Fe-PILC在贫燃条件下催化丙烯选择性还原NO

采用羟基铁离子柱撑Na-Mont制备了铁柱撑黏土催化剂(Fe-PILC),铁物种作为柱撑成分,同时充当活性组分,研究其在贫燃条件下催化丙烯选择性还原NO的特性。通过XRD、N_2吸附-脱附、H_2-TPR、UV-vis、Py-FTIR等方法对催化剂进行物理化学性质表征,进一步研究其反应机理。研究表明,1.0Fe-PILC在450-600℃时NO的转化率超过98%,N_2的选择性可达97%以上,且抗水蒸气和SO_2的能力较强。XRD和N_2吸附-脱附研究表明,Fe-PILC中铁物种柱撑进入Na-Mont层间,使催化剂的比表面积和孔容增大。H_2-TPR研究表明,Fe-PILC在400℃左右还原能力较强,主要体现为Fe~(3+)→Fe~(2+)的还原。UVvis研究表明,Fe-PILC的脱硝活性与铁氧低聚物种FexOy呈正相关。Py-FTIR研究表明,Fe-PILC表面同时含有Lewis酸和Br■nsted酸性位,Lew is酸性位是C_3H_6与NO进行催化反应的主要活性中心。     

Cu改性Fe/Al-PILC催化剂的SCR-C3H6脱硝特性实验研究

为提高Fe/Al-PILC催化剂的SCR脱硝的低温活性,采用Cu对Fe/Al-PILC催化剂进行改性。采用超声浸渍法合成系列xCu-Fe/Al-PILC催化剂,通过XRD、N₂吸附-脱附、H₂-TPR、UV-vis、XPS、Py-FTIR等系列技术手段进行表征。在固定床微反应器上进行C₃H₆的选择性催化还原NO的实验。结果表明,经过铜改性后的xCu-Fe/Al-PILC催化剂有效解决了Fe/Al-PILC催化剂低温SCR活性不足的问题,同时提高了中高温活性。催化剂在200-500℃能够实现80%以上脱硝效率,其中,0.13Cu-Fe/Al-PILC在250-500℃实现了90%以上NO转化率,并在250℃达到最高脱硝效率93%。XRD、N₂吸附-脱附结果表明,经过铜改性的催化剂可以提供更多反应活性位,提高反应速率。H₂-TPR结果表明,掺杂铜使催化剂获得低温还原能力,同时增强了中高温还原能力。UV-vis、XPS结果表明,铜掺杂不仅使铁获得更高氧化态,同时产生了更多低温活性物质孤立Fe³⁺。Py-FTIR结果表明,催化剂表面同时存在Lewis酸和Brønsted酸,Lewis酸是SCR反应活性中心。     

Fe/Ti-PILC用于C_3H_6选择性催化还原NO的研究

采用二氧化钛对蒙脱土进行柱撑改性后,以离子交换法制备了铁负载二氧化钛柱撑蒙脱土催化剂Fe/Ti-PILC,考察了其在富氧条件下催化C_3H_6选择性还原NO(C_3H_6-SCR)的性能。并借助N_2等温吸附-脱附、XRD、UV-vis、H_2-TPR、Py-FTIR等表征方法研究了催化剂的结构与性能之间的关系。结果表明,所制备的19Fe/Ti-PILC催化剂在400℃时即可实现到NO的完全脱除,N2选择性能够达到90%以上。且具有较好的抗水蒸气和抗SO_2的能力。N_2吸附-脱附和XRD结果显示,蒙脱土的结构被撑开,交联柱撑有效,形成了较大的比表面积和孔体积。UV-vis结果表明,催化剂的脱硝活性与铁氧低聚物种FexOy的含量有关,Py-FTIR结果表明,催化剂表面同时存在Lewis酸和Brnsted酸,Fe~(3+)负载到柱撑黏土中能够显著增加Lewis酸的含量,Lewis酸是影响催化剂脱硝活性的影响因素之一。H_2-TPR表征表明,催化剂在400℃左右有较强的还原能力,催化剂的还原能力主要体现为Fe~(3+)→Fe~(2+)的还原。     

