A simple method for the preparation of superhydrophobic PVDF-HMFS hybrid composite coatings

A superhydrophobic surface was obtained by embedding hydrophobically modified fumed silica (HMFS) particles in polyvinylidene fluoride (PVDF) matrix. The water contact angle (WCA) on the PVDF-HMFS hybrid composite coating is influenced by the content and nature of silica particles in the coating. As the silica concentration in PVDF matrix was increased from 33.3% to 71.4%, WCA increased from 117° to 168° and the sliding angle decreased from 90° to <1°. Surface topography of the coating was examined using scanning electron microscopy. An irregular rough surface structure composed of microcavities and nanofilaments was found to be responsible for the superhydrophobicity. The method is simple and cost-effective and can be used for preparing self-cleaning superhydrophobic coating on large areas of different substrates.     

Facile fabrication of superhydrophobic polytetrafluoroethylene surface by cold pressing and sintering

A series of superhydrophobic polytetrafluoroethylene (PTFE) surfaces were prepared by a facile cold pressing and sintering method, and their microstructures and wetting behaviors could be artificially tailored by altering sintering temperature and using different masks. Specifically, the microstructures mainly depended on the sintering temperature, whereas the wetting behaviors, water contact angle (WCA) and sliding angle (SA), greatly hinged on both the sintering temperature and mask. Then a preferable superhydrophobic surface with WCA of 162 ± 2° and SA of 7° could be obtained when the sintering temperature was 360 °C and the 1000 grit abrasive paper was used as a mask. In addition, it was worth noting that the as-prepared surfaces exhibited excellent stability under UV illumination, which was the most key factor for them toward practical applications.     

Fabrication of superhydrophobic coating via a facile and versatile method based on nanoparticle aggregates

Herein, we report a facile and low cost method for the fabrication of superhydrophobic surface via spin coating the mixture of polydimethylsiloxane precursor (PDMS) and silicon dioxide (SiO₂) nanoparticles. The surface hydrophobicity can be well tuned by adjusting the weight percent of PDMS and SiO₂. The water contact angle (WCA) can increase from 106.8 ± 1.2° on PDMS film to 165.2 ± 2.3° on PDMS/SiO₂ coating, companying with a change from adhering to rolling which was observed from tilting angle (TA) characterization. Multi-scale physical structures with SiO₂ nanoparticle aggregates and networks of SiO₂ nanoparticle aggregates are characterized by scanning electron microscopy (SEM) and atomic force microscope (AFM), and they can be observed more clearly from the AFM images treated with software (WSxM). Then the relationship between surface hydrophobicity and structures is further discussed based on Wenzel and Cassie models, indicating that the appearance of networks of nanoparticle aggregates is important in the Cassie state. The superhydrophobic coating can keep the superhydrophobicity at least for one month under environment conditions and readily regenerate after mechanical damage. Additionally, the superhydrophobic coating can be fabricated using other methods including dip coating, spray coating and casting. Thus, a large area of superhydrophobic coatings can be easily fabricated. Therefore the range of possible applications for these facile and versatile methods can be expanded to various actual conditions.     

Electrostatic powder spraying process for the fabrication of stable superhydrophobic surfaces

Nano-sized Al₂O₃ particles were modified by heptadecafluorodecyl trimethoxysilane and 2,3-epoxy propoxy propyl trimethoxysilicane to make it both hydrophobic and reactive. The reactive nano-particles were mixed with polyester resin containing curing agents and electrostatic sprayed on stainless steel substrates to obtain stable superhydrophobic coatings after curing. The water contact angle (WCA) on the hybrid coating is influenced by the content of Al₂O₃ particles in the coating. As the Al₂O₃ concentration in the coating was increased from 0% to 8%, WCA increased from 68° to 165°. Surface topography of the coatings was examined using scanning electron microscopy (SEM). Nano-particles covered on the coating surface formed continuous film with greatly enhanced roughness, which was found to be responsible for the superhydrophobicity. The method is simple and cost effective and can be used for preparing self-cleaning superhydrophobic coating on large areas.     

