Ga2O3组分对Tm3+掺杂GeO2-Ga2O3-Li2O-BaO-La2O3玻璃的光谱性能影响

制备了Tm³⁺(8.0mol%)掺杂(77-x)GeO₂-xGa₂O₃-8Li₂O-10BaO-5La₂O₃(x=4,8,12,16)系列玻璃.系统地研究了Ga₂O₃从4mol%变化到16mol%时,玻璃的光谱性质与热学性质的变化规律.差热分析表明,随着Ga₂O₃含量的增加,锗酸盐玻璃的热稳定性增加.运用Judd-Ofelt(J_O)理论计算得到了Tm³⁺在不同Ga₂O₃含量的GeO₂-Ga₂O₃-Li₂O-BaO-La₂O₃玻璃中的J-O强度参数(Ω₂,Ω₄,Ω₆)及Tm³⁺各激发能级的自发跃迁概率、荧光分支比以及辐射寿命等光谱参量.在808nm激光二极管的激发下,测试并分析了Ga₂O₃对Tm³⁺荧光光谱特性的影响.随着Ga₂O₃从4mol%增加到16mol%,Tm³⁺在1.8μm处的荧光强度呈现先减弱后增强的特性.当Ga₂O₃含量大约在12mol%时,Tm³⁺在1.8μm处的荧光强度最弱,受激发射截面达到最小.还初步讨论了Ga₂O₃对玻璃结构与光谱参数的影响规律. 关键词： 3+掺杂锗酸盐玻璃')" href="#">Tm³⁺掺杂锗酸盐玻璃 光谱性能 Judd-Ofelt参数 热稳定性     

Cr4+在Al2O3多晶体中的光谱性能研究

采用传统无压烧结工艺制备Cr:Al₂O₃透明多晶陶瓷.测定了其退火前后的吸收光谱和荧光光谱，发现在Al₂O₃六配位的八面体结构中，Cr⁴⁺的荧光发射也处在1100—1600nm波段的红外区间，荧光发射峰位于1223nm附近，类似Cr⁴⁺在四面体中的发光行为.同时由于氧化铝晶格常数较小，晶体场强较强，使Cr⁴⁺:Al₂O_{3< 关键词： 4+')" href="#">Cr⁴⁺ 2}O₃透明陶瓷')" href="#">Cr:Al₂O₃透明陶瓷 光谱性质 八面体     

荧光粉CaWO4：Eu3+中WO42-与Eu3+间的能量转递

通过高温固相法分别制备了CaWO₄和CaWO₄:1%Eu³⁺ 样品. 测量了样品不同温度(10–300 K)的荧光光谱、荧光衰减曲线和 时间分辨荧光光谱. 样品的荧光光谱表明: 在240 nm紫外光激发下, 两个样品在430 nm处都展现出来源于WO₄^2-的蓝色发射; 样品CaWO₄:Eu³⁺的Eu³⁺(⁵D₀→⁷F_{1, 2, 3,4})的特征发射则归属于WO₄^2-到Eu³⁺ 间的能量传递.由样品室温(300K)荧光衰减曲线发现: 纯CaWO₄的荧光寿命为8.85μs,Eu³⁺掺杂之后WO₄^2-的荧光寿命缩短至6.27μs,这从另一方面证明了WO₄^2-与Eu³⁺间能量传递的存在. 由荧光寿命得到T=300K时, CaWO₄: 1%Eu³⁺中WO₄^2-与Eu³⁺间的能量传递效率(η_ET)为29.2%, 能量传递速率(ω_ET)为4.65×10⁴ s^-1.通过时间分辨荧光光谱, 获得了从WO₄^2-到Eu³⁺之间的能量传递的时间演变过程,当温度由10 K增加到300 K时, 能量传递出现的时间单调变小. 测试了不同温度(10–300 K)对CaWO₄:Eu³⁺的荧光寿命的影响, 发现在10–50K时,Eu³⁺的荧光寿命增加, 但温度超过50K时发生猝灭, 荧光寿命开始下降; WO₄^2-的荧光寿命则是随着温度的升高逐渐缩短. 关键词： 能量传递 红色荧光粉 温度依赖 4：Eu³⁺')" href="#">CaWO₄：Eu³⁺     