Fe/Al-PILC催化C_3H_6选择性还原NO的实验研究

采用浸渍法制备了负载于铝柱撑黏土的铁基催化剂(Fe/Al-PILC),在固定床反应器上测试其催化C3H6选择性还原NO的性能。通过N2吸附-脱附、X射线衍射(XRD)、H2的程序升温还原(H2-TPR)、紫外可见光谱(Uv-vis)、吡啶吸附红外光谱(Py-FTIR)等手段对催化剂的物理化学性质进行表征。结果表明,9Fe/Al-PILC在400-550℃能够还原98%以上的NO,而且SO2和水蒸气对其催化性能的影响很小。XRD、N2吸附-脱附表征结果表明,Fe/Al-PILC催化剂中铁氧化物高度分散在载体表面,催化剂有较大的比表面积和孔容。H2-TPR结果表明,催化剂的活性主要由Fe_2O_3物相的还原性能决定。Uv-vis结果表明,催化剂的活性与铁氧低聚物种FexOy呈正相关性。Py-FTIR结果表明,催化剂表面同时存在Lewis酸和Brnsted酸,L酸性位是NO和C3H6反应的主要催化活性中心。     

Ag对Fe/Al-PILC的SCR-C_3H_6脱硝特性的影响

为提高低温段(300℃)铝柱撑蒙脱土负载铁基催化剂的脱硝效率,采用银离子对其进行修饰。通过超声浸渍法合成银-铁双金属催化剂,并于固定床反应器中评价催化剂性能。结果表明,Ag的引入显著改善了Fe/Al-PILC催化剂的低温催化活性。在250℃时,Ag-Fe/Al-PILC催化剂的NO转化率达到60%以上,高于Fe/Al-PILC催化剂20%的NO的转化率,其中,2.1Ag-Fe/Al-PILC在250℃时NO转化率达到82%,N_2选择性达到100%。而且,引入银离子后的双金属催化剂保持了铁基催化剂较好的抗H_2O和SO_2性能。通过多种技术探究催化剂的微观结构和物理化学性质。根据N_2吸附-脱附测试结果表明,双金属催化剂形成了稳定的整体结构,并具有较大的内比表面积。同时,XRD和UV-vis表征结果显示,在催化剂表面形成的银-铁固溶体、Ag~+和Ag_n~(δ+)物种是影响其低温活性的关键因素。Ag-Fe/Al-PILC的低温活性与形成的银-铁固溶体有关,同时在催化剂表面形成的Ag~+和Ag_n~(δ+)物种是影响其低温活性的关键因素。XPS结果表明,Ag和Fe之间存在电子转移,形成了双金属协同作用,改变了催化剂表面的银、铁成分含量及其价态。H_2-TPR结果表明,Ag促使Fe/Al-PILC还原特征峰出现在低温区,提高了其低温还原性能。表面酸性的Py-FTIR分析结果表明,Ag-Fe/Al-PILC催化剂同时存在Lewis酸和Br?nsted酸,且Ag提高了Br?nsted酸的稳定性。     

