Green synthesis and characterization of superparamagnetic Fe3O4 nanoparticles

In this paper, we have first demonstrated a facile and green synthetic approach for preparing superparamagnetic Fe₃O₄ nanoparticles using α-d-glucose as the reducing agent and gluconic acid (the oxidative product of glucose) as stabilizer and dispersant. The X-ray powder diffraction (XRD), X-ray photoelectron spectrometry (XPS), and selected area electron diffraction (SAED) results showed that the inverse spinel structure pure phase polycrystalline Fe₃O₄ was obtained. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) results exhibited that Fe₃O₄ nanoparticles were roughly spherical shape and its average size was about 12.5 nm. The high-resolution TEM (HRTEM) result proved that the nanoparticles were structurally uniform with a lattice fringe spacing about 0.25 nm, which corresponded well with the values of 0.253 nm of the (3 1 1) lattice plane of the inverse spinel Fe₃O₄ obtained from the JCPDS database. The superconducting quantum interference device (SQUID) results revealed that the blocking temperature (T_b) was 190 K, and that the magnetic hysteresis loop at 300 K showed a saturation magnetization of 60.5 emu/g, and the absence of coercivity and remanence indicated that the as-synthesized Fe₃O₄ nanoparticles had superparamagnetic properties. Fourier transform infrared spectroscopy (FT-IR) spectrum displayed that the characteristic band of Fe-O at 569 cm⁻¹ was indicative of Fe₃O₄. This method might provide a new, mild, green, and economical concept for the synthesis of other nanomaterials.     

Biosynthesis and magnetic properties of mesoporous Fe3O4 composites

Magnetic Fe₃O₄ materials with mesoporous structure are synthesized by co-precipitation method using yeast cells as a template. The X-ray diffraction (XRD) pattern indicates that the as-synthesized mesoporous hybrid Fe₃O₄ is well crystallized. The Barrett-Joyner-Halenda (BJH) models reveal the existence of mesostructure in the dried sample which has a specific surface area of 96.31 m²/g and a pore size distribution of 8-14 nm. Transmission electron microscopy (TEM) measurements confirm the wormhole-like structure of the resulting samples. The composition and chemical bonds of the Fe₃O₄/cells composites are studied by Fourier transform infrared (FT-IR) spectroscopy. Preliminary magnetic properties of the mesoporous hybrid Fe₃O₄ are characterized by a vibrating sample magnetometer (VSM). The magnetic Fe₃O₄/cells composites with mesoporous structure have potential applications in biomedical areas, such as drug delivery.     

Green synthesis of soya bean sprouts-mediated superparamagnetic Fe3O4 nanoparticles

Superparamagnetic Fe₃O₄ nanoparticles were first synthesized via soya bean sprouts (SBS) templates under ambient temperature and normal atmosphere. The reaction process was simple, eco-friendly, and convenient to handle. The morphology and crystalline phase of the nanoparticles were determined from scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), and X-ray diffraction (XRD) spectra. The effect of SBS template on the formation of Fe₃O₄ nanoparticles was investigated using X-ray photoemission spectroscopy (XPS) and Fourier-transform infrared spectroscopy (FT-IR). The results indicate that spherical Fe₃O₄ nanoparticles with an average diameter of 8 nm simultaneously formed on the epidermal surface and the interior stem wall of SBS. The SBS are responsible for size and morphology control during the whole formation of Fe₃O₄ nanoparticles. In addition, the superconducting quantum interference device (SQUID) results indicate the products are superparamagnetic at room temperature, with blocking temperature (T_B) of 150 K and saturation magnetization of 37.1 emu/g.     

Ag-deposited silica-coated Fe3O4 magnetic nanoparticles catalyzed reduction of p-nitrophenol

In this paper, a novel approach was successfully developed for advanced catalyst Ag-deposited silica-coated Fe₃O₄ magnetic nanoparticles, which possess a silica coated magnetic core and growth active silver nanoparticles on the outer shell using n-butylamine as the reductant of AgNO₃ in ethanol. The as-synthesized nanoparticles have been characterized by X-ray powder diffraction (XRD), transmission electron microscopy (TEM), energy dispersive X-ray analysis (EDX), Fourier transform infrared spectra (FT-IR), vibration sample magnetometer (VSM), and have been exploited as a solid phase catalyst for the reduction of p-nitrophenol in the presence of NaBH₄ by UV-vis spectrophotometry. The obtained products exhibited monodisperse and bifunctional with high magnetization and excellent catalytic activity towards p-nitrophenol reduction. As a result, the as-obtained nanoparticles showed high performance in catalytic reduction of p-nitrophenol to p-aminophenol with conversion of 95% within 14 min in the presence of an excess amount of NaBH₄, convenient magnetic separability, as well as remained activity after recycled more than 6 times. The Fe₃O₄@SiO₂-Ag functional nanostructure could hold great promise for various catalytic reactions.     