Transparent Superhydrophobic silica coatings on glass by sol-gel method

Wetting behavior of solid surfaces is a key concern in our daily life as well as in engineering and science. In the present study, we demonstrate a simple dip coating method for the preparation of Thermally stable, transparent superhydrophobic silica films on glass substrates at room temperature by sol-gel process. The coating alcosol was prepared by keeping the molar ratio of methyltriethoxysilane (MTES), trimethylmethoxysilane (TMMS), methanol (MeOH), water (H₂O) constant at 1:0.09:12.71:3.58, respectively with 13 M NH₄OH throughout the experiments and the films were prepared with different deposition time varied from 5 to 25 h. In order to improve the hydrophobicity of as deposited silica films, the films were derivatized with 10% trimethylchlorosilane (TMCS) as a silylating agent in hexane solvent for 24 h. Enhancement in wetting behavior was observed for surface derivatized silica films which showed a maximum static water contact angle (172°) and minimum sliding angle (2°) for 25 h of deposition time. The superhydrophobic silica films retained their superhydrophobicity up to a temperature of 550 °C. The silica films were characterized by field emission scanning electron microscopy (FE-SEM), surface profilometer, Fourier transform infrared (FT-IR) spectroscopy, thermo-gravimetric and differential thermal analysis (TG-DTA), percentage of optical transmission, water contact angle measurements. The imperviousness behavior of the films was tested with various acids.     

Superhydrophobic sol-gel nanocomposite coatings with enhanced hardness

Sol-gel superhydrophobic coatings with improved hardness were prepared by embedding fumed silica nanoparticles in a partially condensed hybrid sol of methyltriethoxysilane (MTEOS) and colloidal silica. Fumed silica particles of size 25-30 nm were incorporated in the sol and the mixture was spray-coated on glass substrate. Water contact angle (WCA) of the composite coating increased with increase in silica content of the sol mixture. The concentration of silica in the sol mixture was optimized to obtain robust superhydrophobic coatings with a WCA of 162.5° and a pencil hardness of 5H. The wetting state of water droplet on the sol-gel composite coatings was analysed with both Wenzel and Cassie-Baxter models.     

Deposition of superhydrophobic nanostructured Teflon-like coating using expanding plasma arc

A novel approach was used to grow nanostructured Teflon-like superhydrophobic coatings on stainless steel (SS). In this method Teflon tailings were pyrolyzed to generate fluorocarbon precursor molecules, and an expanding plasma arc (EPA) was used to polymerize these precursors to deposit Teflon-like coating. The coating shows super hydrophobic behavior with water contact angle (WCA) of 165°. The coating was observed to be uniform. It consists of nanostructured (∼80-200 nm) features, which were confirmed by scanning electron microscopy. The chemical bond state of the film was determined by XPS and FTIR, which indicate the dominance of -CF₂ groups in the deposited coating. The combination of nanofeature induced surface roughness and the low surface energy imparted by Teflon-like coating is responsible for the observed superhydrophobic nature.     

Preparation of superhydrophobic films on titanium as effective corrosion barriers

Stable superhydrophobic films were prepared on the electrochemical oxidized titania/titanium substrate by a simple immersion technique into a methanol solution of hydrolyzed 1H,1H,2H,2H-perfluorooctyltriethoxysilane [CF₃(CF₂)₅(CH₂)₂Si(OCH₂CH₃)₃, PTES] for 1 h at room temperature followed by a short annealing at 140 °C in air for 1 h. The surface morphologies and chemical composition of the film were characterized by means of water contact angle (CA), field emission scanning electron microscopy (FESEM), atomic force microscope (AFM) and X-ray photoelectron spectroscopy (XPS). The water contact angle on the surface of this film was measured to be as high as 160°. SEM images showed that the resulting surfaces exhibited special hierarchical structure. The special hierarchical structure along with the low surface energy leads to the high surface superhydrophobicity. The corrosion resistance ability and durance property of the superhydrophobic film in 3.5 wt.% NaCl solution was evaluated by the electrochemical impedance spectroscopy (EIS). The anticorrosion properties of the superhydrophobic film are compared to those of unmodified pure titanium and titania/titanium substrates. The results showed that the superhydrophobic film provides an effective corrosion resistant coating for the titanium metal even with immersion periods up to 90 d in the 3.5 wt.% NaCl solution, pointing to promising future applications.     