CuMnCeLa-O/γ-Al2O3催化剂助燃脱硝性能研究

采用等体积浸渍法制备了Cu Mn-O/γ-Al_2O_3、Cu Mn Ce-O/γ-Al_2O_3和Cu Mn Ce La-O/γ-Al_2O_3催化剂.用XRD、BET、SEM、XPS和H_2-TPR技术对其物相和表面性质进行了表征.在连续固定床微反装置上评价了催化剂的CO+O_2和CO+NO反应性能.结果表明,催化剂样品中观测不到Cu O、Mn O_x、Ce O_2和La_2O_3的XRD晶相峰,活性组分在γ-Al_2O_3载体表面呈高度分散状态.Ce、La的引入对催化剂的比表面积、孔容和孔径分布影响不大.SEM谱图中未观测到活性组分的形貌,金属氧化物在载体表面均匀分布.Ce~(3+)!Ce~(4+)之间的可变价转换,引起Cu Mn Ce-O/γ-Al_2O_3催化剂表相Cu O中具有非完整结构的[Cu~(2+)_(1-x)Cu_x~+][O_(1-2)1_x□1_(2x)]增多,Cu~+/Cu~(2+)比例增大,表相氧空位增多,H_2-TPR还原峰温度向低温区偏移.Ce~(4+)、La~(3+)之间不平衡电荷以及共生过程中Cu-Mn-Ce-La-O之间的强相互作用,加大了Cu O和Mn O_x结构的不完整性,导致Cu Mn Ce La-O/γ-Al_2O_3催化剂样品表相产生更多的Cu~+、Mn~(2+)、Mn~(3+)和氧空位,相应的H_2-TPR还原峰温度进一步向低温区偏移.催化氧化CO和CO催化还原NO实验结果表明,在反应空速20 000 h~(-1),350℃反应温度下,Cu Mn Ce La-O/γ-Al_2O_3催化剂CO催化还原NO反应的CO转化率达到88.2%,NO转化率达到了96.1%,表现出了较好的氧化还原活性.     

自蔓延高温燃烧合成法制备CeWTiO_x催化剂及其NH_3-SCR性能

采用自蔓延高温燃烧合成法制备了CeWTiO_x系列催化剂并考察了其氨选择性催化还原NO_x(NH_3-SCR)性能。利用X射线衍射、N_2吸附-脱附、H_2程序升温还原、X射线光电子能谱、NH_3程序升温脱附表征和分析了催化剂晶相、结构、氧化还原能力和酸性强度与其活性之间的关系。结果表明,Ce_(40)W_(10)TiO_x催化剂在150-430℃NO转化率可达80%以上,含硫条件下200℃NO转化率可保持在97%左右。结果表明,该催化剂的低温活性和抗硫性能主要与W的掺杂有关。钨的存在减弱了Ce-O键的强度,降低了CeO2的结晶度和减小了晶粒粒径,增加了催化剂表面活性氧含量和酸量,提高了其性能。     

MnO2-CeO2/Ti0.25Zr0.25Al0.5O1.75整体式催化剂的低温NH3选择性催化还原NO性能研究

采用共沉淀法制备了TiO2、Ti0.5Zr0.5O2(TZ)和Ti0.25Zr0.25Al0.5O1.75载体材料,并以MnO2和CeO2为活性组分,以T、TZ和TZA为载体,制备了3种整体式催化剂.对催化剂进行了低温N2吸附脱附、储氧量(OSC)、NH3-TPD和XPS的表征,并研究了3种催化剂在过量O2存在下的低温NH3-选择催化还原(NH3-SCR)活性及其抗H2O和SO2性能.结果指出,MnO2-CeO2/Ti0.25Zr0.25Al0.5O1.75(TZAC)有最大的比表面积、孔容和储氧能力、最强的表面酸性和最大的表面酸量.而这对选择催化还原(SCR)反应至关重要.活性测试结果指出,TZAC有最好的低温SCR活性和最宽的活性温度窗口.NO在102℃起燃(转化率为50%),在175～325℃之间NO转化率接近100%,而且TZAC表现出了较强的抗H2O和SO2性能.     

