获实验说明,在Bi_(0.85)La_(0.15)FeO_3参与的苯酚降解过程中的主要活性物种是·OH,同时·OH的产生实验也证明了在光照下·OH在Bi_(0.85)La_(0.15)FeO_3光催化剂表面持续产生,并提出了光催化降解机理.     

阳极电沉积Ti/MnO2电极及其苯酚降解的电催化性能

应用阳极电沉积法制备钛基二氧化锰(Ti/MnO2)电极. 采用X射线衍射(XRD)、扫描电子显微镜(SEM)及能谱（EDS）表征电极结构形貌. 用V~logi及苯酚降解实验优化电极制备工艺参数：在电流密度4 mA•cm-2、Mn2+离子浓度0.5 mol•L-1及温度70 ℃条件下阳极电沉积Ti/MnO2电极. 以苯酚为目标有机物,评价该电极电催化氧化性能,降解7h降解效率达49.6%.     

Cu/BiVO_4复合光催化剂的制备及可见光催化活性(英文)

利用水热法制备了Cu掺杂的BiVO4复合可见光催化剂,借助X射线衍射(XRD)、X射线光电子能谱(XPS)、紫外-可见漫反射光谱(DRS)和扫描电子显微镜(SEM)对其进行表征.XRD分析显示所有催化剂都呈现单斜结构.XPS结果显示掺杂元素均以其稳定氧化态形式存在于催化剂表面.DRS谱中掺杂样品的吸收边比纯BiVO4都有不同程度的红移.以甲基橙(MO)的可见光催化降解反应为探针,研究了催化剂的可见光催化性能.结果表明,经Cu掺杂改性的催化剂的催化能力比纯BiVO4有所提高.对其掺杂增强催化能力的可能原因进行了讨论.     

In situ electrodeposition of Pt nanoclusters on glassy carbon surface modified by monolayer choline film and their electrochemical applications

Pt nanoclusters attached to the monolayer choline (Ch) modified glassy carbon surface were successfully synthesized by use of in situ cyclic voltammetry (CV) method. Field emission scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and electrochemical impedance spectroscopy (EIS) were used to characterize the properties of this modified electrode. It was demonstrated that Ch was immobilized onto the carbon surface forming a covalently planted Ch monolayer, which could induce the formation of Pt nanoclusters. The preliminary study found that the homogeneous nanostructured Pt/Ch film exhibited remarkable electrocatalytic activity towards the oxidation of methanol and nitrite.     

ZrO2掺杂铌基二氧化铅电极制备及其甲基橙降解电催化性能

本文利用电沉积制得ZrO₂掺杂铌基二氧化铅电极,通过扫描电镜（SEM）和X射线衍射（XRD）观察表征了Nb/ZrO₂+PbO₂电极表面形貌特征及组成. 用线性伏安曲线、电化学交流阻抗和循环伏安曲线测试了Nb/ZrO₂+PbO₂电极电化学性能,及其甲基橙（MO）的降解电催化效果. 结果表明,ZrO₂掺杂使Nb/PbO₂电极表面更致密、粗糙,结晶尺寸更小,增大了电极比表面积,提高了电极电催化活性. Nb/ZrO₂+PbO₂电极活性层主要由β-PbO₂和少量的α-PbO₂以及部分ZrO₂共沉积而成. 有较高的析氧电位、吸附电容和较低的电荷转移电阻,其甲基橙（MO）降解电催化活性更佳,降解过程受扩散控制.     

硫酸介质中Ti／SnO2／PbO2析氧阳极的研究

由于硫酸溶液具有高的电导、一般条件下性质稳定、价格相对低廉等优点，所以电化学合成大多在硫酸溶液中进行．阳极析氧是电化学合成不可避免的阳极过程．但因硫酸的强腐蚀性，以及从阳极析出的氧的强氧化性，使得能满足工业生产的阳极材料很缺乏．自１９５０年荷兰Ｈｅｎ...     

