Green synthesis and characterization of superparamagnetic Fe3O4 nanoparticles

In this paper, we have first demonstrated a facile and green synthetic approach for preparing superparamagnetic Fe₃O₄ nanoparticles using α-d-glucose as the reducing agent and gluconic acid (the oxidative product of glucose) as stabilizer and dispersant. The X-ray powder diffraction (XRD), X-ray photoelectron spectrometry (XPS), and selected area electron diffraction (SAED) results showed that the inverse spinel structure pure phase polycrystalline Fe₃O₄ was obtained. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) results exhibited that Fe₃O₄ nanoparticles were roughly spherical shape and its average size was about 12.5 nm. The high-resolution TEM (HRTEM) result proved that the nanoparticles were structurally uniform with a lattice fringe spacing about 0.25 nm, which corresponded well with the values of 0.253 nm of the (3 1 1) lattice plane of the inverse spinel Fe₃O₄ obtained from the JCPDS database. The superconducting quantum interference device (SQUID) results revealed that the blocking temperature (T_b) was 190 K, and that the magnetic hysteresis loop at 300 K showed a saturation magnetization of 60.5 emu/g, and the absence of coercivity and remanence indicated that the as-synthesized Fe₃O₄ nanoparticles had superparamagnetic properties. Fourier transform infrared spectroscopy (FT-IR) spectrum displayed that the characteristic band of Fe-O at 569 cm⁻¹ was indicative of Fe₃O₄. This method might provide a new, mild, green, and economical concept for the synthesis of other nanomaterials.     

Magnetic and rheological properties of monodisperse Fe3O4 nanoparticle/organic hybrid

Fe₃O₄ nanoparticle/organic hybrids were synthesized via hydrolysis using iron (III) acetylacetonate at ∼80 °C. The synthesis of Fe₃O₄ was confirmed by X-ray diffraction, selected-area diffraction, and X-ray photoelectron spectroscopy. Fe₃O₄ nanoparticles in the organic matrix had diameters ranging from 7 to 13 nm depending on the conditions of hydrolysis. The saturation magnetization of the hybrid increased with an increase in the particle size. When the hybrid contained Fe₃O₄ particles with a size of less than 10 nm, it exhibited superparamagnetic behavior. The blocking temperature of the hybrid containing Fe₃O₄ particles with a size of 7.3 nm was 200 K, and it increased to 310 K as the particle size increased to 9.1 nm. A hybrid containing Fe₃O₄ particles of size greater than 10 nm was ferrimagnetic, and underwent Verwey transition at 130 K. Under a magnetic field, a suspension of the hybrid in silicone oil revealed the magnetorheological effect. The yield stress of the fluid was dependent on the saturation magnetization of Fe₃O₄ nanoparticles in the hybrid, the strength of the magnetic field, and the amount of the hybrid.     

Magnetic properties of the novel nanocomposite (Zn0.15Ni0.85Fe2O4)0.15/(SiO2)0.85 at room temperature

The value of the effective magnetic anisotropy constant of the ferrimagnetic nanoparticles Zn_0.15Ni_0.85Fe₂O₄ embedded in a SiO₂ silica matrix, determined through ferromagnetic resonance (FMR), is much higher than the magnetocrystalline anisotropy constant. The higher value of the anisotropy constant is due to the existence of surface anisotropy. However, even if the magnetic anisotropy is high, the ferrimagnetic nanoparticles with a 15% concentration, which are isolated in a SiO₂ matrix, display a superparamagnetic (SPM) behavior at room temperature and at a frequency of the magnetization field equal to 50 Hz. The FMR spectrum of the novel nanocomposite (Zn_0.15Ni_0.85Fe₂O₄)_0.15/(SiO₂)_0.85, recorded at room temperature and a frequency of 9.060 GHz, is observed at a resonance field (B_0r) of 0.2285 T, which is substantially lower than the field corresponding to free electron resonance (ESR) (0.3236 T). Apart from the line corresponding to the resonance of the nanoparticle system, the spectrum also contains an additional weaker line, identified for a resonance field of ∼0.12 T, which is appreciably lower than B_0r. This line was attributed to magnetic ions complex that is in a disordered structure in the layer that has an average thickness of 1.4 nm, this layer being situated on the surface of the Zn_0.15Ni_0.85Fe₂O₄ nanoparticles that have a mean magnetic diameter of 8.9 nm.     