Ag对Pd/CeO2-ZrO2-La2O3-Al2O3催化氧化甲醇性能的影响

采用等体积共浸渍法制备了一系列Pd-Ag/CeO2-ZrO2-La2O3-Al2O3催化剂。运用N2吸附-脱附,X射线衍射(XRD),H2程序升温还原(H2-TPR),紫外-可见漫反射光谱(UV-Vis DRS),X射线光电子能谱(XPS)对催化剂进行表征,并考察其对甲醇的催化氧化性能。活性测试结果表明,Ag的添加可显著改善Pd催化剂对甲醇的催化氧化活性,T50、T90以及ΔT分别为125℃,150℃和25℃,具有较好的应用前景。H2-TPR表明,引入Ag可明显改善催化剂的还原性能,使表面易还原氧物种量增多,还原速率加快;UV-Vis DRS及XPS表明,Pd、Ag金属之间以及金属与载体之间存在电子效应,这种效应促使金属与载体界面产生大量具有活性的氧物种,不仅提高了催化剂的低温活性,还提高了催化剂的氧化速率。     

过渡金属对选择性催化还原脱硝CeO_2@TiO_2催化剂低温活性的促进作用

采用过渡金属M(M=Mn、Co、Fe和Cu)掺杂改性自发沉积策略制备的非晶态CeO_2@TiO_2催化剂,考察M-CeO_2@TiO_2选择性催化还原NO_x的低温活性,并通过XRD、TEM、N2吸附-脱附、H2-TPR、NH3-TPD及in-situ FT-IR等表征手段研究M-CeO_2@TiO_2的结构、表面性质以及低温NH3-SCR反应过程。结果表明,M-CeO_2@TiO_2具有更优异的低温氧化还原能力以及更多的表面酸量,且Cu掺杂对CeO_2@TiO_2选择性催化还原NO_x低温活性具有最为显著的促进作用。Cu-CeO_2@TiO_2催化剂在低温NH3-SCR反应过程中同时存在E-R机理和L-H机理,但是由于"快速SCR"使得L-H机理反应起关键作用。     

Chromium(III) Hydroxide Solubility in The Aqueous Na+-OH?-H2PO?4-HPO2?4-PO3?4-H2O System: A Thermodynamic Model

Chromium(III)-phosphate reactions are expected to be important in managing high-level radioactive wastes stored in tanks at many DOE sites. Extensive studies on the solubility of amorphous Cr(III) solids in a wide range of pH (2.8–14) and phosphate concentrations (10^–4 to 1.0 m) at room temperature (22±2)°C were carried out to obtain reliable thermodynamic data for important Cr(III)-phosphate reactions. A combination of techniques (XRD, XANES, EXAFS, Raman spectroscopy, total chemical composition, and thermodynamic analyses of solubility data) was used to characterize solid and aqueous species. Contrary to the data recently reported in the literature,⁽¹⁾ only a limited number of aqueous species [Cr(OH)₃H₂PO^–₄, Cr(OH)₃(H₂PO₄)^2–₂), and Cr(OH)₃HPO^2–₄] with up to about four orders of magnitude lower values for the formation constants of these species are required to explain Cr(III)-phosphate reactions in a wide range of pH and phosphate concentrations. The log K^o values of reactions involving these species [Cr(OH)₃(aq)+H₂PO^–₄⇌Cr(OH)₃H₂PO^–₄; Cr(OH)₃(aq)+2H₂PO^–₄⇌Cr(OH)₃(H₂PO₄)^2–₂; Cr(OH)₃(aq)+HPO^2–₄⇌Cr(OH)₃HPO^2–₄] were found to be 2.78±0.3, 3.48±0.3, and 1.97±0.3, respectively.     

CCl2自由基被无机小分子猝灭的速率常数

对CCl4/Ar混合气体脉冲直流高压放电产生CCl2自由基,用541.52 nm激光将电子基态CCl2激励到A 1B1(0,4,0)振动能级上. 通过检测激发态CCl2时间分辨荧光信号,测得室温下CCl2(A 1B1和a 3B1)被O2、N2、NO、 CO2、 CS2、H2O、SO2,和SF6分子猝灭的实验结果.用我们提出的三能级模型分析处理实验数据,获得了CCl2(A 1B1)态和CCl2(a 3B1)态的碰撞猝灭速率常数kA和ka值.     

