Ni/SnO_2复合薄膜的制备与光电性能

采用旋涂法将溶胶-凝胶法制备的Ni/Sn O2凝胶在玻璃基底上镀膜,得到了Ni/Sn O2复合薄膜,探讨了镍掺杂量、煅烧温度对薄膜结构和形貌的影响。通过X射线衍射、红外光谱、扫描电子显微镜等测试手段对Ni/Sn O2复合膜的结构和形貌进行表征。结果显示,500℃下煅烧的薄膜样品的结晶度较高,粒径小,颗粒分布均匀。用紫外-可见分光光度计和四探针电阻仪对其进行光学、电学性能测试,结果显示:适量的Ni掺杂可以提高Sn O2薄膜在近紫外光区的吸收,Ni/Sn O2薄膜在近紫外光区的吸收随着Ni2+掺杂摩尔分数从5%增加到10%而逐渐减小。当Ni2+掺杂摩尔分数为6%时,Ni/Sn O2复合薄膜的导电性能最好。     

磁控溅射制备W掺杂VO2/FTO复合薄膜及其性能分析

为了获得相变温度低且热致变色性能优越的光学材料, 室温下在F:SnO₂ (FTO)导电玻璃基板表面沉积钨钒金属膜, 再经空气气氛下的热氧化处理, 制备了W掺杂VO₂/FTO复合薄膜, 利用X射线光电子能谱、X射线衍射和扫描电镜对薄膜的结构和表面形貌进行了分析. 结果表明: 高温热氧化处理过程中没有生成W, F, V混合氧化物, W以替换V原子的方式掺杂. 与采用相同工艺和条件制备的纯VO₂/FTO复合薄膜相比, W掺杂VO₂薄膜没有改变晶面取向, 仍具有(110)晶面择优取向, 相变温度下降到35 ℃左右, 热滞回线收窄到4 ℃, 高低温下的近红外光透过率变化量提高到28%. 薄膜的结晶程度明显提高, 表面变得平滑致密, 具有很好的一致性, 对光电薄膜器件的设计开发和工业化生产具有重要意义. 关键词： W掺杂 2')" href="#">VO₂ FTO导电玻璃 磁控溅射     

掺钨VO_2薄膜的电致相变特性

采用直流磁控溅射与后退火工艺相结合的方法,在掺氟SnO_2(FTO)导电玻璃基底上制备了高质量的掺钨VO_2薄膜,对薄膜的结构、表面形貌和光电特性进行测试,分析了钨掺杂对其相变性能的影响.结果表明,室温下掺钨VO_2薄膜的阈值电压为4.2 V,观察到阈值电压下约有两个数量级的电流突变.随着温度升高,相变的阈值电压降低,且电流突变幅度减小.当施加8 V电压时,分别在不同温度下测试了掺钨VO_2薄膜的透过率.温度为20和50℃时,掺钨VO_2薄膜相变前后的红外透过率差量分别为23%和27%.与未掺杂的VO_2薄膜相比,掺钨VO_2薄膜具有相变温度低、阈值电压低和电阻率小的特点,在高速光电器件中有广阔的应用前景.     

W掺杂对β-Ga_2O_3导电性能影响的理论研究

采用密度泛函理论的平面波超软赝势计算方法,对不同W掺杂浓度下β-Ga2O3的导电性能进行研究.计算了β-Ga2(1-x)W2x O3(x=0,0.0625,0.125)的优化参数、总态密度和能带结构.结果表明,W掺入β-Ga2O3使Ga2(1-x)W2x O3材料的体积增大,总能量升高,稳定性降低.当W的掺杂量较小时,其电子迁移率较大,导电性能也很强.当增加W的掺杂量,Ga2(1-x)W2x O3材料的平均电子有效质量就略有增大,能隙变得越窄,这与实验的变化趋势相一致.     

