Fabrication of a superhydrophobic ZnO nanorod array film on cotton fabrics via a wet chemical route and hydrophobic modification

A superhydrophobic ZnO nanorod array film on cotton substrate was fabricated via a wet chemical route and subsequent modification with a layer of n-dodecyltrimethoxysilane (DTMS). The as-obtained cotton sample was characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), scanning probe microscope (SPM) and X-ray photoelectron spectroscopy (XPS), respectively. The wettability of the cotton fabric sample was also studied by contact angle measurements. The modified cotton fabrics exhibited superhydrophobicity with a contact angle of 161° for 8 μL water droplet and a roll-off angle of 9° for 40 μL water droplet. It was shown that the proper surface roughness and the lower surface energy both played important roles in creating the superhydrophobic surface, in which the Cassie state dominated.     

Superhydrophobic cotton fabric coating based on a complex layer of silica nanoparticles and perfluorooctylated quaternary ammonium silane coupling agent

A superhydrophobic complex coating for cotton fabrics based on silica nanoparticles and perfluorooctylated quaternary ammonium silane coupling agent (PFSC) was reported in this article. The complex thin film was prepared through a sol-gel process using cotton fabrics as a substrate. Silica nanoparticles in the coating made the textile surface much rougher, and perfluorooctylated quaternary ammonium silane coupling agent on the top layer of the surface lowered the surface free energy. Textiles coated with this coating showed excellent water repellent property, and water contact angle (CA) increased from 133° on cotton fabrics treated with pure PFSC without silica sol pretreatment up to 145°. The oil repellency was also improved and the contact angle of CH₂I₂ droplet on the fabric surface reached to 131°. In contrast, the contact angle of CH₂I₂ on the fabric surface treated with pure PFSC was only 125°.     

Preparation of hybrid film with superhydrophobic surfaces based on irregularly structure by emulsion polymerization

A superhydrophobic surface originated from quincunx-shape composite particles was obtained by utilizing the encapsulation and graft of silica particles to control the surface chemistry and morphology of the hybrid film. The composite particles make the surface of film form a composite interface with irregular binary structure to trap air between the substrate surface and the liquid droplets which plays an essential role in obtaining high water contact angle and low water contact angle hysteresis. The water contact angle on the hybrid film is determined to be 154 ± 2° and the contact angle hysteresis is less than 5°. This is expected to be a simple and practical method for preparing self-cleaning hydrophobic surfaces on large area.     

A simple method to prepare miniature quartz fiber boats with superhydrophobicity

According to the reformed Cassie-Baxter equation, a superhydrophobic quartz fiber bundle boat was fabricated from mimicking the lotus leaf venation using chemical surface modifications and roughness introductions. Water contact angles as high as 165.8° were achieved for quartz fiber cloths. The loading capacities of the miniature boats made from the superhydrophobic quartz fiber bundles were measured. The highest loading weight, 10.19 g, was obtained by the boats with 2.0 mm spacing distance between fiber bundles. The striking loading capacities were believed to stem from the air film surrounding the superhydrophobic surfaces of the boats. The results of this study presented new applications of artificial hydrophobic surfaces in areas of aquatic devices.     

Fabrication of superhydrophobic cotton fabrics by silica hydrosol and hydrophobization

Superhydrophobic cotton fabrics were prepared by the incorporation of silica nanoparticles and subsequent hydrophobization with hexadecyltrimethoxysilane (HDTMS). The silica nanoparticles were synthesized via sol-gel reaction with methyl trimethoxy silane (MTMS) as the precursor in the presence of the base catalyst and surfactant in aqueous solution. As for the resulting products, characterization by particle size analyzer, scanning electron microscopy (SEM), scanning probe microscopy (SPM), X-ray photoelectron spectroscopy (XPS), and thermal gravimetric analysis (TGA) were performed respectively. The size of SiO₂ nanoparticles can be controlled by adjusting the catalyst and surfactant concentrations. The wettability of cotton textiles was evaluated by the water contact angle (WCA) and water shedding angle (WSA) measurements. The results showed that the treated cotton sample displayed remarkable water repellency with a WCA of 151.9° for a 5 μL water droplet and a WSA of 13° for a 15 μL water droplet.     

