沉积时间对球状微米金刚石聚晶结构的生长及其场发射特性影响

利用微波等离子体化学气相沉积法,在覆盖金属钛层的陶瓷衬底上,通过改变沉积时间制备出不同结构的类球状微米金刚石聚晶碳膜.通过扫描电子显微镜、喇曼光谱、X射线衍射谱对碳膜进行了分析测试,并研究了不同沉积时间下沉积的类球状微米金刚石聚晶薄膜的场致电子发射特性,结果显示:不同的沉积时间所制备的碳膜形貌有很大变化,场致电子发射的...     

类球状微米金刚石聚晶膜场发射的稳定性

在覆盖金属钛层的陶瓷上,利用微波等离子体化学气相沉积(MPCVD)法制备出类球状微米金刚石聚晶膜。通过二极管结构测试了聚晶膜的场致电子发射特性,利用扫描电子显微镜、拉曼光谱、XRD分析了场发射前后薄膜的结构和表面形貌的变化。发现在高场、大电流密度的场发射中,对类球状微米金刚石聚晶薄膜中的金刚石聚晶颗粒影响很小,而对金刚石聚晶颗粒间的非晶碳层影响很大。对类球状微米金刚石聚晶变化机理进行了研究。     

类球状微米金刚石聚晶的场发射

在覆盖金属钛层的陶瓷上,采用微波等离子体化学气相沉积(MPCVD)法制备出类球状微米金刚石聚晶薄膜。利用扫描电子显微镜、拉曼光谱,X射线衍射,分析了薄膜的结构和表面形貌。测试了类球状微米金刚石聚晶膜的场致电子发射特性。开启电场仅为0.55V/μm,在2.18V/μm的电场下,其场发射电流密度高达11mA/cm2。仔细分析了膜的发射过程,发现类球状微米金刚石聚晶的结构对发射有很大影响,并对其发射机理进行了研究。     

氮离子注入对类球状微米金刚石聚晶膜的影响

利用微波等离子体化学气相沉积法,在覆盖金属钛层的陶瓷衬底上制备出类球状微米金刚石聚晶膜,后对膜的表面进行氮离子的注入.通过扫描电子显微镜、拉曼光谱、X射线衍射谱及二级结构场发射测试,对膜进行了注入前后的分析.氮离子注入后场致电子发射的效果变强,这可能是氮离子的注入增加了类球状微米金刚石聚晶膜表面的缺陷度,从而增加了价带和导带间的缺陷能级,使电子更容易跃迁到高能级上,提高了场致电子的发射效果.     

激光刻蚀类球状微米金刚石聚晶薄膜对场致电子发射稳定性的影响

在覆盖金属钛层的陶瓷上,通过微波等离子体化学气相沉积(MPCVD)法制备出类球状微米金刚石聚晶薄膜,并通过激光刻蚀金刚石聚晶薄膜的表面.利用扫描电子显微镜、拉曼光谱,X射线衍射分析了刻蚀前后的结构和表面形貌,测试了刻蚀前后薄膜的场致电子发射特性,发现激光的刻蚀对金刚石聚晶薄膜场致电子发射的稳定性有一定的提高,并对其制备过程及发射机理进行了研究.     

金刚石镶嵌非晶碳膜表面形貌对场致电子发射的影响

用微波等离子体化学气相沉积设备，在经过不同研磨预处理的金属钼衬底上沉积出了表面形貌有较大差异的金刚石镶嵌非晶碳膜，分别用扫描电子显微镜（ＳＥＭ）、金相显微镜和Ｘ射线衍射谱（ＸＲＤ）以及Ｒａｍａｎ光谱对样品进行了分析测试．研究了各样品的场致电子发射特性，结果发现薄膜表面由大量镶嵌有金刚石小晶粒的非晶碳球组成，在我们的实验范围内，薄膜表面非晶碳球尺寸越小，场致电子发射效果越好     

X射线光电子能谱辅助Raman光谱分析类金刚石碳膜的结构细节

分别采用具有和不具有弯曲弧磁过滤器的两种真空阴极弧离子镀方法,在不同工艺参量下制备了类金刚石碳膜.采用Raman光谱和X射线光电子能谱(XPS),分析了不同工艺参量下的类金刚石碳膜的键结构,通过对Raman光谱的D峰、G峰和C1s电子结合能峰位、强度的对比,详细讨论了沉积工艺参量对类金刚石碳膜结构的影响.研究发现,不同工艺下具有高强度D峰Raman光谱的类金刚石碳膜,其C1s电子结合能却分别位于284.15,285.50eV,表明高度石墨化和高度金刚石化两种状态类金刚石碳膜,都可以形成具有高强度D峰Raman光谱曲线 关键词： 类金刚石碳膜 Raman光谱 X射线光电子能谱     

类金刚石和碳氮薄膜的电化学沉积及其场发射性能研究

利用电化学方法在室温下成功地沉积了类金刚石(DLC)薄膜和非晶CN_x薄膜，并 对制备条件进行了讨论.通过扫描电子显微镜、傅里叶变换红外光谱技术，分析了薄膜的表面形貌和化学结合状态.场发射测量结果表明：DLC膜和非晶CN_x的开启场分别为88和 10V/μm；并且在23V/μm的电场下，DLC膜和非晶CN_x膜的发射电流密度分别达到10 和037mA/cm². 关键词： 电化学沉积 类金刚石薄膜 x薄膜')" href="#">CN_x薄膜 场致电子发射     

