不同氧含量Bi2Sr2CaCu2O８+δ单晶电阻率的各向异性

精确测量了在不同氧压下退火的单晶Bi₂Sr₂CaCu₂O_8+δ(Bi2212)样品的Cu-O面内和Cu-O面外的电阻率ρ_c(T)和ρ_ab(T).发现ρ_c(T)和各向异性比(ρ_c(T)/ρ_ab(T))随着载流子浓度增加而迅速下降.在过掺杂样品中,高于120K时,ρ_c随温度线性下降,而各向异性 关键词：     

溅射制备Ge,Nb共掺杂窄光学带隙和低电阻率的TiO2薄膜

采用射频磁控溅射技术制备了Ge,Nb共掺杂的锐钛矿结构TiO₂薄膜,详细探讨了薄膜的结构、电阻率及光学带隙等性质随Ge,Nb掺杂量、溅射功率和热处理温度等参数的变化,发现Ge,Nb共掺杂可以同时调节TiO₂薄膜的光学带隙和电阻率.体积分数约为6%Nb和20%Ge的共掺杂TiO₂薄膜电阻率由10⁴Ω/cm减小至10^-1Ω/cm,光学带隙由3.2 eV减小至1.9 eV.退火后掺杂TiO₂薄膜不仅显示更低的电阻率,还表现出更强的可见-红外光吸收.结果表明,改变Ge,Nb的掺杂量和退火条件能够制备出电阻率和带隙都可调的TiO₂薄膜.     

退火温度和退火气氛对Ni/Au与p-GaN之间欧姆接触性能的影响

研究了不同退火温度和气氛对Ni/Au与p-GaN之间欧姆接触性能的影响. 采用圆形传输线模型方法得到不同退火温度和不同退火气氛下的比接触电阻率. 结果表明, 较适宜的退火温度为500 ℃左右, 退火温度太高或太低都会导致比接触电阻率的增大; 较适宜的退火气氛为适量含氧的氮气气氛, 且氧气含量对比接触电阻率大小的影响并不显著. 经过对退火条件的优化, 得到的比接触电阻率可达7.65×10^-4 Ω·cm². 关键词： p-GaN 欧姆接触 圆形传输线模型 快速热退火     

GaAs及其它半导体欧姆接触模型

n型GaAs欧姆接触的比接触电阻ρ_c与有源层浓度N_D有反比关系,这已为很多实验事实所证明。文献中对这一现象有各种解释。本文对文献中的各种解释模型进行了分析,指出不足之处。提出ρ_c应由两部分ρ_(c1)和ρ_(c2)组成。ρ_(c1)是合金与其下在合金化后形成的高掺杂层间的比接触电阻。此外,在这高掺杂层与原来有源层间有 关键词：     

退火温度对硼掺杂纳米金刚石薄膜微结构和p型导电性能的影响

采用热丝化学气相沉积法制备硼掺杂纳米金刚石 (BDND) 薄膜, 并对薄膜进行真空退火处理, 系统研究退火温度对BDND薄膜微结构和电学性能的影响. Hall效应测试结果表明掺B浓度为5000 ppm (NHB) 的样品的电阻率较掺B浓度为500 ppm (NLB) 的样品的低, 载流子浓度高, Hall迁移率下降. 1000 ℃退火后, NLB和NHB 样品的迁移率分别为53.3和39.3 cm²·V^-1·s^-1, 薄膜的迁移率较未退火样品提高, 电阻率降低. 高分辨透射电镜、紫外和可见光拉曼光谱测试结果表明, NLB样品的金刚石相含量较NHB样品高, 高的硼掺杂浓度使薄膜中的金刚石晶粒产生较大的晶格畸变. 经1000 ℃退火后, NLB和NHB薄膜中纳米金刚石相含量较未退火时增大, 说明薄膜中部分非晶碳转变为金刚石相, 为晶界上B扩散到纳米金刚石晶粒中提供了机会, 使得纳米金刚石晶粒中B浓度提高, 增强纳米金刚石晶粒的导电能力, 提高薄膜电学性能. 1000 ℃退火能够恢复纳米金刚石晶粒的晶格完整性, 减小由掺杂引起的内应力, 从而提高薄膜的电学性能. 可见光Raman光谱测试结果表明, 1000℃退火后, Raman谱图中反式聚乙炔 (TPA) 的1140 cm^-1峰消失, 此时薄膜电学性能较好, 说明TPA减少有利于提高薄膜的电学性能. 退火后金刚石相含量的增大、金刚石晶粒的完整性提高及TPA含量的大量减少有利于提高薄膜的电学性能. 关键词： 硼掺杂纳米金刚石薄膜 退火 微结构 电学性能     

