纳米复合永磁材料的有效各向异性与矫顽力

研究了纳米Nd2Fe14B/α-Fe复合永磁材料中晶粒交换耦合相互作用对有效各向异性的影响和变化规律.结果表明：晶粒之间的交换耦合作用使材料的有效各向异性Keff随晶粒尺寸的减小而下降、随软磁性相成分的增加而降低. 当晶粒尺寸 减小到4nm时，Keff值减小为其各自通常各向异性常数值的1/3—1/4.有效各向异性的变化特点与矫顽力的变化规律基本相同.纳米复合永磁材料矫顽力的降低主要由于有效各向异性的减小而引起. 关键词： 纳米复合永磁材料 交换耦合相互作用 有效各向异性 矫顽力     

交换耦合作用对纳米复合永磁材料有效各向异性的影响

以Nd_2Fe_(14)B/α-Fe纳米复合永磁材料为例,采用立方体晶粒结构模型,研究了单个晶粒中存在不同耦合状态时,有效各向异性随晶粒尺寸的变化关系.采用边界值不为零的变化函数研究了耦合部分各向异性随耦合长度的变化.计算结果表明:当两相耦合时,软磁晶粒的有效各向异性随晶粒尺寸的增加而减小,硬磁晶粒的有效各向异性随晶粒尺寸的增加而增加.对于存在软、硬两相的复合磁体,为保证较高的有效各向异性值,晶粒尺寸应保持在25nm左右.     

交换耦合相互作用对纳米晶粒各向异性的影响

研究纳米磁性材料晶粒间的交换耦合相互作用,提出适合各种耦合条件晶粒界面及表面处各向异性的表达式.结果表明:软、硬磁性相晶粒间的交换耦合相互作用降低了硬磁性相晶粒的各向异性,提高了软磁性相晶粒的各向异性.软硬磁性晶粒的平均各向异性先增加后减小,在某个晶粒尺寸值达到最大值,这种变化趋势与相关的理论及实验结果一致.硬硬磁性晶粒的平均各向异性随晶粒尺寸的变化趋势与相关的实验结果也一致.     

相分布和晶粒尺寸对Nd2Fe14B/ɑ-Fe纳米复合永磁材料矫顽力的影响

本文采用统计平均方法研究了软、硬磁性晶粒尺寸及相分布对Nd2Fe14B/α-Fe纳米复合永磁材料矫顽力的影响。计算结果表明：对于单相纳米硬磁材料，磁体矫顽力随着硬磁性晶粒尺寸的减小而降低；对于软、硬两磁性相组成的Nd2Fe14B/a-Fe纳米复合永磁材料，两相的随机分布将导致磁体矫顽力随硬磁性晶粒尺寸的减小呈现极大值。本文的计算结果还表明当硬磁性晶粒尺寸大于软磁性晶粒的最佳尺寸时(15nm)，具有多层膜结构的Nd2Fe14B/a-Fe纳米复合永磁材料将比两相随机分布时具有更大的矫顽力。     

纳米复合永磁材料中软磁性相交换硬化的研究

本文就纳米复合永磁材料中软磁相被交换硬化问题,从一维模型和三维模拟计算进行了分析研究. 一维和三维各向异性样品研究表明,在相同微结构下,当硬磁相的各向异性降低时,除矫顽力降低外,在磁矩全部反转之前退磁曲线是一样的. 因此,硬磁相各向异性的降低不会导致最大磁能积(BH)_max增大和剩磁增加. 对于三维各向同性样品的模拟计算表明,降低硬磁相的各向异性会使剩磁和(BH)_max都明显降低. 因此,增强硬磁相的各向异性并增大硬磁相晶粒尺寸是提高 关键词： 纳米复合永磁 矫顽力 剩磁 磁能积     

晶粒间界相对纳米Nd_2Fe_(14)B各向异性和矫顽力的影响

本文采用立方晶粒结构模型研究了晶粒间界相对纳米硬磁材料各向异性和矫顽力的影响.结果表明:晶粒间界相减弱了交换耦合作用.当晶粒尺寸D为定值时,随着晶粒间界相厚度d的增加,晶粒平均各向异性单调增加,而材料的有效各向异性Keff、矫顽力单调减小.我们计算的矫顽力随晶粒尺寸的变化与相关理论和实验结果基本一致.     

纳米晶复合永磁材料的交换耦合相互作用和磁性能

本介绍了纳米磁性材料晶粒交换耦合相互作用的有关理论。采用不同模型讨论了晶粒交换耦合相互作用对纳米单相软磁材料、永磁材料及双相复合永磁材料磁性能的影响。简述了用δM（H）曲线和不可逆磁导率的变化研究晶粒交换耦合相互作用及反磁化过程的方法。讨论了合金分配比、添加元素、制备及热处理工艺对磁体硬磁性能的影响。从理论和实验两方面分析、研究了纳米复合永磁材料的反磁化过程和矫顽力机制。     

纳米晶复合永磁材料的交换耦合相互作用和磁性能

本文介绍了纳米磁性材料晶粒交换耦合相互作用的有关理论。采用不同模型讨论了晶粒交换耦合相互作用对纳米单相软磁材料、永磁材料及双相复合永磁材料磁性能的影响。简述了用δM(H)曲线和不可逆磁导率的变化研究晶粒交换耦合相互作用及反磁化过程的方法。讨论了合金成分配比、添加元素、制备及热处理工艺对磁体硬磁性能的影响。从理论和实验两方面分析、研究了纳米复合永磁材料的反磁化过程和矫顽力机制。     