Transparent Superhydrophobic silica coatings on glass by sol-gel method

Wetting behavior of solid surfaces is a key concern in our daily life as well as in engineering and science. In the present study, we demonstrate a simple dip coating method for the preparation of Thermally stable, transparent superhydrophobic silica films on glass substrates at room temperature by sol-gel process. The coating alcosol was prepared by keeping the molar ratio of methyltriethoxysilane (MTES), trimethylmethoxysilane (TMMS), methanol (MeOH), water (H₂O) constant at 1:0.09:12.71:3.58, respectively with 13 M NH₄OH throughout the experiments and the films were prepared with different deposition time varied from 5 to 25 h. In order to improve the hydrophobicity of as deposited silica films, the films were derivatized with 10% trimethylchlorosilane (TMCS) as a silylating agent in hexane solvent for 24 h. Enhancement in wetting behavior was observed for surface derivatized silica films which showed a maximum static water contact angle (172°) and minimum sliding angle (2°) for 25 h of deposition time. The superhydrophobic silica films retained their superhydrophobicity up to a temperature of 550 °C. The silica films were characterized by field emission scanning electron microscopy (FE-SEM), surface profilometer, Fourier transform infrared (FT-IR) spectroscopy, thermo-gravimetric and differential thermal analysis (TG-DTA), percentage of optical transmission, water contact angle measurements. The imperviousness behavior of the films was tested with various acids.     

Thermal stable superhydrophobic polyphenylsilsesquioxane/nanosilica composite coatings

The superhydrophobic polyphenylsilsesquioxane (PPSQ)/nanosilica composite coatings were prepared by spray coating method with nano fumed silica (NFS) particles embedded in PPSQ matrix. The water contact angle (WCA) increased from 92.9° to 152.5° and the sliding angle (SA) decreased from more than 60° to 3.9° as the NFS content increased. The superhydrophobicity retained up to 500 °C, sustained by the hierarchical micro-nano structures and excellent thermal stability of PPSQ. A superhydrophobic PPSQ coating with WCA of 152.6° and SA of 7.8° was obtained by solvent-nonsolvent method for comparison as well. However, it gradually lost superhydrophobicity at 200 °C because of the elimination of nanostructures by the thermal softening of PPSQ.     

Thermal effect on superhydrophobic performance of stearic acid modified ZnO nanotowers

The thermal desorption of stearic acid on superhydrophobic zinc oxide nanotowers has been investigated. The stearic acid passivated zinc oxide nanotowers provide a very high contact angle of ∼173 ± 1.1° with a very low hysteresis of ∼1.4 ± 0.5° due to the presence of a binary structure composed of several nanosteps on each nanotower of height ∼700 nm that eventually reduces the area of contact between the drop and the nanotowers and trapping more air as revealed by the field emission scanning electron microscopy images. The superhydrophobic performance of these nanotowers, however, declines following annealing at elevated temperatures. Fourier transform infrared spectra show a reduction in the intensity of stearic acid -CH_n peaks at elevated temperatures revealing the cause of the decrease in contact angle and confirming the occurrence of thermal desorption at 184 °C. The corresponding activation energy for desorption determined from our data is 0.34 ± 0.05 eV. It is found that the stearic acid has completely disappeared at 350 °C, making the sample hydrophilic.     

Wetting and superhydrophobic properties of PECVD grown hydrocarbon and fluorinated-hydrocarbon coatings

Wetting characteristics of micro-nanorough substrates of aluminum and smooth silicon substrates have been studied and compared by depositing hydrocarbon and fluorinated-hydrocarbon coatings via plasma enhanced chemical vapor deposition (PECVD) technique using a mixture of Ar, CH₄ and C₂F₆ gases. The water contact angles on the hydrocarbon and fluorinated-hydrocarbon coatings deposited on silicon substrates were found to be 72° and 105°, respectively. However, the micro-nanorough aluminum substrates demonstrated superhydrophobic properties upon coatings with fluorinated-hydrocarbon providing a water contact angle of ∼165° and contact angle hysteresis below 2° with water drops rolling off from those surfaces while the same substrates showed contact angle of 135° with water drops sticking on those surfaces. The superhydrophobic properties is due to the high fluorine content in the fluorinated-hydrocarbon coatings of ∼36 at.%, as investigated by X-ray photoelectron spectroscopy (XPS), by lowering the surface energy of the micro-nanorough aluminum substrates.     