Superhydrophobic surfaces based on dandelion-like ZnO microspheres

This study presents a simple method to fabricate superhydrophobic surface based on ZnO nanoneedles. ZnO nanoneedles had been constructed on zinc layers by immersing in an aqueous NH₄OH solution at 80 °C. The ZnO films were characterized by X-ray diffraction, scanning electron microscopy and X-ray photoelectron spectroscopy. The ZnO films exhibited excellent superhydrophilicity (contact angle for water was 0°), while they changed wettability to superhydrophobicity with a water contact angle greater than 150° after further chemical modification with n-dodecanoic acid. The procedure reported here only needs readily available reagents and laboratory equipments, which can be applied to various substrates of any size and shape.     

Investigation into the photo-induced change in wettability of hydrophobized TiO2 films

The photo-induced change in wettability of hydrophobized TiO₂ films has been investigated for steel coated with acidic TiO₂ nanosols containing varying concentrations of dispersed nanocrystalline titania, such as Degussa P25. The photo-induced change in wettability was evaluated by measuring the time-dependent drop of water contact angle (WCA) after samples had been soaked in either n-octyltriethoxysilane (OTS) or decanoic acid (DA). TiO₂ films treated in this way exhibit superhydrophobic behaviour, with WCA greater than 160°. After radiation with UV (black light), the superhydrophobic properties are transformed into superhydrophilic properties, with WCA of almost 0°. As P25 content and layer thickness increase, high rates of photo-induced change are found, but a moderate calcination regime is required. On the other hand, hardness and E modulus pass through a maximum at 25 wt% P25, so that a P25 content between 25 and 50 wt% is the optimum for practical uses. With such stable coatings, wettability can be controlled over a wide range, and the switch between hydrophobic and hydrophilic states can be carried out repeatedly when DA is used as the hydrophobizing agent. Use of a low calcination temperature (450 °C) for the intermediate annealing of the single layers in multilayer coatings and a short final sintering step at a relatively high temperature (e.g. 630 °C for 10 min) allow the preparation of relatively thin TiO₂ films on steel with a high photoactivity.     

Fabrication of superhydrophobic binary nanoparticles/PMMA composite coating with reversible switching of adhesion and anticorrosive property

Ag-TiO₂-Thiol/Poly(methyl methacrylate) (PMMA) coating has been prepared via adsorbed-layer nanoreactor technique and self-assembling method. The composite coating shows a superhydrophobic property with reversible switching of adhesion. In the UV-vis spectra, absorption appeared in ultraviolet region of 229-293 nm (UVC region) and 320-370 nm (UVA region). Additionally, the stability of the superhydrophobic surface was tested under the following conditions: (1) in basic solution (pH = 14); (2) in acid solution (pH = 1); (3) in artificial seawater. The coating shows stability since the contact angle of the sample still remained higher than 150° in the above conditions. The corrosion resistance of the superhydrophobic surfaces was investigated by electrochemical measurements and the results revealed that the superhydrophobic coatings are anticorrosive well.     

Preparation of superhydrophobic surface with a novel sol-gel system

Sol-gel method is a simple and cheap way to prepare superhydrophobic coatings or films, however, most of the researches on sol-gel focus on silica or ZnO sol-gel. The present paper proposes a novel sol-gel which is made from hydrolysis and condensation of the by-product of polymethylhydrosiloxane (PMHS) reacting with γ-aminopropyltriethoxysilane (KH550). The mechanism of formation of the by-product and the sol-gel is discussed and the by-product is characterized by FT-IR. The mass ratio of KH550/PMHS of the sol-gel influences the water contact angle (WCA) and water sliding angle (WSA) of the film made of spraying the sol-gel to microscope glass. When the mass ratio of KH550/PMHS of the sol-gel reaches 0.25, WCA of the corresponding film is 157° and WSA of it is less than 1°. The mechanism of formation of the sol-gel is discussed, and the size of the sol-gel is characterized by polarization microscope as well. The morphology of the film made of the sol-gel is analyzed by means of scanning electron microscope (SEM). It was found that the diameter of the particle of the superhydrophobic film is about 40 μm, nevertheless, from the larger magnification picture, the particle is found to be composed of micro-balls whose diameter is about 2 μm, and the micro-ball is composed of nano-sphere whose diameter is less than 200 nm.     