助熔剂BaF2在制备BaSi2O5:Pb2+过程中的机理

采用高温固相合成法制备出BaSi₂O₅:Pb²⁺荧光体。考察了BaF₂的加入量对产物紫外发射强度的影响。用差示扫描量热分析,X射线衍射,光致发光光谱研究了掺入助熔剂BaF₂后BaSi₂O₅:Pb²⁺紫外发射强度显著增强的机理,并从热力学角度对实验结果作了分析。研究表明少量BaF₂的掺入加快了反应速度;降低了BaSi₂O₅:Pb²⁺形成温度,在高温下与SiO₂反应生成SiF₄气体,生成的SiF₄再与BaCO₃反应形成结晶良好的BaSi₂O₅:Pb²⁺荧光体。     

BeAl2O4:Cr3+的晶场能级

金绿宝石中镜对称格位上Cr³⁺(Ⅱ)离子的⁴T₂,⁴T₁和²E能级与该材料的激光运转有关。⁴T₂和⁴T₁能级各分裂成三个子能级。为从偏振吸收谱上确定BeAl₂O₄:Cr³⁺的能级图,本文计算了⁴T₂和⁴T₁的分裂,找到了对谱方法,得到了表征能级分裂的参量K_{1和K2的值。最后给出了以低点群不可约表示标号的、BeAl2O4:Cr³⁺(Ⅱ)的晶场能级图。 关键词：}     

La2O3对Yb:Y2O3透明陶瓷光谱性能的影响

研究了La₂O₃对Yb：Y₂O₃透明陶瓷光谱性能的影响，添加适量La₂O₃以后，Yb：Y₂O₃透明陶瓷的吸收峰和发射峰的位置不变，但由于La³⁺的离子半径大于Y³⁺的离子半径，在Y₂O₃中引入La³⁺离子后，导致Y₂O₃晶格常数变大，晶场强度变弱，同时降低了Y₂O₃晶体的有序度，致使发射峰强度有所下降，发射截面变小.过量的La₂O₃（x=0.16）造成Yb³⁺激活离子发射强度明显下降；其荧光寿命在添加La₂O₃后总体增大45%—60%. 关键词： 氧化镧 氧化钇 透明陶瓷 光谱性能     

Er3+掺杂的Bi2O3-B2O3-SiO2玻璃的光谱性质

测试了Bi₂O₃-B₂O₃-SiO₂玻璃中的Er³⁺离子的吸收光谱、发射光谱、⁴I_13/2的荧光寿命、拉曼光谱,及OH^-的傅里叶红外吸收光谱。应用Judd-Ofelt理论计算了该玻璃中的Er³⁺离子的J-O参数、振子强度、⁴I_13/2能级的寿命,从而利用测得的⁴I_13/2的荧光寿命得出了⁴I_13/2能级的量子效率(15%)。由于较低量子效率可能与OH^-有关,所以计算了玻璃中的OH^-浓度,发现其浓度较高(1.66×10¹⁹cm^-1,相当于Er³⁺浓度的3倍)。应用McCumber理论和四能级模型计算了Er³⁺离子的受激发射截面和荧光发射光谱的半峰全宽,结果与通过吸收光谱计算所得基本吻合。根据透射率和折射率的关系计算了折射率,发现和测量值相差很大,说明有较大的散射,通过拉曼光谱和显微镜测试,认为是玻璃中的微小气泡造成的。     

Bi离子掺杂GeO2-Al2O3-M(M=Na2O，BaO，Y2O3)玻璃的光学性质

用高温熔融法制备了Bi离子掺杂浓度为1mol%的GeO-B₂O₃-Na₂O (GBNB)，GeO₂-Al₂O₃-Na₂O(GANB)，GeO₂-Al₂O₃-BaO(GABB)和GeO₂-Al₂O₃-Y₂O₃(GAYB)玻璃.测定了样品玻璃的差热曲线、吸收、发射光谱及荧光衰减曲线.实验发现GBNB，GANB，GAYB，GABB的吸收边带逐步发生红移.由于这些吸收边带是由Bi³⁺的6s²电子到Bi⁵⁺ 6s⁰空轨道的跃迁引起.因此推断GBNB，GANB，GAYB，GABB玻璃中Bi⁵⁺离子的含量逐步增加.在GABB，GAYB，GANB三个样品中观察到发光中心约1220nm超宽带荧光发射.荧光强度从GABB，GAYB，GANB逐步减弱，荧光半高宽和荧光寿命逐步变小.这些超宽带的荧光归属为Bi⁵⁺离子的发光所致.从吸收与荧光光谱的变化，推断在GeO₂-Al₂O₃玻璃中引入BaO，Y₂O₃组分有利于Bi⁵⁺离子的形成.讨论了BaO，Y₂O₃化学组分对Bi离子在玻璃中的价态影响的内在机理. 关键词： 5+离子')" href="#">Bi⁵⁺离子 超宽带发光 吸收带 荧光寿命     