Optically transparent, superhydrophobic methyltrimethoxysilane based silica coatings without silylating reagent

The superhydrophobic surfaces have drawn lot of interest, in both academic and industries because of optically transparent, adherent and self-cleaning behavior. Surface chemical composition and morphology plays an important role in determining the superhydrophobic nature of coating surface. Such concert of non-wettability can be achieved, using surface modifying reagents or co-precursor method in sol-gel process. Attempts have been made to increase the hydrophobicity and optical transparency of methyltrimethoxysilane (MTMS) based silica coatings using polymethylmethacrylate (PMMA) instead of formal routes like surface modification using silylating reagents. The optically transparent, superhydrophobic uniform coatings were obtained by simple dip coating method. The molar ratio of MTMS:MeOH:H₂O was kept constant at 1:5.63:1.58, respectively with 0.5 M NH₄F as a catalyst and the weight percent of PMMA varied from 1 to 8. The hydrophobicity of silica coatings was analyzed by FTIR and contact angle measurements. These substrates exhibited 91% optical transmittance as compared to glass and water drop contact angle as high as 171 ± 1°. The effect of humidity on hydrophobic nature of coating has been studied by exposing these films at relative humidity of 90% at constant temperature of 30 °C for a period of 45 days. The micro-structural studies carried out by transmission electron microscopy (TEM).     

A novel simple approach to preparation of superhydrophobic surfaces of aluminum alloys

A novel two-step methodology is successfully developed to fabricate superhydrophobic surfaces of aluminum alloys. The essential procedure is that samples are first immersed and etched in a boiling aqueous solution of NaOH for 5 min without preprocessing, and then they are modified for 30 min in an ethanol solution of lauric acid, cheaper and more efficient than the fluorinated silane frequently adopted by other researchers. If the concentration of NaOH solution is larger than 5 g/L, the contact angle of the prepared surfaces will be larger than 150° with a negligible hysteresis. Such a fast, low-cost, and reliable method for superhydrophobic surfaces implies significant promising industrial applications.     

Fabrication and characterization of a cotton candy like surface with superhydrophobicity

Superhydrophobic thin films were prepared on glass by air-brushing the in situ polymerization compositions of D₅/SiO₂. The wettability and morphology were investigated by contact angle measurement and scanning electron microscopy. The most superhydrophobic samples prepared had a static water contact angle of 157° for a 5 μl droplet and a sliding angle of ∼1° for 10 μl droplet. Thermal stability analysis showed that the surface maintained superhydrophobic at temperature up to 450 °C. Air trapping and capillary force on superhydrophobic behavior were evaluated.     

Mechanically stable and corrosion resistant superhydrophobic sol-gel coatings on copper substrate

Development of the anticorrosion coatings on metals having both passive matrix functionality and active response to changes in the aggressive environment has raised tremendous interest in material science. Using a sol-gel deposition method, superhydrophobic copper substrate could be obtained. The best hydrophobic coating sol was prepared with methyltriethoxysilane (MTES), methanol (MeOH), and water (as 7 M NH₄OH) at a molar ratio of 1:19.1:4.31 respectively. The surface morphological study showed the ball like silica particles distributed on the copper substrate with particle sizes ranging from 8 to 12 μm. The coatings showed the static water contact angle as high as 155° and the water sliding angle as low as 7°. The superhydrophobic nature was maintained even though the deposited copper substrate was soaked for 100 h in 50% of HCl solution. The coatings are stable against humidity and showed superhydrophobic behavior even after 90 days of exposure. The coatings are mechanically stable and water drops maintained the spherical shape on the bent copper substrate, which was bent more than 90°.     

Superhydrophobic sol-gel nanocomposite coatings with enhanced hardness

Sol-gel superhydrophobic coatings with improved hardness were prepared by embedding fumed silica nanoparticles in a partially condensed hybrid sol of methyltriethoxysilane (MTEOS) and colloidal silica. Fumed silica particles of size 25-30 nm were incorporated in the sol and the mixture was spray-coated on glass substrate. Water contact angle (WCA) of the composite coating increased with increase in silica content of the sol mixture. The concentration of silica in the sol mixture was optimized to obtain robust superhydrophobic coatings with a WCA of 162.5° and a pencil hardness of 5H. The wetting state of water droplet on the sol-gel composite coatings was analysed with both Wenzel and Cassie-Baxter models.     

Superhydrophobic wind turbine blade surfaces obtained by a simple deposition of silica nanoparticles embedded in epoxy

Samples of wind turbine blade surface have been covered with a superhydrophobic coating made of silica nanoparticles embedded in commercial epoxy paint. The superhydrophobic surfaces have a water contact angle around 152°, a hysteresis less than 2° and a water drop sliding angle around 0.5°. These surfaces are water repellent so that water drops cannot remain motionless on the surface. Examination of coated and uncoated surfaces with scanning electron microscopy and atomic force microscopy, together with measurements of water contact angles, indicates that the air trapped in the cavity enhances the water repellency similarly to the lotus leaf effect. Moreover, this new coating is stable under UVC irradiation and water pouring. The production of this nanoscale coating film being simple and low cost, it can be considered as a suitable candidate for water protection of different outdoor structures.     