CCl2(A 1B 1,a3B1)自由基被烷烃类分子猝灭动力学

用放电 LIF实验装置,对CCl4/Ar混合气体放电产生CCl2自由基,再用541.52 nm激光将电子基态CCl2激励到激发态A 1B1(0,4,0)振动能级上,通过检测激发态CCl2时间分辨荧光信号,测得室温下CCl2(A 1B1)被烷烃类分子猝灭的实验结果,用我们提出的三能级模型分析处理实验数据,获得CCl2(A 1B1)态和CCl2(a 3B1)态的碰撞猝灭速率常数kA和ka值.     

Eu3+离子在Ca2PbO4一维结构基质中的发光研究

A Eu³⁺-doped Ca₂PbO₄ with one-dimensional structure was prepared with a solid-state reaction method and its characteristics were investigated. The XRD results show that the substitution of Ca²⁺ by Eu³⁺ has no influence on the structure of Ca₂PbO₄. Under the excitation of ultraviolet light， the Ca₂PbO₄:Eu³⁺ phosphor exhibits strong red emission at about 618 nm which is assigned to the ⁵D₀- ⁷F₂ electric-dipole transition. The compounds Sr₂CeO₄ and Ca₂SnO₄ have the same crystal symmetry as that of Ca₂PbO₄ and it is found that the emission intensity of Ca₂PbO₄∶Eu³⁺ is higher than that of Sr₂CeO₄∶Eu³⁺ and lower than that of Ca₂SnO₄∶Eu³⁺. The excitation spectrum of Ca₂PbO₄∶Eu³⁺ appears to be a broad band with two peaks at about 289 nm and 340 nm. The former peak is attributed to the Eu³⁺-O₂- charge transfer transition， while the latter one may be related to the absorption of Ca₂PbO₄ host or its crystal defects.     

纳米微孔NixZn(1-x)Fe2O4的水热合成研究

０引言尖晶石型铁酸盐是一类重要的磁性材料，它可用于防止电磁波辐射设备以及隐身材料中的吸波剂犤１，２犦，具有价格低廉、吸波性能优良的特点。同时尖晶石型铁酸盐也是一类重要的催化剂，９０年代初又发现了氧缺位的该类化合物具有将CO２还原为C的优良催化性能犤３犦。因此，有关铁酸盐的制备及性能研究一直是化学工作者和材料科学工作者感兴趣的领域。随着新的合成方法的不断涌现，对传统铁氧体材料进行结构改造以提高其性能是一个重要的研究发展方向，本文采用模板剂造孔技术，首次在NixZn（１－x）Fe２O４水热合成中选用模板剂，…     

Ti掺杂对(LaMn1-xTixO3)0.67(NiMn2O4)0.33(0≤x≤0.7)陶瓷材料微结构及电性能影响

采用氧化物固相法制备(LaMn1-xTixO3)0.67(NiMn2O4)0.33系列NTC(Negative temperature coefficient)复合热敏电阻材料。利用TG/DSC、激光粒度分析、XRD、SEM、阻-温特性和老化性能测试等手段,确定了粉体煅烧温度,表征了粉体的颗粒尺寸、陶瓷体的物相、形貌及其电学特性、稳定性等与Ti掺杂量的关系。结果表明:在1 200~1 300℃烧结温度范围内,(LaMn1-xTixO3)0.67(NiMn2O4)0.33复合体系的电阻率ρ25℃随Ti含量的增加而显著增加;电阻率ρ25℃和B值变化范围分别为4.4~53 179Ω.cm、1 357~3 998 K。125℃下老化1 000 h阻值变化率ΔR/R0均小于0.51%。该复合体系电阻率、B值调整范围较大,稳定性好,是一种具有实际应用价值的NTC热敏电阻材料。     

