MBE growth of PbSe thin film with a 9×10 cm etch-pits density on patterned (1 1 1)-oriented Si substrate

PbSe thin film was grown on a patterned Si substrate with (1 1 1)-orientation by molecular-beam epitaxy (MBE). On the mesa, a low dislocation density of 9×10⁵ cm⁻² was confirmed by the etch-pits density (EPD) wet-etching technique. The photoluminescence (PL) intensity at room temperature from the low dislocation PbSe film was much higher than that from the PbSe film grown on the planar area, which further indicated the high-quality of PbSe thin film grown on patterned Si substrate.     

Growth of (1 0 1¯ 3¯ ) semipolar GaN on m-plane sapphire by hydride vapor phase epitaxy

The crystalline, surface, and optical properties of the (1 0 1¯ 3¯) semipolar GaN directly grown on m-plane sapphire substrates by hydride vapor phase epitaxy (HVPE) were investigated. It was found that the increase of V/III ratio led to high quality (1 0 1¯ 3¯) oriented GaN epilayers with a morphology that may have been produced by step-flow growth and with minor evidence of anisotropic crystalline structure. After etching in the mixed acids, the inclined pyramids dominated the GaN surface with a density of 2×10⁵ cm⁻², revealing the N-polarity characteristic. In the low-temperature PL spectra, weak BSF-related emission at 3.44 eV could be observed as a shoulder of donor-bound exciton lines for the epilayer at high V/III ratio, which was indicative of obvious reduction of BSFs density. In comparison with other defect related emissions, a different quenching behavior was found for the 3.29 eV emission, characterized by the temperature-dependent PL measurement.     

Heteroepitaxial growth of InN layers on (1 1 1) silicon substrates

Indium nitride (InN) layers were grown on (1 1 1) silicon substrates by reactive magnetron sputtering using an indium target. Atomic force microscope, X-ray diffraction, and Raman spectroscopy analysis revealed that highly c-axis preferred wurtzite InN layers with very smooth surface can be obtained on (1 1 1) silicon substrates at a substrate temperature as low as 100 °C. The results indicate that the reactive sputtering is a promising growth technique for obtaining InN layers on silicon substrates at low substrate temperature with low cost and good compatibility with microelectronic silicon-based devices.     

Molecular beam epitaxial growth of hexagonal boron nitride on Ni(1 1 1) substrate

We demonstrate hexagonal boron nitride (h-BN) epitaxial growth on Ni(1 1 1) substrate by molecular beam epitaxy (MBE) at 890 °C. Elemental boron evaporated by an electron-beam gun and active nitrogen generated by a radio-frequency (RF) plasma source were used as the group-III and -V sources, respectively. Reflection high-energy electron diffraction revealed a streaky (1×1) pattern, indicative of an atomically flat surface in the ongoing growth. Correspondingly, atomic force microscopy images exhibit atomically smooth surface of the resulting h-BN film. X-ray diffraction characterization confirmed the crystallinity of the epitaxial film to be h-BN, and its X-ray rocking curve has a full-width at half-maximum of 0.61°, which is the narrowest ever reported for h-BN thin film. The epitaxial alignments between the h-BN film and the Ni substrate were determined to be [0 0 0 1]_h−BN∥[1 1 1]_Ni, [1 1 2¯ 0]_h−BN∥[1¯ 1 0]_Ni, and [1 1¯ 0 0]_h−BN∥[1¯ 1¯ 2]_Ni.     

