Ni/Al2O3催化2-甲基呋喃加氢制2-甲基四氢呋喃性能的研究

采用浸渍法制备了不同NiO含量的Ni/Al₂O₃催化剂,并进行了2-甲基呋喃加氢制2-甲基四氢呋喃性能的考察。结果表明,在制备的NiO负载量为10%、20%、25%、30%和40%的Ni/Al₂O₃催化剂中,随着NiO负载量增加,加氢反应的选择性与2-甲基呋喃的转化率均呈现出先增加后减小的趋势。其原因是由于适当增加NiO负载量有利于催化剂表面活性中心的形成,有利于加氢反应的进行;但是过度负载的NiO容易堵塞Al₂O₃载体中的介孔通道,降低反应的转化率与选择性。在釜式反应器中进行反应,对加氢反应条件进行了优化,发现在反应压力为3 MPa、反应温度150℃、机械搅拌速率为1000 r/min时,Ni/Al₂O₃催化2-甲基呋喃加氢制2-甲基四氢呋喃具有较高的选择性。当NiO负载量为25%时,2-甲基四氢呋喃的选择性最高为97.1%,2-甲基呋喃的转化率达到99.4%。     

V2O5-Sb2O3-TiO2催化剂 低温NH3还原NO及其抗H2O和SO2毒化性能

浸渍法制备了催化剂V₂O₅-Sb₂O₃-TiO₂,考察了V₂O₅、Sb₂O₃负载量、pH值和焙烧温度对催化剂V₂O₅- Sb₂O₃-TiO₂低温氨选择性催化还原(SCR)NO活性的影响;同时,考察了催化剂V₂O₅-Sb₂O₃-TiO₂抗H₂O和SO₂毒化性能。结果表明,V₂O₅和Sb₂O₃负载量分别为5%和2%、焙烧温度为400℃、pH值为4时,催化剂SCR活性最好,反应温度220℃时,可达97%。Sb₂O₃的加入不仅能增强V₂O₅/TiO₂的催化活性,而且能明显提高催化剂的抗H₂O和SO₂毒化性能。SO₂、NO吸附暂态反应和TG-DTG测试表明,Sb₂O₃的促进机制主要是促进了催化剂在SO₂存在条件下对NO的吸附,同时,减弱了硫酸铵盐与催化剂之间的相互作用,硫酸铵盐更容易分解。     

La_2O_3/γ-Al_2O_3催化剂用于二甲醚二氧化碳重整制氢

采用等体积浸渍法制备了不同负载量的La2O3/γ-Al2O3催化剂,并考察了负载量和反应温度对催化剂用于二甲醚二氧化碳重整制氢反应的性能影响。结果表明,反应温度为550℃、La2O3负载量为15%时,催化剂表现出最好的性能:二甲醚的转化率为100%,二氧化碳的转化率达到85.4%,产物氢气的选择性高达93.3%,一氧化碳的选择性为76.04%,副产物甲烷的选择性仅为6.3%。550℃时其平均积炭速率为1.387 5 mg/(g·h)。研究还利用XRD、BET、TEM、TG等方法对催化剂进行了表征。     

焙烧温度对二甲醚水蒸气重整制氢 Cu/ZnO/Al2O3/Cr2O3+H-ZSM-5双功能催化剂性能的影响

采用共沉淀耦合机械混合法制备了Cu/ZnO/Al₂O₃/Cr₂O₃+H-ZSM-5双功能催化剂,并用于二甲醚水蒸气重整制氢反应,结合热重、傅里叶红外光谱、XRD、BET、H₂-TPR表征,考察了焙烧温度对Cu/ZnO/Al₂O₃/Cr₂O₃催化剂物理化学性质及双功能催化剂催化性能的影响。研究结果表明,400℃焙烧时,析出CuO粒子的同时伴有尖晶石相,进而在反应过程中对金属铜粒子起到良好的隔离作用。而焙烧温度较低时,催化剂分解不完全,催化剂活性位较少。焙烧温度大于500℃时,CuO粒子发生二次团聚,同时尖晶石相大量生成,造成催化剂活性位减少,活性较低。合适的焙烧温度为400℃,此时二甲醚转化率为92.9%,氢气收率可达到76.5%,具有较好的反应效果。     

