磁控溅射制备本征ZnO/Ag/ZnO透明导电薄膜的性质研究

室温下采用射频磁控溅射氧化锌（ZnO）粉末靶、银（Ag）靶,在玻璃衬底上制备ZnO/Ag/ZnO透明导电薄膜。首先,ZnO厚度为30 nm时,改变Ag厚度制备3层透明导电薄膜,研究Ag层厚度及膜层间配比对光电性能的影响;其次,按ZnO∶Ag厚度比为30∶11比例制备不同厚度的3层透明导电薄膜,研究多层厚度对薄膜光电性能的影响。结果表明：Ag厚度为8 nm及11 nm的ZnO/Ag/ZnO表面相对平整,结晶程度较好,在可见光范围内最高透过率达到90%及86%,并且方块电阻为6 Ω/□及3.20 Ω/□,具有优良的光电性;当按配比制备ZnO/Ag/ZnO 3层膜时,增加ZnO厚度对Ag层的增透作用反而减弱,同时增加Ag层厚度也会降低3层薄膜的整体光学性。     

以表面等离子体为媒介的ZnO薄膜发光增强特性研究

采用两步法制备Si基Ag/ZnO双层结构薄膜,研究了Ag覆盖层的厚度和生长温度T对ZnO近带边发光强度的影响.对于厚度为100 nm的ZnO薄膜,发现Ag覆盖层的最佳厚度仅为8 nm,此时双层薄膜相对于单层ZnO薄膜的发光增强因子η达到最大值8.1;同时还发现,在最佳Ag层厚度下,生长温度T≥300 ℃时生长Ag所获Ag/ZnO双层薄膜的ZnO发光强度比生长温度T≤200 ℃时生长的双层薄膜样品大一倍以上,η ≈ 18.结合对双层薄膜表 关键词： 表面等离子体共振 复合薄膜     

TiO2/ZnO纳米薄膜界面热导率的分子动力学模拟

采用平衡分子动力学方法及Buckingham势研究了金红石型TiO₂薄膜与闪锌矿型ZnO薄膜构筑的纳米薄膜界面沿晶面[0001](z轴方向)的热导率.通过优化分子模拟初始条件中的截断半径r_c和时间步后,计算并分析了平衡温度、薄膜厚度、薄膜截面大小对热导率的影响.研究表明,薄膜热导率受薄膜温度和厚度的影响很大,当温度由300 K升高600 K时,薄膜的热导率逐渐减小;当薄膜厚度由1.8 nm增大到5 nm时,热导率会逐渐增大;并在此基础 关键词： 热导率 分子动力学 2/ZnO纳米薄膜界面')" href="#">TiO₂/ZnO纳米薄膜界面 数值模拟     

Al/ZnO:Al薄膜结构的荧光增强效应

利用物理气相沉积设备制备了Al/ZnO:Al薄膜样品,研究了该薄膜结构的发光特性。结果表明,在ZnO:Al薄膜表面镀一层Al岛薄膜可以增强其带边荧光,同时在475 nm附近产生蓝光峰。通过在Al岛薄膜和ZnO:Al薄膜之间引入一层5 nm的Ta₂O₅绝缘层可以使ZnO:Al薄膜的带边荧光和蓝光显著增强,并随着Ta₂O₅绝缘层厚度的增大而减弱。通过对Al/ZnO:Al样品进行退火处理可以使带边荧光和蓝光峰分别增强9倍和83倍。基于局域表面等离子体共振理论,计算了Al/ZnO:Al纳米结构的光学散射和吸收截面曲线。实验结果与理论计算相一致。     

包埋Pt纳米粒子对金属-半导体-金属结构ZnO紫外光电探测器性能的影响

利用射频磁控溅射设备制备ZnO薄膜, 最终制备ZnO/Pt纳米粒子/ZnO 结构的金属-半导体-金属型紫外光电探测器. 研究了Pt纳米粒子处在ZnO薄膜层中的不同深度对金属-半导体-金属型紫外光电探测器响应性能的影响. 结果表明, 探测器的响应度随着Pt纳米粒子在ZnO薄膜层中所处深度的增大而升高. 在60 V偏压下, 包埋Pt最深的探测器在波长365 nm处取得响应度最大值1.4 A·W^-1, 包埋有Pt探测器的响应度最大值为无Pt 纳米粒子探测器响应度最大值的7倍. 结合对ZnO薄膜表面的表征及探测器各项性能的测试, 得出包埋Pt纳米粒子增强器件的响应性能可归因于表面等离子体增强散射.     