The effects of annealing on non-polar (1 1 2¯ 0) a-plane GaN films

Non-polar a-plane (1 1 2¯ 0) GaN films were grown on r-plane sapphire by metal–organic vapor phase epitaxy and were subsequently annealed for 90 min at 1070 °C. Most dislocations were partial dislocations, which terminated basal plane stacking faults. Prior to annealing, these dislocations were randomly distributed. After annealing, these dislocations moved into arrays oriented along the [0 0 0 1] direction and aligned perpendicular to the film–substrate interface throughout their length, although the total dislocation density remained unchanged. These changes were accompanied by broadening of the symmetric X-ray diffraction 1 1 2¯ 0 ω-scan widths. The mechanism of movement was identified as dislocation glide, occurring due to highly anisotropic stresses (confirmed by X-ray diffraction lattice parameter measurements) and evidenced by macroscopic slip bands observed on the sample surface. There was also an increase in the density of unintentionally n-type doped electrically conductive inclined features present at the film–substrate interface (as observed in cross-section using scanning capacitance microscopy), suggesting out-diffusion of impurities from the substrate along with prismatic stacking faults. These data suggest that annealing processes performed close to film growth temperatures can affect both the microstructure and the electrical properties of non-polar GaN films.     

Reduction of the dislocation density in molecular beam epitaxial CdTe(2 1 1)B on Ge(2 1 1)

The high dislocation density (2×10⁷/cm² for a thickness of 7 μm) in CdTe(2 1 1)B on Ge(2 1 1) has become a roadblock for the technological exploitation of this material. We present a systematic study of in situ and post-growth annealing cycles aimed at reducing it. An etch pit density of 2×10⁶/cm² was achieved by optimizing the growth conditions and annealing the samples in situ. This finding was corroborated by high-resolution X-ray diffraction, atomic force microscopy, photoluminescence and ellipsometry measurements.     

Low-temperature/high-temperature AlN superlattice buffer layers for high-quality AlxGa1−xN on Si (1 1 1)

We present MOVPE-grown, high-quality Al_xGa_1−x N layers with Al content up to x=0.65 on Si (1 1 1) substrates. Crack-free layers with smooth surface and low defect density are obtained with optimized AlN-based seeding and buffer layers. High-temperature AlN seeding layers and (low temperature (LT)/high temperature (HT)) AlN-based superlattices (SLs) as buffer layers are efficient in reducing the dislocation density and in-plane residual strain. The crystalline quality of Al_xGa_1−xN was characterized by high-resolution X-ray diffraction (XRD). With optimized AlN-based seeding and SL buffer layers, best ω-FWHMs of the (0 0 0 2) reflection of 540 and 1400 arcsec for the (1 0 1¯ 0) reflection were achieved for a ∼1-μm-thick Al_0.1Ga_0.9N layer and 1010 and 1560 arcsec for the (0 0 0 2) and (1 0 1¯ 0) reflection of a ∼500-nm-thick Al_0.65Ga_0.35N layer. AFM and FE-SEM measurements were used to study the surface morphology and TEM cross-section measurements to determine the dislocation behaviour. With a high crystalline quality and good optical properties, Al_xGa_1−x N layers can be applied to grow electronic and optoelectronic device structures on silicon substrates in further investigations.     

Atomic ordering in GaAsSb (0 0 1) grown by metalorganic vapor phase epitaxy

Epitaxial GaAsSb (0 0 1) semiconductor alloys grown by metalorganic vapor phase epitaxy exhibit several spontaneously ordered structures. A superlattice structure with three-fold ordering in the [1 1 0] direction has been previously observed by different groups. CuAu structures with (1 0 0) and (0 1 0) ordering planes have also been reported. The physical origin of CuAu ordering in III–V semiconductors has not yet been explained. In this work we report the effect of growth conditions on CuAu ordering in GaAsSb, including miscut from (0 0 1), growth rate, bismuth surfactant concentration, and growth temperature. These data point to a surface kinetic mechanism not based on dimer strain, but possibly due to one-dimensional ordering at step edges.     