低接触电阻率Ni/Ag/Ti/Au反射镜电极的研究

研究了Ag的厚度、退火时间、沉积温度对于Ni/Ag/Ti/Au电极的反射率及与p-GaN欧姆接触性能的影响. 利用分光光度计测量反射率, 采用圆形传输线模型计算比接触电阻率. 结果表明: 随着Ag厚度的增加, Ni/Ag/Ti/Au电极的反射率逐渐增大; 在氧气氛围中, 随着退火时间从1 min增至10 min, 300 ℃退火时, 比接触电阻率持续下降, 而对于400-600 ℃退火, 比接触电阻率先减小后增大; 在300和400 ℃氧气中进行1-10 min 的退火后, Ni/Ag/Ti/Au的反射率变化较小, 退火温度高于400 ℃时, 随着退火时间的增加, 反射率急剧下降; 在400 ℃氧气中3 min退火后, 比接触电阻率可以达到3.6×10^-3 Ω·cm². 此外, 适当提高沉积温度可以增加Ni/Ag/Ti/Au的反射率并降低比接触电阻率, 沉积温度为120 ℃条件下的Ni/Ag/Ti/Au电极在450 nm处反射率达到90.1%, 比接触电阻率为6.4×10^-3 Ω·cm². 综合考虑电学和光学性能, 在沉积温度为120 ℃下蒸镀Ni/Ag/Ti/Au (1/200/100/100 nm)并在400 ℃氧气中进行3 min退火可以得到较优化的电极. 利用此电极制作的垂直结构发光二极管在350 mA电流下的工作电压为2.95 V, 输出光功率为387.1 mW, 电光转换效率达到37.5%.     

Ni/Au与N掺杂p型ZnO的欧姆接触

研究了Au,In,Ni/Au三种不同金属膜与N掺杂p型ZnO的接触特性,发现Ni/Au双层膜更适合作为其欧姆电极材料,并比较了不同气氛和不同温度退火对Ni/Au电极的影响.发现在O₂中退火电极性能发生蜕变,而在N₂中退火性能得到改善.指出即使在N₂中退火,退火温度的选择也是至关重要的,本实验在400℃,氮气气氛下退火150s,得到了较好的欧姆接触特性.     

氧离子注入微晶金刚石薄膜的微结构与光电性能研究

本文系统研究了氧离子注入剂量和退火温度对含有Si-V发光中 心的微晶金刚石薄膜的微结构和光电性能的影响. 结果表明, 氧离子注入并在较高温度退火有利于提高薄膜中Si-V中心的发光强度. 当氧离子注入剂量从10¹⁴ cm^-2增加到10¹⁵ cm^-2时, 薄膜中Si-V发光强度增强. Hall效应测试结果表明退火后薄膜的面电阻率降低. 不同温度退火时, 氧离子注入薄膜的Si-V发光强度较强时, 薄膜的面电阻率增加, 说明Si-V发光中心不利于提高薄膜的导电性能. Raman光谱测试结果表明, 薄膜中缺陷数量的增多会增强Si-V的发光强度, 而降低薄膜的导电性能. 关键词： 金刚石薄膜 氧离子注入 电学性能 Si-V缺陷     