SrAl2O4∶Eu2+,Dy3+长余辉发光材料的喷雾热解制备及其表征

采用喷雾热解两段法制备了SrAl₂O₄∶Eu²⁺ ,Dy³⁺长余辉发光材料,并利用XRD、SEM、荧光长余辉亮度测试等方法分析了不同制备工艺条件下SrAl₂O₄∶Eu²⁺ ,Dy³⁺发光材料的结构、形貌以及发光性能的变化。结果表明:采用喷雾热解两段法可制备出球形SrAl₂O₄∶Eu²⁺ ,Dy³⁺长余辉发光材料,SrAl₂O₄∶Eu²⁺ ,Dy³⁺的晶体结构与α-SrAl₂O₄磷石英晶体结构相同。热解温度、还原温度、添加剂对产物的形貌、粒度分布、发光性能有较大影响。较之高温固相法,喷雾热解法制备的SrAl₂O₄∶Eu²⁺ ,Dy³⁺具有发光性能好、形貌好、粒度分布窄等优点。     

新型近红外超长余辉材料Zn3Al2Ge2O10：Cr3+的发光性能

采用高温固相法制备了新型近红外长余辉材料Zn₃Al₂Ge₂O₁₀：Cr³⁺,利用X射线衍射、荧光光谱和余辉衰减曲线等对合成的样品进行了分析。结果表明：样品Zn₃Al₂Ge₂O₁₀：Cr³⁺是Ge⁴⁺取代ZnAl₂O₄：Cr³⁺尖晶石中的部分Al³⁺而形成的固溶体。在397 nm光的激发下,发射光谱主要由两个明显的窄峰叠加在Cr³⁺离子的自旋允许跃迁⁴T₂→⁴A₂辐射的宽发射带上。发光强度随着Cr³⁺离子掺杂浓度的增大和煅烧温度的升高而出现浓度猝灭及温度猝灭现象。当Zn₃Al_2-xGe₂O₁₀：xCr³⁺中的Cr³⁺离子掺杂量x为2%且煅烧温度为1 350 ℃时,样品的近红外发光及余辉强度最大。材料的余辉持续时间超过300 h,余辉发射谱峰位与荧光发射光谱中的N线一致,均位于697 nm附近。最后分析了煅烧温度对样品余辉性能的影响,并对材料的余辉机制进行了探讨。     

Antiferromagnetic phase transition in garnet-type AgCa2Co2V3O12 and AgCa2Ni2V3O12

Antiferromagnetic phase transition in two vanadium garnets AgCa₂Co₂V₃O₁₂ and AgCa₂Ni₂V₃O₁₂ has been found and investigated extensively. The heat capacity exhibits sharp peak due to the antiferromagnetic order with the Néel temperature T_N=6.39 K for AgCa₂Co₂V₃O₁₂ and 7.21 K for AgCa₂Ni₂V₃O₁₂, respectively. The magnetic susceptibilities exhibit broad maximum, and these T_N correspond to the inflection points of the magnetic susceptibility χ a little lower than T(χ_max). The magnetic entropy changes from zero to 20 K per mol Co²⁺ and Ni²⁺ ions are 5.31 J K⁻¹ mol-Co²⁺-ion⁻¹ and 6.85 J K⁻¹ mol-Ni²⁺-ion⁻¹, indicating S=1/2 for Co²⁺ ion and S=1 for Ni²⁺ ion. The magnetic susceptibility of AgCa₂Ni₂V₃O₁₂ shows the Curie-Weiss behavior between 20 and 350 K with the effective magnetic moment μ_eff=3.23 μ_B Ni²⁺-ion⁻¹ and the Weiss constant θ=−16.4 K (antiferromagnetic sign). Nevertheless, the simple Curie-Weiss law cannot be applicable for AgCa₂Co₂V₃O₁₂. The complex temperature dependence of magnetic susceptibility has been interpreted within the framework of Tanabe-Sugano energy diagram, which is analyzed on the basis of crystalline electric field. The ground state is the spin doublet state ²E(t₂⁶e) and the first excited state is spin quartet state ⁴T₁(t₂⁵e²) which locates extremely close to the ground state. The low spin state S=1/2 for Co²⁺ ion is verified experimentally at least below 20 K which is in agreement with the result of the heat capacity.     