Epitaxial NiO (1 0 0) and NiO (1 1 1) films grown by atomic layer deposition

Epitaxial NiO (1 1 1) and NiO (1 0 0) films have been grown by atomic layer deposition on both MgO (1 0 0) and α-Al₂O₃ (0 0 l) substrates at temperatures as low as 200 °C by using bis(2,2,6,6-tetramethyl-3,5-heptanedionato)Ni(II) and water as precursors. The films grown on the MgO (1 0 0) substrate show the expected cube on cube growth while the NiO (1 1 1) films grow with a twin rotated 180° on the α-Al₂O₃ (0 0 l) substrate surface. The films had columnar microstructures on both substrate types. The single grains were running throughout the whole film thickness and were significantly smaller in the direction parallel to the surface. Thin NiO (1 1 1) films can be grown with high crystal quality with a FWHM of 0.02–0.05° in the rocking curve measurements.     

Formation of GaN nanodots on Si (1 1 1) by droplet nitridation

GaN nanodots (NDs) are obtained by Ga metallic droplet formation on Si (1 1 1) substrates followed by their nitridation. The size and density of Ga droplets and GaN NDs can be controlled by varying the growth temperature within the range 514–640 °C. Atomic force microscopy (AFM) investigation of Ga droplets shows an increase in the average diameter with temperature. The average diameter of GaN NDs increases with growth temperature while their density decreases more than one order of magnitude. In addition, the formation of a GaN crystallite rough layer on Si, in-between NDs, indicates that a spreading mechanism takes place during the nitridation process. High-resolution transmission electron microscopy (HRTEM) is used for the investigation of shape, crystalline quality and surface distribution of GaN dots. X-ray photoelectron spectroscopy (XPS) results confirm that Ga droplets that are transformed into GaN NDs spread over the sample surface during nitridation.     

Epitaxial lateral overgrowth on (2 1¯ 1¯ 0) a-plane GaN with [0 1¯ 1 1]-oriented stripes

Epitaxial lateral overgrowth was applied to a-plane GaN on r-plane sapphire using SiO₂ stripe masks oriented parallel to [0 1¯ 1 1]. Coalescence and defect distribution was studied using scanning electron microscopy and cathodoluminescence. Defects, i.e., threading dislocations and basal plane stacking faults from the template propagate into the overgrown layer through the mask openings. Stacking faults spread into the whole overgrown layer, whereas threading dislocations are laterally confined in the region above the mask where a part of them is terminated at the inclined coalescence boundary. Lateral overgrowth and dislocation termination at the coalescence boundary leads to an improvement in luminescence intensity and crystal quality, in comparison to the template. The measured XRD rocking curve FWHM were 453″ with incidence along the [0 0 0 1] c-direction and 280″ with incidence along the [0 1 1¯ 0] m-direction.     

Low-temperature growth of epitaxial (1 0 0) silicon based on silane and disilane in a 300 mm UHV/CVD cold-wall reactor

Epitaxial (1 0 0) silicon layers were grown at temperatures ranging from 500 to 800 °C in a commercial cold-wall type UHV/CVD reactor at pressures less than 7×10⁻⁵ Torr. The substrates were 300 mm SIMOX SOI wafers and spectroscopic ellipsometry was used to assess growth rates and deposition uniformities. High-resolution atomic force microscopy (AFM) was employed to verify the atomic terrace configuration that resulted from epitaxial step-flow growth. Deposition from disilane exhibited a nearly perfect reaction limit for low temperatures and high precursor flow rates (partial pressures) with measured activation energies of ≈2.0 eV, while a linear dependence of growth rate on precursor gas flow was found for the massflow-controlled regime. A similar behavior was observed in the case of silane with substantially reduced deposition rates in the massflow-limited regime and nearly a factor of 2 reduced growth rates deep in the reaction limited regime. High growth rates of up to 50 μm/h and non-uniformities as low as 1σ=1.45% were obtained in the massflow-limited deposition regime. Silicon layers as thin as 0.6 nm (4.5 atomic layers ) were deposited continuously as determined using a unique wet chemical etching technique as well as cross-sectional high-resolution transmission electron microscopy (HRTEM). In contrast, epitaxial silicon deposited in RPCVD at 10 Torr using disilane within the same temperature range showed imperfect reaction limitation. While activation energies similar to that of UHV/CVD were found, no partial pressure limitation could be observed. Furthermore, layers deposited using disilane in RPCVD exhibited a large number of defects that appeared to form randomly during growth. We attribute this effect to gas phase reactions that create precursor fragments and radicals—an effect that is negligible in UHV/CVD.     

