草酸二甲酯加氢制乙二醇催化剂的研究

常规方法制备的草酸二甲酯加氢催化剂活性和选择性较差,通过化学还原沉积法制备了Cu-B/γ-Al2O3、Cu-B/SiO2非晶态合金催化剂并进行了XRD、TDA的表征。在2.0MPa,摩尔氢酯比50:1,体积空速2h-1,反应温度200℃时进行催化剂评价。结果表明,Cu-B/γ-Al2O3、Cu-B/SiO2非晶态合金催化剂的活性和选择性较好,显示出良好的应用前景。     

磁性纳米TiO_2/Fe_3O_4的制备及其光催化性能

采用特殊液相沉淀法分两步制备了壳核结构的磁性纳米TiO2/Fe3O4,并讨论了TiO2/Fe3O4比例对其磁性的影响。利用XRD、TEM和VSM对其进行了表征,用它做催化剂,甲基橙溶液为降解目标,在日光作用下对其光催化活性进行了研究,并测出了其回收率。结果表明,在本实验条件下制备的磁性纳米TiO2/Fe3O4表现为超顺磁性,具有较强的光催化活性和较高的回收率。当TiO2∶Fe3O4为4∶1,在450℃焙烧30min条件下得到的催化剂,对20mg/L的甲基橙溶液在60min内降解率高达91.5%,明显高于纯TiO2的催化活性,在外加强磁场的作用下,此催化剂很快从溶液中分离出来,测得其回收率为88.2%。     

助剂对Pd/γ-Al2 O3催化剂上NO选择催化还原的影响

研究了含氧条件下钯催化剂上进行丙烯选择催化还原NO的反应,考察浸渍法制备的Pd/γ-Al2O3催化剂中加入碱（土）金属或稀土氧化物助剂对NO转化率的影响,并对催化剂进行了XRD表征及在氧化气氛中饱和吸附NO后的TPD研究。结果表明,助剂CeO2、Li2O能较大幅度提高催化剂的的低温活性,使NO的最高转化率增加1-3.5倍。Pd/CeO2-Al2O3、Pd/LiO2-Al2O3催化剂有较高的Pd分散度及较强的NO解离吸附能力。并讨论了NO、N2O、NO2^-和NO3^-等吸附态物种在催化剂表面的形成及脱附特性对催化剂选择催化还原NO性能的影响。     

CH4、CO2、O2制合成气用Ni-Ce/Al2O3催化剂的XPS研究

用XPS表征浸渍法制备的Ni-Ce／Al2O3催化剂,并与活性评价结果相关联,研究了添加Ce对催化剂性能的影响,探讨了催化剂失活的原因。结果表明,稀土Ce在反应过程中存在着部分还原变价过程(Ce^4 e→Ce^2 ),Ce^3 能够迁移至A12O3晶格,增强载体Al2O3的抗烧结能力,提高催化剂的稳定性;Ni-Ce/Al2O3催化剂表面的Ni和Ce在反应过程中向体相迁移,以及Ni晶粒的烧结是造成催化剂活性逐步下降的主要原因。     

ZrO2,Nb2O5助剂改性Au/α-Fe2O3催化剂的光谱研究

通过并流共沉淀方法,制备了一系列添加助剂ZrO2和Nb2O5的Auα-Fe2O3催化剂,并用紫外-可见漫反射光谱,X射线光电子能谱,透射电镜和X射线荧光元素分析对其进行了表征.结果表明ZrO2和Nb2Os之间存在着较强的协同作用;两种助剂的同时添加促进了Au,ZrO2和Nb2O5在Au/α-Fe2O3催化剂表面的富集,有效地阻止了纳米微粒的团聚.经甲醇重整气氛下的催化性能评价,在200℃时,AuFZ的活性达到平衡转化率99.9%;经50 h的稳定性测试,其稳定性远远高于未加助剂的Au/α-Fe2O3样品.这表明ZrO2和Nb2O5双助剂的添加有效地改善了Au/α-Fe2O3催化剂的性能.     