浆态床中Cu/ZnO/Al2O3/ZrO2+γ-Al2O3双功能催化剂一步法合成二甲醚

采用共沉淀法,制备了纤维状CD501甲醇合成催化剂,采用SEM、TEM、XRD和BET等手段对催化剂进行了表征;并将其进一步和γ-Al₂O₃进行混合,获得了Cu/ZnO/Al₂O₃/ZrO₂+γ-Al₂O₃双功能催化剂,考察了其在浆态床中一步法合成二甲醚过程的催化特性。结果表明,相比商业催化剂(COM)和LP201催化剂,新型的CD501催化剂具有更大的比表面积和Cu/Zn分散性。对于浆态床中一步法合成二甲醚过程,采用CD501与γ-Al₂O₃双功能催化剂,相比采用COM或LP201与γ-Al₂O₃双功能催化剂,CO转化率提高了一倍,且经过270h测试,CO转化率从61%降至57%,二甲醚时空产率从0.54g/(g·h)降至0.48g/(g·h),稳定性显著优于COM催化剂。当反应温度为250℃,压力为4.0MPa,空速为3000mL/(g·h),氢碳比为1.0时,该催化剂应用在浆态床一步法合成二甲醚时,CO转化率为61%,DME时空产率达到0.54g/(g·h)。     

磷改性Cr2O3/Al2O3催化4-乙基酚转化制轻质芳烃

以烷基酚转化为轻质芳烃（苯和甲苯）为目标，制备了Cr₂O₃/Al₂O₃催化剂，并以4-乙基酚为模型化合物研究了其加氢反应性能。体积空速、氢油比、反应压力和温度升高时，脱烷基率、芳烃总选择性、轻质芳烃选择性呈先增大后减小的趋势，反应温度对转化率影响较大。以不同浓度磷酸对Cr₂O₃/Al₂O₃进行改性，随着磷酸用量的增大，催化剂酸量总体增大，主要是弱酸和中强酸，酸强度先增加后降低，磷酸用量较高时，弱酸增加幅度较大。与未改性相比，质量分数8%磷酸改性Cr₂O₃/Al₂O₃上4-乙基酚转化率99.5%，脱烷基率提升9.4%，达74.4%，轻质芳烃选择性提高4.0%，达到57.0%，以较高选择性实现了转化制轻质芳烃，同时，芳烃总选择性高达80.4%，较高程度保持了芳环不被破坏。提出了Cr₂O₃/Al₂O₃上4-乙基酚加氢反应的路径并对反应机理进行了研究。     

Fe2O3/Al2O3氧载体用于甲烷化学链燃烧：负载量与制备方法的影响

以不同方法制备了系列Fe₂O₃/Al₂O₃氧载体,采用XRD、H₂-TPR、CH₄-TPR、O₂-TPD和BET等分析技术对氧载体进行了表征。研究了不同Fe₂O₃负载量氧载体的甲烷化学链燃烧性能,考察了不同制备方法对Fe₂O₃/Al₂O₃氧载体结构、反应性和产物选择性的影响。结果表明,Fe₂O₃负载量对氧载体活性及产物中CO₂选择性的影响较大,负载量较低时氧载体活性较低且引起甲烷部分氧化产物CO含量增加。制备方法亦对氧载体与甲烷的反应活性有所影响,整体上共沉淀法制备的质量分数60％Fe₂O₃/Al₂O₃氧载体具有较高的氧化活性和化学链循环稳定性。其在反应温度850℃、反应时间15 min、30次循环后甲烷转化率及产物中CO₂选择性均未见明显降低。     