HVPE growth of semi-polar (1 1 2¯ 2)GaN on GaN template (1 1 3)Si substrate

The hydride-vapour-phase-epitaxial (HVPE) growth of semi-polar (1 1 2¯ 2)GaN is attempted on a GaN template layer grown on a patterned (1 1 3) Si substrate. It is found that the chemical reaction between the GaN grown layer and the Si substrate during the growth is suppressed substantially by lowering the growth temperatures no higher than 900 °C. And the surface morphology is improved by decreasing the V/III ratio. It is shown that a 230-μm-thick (1 1 2¯ 2)GaN with smooth surface is obtained at a growth temperature of 870 °C with V/III of 14.     

Growth of GaN based structures on Si(1 1 0) by molecular beam epitaxy

The growth of GaN based structures on Si(1 1 0) substrates by molecular beam epitaxy using ammonia as the nitrogen precursor is reported. The structural, optical and electrical properties of such structures are assessed and are quite similar to the ones obtained on Si(1 1 1) in-spite of the very different substrate surface symmetry. A threading dislocation density of 3.7×10⁹ cm⁻² is evaluated by transmission electron microscopy, which is in the low range of typical densities obtained on up to 2 μm thick GaN structures grown on Si(1 1 1). To assess the potential of such structure for device realization, AlGaN/GaN high electron mobility transistor and InGaN/GaN light emitting diode heterostructures were grown and their properties are compared with the ones obtained on Si(1 1 1).     

Evolution of ordered one-dimensional and two-dimensional InAs/InP quantum dot arrays on patterned InP (1 0 0) and (3 1 1)B substrates by self-organized anisotropic strain engineering

The formation of ordered InAs/InP quantum dot (QD) arrays is demonstrated on patterned InP (1 0 0) and (3 1 1)B substrates by the concept of self-organized anisotropic strain engineering in chemical beam epitaxy (CBE). On shallow- and deep stripe-patterned InP (1 0 0) substrates, depending on the stripe orientation, the linear one-dimensional InAs QD arrays are rotated away from their natural direction due to the presence of vicinal stepped sidewall planes modifying the self-organization process, coexisting with QD free steep side facets on the deep-patterned substrates. On shallow- and deep-patterned InP (3 1 1)B substrates only QD free side facets form with flat top and bottom areas, not affecting the natural ordering of the two-dimensional InAs QD arrays. On the deep-patterned substrates a row of dense QDs forms on top along the side facets due to their slow-growing behavior. The optical properties of the QD arrays on the patterned substrates are not degraded compared to those of arrays formed on planar substrates for both InP (1 0 0) and (3 1 1)B substrates showing the potential of self-organized anisotropic strain engineering combined with step engineering for the creation of advanced complex QD arrays and networks.     

Electron microscopy analysis of dislocation behavior in HVPE-AlGaN layer grown on a stripe-patterned (0 0 0 1) sapphire substrate

Microstructures were investigated by transmission electron microscopy (TEM) and scanning electron microscopy (SEM) in order to clarify the dislocation behavior in AlGaN layers HVPE-grown on a stripe-patterned sapphire (0 0 0 1) substrate. SEM observation revealed very clearly the growth process: if AlGaN starting to grow from the side-wall of patterned substrate develops, a poly-crystalline region is formed up to the top surface of thin film. When the growth from the upper side (terrace) of patterned substrate is predominant, AlGaN becomes a single-crystalline layer with a flat surface. Threading dislocations (TDs) generated from the interface to the terrace propagate upwards, inclining to the wing regions. They are scarcely merged with one another. The AlGaN layer on the patterned substrate with a wider groove has a smaller density of dislocation to be about 1×10⁹ cm⁻². There are four types of dislocations: (1) TDs inclining toward 〈1 1¯ 0 0〉 normal to their Burgers vector B; (2) TDs inclining toward 〈2 1¯ 1¯ 0〉 on their slip-plane; (3) TDs inclining largely or horizontal dislocations (HDs) along 〈2 1¯ 1¯ 0〉 and (4) roundly curved HDs lying on (0 0 0 1) plane. Some TDs change the direction of inclination, suggesting that internal stress changed intricately during the growth.     