Preparation and characterization of bifunctional, Fe3O4/ZnO nanocomposites and their use as photocatalysts

Bifunctional magnetic-optical Fe₃O₄/ZnO nanocomposites with different molar ratio were successfully synthesized by a facile two-step strategy. Compared with the other methods, it was found to be mild, inexpensive, green, convenient and efficient. Fe₃O₄ nanocrystal was used as seed for the deposit and growth of ZnO nanoparticle. A series of the characterizations manifested that the combination of Fe₃O₄ with ZnO nanoparticles was successful. Photocatalytic activity studies confirmed that as-prepared nanocomposites had excellent photodegradating behavior to Methyl Orange (MO) compared to the pure ZnO nanoparticles. The results showed that the degradation percentage of MO was about 93.6% for 1 h when the amount of catalyst was 0.51 g L⁻¹ and initial concentration of MO was 6 × 10⁻⁵ mol L⁻¹ in the pH 7 solution. Moreover, the kinetics of photocatalytic degradation reaction could be expressed by the first-order reaction kinetic model. Furthermore, the Fe₃O₄/ZnO nanocomposites could be also served as convenient recyclable photocatalysts because of their magnetic properties.     

Chemical synthesis of spinel nickel ferrite (NiFe2O4) nano-sheets

The present investigation is related to the deposition of single-phase nano-sheets spinel nickel ferrite (NiFe₂O₄) thin films onto glass substrates using a chemical method. Nano-sheets nickel ferrite films were deposited from an alkaline bath containing Ni²⁺ and Fe²⁺ ions. The films were characterized for their structural, surface morphological and electrical properties by means of X-ray diffraction (XRD), transmission electron microscope (TEM), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and two-point probe electrical resistivity techniques. The X-ray diffraction pattern showed that NiFe₂O₄ nano-sheets are oriented along (3 1 1) plane. The FT-IR spectra of NiFe₂O₄ films showed strong absorption peaks around 600 and 400 cm⁻¹ which are typical for cubic spinel crystal structure. Microstructural study of NiFe₂O₄ film revealed nano-sheet like morphology with average sheet thickness of 30 nm. The room temperature electrical resistivity of the NiFe₂O₄ nano-sheets was 10⁷ Ω cm.     

Synthesis and characterization of TiO2/Fe2O3 core-shell nanocomposition film and their photoelectrochemical property

TiO₂/Fe₂O₃ core-shell nanocomposition film has been fabricated via two-step method. TiO₂ nanorod arrays are synthesized by a facile hydrothermal method, and followed by Fe₂O₃ nanoparticles deposited on TiO₂ nanorod arrays through an ordinary chemical bath deposition. The phase structures, morphologies, particle size, chemical compositions of the composites have been characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and ultraviolet-visible (UV-vis) spectrophotometer. The results confirm that Fe₂O₃ nanoparticles of mean size ca. 10 nm coated on the surface of TiO2 NRs. After depositing Fe₂O₃, UV-vis absorption property is induces the shift to the visible-light range, the annealing temperature of 600 °C is the best condition for UV-vis absorption property of TiO₂/Fe₂O₃ nanocomposite film, and increasing Fe content, optical activity are enhanced one by one. The photoelectrochemical (PEC) performances of the as-prepared composite nanorods are determined by measuring the photo-generated currents under illumination of UV-vis light. The TiO₂ NRs modified by Fe₂O₃ show the photocurrent value of 1.36 mA/cm² at 0 V vs Ag/AgCl, which is higher than those of unmodified TiO₂ NRs.     