Superhydrophobic cotton fabric fabricated by electrostatic assembly of silica nanoparticles and its remarkable buoyancy

Highly hydrophilic cotton fabrics were rendered superhydrophobic via electrostatic layer-by-layer assembly of polyelectrolyte/silica nanoparticle multilayers on cotton fibers, followed with a fluoroalkylsilane treatment. The surface morphology of the silica nanoparticle-coated fibers, which results in the variety of the hydrophobicity, can be tailored by controlling the multilayer number. Although with the static contact angle larger than 150°, in the case of 1 or 3 multilayers, the fabrics showed sticky property with a high contact angle hysteresis (>45°). For the cotton fabrics assembled with 5 multilayers or more, slippery superhydrophobicity with a contact angle hysteresis lower than 10° was achieved. The buoyancy of the superhydrophobic fabric was examined by using a miniature boat made with the fabric. The superhydrophobic fabric boat exhibited a remarkable loading capacity; for a boat with a volume of 8.0 cm³, the maximum loading was 11.6 or 12.2 g when the boat weight is included. Moreover, the superhydrophobic cotton fabric showed a reasonable durability to withstand at least 30 machine washing cycles.     

Optically transparent, superhydrophobic methyltrimethoxysilane based silica coatings without silylating reagent

The superhydrophobic surfaces have drawn lot of interest, in both academic and industries because of optically transparent, adherent and self-cleaning behavior. Surface chemical composition and morphology plays an important role in determining the superhydrophobic nature of coating surface. Such concert of non-wettability can be achieved, using surface modifying reagents or co-precursor method in sol-gel process. Attempts have been made to increase the hydrophobicity and optical transparency of methyltrimethoxysilane (MTMS) based silica coatings using polymethylmethacrylate (PMMA) instead of formal routes like surface modification using silylating reagents. The optically transparent, superhydrophobic uniform coatings were obtained by simple dip coating method. The molar ratio of MTMS:MeOH:H₂O was kept constant at 1:5.63:1.58, respectively with 0.5 M NH₄F as a catalyst and the weight percent of PMMA varied from 1 to 8. The hydrophobicity of silica coatings was analyzed by FTIR and contact angle measurements. These substrates exhibited 91% optical transmittance as compared to glass and water drop contact angle as high as 171 ± 1°. The effect of humidity on hydrophobic nature of coating has been studied by exposing these films at relative humidity of 90% at constant temperature of 30 °C for a period of 45 days. The micro-structural studies carried out by transmission electron microscopy (TEM).     

Superhydrophobicity of polytetrafluoroethylene thin film fabricated by pulsed laser deposition

Superhydrophobic polytetrafluoroethylene (PTFE) thin films were obtained by pulsed laser deposition (PLD) technique carried out with KrF excimer laser (λ = 248 nm) of about 1 J/cm² at a pressure of 1.33 Pa. The samples exhibit high water contact angle of about 170° and the sliding angle smaller than 2°. From studying the surface morphology of the prepared films, it is believed that the nano-scale surface roughness has enhanced the hydrophobic property of the PTFE. The increase of trapping air and reducing liquid-solid contact area due to the rough surface, as suggested by the Cassie-Baxter's model, should be responsible for superhydrophobicity of the PLD prepared films. This study thus provides a convenient one-step method without using wet-process to produce a superhydrophobic surface with good self-cleaning properties.     

Fabrication of superhydrophobic surfaces on zinc substrates and their application as effective corrosion barriers

Stable superhydrophobic surfaces have been effectively fabricated on the zinc substrates through one-step platinum replacement deposition process without the further modification or any other post processing procedures. The effect of reaction temperatures on the surface morphology and wettability was studied by using SEM and water contact angle (CA) analysis. Under room temperature, the composite structure formed on the zinc substrate was consisted of microscale hexagonal cavities, densely packed nanoparticles layer and micro/nanoscale structures like the flowers. The structure has exhibited great surface roughness and porosity contributing to the superhydrophobicity where the contact angle could reach an ultra high value of around 170°. Under reaction temperature of 80 °C, the composite structure, on the other hand, was hierarchical structure containing lots of nanoscale flowers and some large bushes and showed certain surface roughness (maximum CA value of about 150°). In addition, an optimal superhydrophobic platinum surface was able to provide an effective anticorrosive coating to the zinc substrate when it was immersed into an aqueous solution of sodium chloride (3% NaCl) for up to 20 days. The corrosion process was monitored through electrochemical means and the results are compared with those of unprotected zinc plates.     