Synthesis of Co-Cu-Zn doped Fe3O4 nanoparticles with tunable morphology and magnetic properties

Co-Cu-Zn doped Fe₃O₄ nanoparticles can be successfully synthesized using a simple method. The particles in the size range 20−400 nm with different regular shapes i.e. sphere-like, regular hexane and tetrahedron are controllably achieved by changing the metal ion concentration. Compared to pure Fe₃O₄ without dopants, Co-Cu-Zn doped Fe₃O₄ nanoparticles exhibit better microwave absorbing properties at 2−18 GHz. Among three Co-Cu-Zn doped Fe₃O₄ nanoparticles with different morphologies, tetrahedral Co-Cu-Zn doped Fe₃O₄ nanoparticles represent a better dielectric loss in high frequency range. This work is believed the first known report of Co-Cu-Zn doped Fe₃O₄ nanoparticles with tunable morphology and magnetic properties through the hydrothermal process without using any organic solvents, organic metal salts or surfactants.     

Green synthesis of soya bean sprouts-mediated superparamagnetic Fe3O4 nanoparticles

Superparamagnetic Fe₃O₄ nanoparticles were first synthesized via soya bean sprouts (SBS) templates under ambient temperature and normal atmosphere. The reaction process was simple, eco-friendly, and convenient to handle. The morphology and crystalline phase of the nanoparticles were determined from scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), and X-ray diffraction (XRD) spectra. The effect of SBS template on the formation of Fe₃O₄ nanoparticles was investigated using X-ray photoemission spectroscopy (XPS) and Fourier-transform infrared spectroscopy (FT-IR). The results indicate that spherical Fe₃O₄ nanoparticles with an average diameter of 8 nm simultaneously formed on the epidermal surface and the interior stem wall of SBS. The SBS are responsible for size and morphology control during the whole formation of Fe₃O₄ nanoparticles. In addition, the superconducting quantum interference device (SQUID) results indicate the products are superparamagnetic at room temperature, with blocking temperature (T_B) of 150 K and saturation magnetization of 37.1 emu/g.     

Electro-precipitation of Fe3O4 nanoparticles in ethanol

The preparation of superparamagnetic magnetite (Fe₃O₄) nanoparticles by electro-precipitation in ethanol is proposed. Particle average size can be set from 4.4 to 9 nm with a standard deviation around 20%. Combination of wide-angle X-ray scattering (WAXS), Electron energy loss spectroscopy (EELS) and Mössbauer spectroscopy characterizations clearly identifies the particles as magnetite single-crystals (Fe₃O₄).     

Challenge of ultra high frequency limit of permeability for magnetic nanoparticle assembly with organic polymer—Application of superparamagnetism

Permeability and its upper limitation frequency of superparamagnetic nanoparticle type magneto-dielectric hybrid material were theoretically and experimentally investigated. The Landau-Lifschitz-Gilbert equation without any interaction between nanoparticles revealed that the blocking resonance frequency was able to exceed the ferromagnetic resonance frequency originating from the intrinsic magnetocrystalline anisotropy field by decreasing particle size, resulting in ultra fast switching of superparamagnetic moment in GHz range. In the case of Fe nanoparticles, the blocking resonance frequency can be increased to 130 GHz by reducing particle size to 1 nm. The experiment results for Fe₃O₄ and Fe nanoparticle assemblies supported the validity of our calculation results. Thus, superparamagnetic nanoparticle assembly could be promising material for high frequency use over 10 GHz range.     

Synthesis and magnetic characterization of Zn0.7Ni0.3Fe2O4 nanoparticles via microwave-assisted combustion route

We report on the synthesis of Zn_0.7Ni_0.3Fe₂O₄ nanoparticles via microwave assisted combustion route by using urea as fuel. XRD and FT-IR analyses confirm the composition and structure as spinel ferrite. The crystallite size estimated from XRD (16.4 nm) and the magnetic core size (15.04 nm) estimated from VSM agree well, while a slightly smaller magnetic diameter reflects a very thin magnetically dead layer on the surface of the nanoparticles. Morphological investigation of the products was done by TEM which revealed the existence of irregular shapes such spherical, spherodial and polygon. Magnetization measurements performed on Zn_0.7Ni_0.3Fe₂O₄ nanoparticles showed that saturation was not attained at even in the high magnetic field. The sample shows superparamagnetic behavior at around the room temperature and ferromagnetic behavior below the blocking temperature which is measured as 284 K.     