三氧化二铝含量对Ni／Zr0.4Ce0.6O2—Al2O3催化剂的CH4—CO2重整反应性能影响

采用水热合成法．制备了不同Al2O3含量的Ni／Zr0.4Ce0.6O2-Al2O3催化剂。采用X-射线衍射(XRD)和扩展X光吸收精细结构(EXAFS),对催化剂样品进行结构表征;考察了Al2O3的加入对催化剂结构和CH4-CO2重整反应活性的影响。结构表征和活性测试表明,催化剂中存在的主要晶相是Zr0.4Ce0.6O2.Al2O3的加入,使催化剂颗粒度变小,镍的分散度提高。并使反应活性有明显改进,而过量Al2O3的加入,却容易导致积炭．     

CuO/γ-Al2O3催化吸附剂脱硝性能研究

本文采用溶胶-凝胶法制备CuO/γ-Al2O3催化吸附剂颗粒.分析表明:SO2的存在可以提高CuO/γ-Al2O3催化吸附剂的脱硝活性,SO2存在条件下,CuO/γ-Al2O3催化吸附剂的脱硝活性在载铜量8wt%时达到最高,达到95.7%.载铜量太高会使单位质量催化剂NO脱除率降低.在350℃时,硫酸盐化和未硫酸盐化的8wt%Cu催化吸附剂NO脱除率达到最高.NH3/NO摩尔比在1～1.2之间时,CuO/γ-Al2O3催化吸附剂的脱硝活性较高.     

催化精馏专用填料型固体酸SO42-/ZrO2-Al2O3-Al的研究

为了研制催化精馏专用催化剂 ,采用铝阳极氧化法制备了Al2 O3 Al一体型载体 ,并将活性固体超强酸SO42 -/ZrO2 引入到Al2 O3 Al上 ,得到一种新型催化精馏专用填料式固体酸SO42 -/ZrO2 Al2 O3 Al催化剂 .利用XRD、SEM、BET、XPS、NH3 TPD等手段对其进行了表征 .结果表明 ,所制得的阳极氧化铝膜厚为 5 6 μm ,SO42 -/ZrO2 Al2 O3 Al固体酸具有比表面积大、酸强度适中的特点 .XRD结果表明 ,ZrO2 在Al2 O3 Al上处于高度分散状态 .将该固体酸用于乙酸 /乙醇酯化反应中 ,显示出较高的催化活性 ,且稳定性较好     

H_3PW_(12)O_(40)/La-N-TiO_2复合催化剂可见光下光催化降解吡虫啉研究(英文)

制备出H3PW12O40/La-N-TiO2催化剂并采用红外光谱,N2吸附-脱附分析,透射电镜和紫外漫反射进行结构表征。红外光谱检测表明,复合催化剂中H3PW12O40保留了Keggin结构;掺杂La-N之后,复合催化剂的BET比表面积是母体TiO2的两倍;透射电镜检测表明,催化剂由相对均匀的球形颗粒组成,分散性良好;紫外漫反射检测表明,掺杂La和N元素后所制备的复合催化剂对可将光的光响应性能明显提高。对吡虫啉的光催化实验表明,所制备的不同负载量催化剂中30%H3PW12O40/0.3%La-1.0%N-TiO2具有最好的光催化活性(≥400nm),光照3h后吡虫啉降解率为91.57%,光照6h后吡虫啉降解率达98.89%,基本上完全降解。     

含贵金属的BaZrO3 储存NOx 催化剂结构及性能研究

用溶胶 凝胶法制备了钙钛矿型BaZrO3催化剂 ,再用等量浸渍法制备了Rh/BaZrO3样品 ,并制备了Rh/BaZrO3/γ Al2 O3和Pt/BaZrO3/γ Al2 O3催化剂 .对它们的NOx 储存量 (NSC)及其抗硫性能进行了测试 ,并用X射线衍射 (XRD)、X光电子能谱 (XPS)和傅里叶变换红外光谱 (FT IR)等方法研究了它们的结构及其对性能的影响 .结果表明 ,BaZrO3催化剂具有良好的储氮及抗硫性能 ,直接添加贵金属到BaZrO3中会使NSC降低 ,而混合γ Al2 O3后添加Pt或Rh可以大大提高NSC ,上述两种方式引入贵金属都能改善催化剂的抗硫性能 .     

Physicochemical characteristics of ZSM-5/SAPO-34 composite catalyst for MTO reaction

SAPO-34 and ZSM-5 are the most well-known catalyst for MTO reaction. A combination of ZSM-5 and SAPO-34 might give rise to optimal catalyst to meet a change of market demand for ethylene, propylene and butadiene. In this study, we have developed ZSM-5/SAPO-34 composite catalysts to control the composition of light olefins in MTO reaction. ZSM-5/SAPO-34 composite catalysts showed very different physicochemical and catalytic properties with respect to ZSM-5 and SAPO-34 synthetic procedure. The physicochemical properties of the composite catalysts have been compared by XRD, SEM, N₂ isotherm, FT-IR and NH₃-TPD. Their catalytic performances were also evaluated for MTO reaction. The series composite catalyst synthesized by successive crystallization of SAPO-34 synthetic gel after ZSM-5 crystallization exhibited relatively high catalytic performance.     