海藻酸改性的空心Fe3O4纳米颗粒的制备与应用

不使用任何模板一步制得空心Fe₃O₄纳米颗粒,然后将海藻酸钠嫁接在氨基化的空心Fe₃O₄表面,再利用海藻酸盐与钙离子的作用,在空心Fe₃O₄表面形成一个凝胶化层,制得海藻酸盐凝胶化的空心Fe₃O₄纳米颗粒,粒径约为400～500 nm．采用TEM、XRD、XPS、VSM等手段对纳米微球进行表征．VSM表征结果表明在室温下样品磁性材料为超顺磁性．改性Fe₃O₄纳米颗粒成功地用于柔红霉素的载负和缓释,最大载负率和载药量分别为28.4%和14.2%．缓释结果表明,海藻酸盐凝胶化层的存在,能更有效控制柔红霉素缓慢地释放．     

Exchange coupling behavior in bimagnetic CoFe2O4/CoFe2 nanocomposite

In this work we report a study of the magnetic behavior of ferrimagnetic oxide CoFe₂O₄ and ferrimagnetic oxide/ferromagnetic metal CoFe₂O₄/CoFe₂ nanocomposite. The latter compound is a good system to study hard ferrimagnet/soft ferromagnet exchange coupled. Two steps were followed to synthesize the bimagnetic CoFe₂O₄/CoFe₂ nanocomposite: (i) first, preparation of CoFe₂O₄ nanoparticles using a simple hydrothermal method, and (ii) second, reduction reaction of cobalt ferrite nanoparticles using activated charcoal in inert atmosphere and high temperature. The phase structures, particle sizes, morphology, and magnetic properties of CoFe₂O₄ nanoparticles were investigated by X-Ray diffraction (XRD), Mossbauer spectroscopy (MS), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM) with applied field up to 3.0 kOe at room temperature and 50 K. The mean diameter of CoFe₂O₄ particles is about 16 nm. Mossbauer spectra revealed two sites for Fe³⁺. One site is related to Fe in an octahedral coordination and the other one to the Fe³⁺ in a tetrahedral coordination, as expected for a spinel crystal structure of CoFe₂O₄. TEM measurements of nanocomposite showed the formation of a thin shell of CoFe₂ on the cobalt ferrite and indicate that the nanoparticles increase to about 100 nm. The magnetization of the nanocomposite showed a hysteresis loop that is characteristic of exchange coupled systems. A maximum energy product (BH)_max of 1.22 MGOe was achieved at room temperature for CoFe₂O₄/CoFe₂ nanocomposites, which is about 115% higher than the value obtained for CoFe₂O₄ precursor. The exchange coupling interaction and the enhancement of product (BH)_max in nanocomposite CoFe₂O₄/CoFe₂ are discussed.     

Re-examination of characteristic FTIR spectrum of secondary layer in bilayer oleic acid-coated Fe3O4 nanoparticles

Bilayer oleic acid-coated Fe₃O₄ nanoparticles can be applied in more areas than single layer oleic acid-coated ones because they can be well dispersed not only in nonpolar carrier liquids but also in polar carrier liquids, while the single layer oleic acid-coated ones can be dispersed only in nonpolar carrier liquids. Therefore, it is of significance to characterize the surface structure of bilayer and single layer oleic acid-coated Fe₃O₄ nanoparticles. However, there existed a discrepancy in the characteristic FTIR spectrum of the secondary layer in bilayer oleic acid-coated Fe₃O₄ nanoparticles. The goal of this paper was to resolve the discrepancy through using FTIR and TGA together with dispersibility to characterize the surface structure of bilayer and single layer oleic acid-coated Fe₃O₄ nanoparticles. The results showed that the band at 1710 cm⁻¹ was the characteristic band of the secondary layer in bilayer oleic acid-coated Fe₃O₄ nanoparticles. It can be used to distinguish whether the oleic acid-coated Fe₃O₄ nanoparticles are bilayer or not.     

Synthesis and magnetic characterization of Zn0.7Ni0.3Fe2O4 nanoparticles via microwave-assisted combustion route

We report on the synthesis of Zn_0.7Ni_0.3Fe₂O₄ nanoparticles via microwave assisted combustion route by using urea as fuel. XRD and FT-IR analyses confirm the composition and structure as spinel ferrite. The crystallite size estimated from XRD (16.4 nm) and the magnetic core size (15.04 nm) estimated from VSM agree well, while a slightly smaller magnetic diameter reflects a very thin magnetically dead layer on the surface of the nanoparticles. Morphological investigation of the products was done by TEM which revealed the existence of irregular shapes such spherical, spherodial and polygon. Magnetization measurements performed on Zn_0.7Ni_0.3Fe₂O₄ nanoparticles showed that saturation was not attained at even in the high magnetic field. The sample shows superparamagnetic behavior at around the room temperature and ferromagnetic behavior below the blocking temperature which is measured as 284 K.     