Magnetic properties of prussian blue modified Fe3O4 nanocubes

Size controlled cubic Fe₃O₄ nanoparticles in the size range 90–10 nm were synthesized by varying the ferric ion concentration using the oxidation method. A bimodal size distribution was found without ferric ion concentration and the monodispersity increased with higher concentration. The saturation magnetization decreased from 90 to 62 emu/g when the particle size is reduced to 10 nm. The Fe₃O₄ nanoparticles with average particle sizes 10 and 90 nm were surface modified with prussian blue. The attachment of prussian blue with Fe₃O₄ was found to depend on the concentration of HCl and the particle size. The saturation magnetization of prussian blue modified Fe₃O₄ varied from 10 to 80 emu/g depending on the particle size. The increased tendency for the attachment of prussian blue with smaller particle size was explained based on the surface charge. The prussian blue modified magnetite nanoparticles could be used as a radiotoxin remover in detoxification applications.     

Only Ku-band microwave absorption by Fe3O4/ferrocenyl-CuPc hybrid nanospheres

A novel kind of hybrid nanospheres made of Fe₃O₄ and ferrocenyl-CuPc (FCP) was prepared via effective solvothermal method and performed microwave absorptivity only in Ku-band with minimum reflection loss of −25 dB at 16.0 GHz corresponding to absorbing about 99.7% content of microwave. Scanning electron microscopy images indicated that the nanospheres with uniform particle size distribution have the average diameter of 135 nm. Due to the synergistic reaction between magnetic ferrocenyl-CuPc and Fe₃O₄, the hybrid nanospheres showed novel electromagnetic properties. The real part of complex permittivity of hybrid nanospheres remains stable in the range of 0.5–12.0 GHz and has a large fluctuation at 16.5 GHz. Moreover, the dielectric loss of hybrid nanospheres also appeared a sharp peak at 16.3 GHz with the value of 2.7. The specific gravity of hybrid nanospheres is about 2.08. On the basis of these results, the novel hybrids are believed to have potential applications in the microwave absorbing area in Ku-band.     

High heat generation ability in AC magnetic field for nano-sized magnetic Y3Fe5O12 powder prepared by bead milling

Nano-sized magnetic Y₃Fe₅O₁₂ ferrite having a high heat generation ability in an AC magnetic field was prepared by bead milling. A commercial powder sample (non-milled sample) of ca. 2.9 μm in particle size did not show any temperature enhancement in the AC magnetic field. The heat generation ability in the AC magnetic field improved with a decrease in the average crystallite size for the bead-milled Y₃Fe₅O₁₂ ferrites. The highest heat ability in the AC magnetic field was for the fine Y₃Fe₅O₁₂ powder with a 15-nm crystallite size (the samples were milled for 4 h using 0.1 mm? beads). The heat generation ability of the excessively milled Y₃Fe₅O₁₂ samples decreased. The main reason for the high heat generation property of the milled samples was ascribed to an increase in the Néel relaxation of the superparamagnetic material. The heat generation ability was not influenced by the concentration of the ferrite powder. For the samples milled for 4 h using 0.1 mm? beads, the heat generation ability (W g⁻¹) was estimated using a 3.58×10⁻⁴ fH² frequency (f/kHz) and the magnetic field (H/kA m⁻¹), which is the highest reported value of superparamagnetic materials.     

Microwave synthesis of magnetic Fe3O4 nanoparticles used as a precursor of nanocomposites and ferrofluids

Methods to synthesize magnetic Fe₃O₄ nanoparticles and to modify the surface of particles are presented in the present investigation. Fe₃O₄ magnetic nanoparticles were prepared by the co-precipitation of Fe³⁺ and Fe²⁺, NH₃·H₂O was used as the precipitating agent to adjust the pH value, and the aging of Fe₃O₄ magnetic nanoparticles was accelerated by microwave (MW) irradiation. The obtained Fe₃O₄ magnetic nanoparticles were characterized by Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), X-ray powder diffraction (XRD) and vibrating sample magnetometer (VSM). The average size of Fe₃O₄ crystallites was found to be around 8–9 nm. Thereafter, the surface of Fe₃O₄ magnetic nanoparticles was modified by stearic acid. The resultant sample was characterized by FT-IR, scanning electron microscopy (SEM), XRD, lipophilic degree (LD) and sedimentation test. The FT-IR results indicated that a covalent bond was formed by chemical reaction between the hydroxyl groups on the surface of Fe₃O₄ nanoparticles and carboxyl groups of stearic acid, which changed the polarity of Fe₃O₄ nanoparticles. The dispersion of Fe₃O₄ in organic solvent was greatly improved. Effects of reaction time, reaction temperature and concentration of stearic acid on particle surface modification were investigated. In addition, Fe₃O₄/polystyrene (PS) nanocomposite was synthesized by adding surface modified Fe₃O₄ magnetic nanoparticles into styrene monomer, followed by the radical polymerization. The obtained nanocomposite was tested by thermogravimetry (TG), differential scanning calorimetry (DSC) and XRD. Results revealed that the thermal stability of PS was not significantly changed after adding Fe₃O₄ nanoparticles. The Fe₃O₄ magnetic fluid was characterized using UV–vis spectrophotometer, Gouy magnetic balance and laser particle-size analyzer. The testing results showed that the magnetic fluid had excellent stability, and had susceptibility of 4.46×10⁻⁸ and saturated magnetization of 6.56 emu/g. In addition, the mean size d (0.99) of magnetic Fe₃O₄ nanoparticles in the fluid was 36.19 nm.     