Epitaxial growth of ZnO films on thin FeO(1 1 1) layers

Thin FeO(1 1 1) buffer layers prepared on Mo(1 1 0) substrate were used to grow ordered ZnO films under ultrahigh vacuum condition, and were in situ characterized by various surface analytical techniques. A chemical interaction between Zn (or ZnO) and FeO(1 1 1) can effectively lower the interfacial energy, which is in favor of an epitaxial growth of ZnO on FeO layers. Compared with the MgO(1 1 1) buffer layer used for the growth of ZnO(0 0 0 1) on sapphire (0 0 0 1) surface, the FeO(1 1 1) thin films might be a better one because it is more thermally stable. Our experimental results provide constructive information on the growth mechanism of ZnO-based materials, which is helpful for further understanding the growth mechanism of related oxide materials.     

Fabrication of (1 1 1)-oriented Si layers on SiO2 substrates by an aluminum-induced crystallization method and subsequent growth of semiconducting BaSi2 layers for photovoltaic application

We have prepared (1 1 1)-oriented Si layers on SiO₂ (fused silica) substrates from amorphous-Si(a-Si)/Al or Al/a-Si stacked layers using an aluminum-induced crystallization (AIC) method. The X-ray diffraction (XRD) intensity from the (1 1 1) planes of Si was found to depend significantly on growth conditions such as the thicknesses of Si and Al, deposition order (a-Si/Al or Al/a-Si on SiO₂), deposition technique (sputtering or vacuum evaporation) and exposure time of the Al layer to air before the deposition of Si. The crystal orientation of the Si layers was confirmed by θ−2θ, 2θ XRD and electron backscatter diffraction (EBSD). The photoresponse properties of semiconducting BaSi₂ films formed on the (1 1 1)-oriented Si layers by the AIC method were measured at room temperature. Photocurrents were clearly observed for photon energies greater than 1.25 eV. The external quantum efficiencies of the BaSi₂ were also evaluated.     

Maskless selective growth of semi-polar (1 12¯ 2) GaN on Si (3 1 1) substrate by metal organic vapor phase epitaxy

Semi-polar (1 1 2¯ 2) GaN layers were selectively grown by metal organic chemical vapor phase epitaxy on patterned Si (3 1 1) substrates without SiO₂ amorphous mask. The (1 1 2¯ 2) GaN layers could be selectively grown only on Si (1 1 1) facets when the stripe mask width was narrower than 1 μm even without SiO₂. Inhomogeneous spatial distribution of donor bound exciton (DBE) peak in low-temperature cathodoluminescence (CL) spectra was explained by the difference of growth mode before and after the coalescence of stripes. It was found that the emission intensity related crystal defects is drastically decreased in case of selective growth without SiO₂ masks as compared to that obtained with SiO₂ masks.     

Reduction of dislocations in a (1 1 2¯ 2)GaN grown by selective MOVPE on (1 1 3)Si

Two-step selective epitaxy (SAG/ELO) of (1 1 2¯ 2)GaN on (1 1 3)Si substrate is studied to reduce the defect density in the epitaxial lateral overgrowth. The first SAG/ELO is to prepare a (1 1 2¯ 2)GaN template on a (1 1 3)Si and the second SAG/ELO is to get a uniform (1 1 2¯ 2)GaN. It is found that the reduction of the defect density is improved by optimizing the mask configuration in the second SAG/ELO. The minimum dark spot density obtained is 3×10⁷/cm², which is two orders of magnitude lower than that found in a (0 0 0 1)GaN grown on (1 1 1)Si.