PDDA/SnTsPc静电自组装膜的制备及其形态研究

采用静电层-层自组装技术制备出了含有阴离子磺化酞菁锡(SnTsPc)和阳离子聚二烯丙基二甲基胺盐酸盐(PDDA)交替复合超薄膜.利用紫外-可见光谱表征了PDDA/SnTsPc多层膜的组装过程,表明薄膜的吸收是连续的、有规律的.原子力结果表明,膜表面是光滑的、均匀的;在膜表面紧密堆积的纳米粒子的平均粒径为53.1 nm,平均表面粗糙度是4.021 nm.     

Au@Pt纳米粒子单层膜对甲醇氧化的电催化性能及SERS研究

通过种子生长法合成Au@Pt核壳结构纳米粒子,采用两相成膜法制备单层粒子膜,并转移获得Au@Pt核壳纳米粒子单层膜电极,该电极表面纳米粒子分布均匀,具有较大的比表面,对甲醇的氧化具有较好的电催化活性.研究表明,利用内核Au的长程电磁场增强效应,该单层膜表现出均匀且优良的表面增强拉曼散射(SERS)活性,适合作为基底在分子水平上研究表面的吸附和反应.获得了Au@Pt核壳纳米粒子单层膜表面甲醇电催化氧化过程的SERS光谱,为深入分析表面反应机理提供了实验依据.     

静电组装金纳米粒子制备局域表面等离子体共振传感膜

采用聚电解质自组装技术制备局域表面等离子体共振(LSPR)传感膜的方法, 在玻璃基片上依次沉积聚电解质PDDA, PSS和PVTC, 并通过静电吸附构建胶体金纳米粒子自组装膜形成LSPR传感膜. 利用扫描电镜对LSPR传感膜表面形貌以及膜中金纳米粒子的粒径进行了表征, 同时通过紫外-可见消光光谱对其灵敏度和渗透深度等重要参数进行检测. 研究结果表明, 所制备的LSPR传感膜粒子分布均匀、单分散性好、稳定性高、重现性好; 消光峰位对样品溶液折射率的检测灵敏度为71 nm/RIU, 相应的峰强检测灵敏度为0.21 AU/RIU, 对表面吸附层的渗透深度约为16 nm.     

HRP-纳米金/纳米硫化镉/聚天青Ⅰ修饰玻碳电极的制备及用作过氧化氢生物传感器

以玻碳电极为基底,电聚合一层表面均匀的带正电性的聚天青Ⅰ膜,再通过静电作用吸附一层带负电性的具有大比表面积的纳米硫化镉来固定纳米金和辣根过氧化物酶(HRP)的复合物,制备出性能良好的过氧化氢生物传感器.采用循环伏安法(CV)和计时电流法对该生物传感器的性能进行了研究.试验表明:该方法不仅增加了酶的吸附量,还有效保持了酶的生物催化活性,此生物传感器对过氧化氢浓度在4.0×10-7～1.2×10-3mol·L-1范围内呈线性关系,检出限为1.4×10-7mol·L-1.     

基于聚多巴胺/铜微粒自组装多层膜的无酶葡萄糖传感器

利用多巴胺易于在电极表面发生自聚反应,且聚多巴胺膜中富含邻苯二酚等反应性基团,可通过二次反应实现电极表面的进一步功能化修饰的特点,在玻碳电极(GCE)表面,将多巴胺自聚膜(PDA)与铜微粒(Cu)进行层-层自组装,构建了无酶葡萄糖电化学传感器(GCE/(PDA/ Cu) n )。传感器的灵敏度可通过控制多层膜的组装层数进行调控。采用紫外-可见光谱跟踪表征了多层膜的组装过程,结果表明,多层膜的生长是逐步且均匀的过程。采用循环伏安法和电流-时间曲线法研究了修饰电极对葡萄糖的电催化氧化性能。对于GCE/(PDA/ Cu)4,检测葡萄糖的线性范围为0.5~9.0 mmol/ L,检出限为5.8μmol/ L(S/ N=3)。本传感器具有良好的重现性、稳定性和较强的抗干扰能力。将本传感器用于血清中葡萄糖的测定,结果令人满意。     

聚-4-偶氮磺酸基苯乙烯与四-(三甲氨基苯基)-卟啉的自组装膜及其光电转换性能

聚-4-重氮基苯乙烯(PDS)在碱性水溶液下通过与Na₂SO₃反应,制备了聚-4-偶氮磺酸基苯乙烯(PDSS).作为负离子聚电解质PDSS能与四-(三甲氨基苯基)-卟啉(TTMAP)通过离子相互作用进行层-层自组装.光照下该组装膜中的离子键转变为共价键,结果是组装膜对极性溶剂和盐水溶液变为非常稳定,从而能直接在KCl水溶液中测定其光电流.结果表明,该组装膜具有良好的光电转换性质.     