Synthesis and magnetic properties of Au-coated amorphous Fe20Ni80 nanoparticles

Gold-coated nanoparticles of Fe₂₀Ni₈₀ (permalloy) have been synthesized by a microemulsion process. The as-prepared samples consist of ∼5 nm diameter particles of amorphous Fe₂₀Ni₈₀ that are likely encapsulated in B₂O₃. One or more Fe₂₀Ni₈₀@B₂O₃ particles are subsequently encapsulated in 8-20 nm gold nanospheres, as determined by TEM and X-ray powder diffraction (XRD) line broadening. The gold shells were found to be under expansive strain. Magnetic data confirm the existence of a superparamagnetic phase with a blocking temperature, T_B, of ∼33 K. The saturation magnetization, M_S, of the as-prepared, Au-coated sample is ∼65 emu g⁻¹ at 5 K and ∼16 emu g⁻¹ at 300 K. The coercivity, H_C, is ∼280 Oe at 5 K.     

An easy and novel approach for the decoration of graphene oxide by Fe3O4 nanoparticles

A new and relatively general route was developed to fabricate graphene oxide (GO)-Fe₃O₄ hybrid. X-ray diffraction, transmission electron morphology, X-ray photoelectron spectroscopy (XPS) and energy-dispersive spectrum were used to demonstrate the successful attachment of iron oxide nanoparticles to GO sheets. Transmission electron microscopy observation indicates that the size of the Fe₃O₄ nanoparticles was about 2.7 nm with narrow size distribution. Moreover, this hybrid shows superparamagnetic property and allows the rapid separation under an external-magnetic field. In addition, the method could be extended to further development of graphene-based nanoelectronics.     

Synthesis of magnetite nanoparticles via a solvent-free thermal decomposition route

Superparamagnetic nanoparticles have been widely applied in various bio-medical applications. To date, it is still a challenge to synthesize nanosized Fe₃O₄ particles with controlled size and distribution. In this paper, a novel solvent-free thermal decomposition method is reported for synthesizing Fe₃O₄ nanoparticles. Size and morphology of the nanoparticles are determined by TEM while the structure of the nanoparticles is identified by FTIR, XPS and TGA measurements. Magnetic properties of the obtained particles are determined using VSM and SQUID measurement. The particle size of the Fe₃O₄ can be tailored by adjusting either reaction temperature or time. When the reaction temperature is increased to 330 °C and the reaction time is extended to 4 h, the average particle size of the obtained nanoparticles is ∼9 nm, while Ms value reaches ∼76 emu/g. The as synthesized Fe₃O₄ nanoparticles show well-established superparamagnetic properties with the blocking temperature at around 100 K.     

The structure and magnetic properties of Zn1−xNixFe2O4 ferrite nanoparticles prepared by sol–gel auto-combustion