High heat generation ability in AC magnetic field for nano-sized magnetic Y3Fe5O12 powder prepared by bead milling

Nano-sized magnetic Y₃Fe₅O₁₂ ferrite having a high heat generation ability in an AC magnetic field was prepared by bead milling. A commercial powder sample (non-milled sample) of ca. 2.9 μm in particle size did not show any temperature enhancement in the AC magnetic field. The heat generation ability in the AC magnetic field improved with a decrease in the average crystallite size for the bead-milled Y₃Fe₅O₁₂ ferrites. The highest heat ability in the AC magnetic field was for the fine Y₃Fe₅O₁₂ powder with a 15-nm crystallite size (the samples were milled for 4 h using 0.1 mm? beads). The heat generation ability of the excessively milled Y₃Fe₅O₁₂ samples decreased. The main reason for the high heat generation property of the milled samples was ascribed to an increase in the Néel relaxation of the superparamagnetic material. The heat generation ability was not influenced by the concentration of the ferrite powder. For the samples milled for 4 h using 0.1 mm? beads, the heat generation ability (W g⁻¹) was estimated using a 3.58×10⁻⁴ fH² frequency (f/kHz) and the magnetic field (H/kA m⁻¹), which is the highest reported value of superparamagnetic materials.     

Cation distribution dependence of magnetic properties of sol-gel prepared MnFe2O4 spinel ferrite nanoparticles

MnFe₂O₄ nanoparticles have been synthesized with a sol-gel method. Both differential thermal and thermo-gravimetric analyses indicate that MnFe₂O₄ nanoparticles form at 400 °C. Samples treated at 450 and 500 °C exhibit superparamagnetism at room temperature as implied from vibrating sample magnetometry. Mössbauer results indicate that as Mn²⁺ ions enter into the octahedral sites, Fe³⁺ ions transfer from octahedral to tetrahedral sites. When the calcination temperature increases from 450 to 700 °C, the occupation ratio of Fe³⁺ ions at the octahedral sites decreases from 43% to 39%. Susceptibility measurements versus magnetic field are reported for various temperatures (from 450 to 700 °C) and interpreted within the Stoner-Wohlfarth model.     

Study on dielectric and magnetic properties of Ho3Fe5O12 ceramics

Ho₃Fe₅O₁₂ ceramics with garnet structure were prepared by the solid-state reaction method. The results revealed the existence of Fe²⁺ ions have intensive influence on dielectric and magnetic properties of Ho₃Fe₅O₁₂ ceramics, which could be further confirmed by oxygen treatment. With a magnetic field lower than 10 kOe, the ME coefficient reaches 33 ps m⁻¹ at room temperature. And the ME coupling was further verified by dielectric anomaly near Néel temperature.     

Magnetic field synthesis of Fe3O4 nanoparticles used as a precursor of ferrofluids

Methods to synthesize magnetic Fe₃O₄ nanoparticles and to modify the nanoparticle surface are presented in this paper. In these methods, Fe₃O₄ nanoparticles were prepared by co-precipitation, and the aging of nanoparticles was improved by applied magnetic field. The obtained nanoparticles were characterized by Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), X-ray powder diffraction (XRD), and vibrating sample magnetometer (VSM). Thereafter, to enhance the compatibility between nanoparticles and water, an effective surface modification method was developed by grafting acrylic acid onto the nanoparticle surface. FT-IR, XRD, transmission electron microscopy (TEM), and thermogravimetry (TG) were used to characterize the resultant sample. The testing results indicated that the polyacrylic acid chains have been covalently bonded to the surface of magnetic Fe₃O₄ nanoparticles. The effects of initiator dosage, monomer concentration, and reaction temperature on the characteristics of surface-modified Fe₃O₄ nanoparticles were investigated. Moreover, the Fe₃O₄-g-PAA hybrid nanoparticles were dispersed in water to form ferrofluids (FFs). The obtained FFs were characterized by UV–vis spectrophotometer, Gouy magnetic balance and laser particle-size analyzer. The testing results showed that the high-concentration FF had excellent stability, with high susceptibility and high saturation magnetization. The rheological properties of the FFs were also investigated using a rotating rheometer.     

Effect of high magnetic field annealing on the microstructure and magnetic properties of Co-Fe layered double hydroxide

The effects of high magnetic field (10 T) on the products obtained by calcination of Co-Fe LDH precursors at different temperatures were investigated. The XRD results indicated that Fe^III substituted for Co^III in Co₃O₄ to yield Co^IICo^IIIFe^IIIO₄ under the calcination of Co-Fe LDH precursors at 400 °C. The products obtained by magnetic field annealing at 400 °C had a porous plate-like morphology, whereas the products without magnetic field annealing were composed of nanoparticles. It was seen that CoFe₂O₄ phase could be formed at low temperature (about 500 °C) under the magnetic field annealing. The grain size of products obtained by magnetic field annealing at 800 °C was larger than that of zero magnetic field. It was found that the saturation magnetization was significantly enhanced after magnetic field annealing, especially at lower temperature (≤600 °C). The possible reason for the effects on the microstructure and magnetic properties of products obtained by magnetic field annealing was discussed.     