Mg-F受主-施主共掺SnO_2的第一性原理研究

利用基于密度泛函理论(DFT)的第一性原理平面波赝势法,研究了Mg-F受主-施主共掺杂SnO_2的结构稳定性、能带结构、态密度及布居分布.结果表明,Mg-F掺杂能形成稳定的掺杂体系,在价带顶附近F 2p的态密度峰值强度较大,Mg-F原子之间杂化强,引入施主掺杂元素F有利于Mg受主掺杂的稳定性,同时Mg-O之间电子重叠布居值增大,原子之间的重叠增加,共有化增强,可使导电性能进一步提升.     

化学蒸镀掺锑的氧化锡膜

美国无线电公司有人用化学蒸汽淀积法镀掺锑的氧化锡透明导电薄膜。用双醋酸锡二丁酯、五氯化锑、O_2、H_2O和N_2为运载气体,衬底温度350～500℃。SnO_2中Sb的最佳掺杂浓度是0.6％(克原子百分比)。薄膜的厚度在0.1～0.2微米范围内。膜中不含挥发的氯原子,在1000℃的空气中稳定。对可见光的透射率在80％以上。面电阻率是     

花状掺杂W-VO_2/ZnO热致变色纳米复合薄膜研究

为解决掺杂引起的二氧化钒薄膜的红外调制幅度下降以及二氧化钒复合薄膜相变温度需要进一步降低等问题,采用纳米结构、掺杂改性和复合结构等多种机理协同作用的方案,利用共溅射氧化法,先在石英玻璃上制备高(002)取向的Zn O薄膜,再在Zn O层上室温共溅射沉积钒钨金属薄膜,最后经热氧化处理获得双层钨掺杂W-VO2/Zn O纳米复合薄膜.利用X射线衍射、X射线光电子能谱、扫描电镜和变温光谱分析等对薄膜的结构、组分、形貌和光学特性进行了分析.结果显示,W-VO2/Zn O纳米复合薄膜呈花状结构,取向性提高,在保持掺杂薄膜相变温度(约39?C)和热滞回线宽度(约6?C)较低的情况下,其相变前后的红外透过率差量增加近2倍,热致变色性能得到协同增强.     

电化学方法制备ZnO纳米颗粒掺杂类金刚石薄膜及其场发射性能研究

采用液相电化学沉积技术制备了ZnO纳米颗粒掺杂的类金刚石(DLC)薄膜, 研究了ZnO纳米颗粒掺杂对DLC薄膜场发射性能的影响. 利用X射线光电子能谱、透射电子显微镜、Raman光谱以及原子力显微镜分别对薄膜的化学组成、 微观结构和表面形貌进行了表征. 结果表明: 薄膜中的ZnO纳米颗粒具有纤锌矿结构, 其含量随着电解液中Zn源的增加而增加. ZnO纳米颗粒掺杂增强了DLC薄膜的石墨化和表面粗糙度. 场发射测试表明, ZnO纳米颗粒掺杂能提高DLC薄膜的场发射性能, 其中Zn与Zn+C的原子比为10.3%的样品在外加电场强度为20.7 V/μm时电流密度达到了1 mA/cm². 薄膜场发射性能的提高归因于ZnO掺杂引起的表面粗糙度和DLC薄膜石墨化程度的增加.     