Co-Mo/Al2O3加氢脱硫催化剂的CO吸附原位红外光谱表征及应用研究

燃油的无硫化成为车用燃料发展的必然趋势.为开发高性能的柴油超深度加氢脱硫催化剂,文章采用CO吸附原位红外光谱法对系列还原态Co-Mo/Al2O3催化剂和高活性工业剂进行了表征,并将表征结果与微反加氢脱硫活性评价结果进行了关联分析.结果表明:随金属负载量的变化CO吸附的光谱特征发生变化,当MoO3负载量达20%、助剂CoO量为4.16%时,在2 179 cm-1出现一个新的CO特征吸收峰,该活性中心的出现明显有利于加氢脱硫(HYD)的反应.在相同金属负载量的情况下,与采用化学处理法制备的催化剂相比较,后者对应的2179 cm-1的特征吸收明显增强,微反评价显示该催化剂的催化活性特别是HYD反应活性明显提高.     

Methane non-oxidative aromatization on Mo/ZSM-5: Effect of adding triethoxyphenylsilanes into the synthesis system of ZSM-5

A series of ZSM-5 zeolites were synthesized by adding triethoxyphenylsilane (PTEOS) into the initial sol of the synthesis system. The samples were studied by XRD, SEM, N₂ adsorption-desorption and acid assessment of d₃-acetonitrile adsorption. Characterization results showed that the crystal size of the ZSM-5 zeolites could be adjusted in a certain range by introducing different contents of PTEOS. Besides, the resultant materials possess hierarchical porosity in addition to those micropores generated by the MFI channels. Moreover, supported Mo/ZSM-5 catalysts were prepared, and their catalytic performances were investigated in the methane non-oxidative aromatization. It was found that the Mo/ZSM-5 catalyst, bearing suitable crystal size and mesoporous characteristic showed relatively high shape-selectivity to benzene and high stability for the reaction of methane aromatization.     

CuCoMn-zeolite双功能催化剂转化生物质基合成气制取液态烃

选用四种不同的分子筛(SAPO-34, ZSM-5, Y, MCM-41)与CuCoMn(高醇合成组元)构成双功能催化剂,利用N₂吸脱附、H₂-TPR、XRD、NH₃-TPD等表征了催化剂的结构性质. 研究了催化剂在生物质基合成气一段法制取液态烃燃料的应用. 相比于CuCoMn催化剂,加入分子筛的双功能催化剂均不同程度地提高了液体烃燃料的选择性及收率,且收率按顺序递减呈CCM-ZSM-5>CCM-SAPO-34>CCM-Y>CCM-MCM-41. 同时,共沉淀法制备的CuCoMn-ZSM-5 (20wt%, Si/Al=100) 具有最佳的CO转化率(76%)及液体产物收率(30%). 相比于CuCoMn氧化物,双功能催化剂的比表面及孔容均得到提高. CCM-ZSM-5具有适中的微孔尺寸和中等强度的酸性,增加CCM-ZSM-5中ZSM-5含量或降低ZSM-5中的Si/Al比,均有利于提高酸性位的数量,主要是较弱的酸性位. 而共沉淀法制备的CCM-ZSM-5具有更好的金属分散性及还原性能.     

Fe-ZSM-5杂原子分子筛的合成与表征

采用静态水热法分别以正丁胺、四丙基溴化铵为模板剂合成ZSM-5分子筛及Fe-ZSM-5杂原子分子筛；利用XRD与FT-IR对其结构进行表征；考察了Mo改性后分子筛催化剂上甲烷脱氢芳构化的反应性能。结果表明，Fe部分进入了分子筛的骨架，导致分子筛的结晶度及表面酸强度的下降，使Mo／Fe-ZSM-5催化剂的反应性能较Mo／HZSM-5显著下降。     