Synthesis of (Mg0.476Mn0.448Zn0.007)(Fe1.997Ti0.002)O4 powder and sintered ferrites by high energy ball-milling process

(Mg_0.476Mn_0.448Zn_0.007)(Fe_1.997Ti_0.002)O₄ nanocrystalline powder prepared by high energy ball-milling process were consolidated by microwave and conventional sintering processes. Phases, microstructure and magnetic properties of the ferrites prepared by different processes were investigated. The (Mg_0.476Mn_0.448Zn_0.007)(Fe_1.997Ti_0.002)O₄ nanocrystalline powder could be prepared by high energy ball-milling process of raw Fe₃O₄, MnO₂, ZnO, TiO₂ and MgO powders. Prefired and microwave sintered ferrites could achieve the maximum density (4.86 g/cm⁻³), the average grain size (15 μm) was larger than that (10 μm) prepared by prefired and conventionally sintered ferrites with pure ferrite phase, and the saturation magnetization (66.77 emu/g) was lower than that of prefired and conventionally sintered ferrites (88.25 emu/g), the remanent magnetization (0.7367 emu/g) was higher than that of prefired and conventionally sintered ferrites (0.0731 emu/g). Although the microwave sintering process could increase the density of ferrites, the saturation magnetization of ferrites was decreased and the remanent magnetization of ferrites was also increased.     

Strongly interacting superspins in Fe3O4 nanoparticles

In this paper we report structural and magnetic properties of Fe₃O₄ nanoparticles synthesized by thermal decomposition of ball milled iron nitrate and citric acid in N₂ and air ambient. The XRD pattern of samples which are prepared in air shows some impurity phases, while the samples synthesized in the N₂ atmosphere are almost pure Fe₃O₄ phase. The result shows that by increasing the particle size, the magnetization of the samples increases. The increase of magnetization by increasing the particle size could be attributed to the lower surface spin canting and surface spin disorder of the larger magnetic nanoparticles. The results of ac magnetic susceptibility measurements show that the susceptibility data are not in accordance with the Néel -Brown model for superparamagnetic relaxation, but fit well with conventional critical slowing down model which indicates that the dipole-dipole interactions are strong enough to cause superspin-glass like phase in these samples.     

Synthesis and magnetic properties of hard magnetic (CoFe2O4)-soft magnetic (Fe3O4) nano-composite ceramics by SPS technology

CoFe₂O₄/Fe₃O₄ nano-composite ceramics were synthesized by Spark Plasma Sintering. The X-ray diffraction patterns show that all samples are composed of CoFe₂O₄ and Fe₃O₄ phases when the sintering temperature is below 900 °C. It is found that the magnetic properties strongly depend on the sintering temperature. The two-step hysteresis loops for samples sintered below 500 °C are observed, but when sintering temperature reaches 500 °C, the step disappears, which indicates that the CoFe₂O₄ and Fe₃O₄ are well exchange coupled. As the sintering temperature increases from 500 to 800 °C, the results of X-ray diffractometer indicate the constriction of crystalline regions due to the ion diffusion at the interfaces of CoFe₂O₄/Fe₃O₄ phases, which have great impact on the magnetic properties.     

A simplified method for synthesis of Fe3O4@PAA nanoparticles and its application for the removal of basic dyes

A simplified method for synthesis of polyacrylic acid-bound iron oxide magnetic nanoparticles (Fe₃O₄@PAA NPs) was reported. The as-prepared nanoparticles were characterized by TEM, FT-IR, VSM and XRD. Characterization results indicated that PAA was successfully introduced onto the surface of Fe₃O₄ and did not cause any changes in magnetic property. The Fe₃O₄@PAA NPs were used to adsorb rhodamine 6G (R6G) as a model basic dye pollutant from aqueous solution. Kinetics data and adsorption isotherms were better fitted by pseudo-second-order kinetic model and Langmuir isotherm, respectively. The adsorption equilibrium could be reached at about 20 min, showing that the as-prepared adsorbent exhibited extremely rapid adsorption rate. The aqueous solution of the Yellow River was chosen as the test sample, and the results showed that the magnetic adsorbent was efficient for the removal of the basic dye in the real sample.