准一维反铁磁体CsMnCl3·2D2O中激子的能量转移

在2—300K温度范围,研究了纯的及掺Mg²⁺,Ni²⁺和Co²⁺的准一维反铁磁体CsMnCl₃·2D₂O(CMC)中Mn²⁺离子的⁴T₁激子的能量转移动力学过程,发现在2—10K范围,激子的荧光强度和寿命随温度很快下降,较高浓度的杂质离子将进一步加快荧光的减弱和寿命的缩短。这种现象被归结为与磁相互作用和自旋有序相关联的多声子无辐射跃迁及施主—受主之间的能量转移。在更高的温度,能量转移速率增高,但由于仍然存在的自旋短程有序和Jahn-Teller效应,施主之间的能量迁移受到一定限制,出现非指数衰减过程。各种不同的杂质离子在某种程度上显示出不同的陷落作用和弛豫特性。 关键词：     

Emission features of Ho ion in Nb2O5, Ta2O5 and La2O3 mixed Li2O-ZrO2-SiO2 glasses

Li₂O-ZrO₂-SiO₂: Ho³⁺ glasses mixed with three interesting d-block elemental oxides, viz., Nb₂O₅, Ta₂O₅ and La₂O₃, were prepared. Optical absorption and photoluminescence spectra of these glasses have been recorded at room temperature. The luminescence spectra of Nb₂O₅ and Ta₂O₅ mixed Li₂O-ZrO₂-SiO₂ glasses (free of Ho³⁺ ions) have also exhibited broad emission band in the blue region. This band is attributed to radiative recombination of self-trapped excitons (STEs) localized on substitutionally positioned octahedral Ta⁵⁺ and Nb⁵⁺ ions in the glass network. The Judd-Ofelt theory was successfully applied to characterize Ho³⁺ spectra of all the three glasses. From this theory various radiative properties, like transition probability A, branching ratio β_r and the radiative lifetime τ_r, for ⁵S₂ emission levels in the spectra of these glasses have been evaluated. The radiative lifetime for ⁵S₂ level of Ho³⁺ ions has also been measured and quantum efficiencies were estimated. Among the three glasses studied the La₂O₃ mixed glass exhibited the highest quantum efficiency. The reasons for such higher value have been discussed based on the relationship between the structural modifications taking place around the Ho³⁺ ions.     

Tuning the magnetocaloric properties of La0.7Ca0.3MnO3 manganites through Ni-doping

The effect of Ni²⁺ doping on the magnetic and magnetocaloric properties of La_0.7Ca_0.3MnO₃ manganites synthesized via the auto-combustion method is reported. The aim of studying Ni²⁺-substituted La_0.7Ca_0.3Mn_1 ? xNi_xO₃ ($x=0,0.02,0.07$, and 0.1) manganites was to explore the possibility of increasing the operating temperature range for the magnetocaloric effect through tuning of the magnetic transition temperature. X-ray diffraction analysis confirmed the phase purity of the synthesized samples. The substitution of Mn³⁺ ions by Ni²⁺ ions in the La_0.7Ca_0.3MnO₃ lattice was also corroborated through this technique. The dependence of the magnetization on the temperature reveals that all the compositions exhibit a well-defined ferromagnetic to paramagnetic transition near the Curie temperature. A systematic decrease in the values of the Curie temperature is clearly observed upon Ni²⁺ doping. Probably the replacement of Mn³⁺ by Ni²⁺ ions in the La_0.7Ca_0.3MnO₃ lattice weakens the Mn³⁺–O–Mn⁴⁺ double exchange interaction, which leads to a decrease in the transition temperature and the magnetic moment in the samples. By using Arrott plots, it was found that the phase transition from ferromagnetic to paramagnetic is second order. The maximum magnetic entropy changes observed for the $x=0,0.02,0.07$, and 0.1 composites was 0.85, 0.77, 0.63, and 0.59 J/kg?K, respectively, under a magnetic field of 1.5 T. In general, it was verified that the magnetic entropy change achieved for La_0.7Ca_0.3Mn_1 ? xNi_xO₃ manganites synthesized via the auto-combustion method is higher than those reported for other manganites with comparable Ni²⁺-doping levels synthesized via standard solid state reaction. The addition of Ni²⁺ increases the value of the relative cooling power as compared to that of the parent compound. The highest value of this parameter (～60 J/kg) is found for a Ni-doping level of 2% around 230 K in a field of 1.5 T.     