改性ZSM-5分子筛催化合成乙酸戊酯

以ZSM-5为原料,采用浸渍法将其交换成HZSM-5,以HZSM-5为催化剂,对以冰乙酸和正戊醇为原料合成乙酸戊酯的反应条件进行了研究。研究表明,以1.0m ol/L硫酸浸渍后的ZSM-5催化活性最高,当醇酸摩尔比为1.1∶1,催化剂用量为0.4g,反应时间为90m in,反应温度为125—135℃,酯化率可达82.5%。     

镍改性ZSM-5催化剂及其SCR催化性能

采用液态离子交换法制备了不同负载量的镍改性ZSM-5分子筛催化剂,并考察了上述催化剂的微观结构和物理化学特性及其在NH3-SCR反应中的催化性能。结果表明:在负载量<10.9%时镍在分子筛中具有高度的分散性,而随着镍负载量的进一步增加,分子筛表面开始出现较大的NiO颗粒;镍元素只以+2价存在于分子筛催化剂中;在NH₃-SCR反应中,镍负载量低于14.9%时,增加镍负载量将提高催化剂的低温活性;当反应温度超过300℃时,高温催化中心开始起作用,但随镍负载量的增加,高温活性开始下降时的温度逐渐降低。     

Synthesis of Pt modified ZSM-5 and beta zeolite catalysts: influence of ultrasonic irradiation and preparation methods on physico-chemical and catalytic properties in pentane isomerization

Influence of preparation methods and ultrasound irradiation on physico-chemical and catalytic properties was investigated by synthesizing Pt-ZSM-5 and Pt-Beta catalysts by in-situ and impregnation methods and applying ultrasound irradiation to synthesis gel mixture of ZSM-5 and Beta zeolites. It was concluded from the X-ray powder diffraction patterns of Pt-ZSM-5 and Pt-Beta zeolite catalysts that introduction of Pt by in-situ method and ultrasound irradiation did not influence the structures of ZSM-5 and Beta zeolites. Morphology of ZSM-5 and Beta zeolites were investigated by scanning electron microscopy. SEM micrographs showed that the Pt-ZSM-5-IS-US catalyst synthesized by in-situ method with ultrasound irradiation resulted in smaller crystals of ZSM-5 than Pt-ZSM-5-IS catalyst prepared without ultrasound irradiation. Furthermore SEM micrographs of Pt-Beta-11-IS-US zeolite synthesized using ultrasound irradiation showed much smaller crystals than Pt-Beta-11-IM indicating that ultrasound irradiation had a significant effect on the morphology of Beta zeolite. Conversion of n-pentane and selectivity to iso-pentane over the Pt-ZSM-5-IS-US zeolite catalysts prepared by ultrasound irradiation during in-situ introduction of platinum was higher than the catalysts prepared without the ultrasound irradiation. Furthermore ultrasound irradiated and in-situ synthesized Pt-Beta-11-IS-US catalyst also showed higher selectivity to iso-pentane than Pt-H-Beta-11-IM prepared by impregnation method.     

甲烷部分氧化制合成气Pt/Al_2O_3催化剂的表征及其反应性能评价

采用浸渍法制备了3种不同负载量的Pt/Al2O3催化剂,考察了催化剂的甲烷选择氧化性能,并用程序升温还原技术,程序升温脱附技术以及微型脉冲催化色谱技术对催化剂进行表征。结果表明,随着Pt的负载量升高,甲烷催化氧化的性能也越好,对CO与H2的选择性也越高。其中,在750℃原料气组成CH4/O2为2∶1,4%Pt负载量的催化剂,甲烷转化率达到98%以上。     

不同制备工艺钒系SCR催化剂理化及催化性能研究

本文研究了制备工艺对 TiO2-WO3-V2O5- 载体型催化剂理化特性及其在 NH3-SCR 反应中催化性能的影响.通过 XRD、TG/DTA 等分析方法考察了煅烧温度等对催化剂中各组分晶体结构的影响,确定了制备负载型催化剂的最佳煅烧温度为 500℃.不同制备工艺催化剂理化性能的对比表明,多步浸渍法不仅提高了锐钛矿型 TiO2 向金红石型 TiO2 的转变温度,而且使更多的钒氧化物处于较低的价态,有利于提高还原反应的催化性能;催化活性评价试验也表明使用多步浸渍法制备的 SCR 催化剂具有较高的催化活性和更宽的高活性反应温度窗口.最后考察了反应空速对多步浸渍法所制备催化剂 NOx 转化效率的影响,结果表明:随空速的增加,NOx 转化效率逐渐降低.