牺牲Ni退火对硅衬底GaN基发光二极管p型接触影响的研究

本文通过在硅衬底发光二极管(LED)薄膜p-GaN表面蒸发不同厚度的Ni覆盖层,将其在N₂ ∶O₂=4 ∶1的气氛中、400℃—750℃的温度范围内进行退火,在去掉薄膜表面Ni覆盖层之后制备Pt/p-GaN欧姆接触层.实验结果表明:退火温度和Ni覆盖层厚度均对硅衬底GaN基LED薄膜p型欧姆接触有重要影响,Ni覆盖退火能够显著降低p型层中Mg受主的激活温度.经牺牲Ni退火后,p型比接触电阻率随退火温度的升高呈先变小后变大的规律,随Ni覆盖层厚度的增加呈先变小后变 关键词： 氮化镓 发光二极管 牺牲Ni退火 p型接触     

硅衬底GaN基LED N极性n型欧姆接触研究

在Si衬底GaN基垂直结构LED的N极性n型面上,利用电子束蒸发的方法制作了Ti/Al电极,通过了I-V曲线研究了有无AlN缓冲层对这种芯片欧姆接触的影响.结果显示,去除AlN缓冲层后的N极性n型面与Ti/Al电极在500到600 ℃范围内退火才能形成欧姆接触.而保留AlN缓冲层的N极性n型面与Ti/Al电极未退火时就表现为较好的欧姆接触,比接触电阻率为2×10^-5 Ω·cm²,即使退火温度升高至600 ℃,也始终保持着欧姆接触特性.因此,AlN缓冲层的存在是Si衬底GaN基垂直结构LED获得高热稳定性n型欧姆接触的关键. 关键词： 硅衬底 N极性 AlN缓冲层 欧姆接触     

Ti--Al based ohmic contacts to n-type 6H-SiC with P+ ion implantation

The Ti--Al ohmic contact to n-type 6H-SiC has been fabricated. An array of TLM (transfer length method) test patterns with Au/Ti/Al/Ti/SiC structure is formed on N-wells created by P⁺ ion implantation into Si-faced p-type 6H-SiC epilayer. The specific contact resistance \rho _c as low as 8.64×10^-6\Omega\cdot cm² is achieved after annealing in N₂ at 900℃ for 5\,min. The sheet resistance R_sh of the implanted layers is 975\Omega/\sqcap\!\!\!\!\sqcup. X-ray diffraction (XRD) analysis shows the formation of Ti_-3SiC₂ at the metal/n-SiC interface after thermal annealing, which is responsible for the low resistance contact.     

ZrB2-based Ohmic contacts to p-GaN

The annealing temperature dependence of contact resistance and layer stability of ZrB₂/Ti/Au and Ni/Au/ZrB₂/Ti/Au Ohmic contacts on p-GaN is reported. The as-deposited contacts are rectifying and transition to Ohmic behavior for annealing at ≥750 °C, a significant improvement in thermal stability compared to the conventional Ni/Au Ohmic contact on p-GaN, which is stable only to <600 °C. A minimum specific contact resistance of ∼2 × 10⁻³ Ω cm⁻² was obtained for the ZrB₂/Ti/Au after annealing at 800 °C while for Ni/Au/ZrB₂/Ti/Au the minimum value was 10⁻⁴ Ω cm⁻² at 900 °C. Auger Electron Spectroscopy profiling showed significant Ti, Ni and Zr out diffusion at 750 °C in the Ni/Au/ZrB₂/Ti/Au while the Ti and Zr intermix at 900 °C in the ZrB₂/Ti/Au. These boride-based contacts show promise for contacts to p-GaN in high temperature applications.     

Study of Ti/Au,Ti/Al/Au,and Ti/Al/Ni/Au ohmic contacts to <Emphasis Type="Italic">n</Emphasis>-GaN

The contacts of Ti/Au, Ti/Al/Au, and Ti/Al/Ni/Au films deposited on n-GaN were studied by current–voltage (I–V) and transmission-line-method measurements. The effect of annealing temperature on specific contact resistivity has been investigated by changing the annealing temperature from 400 to 900 °C. Ti/Al/Au and Ti/Al/Ni/Au films were superior to the bilayer (Ti/Au) in ohmic contact characteristics and thermal stability. The Ti/Al/Ni/Au composite showed the best thermal stability due to the fact that Ni plays a more important role than the alloy of Ti/Al in preventing the interdiffusion of Ti, Al, and Au. The lowest contact resistivity (10^-7cm²) to n-GaN was obtained for the Ti/Al/Ni/Au sample by short-time/high-temperature annealing. The formation mechanism of ohmic contacts to n-GaN is also discussed. PACS 73.40.Cg; 73.61.Ey     