KF/Al2O3催化剂上苯脲醇解合成苯氨基甲酸甲酯的研究

采用浸渍法制备负载KF固体碱催化剂,应用于苯脲和甲醇制备苯氨基甲酸甲酯的反应,考察了氧化物载体、卤化钾种类对催化剂性能的影响,KF/Al₂O₃催化剂显示出良好的催化活性和苯氨基甲酸甲酯的选择性。通过对KF/Al₂O₃催化剂中KF的负载量和催化剂焙烧温度的研究发现,在500 ℃焙烧4 h、负载质量分数50%KF的催化剂能够更好地促进MPC生成,苯脲转化率和苯氨基甲酸甲酯选择性分别达到96.5%和86.3%。XRD分析表明,KF与Al₂O₃之间存在较强的相互作用,部分转化为K₃AlF₆。KF与K₃AlF₆分别对甲醇的活化和苯脲的选择性起促进作用,两者的协同效应共同促进了目标产物苯氨基甲酸甲酯的生成。     

丙烷在Ce-Fe/Al2O3/cordierite上选择性催化还原NO

利用凝胶溶胶法和浸渍法制备了Ce-Fe/Al₂O₃/cordierite催化剂,实验研究了其催化丙烷选择性还原NO的特性。结果表明,当铈的负载量从1%增加至5%时,Ce-Fe/Al₂O₃/cordierite的C₃H₈-SCR性能先增强后减弱,3.5Ce-Fe/Al₂O₃/cordierite具有最佳的脱硝性能,在有氧条件下,600℃时可实现96.5%的脱硝效率。Ce的加入能够提升Fe/Al₂O₃/cordierite催化剂的抗硫性能。烟气中通入0.02%的SO₂后,3.5Ce-Fe/Al₂O₃/cordierite催化丙烷还原NO的转化率始终维持在93%,而没有经过Ce修饰的Fe/Al₂O₃/cordierite的NO转化率从88%下降为80%左右。利用XRD、N₂吸附-脱附、SEM、H₂-TPR、吡啶吸附红外光谱等手段研究了催化剂的物理化学性质。结果表明,加入助剂铈能与Fe形成了固溶体,增加催化剂表面Lewis酸浓度和氧化还原能力,从而提高了催化丙烷还原NO的性能。过多的铈引入会减少Fe₂O₃结晶体的形成,不利于在C₃H₈-SCR反应中形成NO₂/NO₃^-物种,从而导致NO还原效率下降。     

混合丁烯齐聚Fe(2/3)xNi1-xSO4-P2O5/γ-Al2O3催化剂制备及性能研究

浸渍法制备了用于混合丁烯齐聚反应的负载型Fe_(2/3)xNi_1-xSO₄-P₂O₅/γ-Al₂O₃催化剂,在高压微型固定床反应器上考察了催化剂制备参数和反应条件对混合丁烯齐聚反应转化率和目的产物选择性的影响。结果表明,在3.0 MPa、100 ℃、空速为2 h^-1的反应条件下,Fe/Ni原子比为2,Fe担载量为0.7 mmol/g(γ-Al₂O₃)时,用共浸渍法制备的催化剂对混合丁烯齐聚转化率和二聚物选择性分别高达50.7%和52.2%。此外,SO₄^2-同γ-Al₂O₃相互作用对混合丁烯齐聚反应的有效活性中心有重要影响。     