F,Al共掺杂ZnO透明导电薄膜的制备及掺杂机理研究

本文采用磁控溅射技术,对F和Al共掺杂ZnO (FAZO)薄膜进行研究,系统地研究了溅射气压对薄膜结构、形貌、光电等特性的影响.实验研究结果表明:F, Al共掺入并未改变ZnO的生长方式,所制备的薄膜都呈(002)择优生长;随着溅射气压增加, FAZO薄膜的沉积速率降低,结晶质量恶化,表面形貌由"弹坑状"逐渐变为"弹坑状"与"颗粒状"并存的形貌特性,表面粗糙度增加.在0.5 Pa时制备的FAZO薄膜性能最优,迁移率40.03 cm~2/(V·s),载流子浓度3.92×10~(20) cm~(–3),电阻率最低,为3.98×10~(–4) W·cm, 380—1200 nm平均透过率约90%.理论模拟结果表明:F和Al的共掺杂兼顾了F, Al单独掺杂的优点,克服了以往金属元素掺杂仅依靠金属元素轨道提供导电电子的不足,实现了既增加载流子浓度又减少了掺入原子各轨道间相互作用对载流子散射的影响.掺入的F 2p电子轨道对O 2p及Zn 4s电子轨道产生排斥,使它们分别下移,提供导电电子;同时掺入的Al的3s和3p电子轨道也为导电电子提供了贡献. F和Al共掺之后载流子浓度提升更加显著,导电性能增强.     

Zn,Cu共掺杂的TiO_2:SnO_2薄膜的制备及性能研究

用溶胶-凝胶法制得Zn,Cu共掺杂的TiO_2∶SnO_2凝胶,旋转法于玻璃基底镀膜,制备出Zn,Cu共掺杂的TiO_2∶SnO_2薄膜,探讨了掺杂比例、煅烧温度对其结构、形貌和性能的影响。采用XRD、FTIR、FESEM、PL等测试技术对薄膜进行表征,并考察了其对甲基橙的光催化降解性能。结果表明:600℃时,薄膜粒子的结晶度较高,粒径小,分布均匀,表面平整且无明显裂痕;紫外-可见光谱(UV-Vis)表明:该薄膜在可见光区和紫外区都有很强的吸收;光催化性能测试表明:与纯相TiO_2对比,该样品对甲基橙的光催化降解率有较大提高,在最佳掺杂量比为n(Ti)∶n(Sn)∶n(Zn)∶n(Cu)=10∶3∶1∶1时,光催化降解率最高。     

基于FTO/VO2/FTO结构的VO2薄膜电压诱导相变光调制特性

采用直流磁控溅射和后退火工艺在掺氟的SnO₂(FTO)导电玻璃衬底上制备VO₂薄膜, 研究了不同退火时间和不同比例的氮氧气氛对VO₂薄膜性能的影响, 对VO₂薄膜的结晶取向、表面形貌、表面元素的相对含量和透过率随波长变化进行了测试分析, 结果表明在最佳工艺条件下制备得到了组分相对单一的VO₂薄膜. 基于FTO/VO₂/FTO结构在VO₂薄膜两侧的透明导电膜上施加电压并达到阈值电压时, 观察到了明显的电流突变. 当接触面积为3 mm×3 mm时, 阈值电压为1.7 V, 阈值电压随接触面积的增大而增大. 与不加电压的情况相比, FTO/VO₂/FTO结构在电压作用下高低温的红外透过率差值可达28%, 经反复施加电压, 该结构仍保持性能稳定, 具有较强的电致调控能力.     

Effect of freon flow rate on tin oxide thin films deposited by chemical vapor deposition

High quality fluorine-doped tin oxide (SnO₂:F) films on glass substrates were been prepared using chemical vapor deposition (CVD) method. The electrical properties, surface morphologies, structural properties and optical properties of the films were studied by varying the freon flow rates. The structure was analyzed by X-ray diffraction (XRD). Scanning electron microscopy (SEM) and atomic force microscopy (AFM) were used to study the morphology. Energy-dispersive spectroscopy (EDS) was conducted to understand the surface fluorine composition of the film. The results showed that crystalline structure of the film had a have cassiterite-like diffraction patterns with a preferred orientation of (1 1 0). Surface roughness was evaluated by atomic force microscopy, characterized by root mean square (RMS) and average value (Ra). The SnO₂:F resistivity decreased as the freon flow rate increased. The films had a uniform thickness and a transmittance of 80–90% within the visible region of the spectrum.     