Specific contact resistance of IGZO thin film transistors with metallic and transparent conductive oxides electrodes and XPS study of the contact/semiconductor interfaces

In this work, the specific contact resistance (ρ_c) between amorphous indium-gallium-zinc-oxide (IGZO) semiconductor and different contact electrodes was obtained from thin film transistors (TFTs). Ti/Au (10/100 nm), aluminum doped zinc oxide (AZO, 100 nm) and indium tin oxide (ITO, 100 nm) were used as source/drain electrodes to fabricate IGZO TFTs. Chemical states of the contacts/semiconductor interfaces were examined by depth profile X-ray photoelectron spectroscopy (XPS) analysis to explain the origin of the differences on specific contact resistance. The lowest ρ_c achieved using Ti/Au was related to the formation of a TiO_x interlayer due to oxygen atoms diffusing out from the semiconductor under layer, increasing the carrier concentration of IGZO at the interface and lowering the ρ_c. On the contrary, no interfacial reactions were observed between IGZO and AZO or ITO source/drain. However, IGZO resistivity increased with ITO contacts likely due to oxygen vacancies filling during ITO deposition. This fact seems to be the origin of the high contact resistance between IGZO and ITO, compared to IGZO-AZO and IGZO-Ti/Au interfaces.     

Thermal stability of Ti/Al/Pt/Au and Ti/Au Ohmic contacts on n-type ZnCdO

The specific contact resistivity and chemical intermixing of Ti/Au and Ti/Al/Pt/Au Ohmic contacts on n-type Zn_0.05Cd_0.95O layers grown on ZnO buffer layers on GaN/sapphire templates is reported as a function of annealing temperature in the range 200-600 °C. A minimum contact resistivity of 2.3 × 10⁻⁴ Ω cm² was obtained at 500 °C for Ti/Al/Pt/Au and 1.6 × 10⁻⁴ Ω cm² was obtained at 450 °C for Ti/Al. These values also correspond to the minima in transfer resistance for the contacts. The Ti/Al/Pt/Au contacts show far smoother morphologies after annealing even at 600 °C, whereas the Ti/Au contacts show a reacted appearance after 350 °C anneals. In the former case, Pt and Al outdiffusion is significant at 450 °C, whereas in the latter case the onset of Ti and Zn outdiffusion is evident at the same temperature. The improvement in contact resistance with annealing is suggested to occur through formation of TiO_x phases that induce oxygen vacancies in the ZnCdO.     

Metal-diamond semiconductor interface and photodiode application

Carrier transport mechanism at p-diamond/metal interfaces are studied by analyzing dependencies of specific contact resistance (ρ_c) on measurement temperature and acceptor concentration (N_A). A variety of metals, such as Ti, Mo, Cr (carbide-forming metals), Pd, and Co (carbon-soluble metals), are deposited on boron-doped polycrystalline diamond layers, and the ρ_c values are measured by a transmission line method. Thermal annealing which produces metallurgical reactions between diamond and metal reduces Schottky barrier heights of the contact metals to a constant value. It is found that use of a metal compound which does not react with diamond at elevated temperatures is the key to develop the thermally stable Schottky contact material for p-diamond. Along this guideline, we test the suitability of tungsten carbide (WC) and hafnium nitride (HfN) as thermally stable Schottky contacts to develop a thermally stable, deep-ultraviolet (DUV) photodiode using a boron-doped homoepitaxial p-diamond epilayer. Thermal annealing at 500 °C improves the rectifying current-voltage characteristics of the photodiode, resulting in the excellent thermal stability. The discrimination ratio between DUV and visible light is measured to be as large as 10⁶ at a reverse bias voltage as small as 2 V, and it remains almost constant after annealing at 500 °C for 5 h. Metal carbide and nitride contacts for diamond are thus useful for developing a thermally stable diamond DUV photodetector.     