纳米ZnO薄膜对有机电致发光器件性能的影响

由于有机电致发光器件(Organic light-emitting devices,OLEDs)的主动发光、高亮度等优点,在显示和照明领域有极大的应用前景。报道了纳米ZnO薄膜对这种发光器件性能的影响。在普通有机电致发光器件空穴传输层和发光层之间直接蒸镀一层纳米ZnO薄膜,当纳米ZnO薄膜的厚度为1nm时,器件的电流效率可达3.26cd/A,是没有纳米ZnO薄膜同类器件的1.24倍。适当厚度的纳米ZnO薄膜降低了发光层空穴的浓度,提高了电子和空穴的平衡,从而提高了器件的效率。     

银修饰的ZnO纳米线的发光和光响应性质

采用不同浓度的银溶液对水热方法生长的ZnO纳米线进行了银修饰,并对其形貌、光致发光和光响应特性进行了研究.实验结果表明,随着修饰用银浓度的加大,光致发光的强度减弱.对原生的和用浓度为10mmol/L的银修饰的ZnO纳米线的光响应进行了测试和比较,发现银修饰的ZnO纳米线在380 nm的响应度达4.6 mA/W,其值是未...     

ZnO/Si异质结的光电转换特性研究

利用直流反应溅射方法在p型Si衬底上生长掺Al的n型ZnO薄膜,测量了由n型ZnO薄膜和p型Si衬底组成的异质结在黑暗和光照条件下的I-V特性,结果表明该异质结具有优良的整流特性,而且在光照条件下的反向电流迅速增大并很快趋于饱和.通过测量ZnO薄膜的光电流和异质结的光电压的光谱响应,初步分析了异质结的光电转换机理.测量结果显示,在入射光波长为380nm时光电流强度明显下降,反映出光电流与ZnO薄膜禁带宽度的密切关系;同时还发现,在与ZnO禁带宽度相对应的波长前后所产生的光生电压方向相反.推测这一现象与异质结的能带结构密切相关. 关键词： ZnO薄膜 异质结 光电转换 光谱响应     

纳米VO2/ZnO复合薄膜的热致变色特性研究

为提高VO₂薄膜的热致变色性能,采用纳米结构和复合结构二者相结合的方法,通过磁控溅射技术先在玻璃衬底上制备高(002)取向ZnO薄膜,再在ZnO层上室温沉积钒金属薄膜,最后经热氧化处理获得纳米结构VO₂/ZnO复合薄膜.利用变温拉曼光谱观察分析了VO₂/ZnO薄膜相变前后的晶格畸变和键态的演变过程,讨论了薄膜的结构与热致红外开关特性和相变温度的内在关系.结果显示,与相同条件获得的同厚度的单层VO₂薄膜相比,纳米VO关键词： ZnO 2')" href="#">VO₂ 纳米复合薄膜 热致变色 拉曼光谱     

ZnO/SiO2 复合薄膜的光学性能

采用溶胶-凝胶法在玻璃衬底上制备ZnO/SiO₂复合薄膜,分别用XRD、TEM、SEM对样品的结构和形貌进行表征,并研究了不同ZnO含量对复合薄膜透过率及荧光特性的影响。结果表明,样品经500 ℃退火处理生成了SiO₂和ZnO,其晶粒尺寸为18.7 nm,薄膜具有双层结构。复合薄膜的透过率随着其中ZnO含量的增加而降低,禁带宽度减小,光学吸收边红移。样品在355 nm波长激发下产生了384 nm的紫外发射峰和440 nm的蓝光发射带,并随ZnO含量的增加而增强,它们分别来自ZnO的电子-空穴复合发光和缺陷发光,及ZnO/SiO₂复合薄膜双层结构的缺陷发光。     

ZnO/Ag/ZnO multilayer films for the application of a very low resistance transparent electrode

Transparent conductive ZnO/Ag/ZnO multilayer electrodes having much lower electrical resistance than the widely used transparent electrodes were prepared by simultaneous RF magnetron sputtering of ZnO and DC magnetron sputtering of Ag. An Ag film with different thickness was used as intermediate metallic layers. The optimum thickness of Ag thin films was determined to be 6 nm for high optical transmittance and good electrical conductivity. With about 20-25 nm thick ZnO films, the multilayer showed high optical transmittance in the visible range of the spectrum and had color neutrality. The electrical and optical properties of the multilayers were changed mainly by Ag film properties. A high quality transparent electrode, having sheet resistance as low as 3 ohm/sq and high transmittance of 90% at 580 nm, was obtained and could be reproduced by controlling the preparation parameter properly. The above property is suitable as transparent electrode for dye sensitized solar cells (DSSC).     

ZnO nanorods/plates on Si substrate grown by low-temperature hydrothermal reaction

The zinc oxide (ZnO) nanorods/plates are obtained via hydrothermal method assisted by etched porous Al film on Si substrate. The products consist of nanorods with average diameter of 100 nm and nanoplates with thickness of 200-300 nm, which are uniformly distributed widely and grown perpendicularly to the substrate. The ZnO nanoplates with thickness of 150-300 nm were grown on Si substrate coated with a thin continuous Al film (without etching) in the same aqueous solution. The growth mechanism and room temperature photoluminescence (PL) properties of ZnO nanorods/plates and nanoplates were investigated. It is found that the introduction of the etched Al film plays a key role in the formation of ZnO nanorods/plates. The annealing process is favorable to enhance the UV PL emissions of the ZnO nanorods/plates.     