Optoelectronic properties of SnO_2 thin films sprayed at different deposition times

This article presents the elaboration of tin oxide(SnO_2) thin films on glass substrates by using a home-made spray pyrolysis system. Effects of film thickness on the structural, optical, and electrical film properties are investigated. The films are characterized by several techniques such as x-ray diffraction(XRD), atomic force microscopy(AFM), ultravioletvisible(UV–Vis) transmission, and four-probe point measurements, and the results suggest that the prepared films are uniform and well adherent to the substrates. X-ray diffraction(XRD) patterns show that SnO_2 film is of polycrystal with cassiterite tetragonal crystal structure and a preferential orientation along the(110) plane. The calculated grain sizes are in a range from 32.93 nm to 56.88 nm. Optical transmittance spectra of the films show that their high transparency average transmittances are greater than 65% in the visible region. The optical gaps of SnO_2 thin films are found to be in a range of 3.64 e V–3.94 e V. Figures of merit for SnO_2 thin films reveal that their maximum value is about 1.15 × 10-4-1?atλ = 550 nm. Moreover, the measured electrical resistivity at room temperature is on the order of 10-2?·cm.     

不同Sb含量p-SnO2薄膜的制备和特性

采用化学气相沉积方法, 利用Sb₂O₃/SnO作为源材料, 在蓝宝石衬底上制备出不同Sb掺杂量的SnO₂薄膜, 并在此基础上制作出p-SnO₂:Sb/n-SnO₂同质p-n 结器件. 研究表明, 随着Sb含量的增加, 样品表面变得平滑, 晶粒尺寸逐渐增大, 且晶体质量有所改善, 发现少量Sb的掺入可以起到表面活化剂的作用. Hall测量结果证实适量Sb的掺杂可以使SnO₂呈现p型导电特性, 当Sb₂O₃/SnO的质量比为1:5时, 其电学参数为最佳值. 此外, p-SnO₂:Sb/n-SnO₂同质p-n结器件展现出良好的整流特性, 其正向开启电压为3.4 V.     

微晶硅锗薄膜作为近红外光吸收层在硅基薄膜太阳电池中的应用

采用射频等离子体增强化学气相沉积技术,制备了具有一定晶化率不同Ge含量的氢化微晶硅锗(μcSi1-xGex:H)薄膜.通过Ⅹ射线荧光谱、拉曼光谱、X射线衍射谱、傅里叶红外谱、吸收系数谱和电导率的测试,表征了μc-Si_(1-x)Ge_x:H的材料微结构随Ge含量的演变.研究表明:提高Ge含量可以增强μc-Si_(1-x)Ge_x:H薄膜的吸收系数.将其应用到硅基薄膜太阳电池的本征层中可以有效提高电池的短路电流密度(J_(sc)).特别是在电池厚度较薄或陷光不充分的情况下,长波响应的提高会更为显著.应用ZnO衬底后,在Ge含量分别为9%和27%时,μc-Si_(1-x)Ge_x:H太阳电池的转换效率均超过了7%.最后,将μc-Si_(1-x)Ge_x:H太阳电池应用在双结叠层太阳电池的底电池中,发现μc-Si_(0.73)Ge_(0.27):H底电池在厚度为800 nm时即可得到比1700 nm厚微晶硅(μc-Si:H)底电池更高的长波响应.以上结果体现μc-Si_(1-x)Ge_x:H太阳电池作为高效近红外光吸收层,在硅基薄膜太阳电池中应用的前景.     