复合金属氧化物Sn-Sb-Mn/陶瓷粒子电极体系的电催化性能

通过热分解法制备了复合金属氧化物Sn-Sb-Mn/陶瓷粒子电极, 分别采用扫描电子显微镜(SEM)、能量色散X 射线能谱(EDS)、X射线衍射(XRD)和N2吸附-脱附等技术对电极的形貌、晶相组成、比表面积和孔径分布进行了表征. 考察了该三维粒子电极系统的析氧特性, 采用循环伏安法分析了三维系统的电催化性能, 并且进行了电化学催化降解苯酚的试验. 结果表明, 制备的陶瓷粒子电极涂层比表面较大、孔结构发达, 有利于电催化反应; 电催化降解主要发生在电化学析氧区; 粒子电极系统对苯酚降解作用显著, 明显高于二维电极系统, 苯酚的去除率为92.3%, 总有机碳(TOC)的去除率为66.7%. 研究结果表明, 该三维粒子电极系统具有优良的电催化性能.     

Novel Bi/BiOBr/AgBr composite microspheres: Ion exchange synthesis and photocatalytic performance

Novel Bi/BiOBr/AgBr composite microspheres were prepared by a rational in situ ion exchange reaction between Bi/BiOBr microspheres and AgNO₃. The characteristic of the as-obtained ternary microspheres was tested by X-ray diffraction (XRD), energy dispersive X-ray spectrometer (EDS), scanning electron microscope (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV–vis diffuse reflectance spectroscopy (UV–vis DRS) and photoluminescence (PL). Under visible light irradiation, Bi/BiOBr/AgBr microspheres exhibited an excellent photocatalytic efficiency for rhodamine B (RhB) degradation, which was about 1.4 and 4.9 times as high as that of Bi/BiOBr and BiOBr/AgBr, demonstrating that the highest separation efficiency of charge carriers in the heterostructured Bi/BiOBr/AgBr. The photocatalytic activity of Bi/BiOBr/AgBr microspheres just exhibited a slight decrease after three consecutive cycles. The photocatalytic mechanism investigation confirmed that the superoxide radicals (O₂^•−) were the dominant reactive oxygen species for RhB degradation in Bi/BiOBr/AgBr suspension.     

Comparison Between Performances of PbO2 and F--doped PbO2 Anodes for Electrochemical Degradation of Aniline

The paper deals with the influence of anode material on the efficiency of degradation for organic pollutants in water system.The electrochemical performance of fluorine ion doped lead dioxide(F--PbO2) electrode for the degradation of aniline was compared with that of undoped lead dioxide(PbO2) electrode by ultraviolet-visible(UV-Vis) spectroscopy,linear voltammetry and other analytical methods,such as the measurement by chemical oxygen demand analyzer,high performance liquid chromatography and scanning electron micrography.It was shown that both PbO2 electrode and F--PbO2 electrode could make aniline be mineralized completely and have the same degradation course,but F--PbO2 electrode has much higher electrocatalytic activity than undoped PbO2 electrode for the electrochemical degradation of aniline.The experimental results confirm that F--PbO2 electrode has much higher potential for oxygen evolution than undoped PbO2 electrode.     

钴掺杂二氧化钛的光催化制氢性能

采用聚合络合法（PCM）制备出钴掺杂二氧化钛（CO/TiO₂）光催化剂.以热重-差示扫描量热同步热分析（TGA-DSC）,傅里叶变换红外（FT-IR）光谱,X射线粉末衍射（XRD）,氮气吸附-脱附,紫外-可见漫反射光谱（UV-Vis DRS）,X射线光电子能谱（XPS）等手段对材料进行了表征.采用光催化制氧作为探针反应,以氧气的产量评价材料的光催化性能结果表明:采用聚合络合法制备的样品主体成分为锐钛矿晶型的二氧化钛,钴元素呈高度分散,钴的掺杂能够明显提升二氧化钛光催化材料的光催化制氢活性,当钴钛物质的量之比为0.3%时,催化剂具有最佳的光催化制氢活性,达到2499μmol,是同等条件下制备的无掺杂二氧化钛的近六倍.还对钴离子掺杂增强机理进行了探讨.