不同pH条件下木质素磺酸钠的静电逐层自组装研究

以来源于造纸废液中的木质素磺酸钠(SL)为研究对象,利用静电逐层自组装技术,与聚二烯丙基二甲基氯化铵(PDAC)交替吸附,制备木质素磺酸钠的自组装多层吸附膜.研究了不同pH值条件下木质素磺酸钠在固体表面的静电吸附规律.木质素磺酸钠的自组装过程用紫外-可见光吸收光谱来监控,而自组装膜的表面形貌用原子力显微镜来观察.研究表明,SL与PDAC多层吸附膜的紫外-可见光吸收光谱强度随层数增加而线性增长,说明SL/PDAC多层吸附膜的厚度增长是以逐层自组装的方式进行的.木质素磺酸钠浸渍溶液的pH值对多层吸附膜的厚度和表面形貌产生重要的影响.在所研究的pH范围内,pH值越低,越有利于生成吸光度高的自组装膜,而得到的自组装膜的表面粗糙度越大。     

一种新型的氢键自组装液晶光控取向膜

报道了一种新型的以氢键为驱动力的液晶自组装光控取向膜, 研究了薄膜的制备方法与光敏特性. 通过聚(4-乙烯基吡啶)中的吡啶基团与光敏聚丙烯酰氧基肉桂酸间的氢键作用制备了LBL(layer-by-layer)型的自组装多层膜, 制备过程的紫外-可见光谱表明, 该组装过程为逐层、均匀沉积过程. 傅里叶变换红外光谱表明, 多层膜的成膜驱动力为氢键. 用线性偏振紫外光辐照该薄膜, 多层膜中与光矢量方向匹配的光敏基团发生[2+2]环加成反应, 形成表面张力各向异性的薄膜. 用该薄膜作为向列相液晶的取向膜制成平行液晶器件, 在偏光显微镜下观察, 发现获得了均一、稳定的取向效果.     

钒取代多金属氧酸盐/聚酰胺-胺多层膜的制备及其电催化性能

用层接层自组装的方法制备了过渡金属钒取代的多金属氧酸盐PMo11VO4-40/聚酰胺-胺多层纳米复合膜. X射线光电子能谱(XPS)、紫外-可见光谱(UV-Vis)、循环伏安(CV)测定和分析结果表明, PMo11VO4-40和聚酰胺-胺通过静电相互作用形成了纳米交替多层膜,且膜的增长均匀. 复合膜的循环伏安图呈现出四对氧化还原峰(一个V的单电子和三个Mo的双电子), 峰电流与扫描速率成正比, 其式量电位随着pH 的增加而线性负移, 表明电极过程属于表面控制过程, 电荷传递很快且有氢离子参与多金属氧酸盐的氧化还原反应. 该方法制备的多层膜修饰电极稳定性好, 对NO-2、BrO-3及H2O2具有良好的催化还原活性.     

聚甲苯胺蓝-(多壁碳纳米管/PDDA)_n杂化膜修饰印刷电极的制备及其对NADH的测定

利用静电层层组装的方式在印刷电极表面制备了(多壁碳纳米管/邻苯二甲酸二乙二醇二丙烯酸酯(PDDA))n多层膜,采用电位扫描电聚合法在修饰有多层膜的印刷电极表面聚合甲苯胺蓝,制备了聚甲苯胺蓝-(多壁碳纳米管/PDDA)n杂化膜修饰电极。扫描电镜实验表明,多壁碳纳米管均匀分布在杂化膜中,且多壁碳纳米管的掺杂使杂化膜表现出明显的多孔性。电化学实验表明,杂化膜具有良好的导电性且多壁碳纳米管的掺杂显著增加了聚甲苯胺蓝在电极表面的担载量,提高了检测灵敏度。在pH7.4的磷酸盐缓冲液中,杂化膜修饰电极对β-烟酰胺腺嘌呤二核苷酸(NADH)的氧化具有良好的催化作用,与裸电极相比氧化电位降低了560 mV,灵敏度明显提高。在8.7×10-8~1.3×10-4mol/L范围内,NADH的浓度与氧化电流呈线性关系,检出限为2.8×10-8mol/L,该修饰电极可用于NADH的测定。     

ZnO-CNTs纳米复合材料的制备及性能表征

以醋酸锌(Zn(CH3COO)2•2H2O)和经硝酸处理过的碳纳米管(CNTs)为原料, 一缩二乙二醇(DEG)为溶剂, 采用溶胶法制备得到ZnO-CNTs纳米复合材料, 并通过XRD、TEM、SEM、IR、PL等手段对样品进行了表征, TEM及SEM结果显示, 负载在碳纳米管上的氧化锌纳米颗粒的尺寸小于25 nm. 讨论了反应时间、反应温度等因素对产品形貌的影响, 并对复合材料的光致发光效应及其形成机理进行了初步的探讨. PL结果表明, 相对于纯ZnO, ZnO-CNTs纳米复合材料的近紫外发射峰峰位发生了明显的蓝移.     