白碳纳米晶薄膜及其场致电子发射特性

利用微波等离子体化学气相沉积方法,以甲烷、氢混合气体为反应气体,具有钛镀层的玻璃作为衬底,制备了具有sp¹杂化结构的白碳纳米晶薄膜。利用X射线衍射、俄歇电子能谱,以及扫描电子显微镜对薄膜结构进行了表征。以白碳纳米晶薄膜为阴极,以镀有ITO透明导电薄膜玻璃为阳极,采用二极管结构,测试了白碳纳米晶薄膜的场致电子发射特性。开启电场为2.5 V/μm,在电场为5 V/μm时的电流密度为200μA/cm²。对白碳纳米晶薄膜生长机理,以及其场致电子发射机制进行了讨论。     

铜上采用过渡层沉积类金刚石薄膜的研究

将等离子增强非平衡磁控溅射物理气相沉积(PEUMS-PVD)和电子回旋共振-微波等离子体增强化学气相沉积(MW-ECRPECVD)技术相结合，通过制备不同的过渡层，在铜基上成功地制备了类金刚石膜.拉曼光谱分析表明，所制备的碳膜具有典型的类金刚石结构特征.检测结果表明，随着沉积偏压的增大，D峰和G峰均向高波数漂移，I_D/I_G值增大，表面粗糙度减小，而平均硬度和弹性模量呈先增大后减小的趋势. 关键词： 铜基体 类金刚石膜 过渡层 拉曼光谱     

Growth and field emission properties of globe-like diamond microcrystalline-aggregate

The globe-like diamond microcrystalline-aggregates were fabricated by microwave plasma chemical vapor deposition (MPCVD) method. The ceramic with a Ti mental layer was used as substrate. The fabricated diamond was evaluated by Raman scattering spectroscopy, X-ray diffraction spectrum (XRD), and scanning electron microscope (SEM). The field emission properties were tested by using a diode structure in a vacuum. A phosphor-coated indium tin oxide (ITO) anode was used for observing and characterizing the field emission. It was found that the globe-like diamond microcrystalline-aggregates exhibited good electron emission properties. The turn-on field was only 0.55 V/μm, and emission current density as high as 11 mA/cm² was obtained under an applied field of 2.9 V/μm for the first operation. The growth mechanism and field emission properties of the globe-like diamond microcrystalline-aggregates are discussed relating to microstructure and electrical conductivity.     

Field electron emission in graphite-like films

Results of investigation of carbon films deposited with the use of gas-phase chemical reactions in the plasma of a dc discharge are presented. Films obtained at different parameters of the deposition process varied widely in their structure and phase composition, from polycrystalline diamond to graphite-like material. Comparative study of the structure and phase composition of the films using Raman spectroscopy, cathodoluminescence, electron microscopy, and diffractometry, as well as the obtained field electron emission characteristics, have shown that the threshold value of the electric field strength for electron emission decreases with a decrease in the size of diamond crystallites and growth of the fraction of non-diamond carbon. The lowest threshold fields (less than 1.5 V/μm) are obtained for films consisting mainly of graphite-like material. A model based on the experimental data is proposed, which explains the mechanism of field electron emission in carbon materials.     

电子助进化学气相沉积金刚石中发射光谱的蒙特卡罗模拟

采用蒙特卡罗方法，对源料气体为CH4/H2混合气的电子助进化学气相沉积（EACVD）中 的氢原子(H)、碳原子(C)以及CH基团的发射过程进行了模拟.研究了CH4浓度、反应室气压 和衬底偏压等工艺参数对发射光谱及成膜的影响.研究发现，CH基团可能是有利于金刚石薄 膜生长的活性基团，而碳原子不是；偏压的升高可提高电子平均温度及衬底表面附近氢原子 的相对浓度；通过氢原子谱线可测定电子平均温度并找到最佳成膜实验条件.该结果对EACVD 生长金刚石薄膜过程中实时监测电子平均温度，有效控制工艺条件，生长出高质量的金刚石 薄膜具有重要的意义. 关键词： 蒙特卡罗模拟 金刚石薄膜 发射光谱     

非晶金刚石薄膜的场致电子发射性能研究

利用真空磁过滤弧沉积技术制备出一种高sp³含量的非晶碳膜———非晶金刚石薄膜，并对这种非晶金刚石薄膜的场电子发射特性及其发射机理进行了研究．实验结果表明，在阈值电场低于20V/μm情况下，得到的场发射电流达20—40μA，薄膜的电子发射行为符合Fowler-Nordheim场发射理论．研究表明，这种非晶金刚石薄膜具有负的电子亲合势和较小的有效功函数以及相对较低的禁带宽度 关键词：     

催化剂对纳米非晶碳膜场发射性能的影响

利用微波等离子体增强化学气相沉积(MPECVD)法,在经处理的单晶硅衬底上沉积了纳米非晶碳薄膜.通过Raman、SEM、XRD表征,研究了催化剂对纳米非晶碳膜的生长速率及场发射性能的影响.结果表明,在制备纳米非晶碳膜时使用FeC13,作为催化剂可大幅提高其生长速率.在相同的制备条件下,与未加FeCl3催化剂制备的纳米非...     

N离子注入对金刚石膜场发射特性的影响

不同剂量的N离子被注入到化学气相沉积金刚石膜内，研究了表面结构及场发射特性的变化.Raman谱和x射线光电子能谱分析表明，N离子的注入破坏了金刚石膜表面原有的sp3结构，并在膜内形成大量的sp2 C—C 和sp2 C—N 键.样品的场发射测试显示N离子的注入显著提高了金刚石膜场发射特性，膜的场发射阈值电场从注入前的18 V/μm下降到注入后的4 V/μm.金刚石膜场发射特性的提高归因于N离子注入后膜内sp2 C键含量的增加和体内缺陷带的形成，这些变化能改变膜的表面功函数，提高Feimi能级，降低电子隧穿表面的能量势垒. 关键词： 场致电子发射 N离子注入 金刚石膜 热丝化学气相沉积