Pd-Cu/γ-Al2O3催化苯乙炔选择性加氢反应

为了提高苯乙炔加氢反应中的苯乙烯选择性, 本文采用“胶体-等体积浸渍”两步法制备了Pd-Cu/γ-Al₂O₃双金属催化剂. 利用高分辨率透射电镜(HRTEM)、X射线光电子能谱(XPS)、CO脉冲化学吸附、N2物理吸附、电感耦合等离子体原子发射光谱(ICP-AES)等技术表征了Pd-Cu/γ-Al₂O₃的结构性质, 考察了Cu/Pd 摩尔比、Pd负载量以及金属引入顺序对Pd-Cu/γ-Al₂O₃催化苯乙炔选择性加氢性能的影响. 结果表明, 与Pd/γ-Al₂O₃单金属催化剂相比, Pd-Cu/γ-Al₂O₃的苯乙烯选择性大幅度提高, 尤其是当Pd负载量为0.3%(w), 且Cu/Pd摩尔比为0.6时, Pd-Cu/γ-Al₂O₃表现出优异的加氢选择性; 在0.1 MPa和40 ℃下, 当苯乙炔转化率为90%时, 双金属催化剂的苯乙烯选择性可达95%; 当转化率达到99%以上时, 苯乙烯选择性仍保持在82%左右. 分析表明, Pd-Cu/γ-Al₂O₃中形成了Pd-Cu合金, 但是两种金属间不存在电子转移, Cu对Pd的几何效应才是导致Pd-Cu/γ-Al₂O₃苯乙烯选择性增加的主要原因.     

Effect of La2O3 on a Precipitated Iron Catalyst for Fischer-Tropsch Synthesis

A series of La₂O₃-promoted precipitated iron catalysts (100Fe/2.8Si/nLa, n = 0, 0.5, 1, 2, and 4, atomic ratio) were prepared and characterized by in situ X-ray diffraction, CO temperature-programmed reduction, and N₂ adsorption-desorption. The catalytic performance for Fischer-Tropsch synthesis was studied in a fixed-bed reactor. It was found that the addition of a small amount of La₂O₃ (La/Fe ≤ 0.01) gave a large decrease in the particle size of Fe₂O₃, which increased the specific surface area and dispersion of the catalysts. This also favored the formation of iron carbides, which gave a high catalytic activity in Fischer-Tropsch synthesis. With increasing La₂O₃ content (La/Fe ≥ 0.02), a high La₂O₃ coverage and the formation of a LaFeO₃ compound decreased the formation of iron carbides, and the reaction activity decreased. The optimum La₂O₃ content was La/Fe = 0.01. The addition of La₂O₃ increased the selectivity for methane and suppressed the formation of C₅₊ hydrocarbons.     

The influence of La2O3 and TiO2 on NiO/MgO/α-Al2O3

Summary The effect of La₂O₃ and TiO₂ on product selectivity, methane conversion and coke formation over NiO/MgO/ α -Al₂O₃ catalyst were studied in a simultaneous steam and CO₂ reforming of methane to syngas. La₂O₃ and TiO₂ were added to the catalyst via incipient wetness impregnation and bulk precipitation techniques and catalyst activity was tested in a fixed bed quartz reactor. Results reveal that although the addition of these oxides has no effect on the product selectivity and methane conversion, but can reduce coke formation on the surface of the catalysts as it can enhance the mobility of lattice oxygen anions. The results further show that the catalysts prepared by bulk precipitation technique decrease the coke formation more effectively.     

Toluene methylation on AlPO4-Al2O3 catalysts (5–15 wt.% Al2O3)

The alkylation of toluene with methanol over AlPO₄-Al₂O₃ (5–15 wt.% Al₂O₃) catalysts produces a mixture of xylenes (XYL) although trimethylbenzenes (TMB) were also found. The TMB selectivity increased with temperature at the expense of XYL selectivity. Isomer distribution was approximately 48, 24 and 27 mol% foro-, m- andp-XYL, and 74, 26 and 0 mol% for 1,2,3-, 1,2,4- and 1,3,5-TMB, both quite different from the equilibrium isomer composition. The catalytic activity increased with alumina content, however, it decreased on increasing the calcination temperature in the 923–1273 K range. Good correlations between catalytic activity and the increase in acidic properties with Al₂O₃ loading (as determined by base chemisorption, in the gas phase,versus pyridine and 2,6-dimethylpyridine) have been obtained.     