Zn_1−xNi_xFe₂O₄ ferrite nanoparticles were prepared by sol–gel auto-combustion and then annealed at 700 °C for 4 h. The results of differential thermal analysis indicate that the thermal decomposition temperature is about 210 °C and Ni–Zn ferrite nanoparticles could be synthesized in the self-propagating combustion process. The microstructure and magnetic properties were investigated by means of X-ray diffraction, scanning electron microscope, and Vibrating sample magnetometer. It is observed that all the spherical nanoparticles with an average grain size of about 35 nm are of pure spinel cubic structure. The crystal lattice constant declines gradually with increasing x from 0.8435 nm (x=0.20) to 0.8352 nm (x=1.00). Different from the composition of Zn_0.5Ni_0.5Fe₂O₄ for the bulk, the maximum M_s is found in the composition of Zn_0.3Ni_0.7Fe₂O₄ for nanoparticles. The H_c of samples is much larger than the bulk ferrites and increases with the enlarging x. The results of Zn_0.3Ni_0.7Fe₂O₄ annealed at different temperatures indicate that the maximum M_s (83.2 emu/g) appears in the sample annealed at 900 °C. The H_c of Zn_0.3Ni_0.7Fe₂O₄ firstly increases slightly as the grain size increases, and presents a maximum value of 115 Oe when the grains grow up to about 30 nm, and then declines rapidly with the grains further growing. The critical diameter (under the critical diameter, the grain is of single domain) of Zn_0.3Ni_0.7Fe₂O₄ nanoparticles is found to be about 30 nm.     

Fabrication, characterization and measurement of thermal conductivity of Fe3O4 nanofluids

Magnetite Fe₃O₄ nanoparticles were synthesized by a co-precipitation method at different pH values. The products were characterized by X-ray diffraction, Fourier transform infrared spectroscopy, and transmission electronic microscopy. Their magnetic properties were evaluated on a vibrating sample magnetometer. The results show that the shape of the particles is cubic and they are superparamagnetic at room temperature. Magnetic nanofluids were prepared by dispersing the Fe₃O₄ nanoparticles in water as a base fluid in the presence of tetramethyl ammonium hydroxide as a dispersant. The thermal conductivity of the nanofluids was measured as a function of volume fraction and temperature. The results show that the thermal conductivity ratio of the nanofluids increases with increase in temperature and volume fraction. The highest enhancement of thermal conductivity was 11.5% in the nanofluid of 3 vol% of nanoparticles at 40 °C. The experimental results were also compared with the theoretical models.     

One-step synthesis of Fe3O4@C/reduced-graphite oxide nanocomposites for high-performance lithium ion batteries

In this paper, we propose a facile one-step strategy to prepare Fe₃O₄@amorphous carbon/reduced graphite oxide nanocomposites (FCRGs) under hydrothermal conditions. A transmission electron microscopy image has shown that the as-formed Fe₃O₄ nanoparticles coated with a layer of amorphous carbon are wrapped by reduced graphite oxide (r-GO) sheets. The diameter of Fe₃O₄ nanoparticles is less than 50 nm. N₂ adsorption/desorption isotherms indicate that the specific surface area of FCRG is 31.6 m²/g with porous structure. FCRG exhibits improved cycling stability and rate performances as a potential anode material for high-performance lithium ion batteries.     

Synthesis and properties of magnetic and luminescent Fe3O4/SiO2/Dye/SiO2 nanoparticles

A simple and reproducible method was developed to synthesize a novel class of Fe₃O₄/SiO₂/dye/SiO₂ composite nanoparticles. As promising candidates for use in bioassays, the obtained nanoparticles have an average diameter of 30 nm, and the thickness of the outer shell of silica could be tuned by changing the concentration of the silicon precursor tetraethyl orthosilicate during the synthesis. These multifunctional nanoparticles were found to be highly luminescent, photostable and superparamagnetic. The luminescence intensity of the nanoparticles was increased as the dye concentration was increased in the preparation process. The color of the luminescence was successfully tuned by incorporating different dyes into the nanoparticles. The measurements of the emission spectra indicated that relative to the dye molecules dissolved in ethanol, the emission of the dye-doped nanoparticles exhibited either a red shift or a blue shift, to which a tentative explanation was given.     

Synthesis and investigation of magnetic properties of substituted ferrite nanoparticles of spinel system Mn1−xZnx[Fe2−yLy]O4

Superparamagnetic nanoparticles of the spinel ferrite four-element system Mn_1−xZn_x[Fe_2−yL_y]O₄ (where L:Gd³⁺, La³⁺, Ce³⁺, Eu³⁺, Dy³⁺, Er³⁺,Yb³⁺) were synthesized by the co-precipitation method. The magnetic moments of the 10 nm diameter nanoparticles were comparable to the ones of Fe₃O₄ nanoparticles. A comparatively low T_C (∼52–72 °C) was observed for some of the compositions. The heating mechanism of the superparamagnetic particles in the AC magnetic field at radiofrequency range is discussed and especially the absence of the hysteresis loop in the M–H curve at room temperature. One possible explanation—spontaneous particle agglomeration—was experimentally verified.