Magnetic and rheological properties of monodisperse Fe3O4 nanoparticle/organic hybrid

Fe₃O₄ nanoparticle/organic hybrids were synthesized via hydrolysis using iron (III) acetylacetonate at ∼80 °C. The synthesis of Fe₃O₄ was confirmed by X-ray diffraction, selected-area diffraction, and X-ray photoelectron spectroscopy. Fe₃O₄ nanoparticles in the organic matrix had diameters ranging from 7 to 13 nm depending on the conditions of hydrolysis. The saturation magnetization of the hybrid increased with an increase in the particle size. When the hybrid contained Fe₃O₄ particles with a size of less than 10 nm, it exhibited superparamagnetic behavior. The blocking temperature of the hybrid containing Fe₃O₄ particles with a size of 7.3 nm was 200 K, and it increased to 310 K as the particle size increased to 9.1 nm. A hybrid containing Fe₃O₄ particles of size greater than 10 nm was ferrimagnetic, and underwent Verwey transition at 130 K. Under a magnetic field, a suspension of the hybrid in silicone oil revealed the magnetorheological effect. The yield stress of the fluid was dependent on the saturation magnetization of Fe₃O₄ nanoparticles in the hybrid, the strength of the magnetic field, and the amount of the hybrid.