Improved device performance in nonpolar a ‐plane GaN LEDs using a Ni/Al/Ni/Au n‐type ohmic contact

The authors report upon the increased light‐output power (P_out) via a reduction in the forward voltage (V_f) for nonpolar a ‐plane GaN LEDs using Ni/Al/Ni/Au n‐type ohmic contacts. The specific contact resistivity of the Ni/Al/Ni/Au contact is found to be as low as 5.6 × 10^–5 whereas that of a typical Ti/Al/Ni/Au contact is 6.8 × 10^–4 Ω cm², after annealing at 700 °C. The X‐ray photoelectron spectroscopy results show that the upward surface band bending is less pronounced for the Ni/Al contact compared to the Ti/Al contact, leading to a decrease in the effective Schottky barrier height (SBH). The V_f of the nonpolar LEDs decreases by 10% and P_out increases by 15% when the Ni/Al/Ni/Au scheme is used instead of the typical Ti/Al/Ni/Au metal scheme. (© 2011 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Use of TiB2 diffusion barriers for Ni/Au ohmic contacts on p-GaN

The use of a TiB₂ diffusion barrier for Ni/Au contacts on p-GaN is reported. The annealing temperature (25-950 °C) dependence of ohmic contact characteristics using a Ni/Au/TiB₂/Ti/Au metallization scheme deposited by sputtering were investigated by contact resistance measurements and auger electron spectroscopy (AES). The as-deposited contacts are rectifying and transition to ohmic behavior for annealing at ≥500 °C . A minimum specific contact resistivity of ∼3 × 10⁻⁴ Ω cm⁻² was obtained after annealing over a broad range of temperatures (800-950 °C for 60 s). The contact morphology became considerably rougher at the higher end of this temperature range. AES profiling showed significant Ti and Ni outdiffusion through the TiB₂ at 800 °C. By 900 °C the Ti was almost completely removed to the surface, where it became oxidized. Use of the TiB₂ diffusion barrier produces superior thermal stability compared to the more common Ni/Au, whose morphology degrades significantly above 500 °C.     

Electrical, structural and surface morphological properties of thermally stable low-resistance W/Ti/Au multilayer ohmic contacts to n-type GaN

A W/Ti/Au multilayer scheme has been fabricated for achieving thermally stable low-resistance ohmic contact to n-type GaN (4.0 × 10¹⁸ cm⁻³). It is shown that the as-deposited W/Ti/Au contact exhibits near linear I-V behaviour. However, annealing at temperature below 800 °C the contacts exhibit non-linear behaviour. After annealing at a temperature in excess of 850 °C, the W/Ti/Au contact showed ohmic behaviour. The W/Ti/Au contact produced specific contact resistance as low as 6.7 × 10⁻⁶ Ω cm² after annealing at 900 °C for 1 min in a N₂ ambient. It is noted that the specific contact resistance decreases with increase in annealing temperature. It is also noted that annealing the contacts at 900 °C for 30 min causes insignificant degradation of the electrical and thermal properties. It is further shown that the overall surface morphology of the W/Ti/Au stayed fairly smooth even after annealing at 900 °C. The W/Ti/Au ohmic contact showed good edge sharpness after annealing at 900 °C for 30 min. Based on the Auger electron spectroscopy and glancing angle X-ray diffraction results, possible explanation for the annealing dependence of the specific contact resistance of the W/Ti/Au contacts are described and discussed.     

The effect of a surface layer capping p-InGaN/p-GaN superlattices on the contact to p-GaN

In this study, the influence of the surface layer (p-InGaN or p-GaN) capping p-InGaN/p-GaN superlattices (SLs) on the contact to p-type GaN was investigated. It was found that the specific contact resistance (_ρc)$\left({\rho }_c\right)$ to p-type GaN is lower when using p-InGaN as the surface layer. The lowest value of _ρc${\rho }_c$ was 1.99×10⁻⁴ Ω cm² at room temperature. It was also found that low temperature growth of the p-GaN layers in the SLs is beneficial for lowering the ohmic contact resistance. Unlike Ni/Au deposited directly on p-GaN (without the strained p-InGaN/p-GaN SLs), Ni/Au deposited on p-InGaN/p-GaN SLs produces ohmic behavior even before annealing.