浸渍法制备的Pd-MnO_x/γ-Al_2O_3催化剂及不同载体对地表O_3降解的影响(英文)

在γ-Al2O3载体上用等体积浸渍法浸渍Pd、MnOx活性组分,然后涂覆于堇青石基体上制备Pd-MnOx/γ-Al2O3整体式催化剂.分别用X射线衍射(XRD)、H2-程序升温还原(H2-TPR)、低温N2吸附-脱附及X射线光电子能谱(XPS)对制备的催化剂进行表征.研究了Pd、MnOx浸渍顺序对催化剂活性、氧化还原性能及织构性质的影响.实验结果表明,Pd、MnOx共浸渍较分别浸渍制备的催化剂活性好,Pd和MnOx之间存在一定的协同作用.考察了不同载体如La-Al2O3、SiO2、γ-Al2O3和Zr-Al2O3对催化剂活性、氧化还原性能、织构性质及表面电子性能的影响.研究表明,以La-Al2O3或SiO2为载体的催化剂活性最好,即,14°C时O3转化率为82%,完全转化温度为36°C.γ-Al2O3载体次之,Zr-Al2O3载体较差.不同载体制备的催化剂中MnOx的氧化还原性能顺序为:PdMnOx/SiO2Pd-MnOx/La-Al2O3Pd-MnOx/γ-Al2O3Pd-MnOx/Zr-Al2O3.     

介孔CuO/γ-Al2O3催化剂的 制备及其在合成气制二甲醚反应中的应用

以三嵌段共聚物F₁₂₇为模板剂,以异丙醇铝、硝酸铜为原料,采用溶剂挥发自组装法制备具有介孔结构的CuO/γ-Al₂O₃复合催化剂.通过XRD、SEM-EDS、H₂-TPR、N₂-吸附脱附、TEM等技术对该催化剂的结构进行了表征.实验结果表明,通过溶剂挥发自组装法制备的催化剂CuO/γ-Al₂O₃具有有序的介孔结构,并且具有较大的比表面积以及均一的介孔结构,并且Cu元素均匀地分布在γ-Al₂O₃的表面.将该复合催化剂用于合成气直接制备二甲醚的反应,在空速1 500 h^-1、温度320 ℃、压力5 MPa的条件下,CO转化率最高达到68.8%、DME选择性达到59.0%.连续反应50 h后,CO转化率从68.8%降低至59.5%,DME选择性基本保持不变,催化剂部分失活的原因是由于铜元素部分发生了聚集.     

TiO2-Al2O3载体的制备方法对其负载的磷化镍催化剂加氢脱氮反应性能的影响

采用共沉淀法和原位溶胶-凝胶法制备了TiO₂-Al₂O₃复合载体,其负载的磷化镍催化剂采用等体积浸渍法和H₂原位还原法制备. 通过N₂吸附（BET）、X射线衍射（XRD）、透射电镜（TEM）、程序升温还原（TPR）,X射线光电子能谱（XPS）和等离子体发射光谱（ICP-AES）表征技术对催化剂进行了表征,并通过喹啉的加氢脱氮反应评价了催化剂的加氢脱氮性能. 结果表明,原位溶胶-凝胶法制成的复合载体基本保留了原有的γ-Al₂O₃的孔特征,具有较大的比表面积和较宽的孔分布,TiO₂主要以表面富集的形式分散在管状的γ-Al₂O₃表面,其负载的磷化镍催化剂还原后所形成的活性相为Ni₂P和Ni₁₂P₅;而共沉淀法制成的复合载体比表面积较小,孔径分布更加集中,TiO₂趋于在块状的Al₂O₃表面均匀分散,其负载的磷化镍催化剂具有更好的可还原性,还原后所形成的活性相为Ni₂P. 不同的载体制备方法和不同的钛铝比对催化剂加氢脱氮性能影响较大,当n（Ti）/n（Al）=1/8时,共沉淀法载体负载的催化剂表现出最佳的加氢脱氮性能,在340 ℃,3 MPa,氢油体积比500,液时空速3 h^-1的反应条件下,喹啉的脱氮率可以达到91.3%.     