微电极结构Ag/ZnO/NiO三层复合膜的制备及光催化性能的研究

通过溶胶-凝胶结合光还原沉积法在普通玻璃片上制备了Ag-ZnO-NiO系复合薄膜。使用SEM,PL,XRD,UV-Vis等手段对薄膜的表面形貌,物相组成及光学性质作了考察和研究。XRD和UV-Vis分析表明复合薄膜中包含NiO和ZnO的双层异质结构;FESEM结果表明Ag和ZnO分别在其各自的衬底上生长但没有形成完全覆盖,PL光谱表明三层膜的发光强度小于双层膜和单层膜。使用甲基橙为模型底物测试了薄膜在紫外线下的光催化氧化能力,结果表明,三层复合薄膜Ag/ZnO/NiO的活性相比氧化锌单层薄膜和双层薄膜有不同程度的提高。这是由于上层薄膜不能完全包裹下层膜,导致在表面形成了许多微电极结构,这些微电极结构能够使光生电子空穴对得到有效分离。     

Photoactivity Characteristics of a Biodevice Using Primary Photosynthetic Reaction Centers

Films with alternating layers of thylakoid membrane from the cyanobacterium Spirulina platensis and the positively charged polyion poly(ethylenimine) (PEI) were prepared by means of alternate electrostatic layer‐by‐layer assembly. The thylakoid membrane/PEI bilayers were functionally and structurally characterized by visible spectra, electrochemical methods and SEM techniques, respectively. The films deposited onto gold electrodes were molecularly smooth and consistent with thylakoid membrane/PEI bilayers as observed by SEM. The photoactivity of the thylakoid membrane/PEI assembly was dependent on thickness of the film that increased with the number of bilayers. There was an obvious difference in the current responses of 1‐ and 5‐bilayer thylakoid membrane/PEI films under illumination. The photosynthetic electron transfer process in the thylakoid membrane/PEI single‐bilayer film was demonstrated by an inhibition of the photoactivity by herbicide. Biodevices for the detection of phytotoxicity were constructed using the isolated thylakoid membrane from chloroplast as biosensing elements by means of electrostatic layer‐by‐layer assembly.     

双层分等级TiO_2纳米线制备及其光伏性能研究

采用两步溶剂热反应制备了底层为分等级锐钛矿的TiO_2纳米线阵列,上层为分等级锐钛矿的TiO_2纳米线薄膜的双层结构电极.通过XRD和SEM对其组成和形貌进行了表征,并考察了纳米线薄膜对染料敏化太阳电池(DSSC)光伏性能的影响.实验结果表明,分等级锐钛矿的TiO_2纳米线作为DSSC的光阳极,光电转换效率为4.39%,其效率高于光滑的TiO_2纳米线光阳极电池效率(2.07%).     

Modification and Characterization of Chitosan Films Using 3-trimethoxyl Silyl Propylmethacrylate

The biodegradable flexible chitosan film was prepared by solution casting. The physico-mechanical properties, polymer loading (PL), gel content and water uptake of the chitosan film were studied. The tensile strength (TS) and % elongation at break (Eb) of the uncured chitosan film were 7.0 (MPa) and 8%, respectively. Four formulations were developed using 3-trimethoxyl silyl propylmethacrylate (TSPMA) (varied from 10–80% by weight) in methanol along with photoinitator (Darocur-1664). The raw chitosan films were then soaked in the prepared formulations and cured under UV radiation at different intensities to improve the physico-mechanical properties of the films. TS for the photocured chitosan film was 28.0 (MPa) which was 4 times higher compared to the uncured chitosan film. This TS was obtained for the formulation containing 30% silane (TSPMA) at 24th UV pass for 4 min soaking time. The maximum PL of 45.1% was obtained for the same formulation at 24th UV pass for 4 min soaking time. The water uptake and gel content of the photocured chitosan films were also studied. The scanning electron micrographs of the photocured chitosan film showed smooth surface, compact and homogeneous structure.     

The structure of ultrathin Langmuir-Blodgett films of cadmium behenate

Grazing incidence x-ray-diffraction investigations of the structures of Langmuir-Blodgett films of cadmium behenate with 1, 2, 3, 5, and 21 monolayers are reported. The single monolayer film, deposited on a hydrophilic substrate, showed a hexagonal structure, whereas the bilayer film, deposited on a hydrophobic substrate, had a rectangular structure with herringbone orientation of the acyl chains. With multilayer films formed on a hydrophilic substrate, it was possible to detect that the hexagonal structure of the first layer was retained when additional layers were deposited and that the additional layers had the same rectangular structure as the bilayer.     