YGG:Cr3+晶体的光谱特性

本文通过实验研究了YGG:Cr³⁺晶体的光谱特性,报道了室温下的吸收谱,10,133,300K的荧光谱,以及荧光寿命、无辐射跃迁几率、辐射量子效率与温度之间的依赖关系。从吸收谱及荧光谱中确定在C_3i(S₆)低对称场微扰下,Cr³⁺离子在基质YGG中²T₁能级分裂的子能级及基态⁺A₂→²E零声子跃迁R线的位置。 关键词：     

Synthesis and magnetic properties of InM2+CrS4(M2+ = Mn,Fe,Co, Ni)

The crystallographic and magnetic properties of the compounds InM²⁺CrS₄(M = Mn, Fe, Co, Ni) were studied. Three of these compounds except MnInCrS₄ were antiferromagnetic. The Néel termperature and paramagnetic Curie temperature were determined to be 20 and 82K for InFeCrS₄, 36 and 115K for InCoCrS₄ and 22 and 26K for InNiCrS₄, respectively.     

Absorption spectra of Ni2+ in (NH4)2Mg(SO4)2·6H2O and Co2+ in Na2Zn(SO4)2·4H2O

Optical absorption spectra of Ni²⁺ in (NH₄)₂Mg(SO₄)₂·6H₂O and Co²⁺ in Na₂Zn(SO₄)₂·4H₂O single crystals have been studied at room and liquid nitrogen temperatures. From the nature and position of the observed bands, a successful interpretation could be made assuming octahedral symmetry for both the ions in the crystals. The splitting observed for ${}^3\text{T}{}_{\mathrm{1g}}\text{(F)}$ band in Ni²⁺ and ${}^4\text{T}{}_{\mathrm{2g}}\text{(F)}$ band in Co²⁺ at liquid nitrogen temperature have been explained as due to spin-orbit interaction. The extra band observed at 16,325 cm^-1 in the case of Ni²⁺ at low temperature has been interpreted to be the superposition of vibrational mode of SO^2-₄ radical on ${}^3\text{T}{}_{\mathrm{1g}}\text{(F)}$ band. The observed band positions in both the crystals have been fitted with four parameters B, C, Dq and ζ.     

X-ray absorption spectroscopic study of mixed valence systems EuCu2Si2, YbCu2Si2 and Sm4Bi3

X-ray absorption spectroscopy technique is employed to determine the valence of the rare earth ions in EuCu₂Si₂, YbCu₂Si₂ and Sm₄Bi₃. In each case, two absorption peaks corresponding to two different valence states of respective rare earth ions have been observed. Low temperature (77 K) study of EuCu₂Si₂ indicates distinct change in the relative intensities of the absorption peaks compared to those registered at room temperature (300 K). It is inferred from the change in the relative intensities that the population of Eu²⁺ in EuCu₂Si₂ decreases at liquid nitrogen temperature compared to Eu³⁺. Conclusions drawn from these results agree well with those reported by others using different experimental techniques. In Sm₄Bi₃, Sm²⁺ and Sm³⁺ are found to occur in the ratio of 3:1.     

Photoluminescence of F2+2 centres in additively coloured magnesium oxide

The principle luminescence bands excited in additively coloured MgO by radiation in the wavelength range 170–400 nm are observed at wavelengths of 520, 475, 441 and 375 nm. Polarised luminescence and uniaxial stress measurements on the 441 nm band, the radiative lifetime of 25 msec at 1.6 K and temperature dependence of luminescence intensities of the 375, 441 and 375 nm bands are consistent with the 441 nm band being due to ³B_1u → ¹A_g transitions of the F²⁺₂ centre.     

含Co2+与含Ni2+铁氧体的感生单轴各向异牲

本文分别计算了含Co²⁺与含Ni²⁺铁氧体的感生单轴各向异性。前者从Iida提出的物理机构出发,考虑了阳离子缺位对Co²⁺能级和波函数的影响;后者从Schnettler-Gyorgy所提出的物理机构出发,考虑了四面体位置中Ni²⁺的Jahn-Teller效应,求出了它的能级和波函数。由此算得此二类物质的感生单轴各向异性和实验结果符合得较好。另外,还解释了θ_u和θ_α产生偏离的原因。