电镀法在氧化铟锡上制备铜锌锡硫薄膜的光谱特征

低成本、环境友好的铜锌锡硫替代含贵金属和有毒金属的铜铟镓硒,是薄膜太阳能电池的最佳选择。电镀法是一种无需真空设备和靶材的低成本方法。一种更简单的制膜方法是在水溶液中共电镀沉积Cu-Zn-Sn（CZT)合金于FTO衬底上。采用氩气保护气氛下在550 ℃硫化电镀法制得的CZT合金前驱体,成功制备了CZTS薄膜。采用三电极体系将CZT合金前驱体电镀在FTO上,其中FTO作为工作电极,铂（Pt）网和Ag/AgCl分别作为对电极和参比电极。电解质由CuSO₄,ZnSO₄,SnSO₄,络合剂-三乙醇胺（TEA）和柠檬酸钠组成。前驱体在氩气保护气氛下550℃硫化得到CZTS薄膜。采用X射线衍射（XRD）、拉曼光谱、扫描电子显微镜（SEM）、紫外可见光光谱仪和光电化学测量（PEC）等方法,表征了CZTS薄膜的结构、形貌、成分和光谱学性质。XRD和拉曼光谱证明了550 ℃硫化后的CZTS薄膜具有锌黄锡矿结构。一个Raman主峰位于342 cm-1,两个Raman次强峰分别位于289和370 cm-1,这些峰位与锌黄锡矿CZTS的峰位相吻合。SEM结果证明优化后CZTS薄膜成分接近CZTS的理想化学计量比,CZTS薄膜中Cu/(Zn+Sn）和 S/(Zn+Sn+Cu)分别为0.52和1.01,这表明CZTS薄膜中S的含量非常合适。PEC结果证实,采用前照射或后照射FTO/CZTS均产生光电流,并且两种照射下产生的光电流方向一致。通过紫外可见光光谱测量并由此计算出的CZTS能隙为1.45 eV。通过上述分析证明制备的CZTS薄膜具有高品质,可用于制备CZTS薄膜太阳能电池。     

Cu掺杂SnO_2/TiO_2复合薄膜的制备及性能研究

制备Cu掺杂的纳米Sn O2/Ti O2溶胶,采用旋涂法在载玻片上镀膜,经干燥、煅烧制得Cu掺杂的Sn O2/Ti O2薄膜,通过对比实验探讨掺杂比例、条件、复合形式等对结构和性能的影响。采用XRD、SEM、EDS、UVVis等测试手段对样品进行表征,并以甲基橙为探针考察了其光催化降解性能。XRD测试结果显示薄膜的晶型为锐钛矿型,结晶度较高。SEM谱图显示薄膜表面无明显开裂,粒子分布均匀,粒径约为20 nm。EDS测试结果表明薄膜材料中含有Cu元素,谱形一致。UV-Vis吸收光谱表明Cu掺杂以及Sn O2/Ti O2的复合使得在近紫外区的光吸收比纯Ti O2明显增强。光催化实验表明Cu掺杂后使得Sn O2/Ti O2复合薄膜对甲基橙的光催化降解效率进一步提高,Sn O2/Ti O2复合薄膜的光催化活性在10%Cu掺杂时达到最高。     

Studies of synthesizing behaviors and superconductivity of sol-gel YBaCuO samples in flowing oxygen atmosphere

Systematic studies of synthesizing behaviors of sol-gel YBa₂Cu₃O_7-x samples in flowing oxygen atmosphere and their superconductivity have been performed. A set of high temperature ?-T curves has been obtained for the whole synthesizing process. After four rounds of synthesizing, the resistivity of the sample was around ? = 1.00 × 10^-3 ?cm at room temperature. The ?-T curve of the fourth round shows that the orthorhombic to tetragonal phase transformation of the sample occurs around 600°C, which is lower than that of the YBa₂Cu₃O_7-x sample prepared by conventional solid-state reaction method. Other measurements, such as X-ray diffraction, SEM measurement and low temperature R-T and M-T measurement, were also performed. And the R-T and M-T measurement results suggest that during the synthesizing process, there exist some state at which the sample has better superconductivity than the other states. Moreover, we found screw dislocations presenting on the sample broken surface from the SEM images. This will change the concept that the screw dislocations can only grow on the surface of the YBCO thin films and single crystals.