Preparation of vertically aligned carbon nanotube arrays grown onto carbon fiber fabric and evaluating its wettability on effect of composite

Vertically aligned carbon nanotube (CNT) arrays have been grown onto the carbon fiber fabric using a catalytic chemical vapor deposition (CCVD) method. The as-synthesized CNT arrays are about 20 μm in height, and the nanotube has a mean inner and outer diameter of 2.6 nm, 5.5 nm, respectively. The CNT-grafted carbon fabric shows a hydrophobic property with a contact angle over 145°, and the single CNT-grafted carbon fiber shows a sharp increase of dynamic contact angle in de-ionized water from original 71.70° to about 103°, but a little increase does in diiodomethane or E-51 epoxy resin. However, the total surface energy of carbon nanotube-grafted carbon fiber is almost as same as that of as-received carbon fiber. After CNTs growth, single fiber tensile tests indicated a slight tensile strength degradation within 10% for all different lengths of fibers, while the fiber modulus has not been significantly damaged. Compared with the as-received carbon fibers, a nearly 110% increase of interfacial shear strength (IFSS) from 65 to 135 MPa has been identified by single fiber pull-out tests for the micro-droplet composite, which is reinforced by as-received carbon fiber or CNT-grafted carbon fiber.     

Superhydrophobic and icephobic surfaces prepared by RF-sputtered polytetrafluoroethylene coatings

A superhydrophobic and icephobic surface were investigated on aluminum alloy substrate. Anodizing was used first to create a micro-nanostructured aluminum oxide underlayer on the alloy substrate. In a second step, the rough surface was coated with RF-sputtered polytetrafluoroethylene (PTFE or Teflon^®). Scanning electron microscopy images showed a “bird's nest”-like structure on the anodized surface. The RF-sputtered PTFE coating exhibited a high static contact angle of ∼165° with a very low contact angle hysteresis of ∼3°. X-ray photoelectron spectroscopy (XPS) results showed high quantities of CF₃ and CF₂ groups, which are responsible for the hydrophobic behavior of the coatings. The performance of this superhydrophobic film was studied under atmospheric icing conditions. These results showed that on superhydrophobic surfaces ice-adhesion strength was 3.5 times lower than on the polished aluminum substrate.     

Superhydrophobicity of polytetrafluoroethylene thin film fabricated by pulsed laser deposition

Superhydrophobic polytetrafluoroethylene (PTFE) thin films were obtained by pulsed laser deposition (PLD) technique carried out with KrF excimer laser (λ = 248 nm) of about 1 J/cm² at a pressure of 1.33 Pa. The samples exhibit high water contact angle of about 170° and the sliding angle smaller than 2°. From studying the surface morphology of the prepared films, it is believed that the nano-scale surface roughness has enhanced the hydrophobic property of the PTFE. The increase of trapping air and reducing liquid-solid contact area due to the rough surface, as suggested by the Cassie-Baxter's model, should be responsible for superhydrophobicity of the PLD prepared films. This study thus provides a convenient one-step method without using wet-process to produce a superhydrophobic surface with good self-cleaning properties.     

Wettability behaviour of RTV silicone rubber coated on nanostructured aluminium surface

A nanostructutered superhydrophobic surface was elaborated by applying an RTV silicone rubber coating on electrochemically processed aluminium substrates. Study of anodisation voltage on surface morphology showed that higher anodising voltage led to larger pore sizes. Scanning electron microscopy image analysis showed bird's nest and beehive structures formed on anodised surfaces at 50 V and 80 V. Water static contact angle on the treated surfaces reached up to 160° at room temperature. Study of superhydrophobic surfaces at super cooled temperature showed important delayed freezing time for RTV hydrophobic surfaces when compared to non-treated aluminium. However, lower wettability was observed when surface temperature went down from 20 °C to −10 °C. Also, it was found that the capacitance of superhydrophobic surfaces decreased with increasing anodising voltage.     

A novel method to fabricate superhydrophobic surfaces based on well-defined mulberry-like particles and self-assembly of polydimethylsiloxane

A superhydrophobic surface was obtained by combining application of CaCO₃/SiO₂ mulberry-like composite particles, which originated from violent stirring and surface modification, and self-assembly of polydimethylsiloxane. Water contact angle and sliding angle of the superhydrophobic surface were measured to be about 164 ± 2.5° and 5°, respectively. The excellent hydrophobicity is attributed to the synergistic effect of micro-submicro-nano-meter scale roughness (fabricated by composite particles) and the low surface energy (provided by polydimethylsiloxane). This procedure makes it possible for widespread applications of superhydrophobic film due to its simplicity and practicability.