Fabrication of a superhydrophobic ZnO nanorod array film on cotton fabrics via a wet chemical route and hydrophobic modification

A superhydrophobic ZnO nanorod array film on cotton substrate was fabricated via a wet chemical route and subsequent modification with a layer of n-dodecyltrimethoxysilane (DTMS). The as-obtained cotton sample was characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), scanning probe microscope (SPM) and X-ray photoelectron spectroscopy (XPS), respectively. The wettability of the cotton fabric sample was also studied by contact angle measurements. The modified cotton fabrics exhibited superhydrophobicity with a contact angle of 161° for 8 μL water droplet and a roll-off angle of 9° for 40 μL water droplet. It was shown that the proper surface roughness and the lower surface energy both played important roles in creating the superhydrophobic surface, in which the Cassie state dominated.     

Wettability behaviour of RTV silicone rubber coated on nanostructured aluminium surface

A nanostructutered superhydrophobic surface was elaborated by applying an RTV silicone rubber coating on electrochemically processed aluminium substrates. Study of anodisation voltage on surface morphology showed that higher anodising voltage led to larger pore sizes. Scanning electron microscopy image analysis showed bird's nest and beehive structures formed on anodised surfaces at 50 V and 80 V. Water static contact angle on the treated surfaces reached up to 160° at room temperature. Study of superhydrophobic surfaces at super cooled temperature showed important delayed freezing time for RTV hydrophobic surfaces when compared to non-treated aluminium. However, lower wettability was observed when surface temperature went down from 20 °C to −10 °C. Also, it was found that the capacitance of superhydrophobic surfaces decreased with increasing anodising voltage.     

Fabrication and wear protection performance of superhydrophobic surface on zinc

A simple two-step process has been developed to render zinc surface superhydrophobic, resulting in low friction coefficient and long wear resistance performance. The ZnO film with uniform and packed nanorod structure was firstly created by immersing the zinc substrates into 4% N,N-dimethylformamide solution. The as-fabricated surface was then coated a layer of fluoroalkylsilane (FAS) by gas phase deposition. Scanning electron microscopy (SEM) and water contact angle (WCA) measurement have been performed to characterize the morphological feature, chemical composition and superhydrophobicity of the surface. The resulting surfaces have a WCA as high as 156° and provide effective friction-reducing and wear protection for zinc substrate.     

Organic-inorganic hybrid superhydrophobic surfaces using methyltriethoxysilane and tetraethoxysilane sol-gel derived materials in emulsion

By applying alkaline-catalyzed co-hydrolysis and copolycondensation reactions of tetraethoxysilane (TEOS) and methyltriethoxysilane (MTES) in organic siloxane modified polyacrylate emulsion (OSPA emulsion), we are able to demonstrate the potential for developing a sol-gel derived organic-inorganic hybrid emulsion for a superhydrophobic surface research. TEOS and MTES derived sol-gel moieties can be designed for a physical roughness and hydrophobic characteristic (Si-CH₃) of the hybrid superhydrophobic surface, while OSPA emulsion can be endowed for good film-forming property. The effect of formulation parameters on superhydrophobicity and film-forming property was analyzed. The water contact angle (WCA) on the sol-gel derived hybrid film is determined to be 156°, and the contact angle hysteresis is 5° by keeping the mole ratio of TEOS:MTES:C₂H₅OH:NH₃·H₂O:AMP-95 at 1:4:30:10:0.63 and the mass percentage of OSPA emulsion at 25%. The nanoparticle-based silica rough surface is observed as the mole ratio of MTES/TEOS at 4:1. The sol-gel derived organic-inorganic hybrid emulsion shows remarkable film-forming property when the mole ratio of MTES/TEOS reaches or exceeds 4:1. With the primer coating, the performance of superhydrophobic film achieve actual use standard. It reveals that this new procedure is an effective shortcut to obtain a superhydrophobic surface with potential applications.