Preparation, characterization, and optical, electrochemical property research of CdS/PAM nanocomposites

CdS/PAM nanocomposites have been successfully synthesized in situ via a ultrasound-assisted route under ambient condition, employing CdCl(2) and Na(2)S(2)O(3) as Cd(2+) and S(2-) ion sources and acrylamide (AM) and (NH(4))(2)S(2)O(8) as organic monomers and initiating reagents, respectively. The results from X-ray powder diffraction (XRD) analysis and the IR spectrum of the final product showed the formation of CdS nanoparticles and the polymerization of AM monomers. SEM observations showed that the CdS/PAM nanocomposites could film on the quartz substrate and some holes in which many nanorods regularly arranged distributed on the film. The UV-vis absorption and PL spectra of CdS/PAM nanocomposites obviously differed from those of CdS nanoparticles prepared under the same conditions due to the presence of PAM. The electrochemical research showed that CdS/PAM nanocomposites had a stronger ability to promote electron transfers between Hb and the Au electrode than CdS nanoparticles prepared under the same conditions. A possible formation mechanism was also suggested based on the results of experiments.     

A silicate gel for promoting deposition of lipid bilayers

A simple method for modifying a polymer surface to induce lipid bilayer formation by vesicle fusion is described. A silicate gel was prepared by condensation of tetraethyl orthosilicate (TEOS) in the presence of acid. When applied to a poly(methylmethacrylate) substrate, either a rough or a smooth layer could be produced, depending on the method used for the application. The smooth surface induced formation of a supported lipid bilayer by fusion of lipid vesicles; the rough silicate surface induced adsorption of a vesicle layer. A high-frequency acoustic waveguide device was used to follow the initial adsorption of vesicles, the transition from a vesicle layer to a bilayer, and the formation of a complete bilayer; the time required to form a bilayer was determined as a function of lipid concentration in suspension. The presence of a bilayer on the smooth silicate surface was confirmed by fluorescence recovery after photobleaching. An additional procedure is described to modify a gold surface to induce bilayer formation.     

Fabrication and Characterization of DNA/QPVP‐Os Redox‐Active Multilayer Film

Calf thymus DNA was immobilized on functionalized glassy carbon, gold and quartz substrates, respectively, by the layer‐by‐layer (LBL) assembly method with a polycation QPVP‐Os, a quaternized poly(4‐vinylpyridine) partially complexed with osmium bis(2,2′‐bipyridine) as counterions. UV‐visible absorption and surface plasmon resonance spectroscopy (SPR) showed that the resulting film was uniform with the average thickness 3.4 nm for one bilayer. Cyclic voltammetry (CV) showed that the total surface coverage of the polycations increases as each QPVP‐Os/DNA bilayer added to the electrode surface, but the surface formal potential of Os‐centered redox reaction shifts negatively, which is mainly attributed to the intercalation of redox‐active complex to DNA chain. The electron transfer kinetics of electroactive QPVP‐Os in the multilayer film was investigated by electrochemical impedance experiment for the first time. The permeability of Fe(CN) in the solution into the multilayer film depends on the number of bilayers in the film. It is worth noting that when the multilayer film is up to 4 bilayers, the CV curves of the multilayer films display the typical characteristic of a microelectrode array. The nanoporous structure of the multilayer film was further confirmed by the surface morphology analysis using atomic force microscopy (AFM).     

Layer-by-layer Multilayer Films Self-assembled from a Rare-earth-containing Poly-oxometalate Na_9[Eu(W_5O_(18))_2] and Poly(allylamine hydrochloride) and Their Photoluminescent Properties

ＩｎｔｒｏｄｕｃｔｉｏｎＲｅｃｅｎｔｌｙ ,ｃｏｎｓｉｄｅｒａｂｌｅｉｎｔｅｒｅｓｔｈａｓｂｅｅｎｄｅｖｏｔｅｄｔｏａｓｓｅｍｂｌｉｎｇｎａｎｏｓｃａｌｅｂｕｉｌｄｉｎｇｂｌｏｃｋｓｗｉｔｈｖａｒｉｏｕｓｉｎｏｒ ｇａｎｉｃａｎｄ/ｏｒｏｒｇａｎｉｃｃｏｍｐｏｓｉｔｉｏｎｓｉｎｔｏｕｌｔｒａｔｈｉｎｍｕｌｔｉｌａｙ ｅｒｅｄｆｉｌｍｓｂｙｖｅｒｓａｔｉｌｅａｓｓｅｍｂｌｉｎｇｓｔｒａｔｅｇｉｅｓａｓｔｈｅｓｅｆｉｌｍｓｃａｎｏｆｆｅｒｇｒｅａｔｐｏｔｅｎｔｉａｌｆｏｒａｐｐｌｉｃａｔｉｏｎｓｓｕｃｈ…