Ba0.98Bi0.02(Ti0.9Zr0.1)1-xCuxO3陶瓷的介电性能、弛豫行为与结晶化学特性

采用固相合成法,Bi3+作施主掺杂A位,Cu2+作受主掺杂B位,制备了Ba0.98Bi0.02(Ti0.9Zr0.1)1-xCuxO3(x=0,0.01,0.02,0.03)陶瓷样品。借助XRD、LCR等研究了该陶瓷的结构与介电性能。结果表明:当x=0.03时,陶瓷样品出现第二相。通过GULP模拟,缺陷偶极子的稳定性从低到高依次为:[2BiBa.+VBa″]、[2BiBa.+CuTi/Zr″]、[CuTi/Zr″+VO..],结合实验可知:介电弛豫程度与晶体中缺陷偶极子的存在形式相关,其中x=0.01时,晶体中以[2BiBa.+CuTi/Zr″]为主。随Cu2+掺杂量的增加,介电常数增加,介电常数与B位键价和呈反比变化、与八面体BO6的体积呈正比变化。     

Ba0.98Bi0.02(Ti0.9Zr0.1)1-xCuxO3陶瓷的介电性能、弛豫行为与结晶化学特性

采用固相合成法, Bi3+作施主掺杂A位, Cu₂₊作受主掺杂B位, 制备了Ba_0.98Bi_0.02(Ti_0.9Zr_0.1)_1-xCu_xO₃(x=0, 0.01, 0.02, 0.03)陶瓷样品。借助XRD、LCR等研究了该陶瓷的结构与介电性能。结果表明:当x=0.03时, 陶瓷样品出现第二相。通过GULP模拟, 缺陷偶极子的稳定性从低到高依次为:[2Bi_Ba^·+V_Ba"]、[2Bi_Ba^·+Cu_Ti/Zr"]、[Cu_Ti/Zr"+V_O^··], 结合实验可知:介电弛豫程度与晶体中缺陷偶极子的存在形式相关, 其中x=0.01时, 晶体中以[2Bi_Ba^·+Cu_Ti/Zr"]为主。随Cu₂₊掺杂量的增加, 介电常数增加, 介电常数与B位键价和呈反比变化、与八面体BO₆的体积呈正比变化。     

xLi2MnO3-(1-x)LiNi0.7Co0.3O2的低温燃烧合成及电化学性能研究

采用低温燃烧法合成了锂离子电池正极材料xLi₂MnO₃-(1-x)LiNi_0.7Co_0.3O₂,对合成产物的结构、形貌和电化学性能进行了系统的研究, 通过单因素试验对合成条件和材料的组成进行了优化。结果表明:采用低温燃烧法合成的富锂层状正极材料具有α-NaFeO₂型层状结构、球状形貌和良好的电化学性能;其最佳合成条件为:回火温度850℃, 回火时间20 h;Li₂MnO₃的最佳配比为x=0.7.在此条件下合成的0.7Li₂MnO₃-0.3LiNi_0.7Co_0.3O₂,最高放电比容量达到263.1 mAh·g^-1,并具有良好的循环性能和倍率性能。     

SnO_2改性TiO_2对V_2O_5-WO_3/TiO_2催化剂结构和SCR性能影响

采用共沉淀法将SnO_2组分掺入到V_2O_5-WO_3/TiO_2催化剂载体TiO_2中,并通过多种物理化学手段,考察了不同SnO_2掺入量时对催化剂结构,表面分散物种和SCR性能影响.结果表明,SnO_2掺入到TiO_2中,元素Sn与Ti以Sn—O—Ti键形式相互作用,促进锐钛矿型TiO_2向金红石型TiO_2转变.在特定条件下,VO_x与WO_x物种和SnTi氧化物之间以V—O—Ti(Sn)和W—O—Ti(Sn)键形式相互作用,提高了VO_x物种可还原能力、促进了具有更多B酸酸量四面体WOx物种和V~(5+)物种生成.VW/SnTi催化剂表面VO_x物种与WO_x物种之间的相互作用更强.因此,VW/SnTi催化剂具有更好的SCR活性.