Nd-Fe-B/FeCo多层纳米复合膜的结构和磁性

制备了Nd₂₈Fe₆₆B₆/Fe₅₀Co₅₀多层纳米复合磁性薄膜，对溅射态和650℃退火处理15 min试样的相成分分析和微结构的观察显示，溅射态薄膜呈非晶态，经650℃退火处理15 min后，薄膜主要相成分为硬磁性Nd₂Fe₁₄B相和软磁性相FeCo(110)相.Nd₂Fe₁₄B相呈柱状，其易磁化c轴垂直于膜面，尺寸约10 nm.在硬磁性相和软磁性相之间存在少量富Nd相和非晶态，富Nd相大小约7 nm.磁性测量和分析表明，1)该系列薄膜退火态具有垂直于膜面的磁晶各向异性.2)对于固定厚度(10 nm)层Nd-Fe-B和不同厚度(t_FeCo=1—100 nm)层FeCo多层纳米复合膜,剩磁随软磁相FeCo 厚度的增加快速增加，而矫顽力则减小.当t_FeCo=5 nm时，最大磁能积达到200 kJ/m³. 3)硬磁相Nd-Fe-B层和软磁相FeCo层之间交换耦合导致剩磁和磁能积增强. 关键词： Nd-Fe-B/FeCo多层纳米复合膜 交换耦合 磁各向异性     

FePt薄膜中磁相互作用

采用磁控溅射方法在自然氧化的单晶Si(100)衬底上制备了纳米结构的Fe₅₃Pt₄₇薄膜，并研究热处理后薄膜中的磁相互作用、晶粒尺寸与热处理温度的关系.经400℃热处理后，FePt薄膜中有明显的面心四方相形成，薄膜表现出硬磁性，晶粒尺度在20 nm，薄膜内部存在软硬磁交换耦合作用；随着热处理温度升高，硬磁相含量增加.同时由于FePt薄膜的晶粒长大，部分软硬磁晶粒之间的交换耦合作用失效；600℃热处理后，FePt的面心立方相已经完全转变为面心四方相，薄膜矫顽力由硬磁相之间的静磁作用贡献. 关键词： 磁性薄膜 纳米晶 磁性能 热处理     

Effective anisotropy and coercivity in nanocrystalline single-phase NdFeB permanent magnetic material

The effect of exchange-coupling interaction on the effective anisotropy and its varying tendency in nanocrystalline single-phase NdFeB permanent magnetic material have been investigated. The results show that the exchange-coupling interaction between grains makes the effective anisotropy of material, Keff, decrease with the reduction of grain size. The variation of Keff is basically the same as that of coercivity. The decrease in effective anisotropy is the main reason of the reduction of coercivity for nanocrystalline single-phase NdFeB permanent magnetic material. In order to get high anisotropy and coercivity in nanocrystalline single-phase NdFeB permanent material, the grain size should be larger than 35 nm.     

Effective anisotropy between magnetically soft and hard grains in nanocomposite magnets

Effect of grain size on the effective anisotropy constant between magnetically soft (α-Fe) and hard (Nd₂Fe₁₄B) grains in nanocomposite magnets, 〈K_sh〉, has been investigated. The results show that the values of 〈K_sh〉 increase with decreasing size of soft grain, D_s, for the given size of hard grain, D_h. For the given D_s, 〈K_sh〉 increases with increasing D_h, and then approaches a steady value. In order to get a high value of 〈K_sh〉, the hard grain size should be larger than 30 nm and the soft grain size should be about 10 nm. PACS 75.30.E, 75.30.G, 75.50.T     

Anisotropy at nano-grain boundary and effective anisotropy between magnetically soft and hard nano-grains

An expression of anisotropy at grain boundary suitable for different coupling conditions has been given, based on which the effective anisotropy between soft and hard grains 〈K_sh〉 has been calculated in nanoscaled magnetic materials. The results showed that 〈K_sh〉 increases rapidly first, then the increase becomes slow, and 〈K_sh〉 decreases with increasing D_s for the same value of D_h. 〈K_sh〉 decreases with increasing D_s for all given D_h, and the decrease rate becomes slow with increasing D_h. In order to obtain higher effective anisotropy between magnetically soft and hard grains, D_h should not be less than 25 nm, and D_s should be about 10 nm.     

Investigation on magnetic properties of orientated nanocomposite Pr2Fe14B/α-Fe permanent magnets by micromagnetic finite-element method

Demagnetization curves for nanocomposite Pr₂Fe₁₄B/α-Fe permanent magnets with different hard grain alignment are calculated by a micromagnetic finite-element method. The results show that both remanence and coercivity increase with improving hard grains alignment. The demagnetization curves show a single-phase demagnetization behavior for the samples with grain size d of 10 nm and two-phase behavior for the samples with d of 20 and 30 nm. H_ex (reflecting the magnetic hardening of α-Fe) and H_irr (expressing the irreversible reversal of hard phase) are both enhanced with improving the hard grain alignment. The magnetic reversal in orientated nanocomposite permanent magnets is mainly controlled by inhomogeneous pinning of the nucleated type.