ITO-free inverted organic solar cells fabricated with transparent and low resistance ZnO/Ag/ZnO multilayer electrode

Inverted organic solar cells (OSCs) based on poly (3-hexylthiophene) (P3HT):[6,6]-phenyl-C61 butyric acid methyl ester (PCBM) bulk heterojunctions (BHJ) were fabricated with optimized ZnO/Ag/ZnO multilayer and conventional indium–tin oxide (ITO) cathode electrodes and their performance was compared. The ZnO/Ag/ZnO multilayer films showed sheet resistances in the range 3.6–3.9 Ω/sq, while ITO exhibited 14.2 Ω/sq. On the one hand, the carrier concentration gradually decreased from 1.74 × 10²² to 4.33 × 10²¹ cm⁻³ as the ZnO thickness increased from 8 to 80 nm, respectively. The transmittance of the ZnO(40 nm)/Ag(19 nm)/ZnO(40 nm) films was ∼95% at 550 nm, which is comparable to that of ITO (∼96%). The multilayer films were smooth with a root mean square (RMS) roughness of 0.81 nm. OSCs fabricated with the ZnO(40 nm)/Ag(19 nm)/ZnO(40 nm) film showed a power conversion efficiency (2.63%) comparable to that of OSCs with a conventional ITO cathode (2.71%).     

制备温度对TiO2基膜表面非晶态ZnO薄膜发光特性影响的研究

利用电子束热蒸发镀膜的方式，以高纯度的ZnO和TiO₂颗粒为原料，以Si为基底在有氧的气氛中制备ZnO/TiO₂复合薄膜。研究制备温度对ZnO/TiO₂薄膜的结构以及发光性能的影响。通过拉曼(Raman)谱和X射线衍射(XRD)谱分析了ZnO/TiO₂薄膜的结构，表明所制备的ZnO薄膜为非晶态。用光致发光 (PL) 谱表征了它的发光特性，数据表明在250℃时制备的非晶态ZnO薄膜在波长389nm处具有极强的紫外光发射，在波长431nm处发出很强的紫光，在波长519nm处发出较强的黄绿光。     

Effects of Ag layer and ZnO top layer thicknesses on the physical properties of ZnO/Ag/Zno multilayer system

Two groups of transparent conductive ZnO/Ag/ZnO, ZAZ, multilayer coatings were successively deposited by direct current (DC) magnetron sputtering. Sputtering was carried out from zinc (Zn) and silver (Ag) metallic targets. The effects of Ag layer thickness and ZnO top layer thickness on the properties of the ZAZ multilayer system were examined using different analytical methods. The influences of the Ag layer thickness and ZnO top layer thickness on structural properties were studied using X-ray diffraction. The thicknesses of ZAZ multilayer system were determined using X-ray reflectometry. A sheet resistance of 2.3 Ω/sq at an Ag layer thickness of 17.7 nm was obtained. The sheet resistance changes slightly with ZnO top layer thickness. The optical properties of the films were analyzed. Both Ag layer thickness and ZnO top layer thickness affect transmittance. The optical constants of the ZAZ multilayer system were calculated from transmittance and reflectance measurements. The figure of merit was applied on the ZAZ coatings and the most suitable films for the application as transparent conductive electrodes were determined.     

脉冲激光沉积法在多孔铝衬底上生长的ZnO薄膜的结构与光学性质

ZnO是一种性质优良很有前途的紫外光电子器件材料,多孔铝是一种良好的模板型衬底,试图将二者结合起来以制备出一种全新的光电功能材料。制备了三种不同孔径多孔铝衬底,采用脉冲激光沉积法,在真空背景下,在多孔铝衬底上生长了氧化锌薄膜。利用扫描电子显微镜、X射线衍射和光致荧光对样品进行了测试和分析。研究表明:利用不同孔径的多孔铝衬底生长的氧化锌薄膜的结构和光学性质差异很大。样品A的光致发光主要是394nm的紫外发射和498nm的蓝绿光发射;样品B的光致发光主要是417nm的紫光发射和466nm蓝光发射;样品C的光致发光主要是415nm的紫光发射和495nm的蓝绿光发射。由于薄膜是富锌的,随着在空气中氧化的进行,光谱发生变化。利用固体能带理论对光谱进行了全面的分析。     

ZnO/Ag/ZnO multilayer transparent electrode for highly-efficient ITO-Free polymer solar cells

Ultrathin metal film (UTMF) with a ZnO/Ag/ZnO hybrid structure was used as transparent electrode in a high-efficiency bulk heterojunction system for the fabrication of ITO-free polymer solar cells. The performance of the devices was carefully tuned through optical simulation using transfer matrix method by varying the thickness of ZnO seed layer and thin absorber layer. By employing appropriate device architecture, polymer solar cells fabricated using this UTMF-based electrode show efficiency as high as 9.49%, which is slightly higher compared to that of ITO-based device. From good agreement between the external quantum efficiency and optical modeling, it was found that the optimized microcavity configuration formed in UTMF-based device can greatly enhance the absorbance of the BHJ layer at longer wavelength as well as the favored exciton distribution for better charge transport and collection.