ZrO4/SiO2-Al2O3催化肉桂醛MPV转移加氢性能

以九水合硝酸铝（Al（NO₃）₃·9H₂O）与正硅酸乙酯（TEOS）为前驱盐,采用溶胶-凝胶法制备一系列不同Al₂O₃含量的SiO₂-Al₂O₃复合氧化物,并通过浸渍硝酸氧锆引入ZrO₂,制备ZrO₂/SiO₂-Al₂O₃复合氧化物催化剂,考察催化剂在肉桂醛（CAL）MPV转移加氢中的催化性能,并结合N₂物理吸附、X射线粉末衍射（XRD）、傅里叶变换红外光谱（FTIR）、NH₃-程度升温脱附（NH₃-TPD）、Py-原位红外（Py-IR）等技术,研究催化剂结构、织构以及表面性质与其催化性能间的构效关系.研究表明,所制备的催化剂均以L酸为主,并含有少量B酸中心,这使得加氢产物以肉桂醇（COL）为主,并含有少量1-苯丙烯-2-丙基醚（CPE）.Al₂O₃含量不仅影响催化剂表面的酸中心数量,而且对催化剂的织构参数有较大影响.随Al₂O₃含量的增加,催化剂表面L酸与B酸中心均有所增加,而孔径则持续变小,这使得催化反应呈现CAL转化率先增加后减少、目标产物COL选择性先稍有减小后有所增加的趋势.在Si/Al比为2时,催化剂具有最优的催化性能,优化反应条件下,CAL转化率达96%,目标产物COL选择性达90%.     

Ce改性的Pt/γ-AlO3催化剂用于富氢气氛下CO选择氧化

研究了Ce改性的Pt/γ-AlO3对于富氢气氛下CO选择氧化反应的催化行为考察了制备条件（共沉积沉淀法、分步沉积沉淀法以及沉积沉淀温度）对催化活性的影响．结果表明，在80℃时用共沉积沉淀方法制备的催化剂Pt/γ-AlO3-CP-80对CO氧化反应表现出良好的活性和选择性，CO转化率在120℃时可以达到85％．利用氢气程序升温还原和原位漫反射红外光谱对不同条件下制备的催化剂进行了表征，分析了Cc的促进作用．     

Cu/La2O3-ZrO2-Al2O3催化剂的制备及其对NO选择性还原的催化性能

采用将Al(NO3)3、La(NO3)3和ZrOCl2的混合液滴入沉淀剂(NH4)2CO3中的共沉淀法制备La2O3-ZrO2-Al2O3复合载体,然后负载上Cu2+,制成Cu/La2O3-ZrO2-Al2O3催化剂。考察了该催化剂在富氧条件下对C3H6选择还原NO的催化性能,并借助扫描电子显微镜（SEM）、X射线衍射（XRD）、比表面积测定（BET）、吡啶吸附红外光谱（Py-IR）、程序升温还原（TPR）和热重分析（TG）等方法研究催化剂制备方法与结构、性能的关系。实验结果表明,采用将Al(NO3)3滴入(NH4)2CO3制得的γ-Al2O3能有效地增大催化剂的比表面积,加入La2O3能提高催化剂的热稳定性,加入ZrO2能大幅度增加催化剂表面L酸和B酸的酸量。因此,采用共沉淀法制备的La2O3-ZrO2-Al2O3复合载体能够使Cu/La2O3-ZrO2-Al2O3催化剂具有良好的催化性能,最佳催化活性温度为300℃,NO最大转化率高达88.9%,在有10%水蒸气存在的情况下,仍可达81.9%。