CNT/Fe-Ni/TiO_2/ZnO阵列修饰Ni阳极的制备及光催化制氢性能

采用层层自组装方法在Ni片阳极上构建TiO2/Zn O纳米棒阵列,以二氧化钛前驱体溶胶中掺杂的铁和镍为催化剂,通过气相沉积法在TiO2/Zn O纳米棒阵列间原位生长碳纳米管(CNTs),得到CNT/Fe-Ni/TiO2/Zn O复合光催化剂修饰的光活性Ni片阳极.以碱性电解池为基础,用紫外线辐照修饰的Ni阳极实现光催化和电解水的有机耦合制氢过程.通过场发射扫描电子显微镜(FESEM)、透射电子显微镜(TEM)、拉曼光谱(Raman)和电化学阻抗谱(EIS)对CNT/Fe-Ni/TiO2/Zn O复合膜光催化剂的结构进行了表征,并测试了其光催化辅助电解水制氢(WEAP)活性.结果表明,生长了碳纳米管的光催化复合膜CNT/Fe-Ni/TiO2/Zn O修饰的Ni阳极的产氢速率分别比Fe-Ni/TiO2/Zn O修饰的Ni阳极和纯Ni片提高了93.7%和533.0%.     

过渡金属掺杂和碳纳米管（CNT）接枝双重改性TiO2光催化剂

提出了一种过渡金属掺杂和碳纳米管(CNT)双重改性TiO2的新方法:首先采用溶胶-凝胶法合成掺杂镍和铁的二氧化钛基催化剂,然后采用流化床化学气相沉积方法(FBCVD)在二氧化钛基催化剂表面接枝生长CNT,得到CNT/Fe-Ni/TiO2复合光催化剂.通过X射线衍射、扫描电子显微镜、比表面分析、拉曼光谱、紫外-可见吸收光谱、荧光光谱等方法考察了双重改性复合光催化剂CNT/Fe-Ni/TiO2的结构和性能,通过降解亚甲基蓝溶液评价了双重改性复合光催化剂的活性.结果表明,在TiO2表面接枝的CNT具有较好的石墨化结构,CNT生长过程中小部分TiO2由锐钛矿向金红石晶型转变.过渡金属和CNT双重改性有效地克服了TiO2的比表面积小、量子效率低等缺点,明显提高了TiO2的光催化活性.     

氟掺杂纳米 TiO2 薄膜的低温制备及其光催化性能

 以氟化铵为氟源, 采用水热法制得氟掺杂 TiO2 (FTO) 溶胶, 并通过浸渍提拉法在低温下制备了 FTO 薄膜. 其中在 120 oC 下水热处理 10 h 所得的 TiO2 溶胶制备的薄膜均匀透明, 具有较高的光催化活性. 氟掺杂后的 TiO2 晶粒尺寸并未发生明显变化, 但薄膜的光催化活性显著升高. F/Ti 摩尔比为 0.01 时, FTO 薄膜的光催化活性最高, 比 TiO2 薄膜的活性升高了 23%. X 射线光电子能谱结果表明, 氟掺杂 TiO2 中的氟离子存在晶格取代掺杂和表面化学吸附两种形式. 这两种氟离子的共同作用是 FTO 薄膜光催化活性升高的主要原因.     

Fe-Ni 共掺杂 ZnO 的制备及其光催化降解甲基橙活性

 采用溶液法制备了 Fe-Ni 共掺杂 ZnO 光催化剂, 并运用 X 射线衍射、扫描电镜和原子发射光谱等对催化剂进行了表征. 以甲基橙 (MO) 为模型污染物, 评价了样品的光催化活性, 考察了甲基橙初始浓度及其 pH 值, 以及催化剂用量等对光催化反应性能的影响. 结果表明, Fe-Ni 共掺杂降低了 ZnO 的结晶度, 并促进了晶粒的长大. 光催化降解反应表明, Fe-Ni 共掺杂显著提高了 ZnO 光催化降解甲基橙的活性, 当催化剂用量为 0.6 g/L, 经 120 min 紫外光照射时, 可使甲基橙溶液 (10 mg/L) 降解率达到 93.5%. 关键词：铁; 镍; 共掺杂; 氧化锌; 光催化; 甲基橙; 降解     

Gd掺杂TiO2/活性炭纤维复合材料的制备及表征

以TiCl4和Gd(NO3)3·6H2O为主要原料,采用酸催化水解法制备Gd掺杂TiO2光催化剂并通过浸涂法将其负载在活性炭纤维(ACF)表面,制得Gd掺杂TiO2/ACF复合材料。 以气相苯为模型物,考察材料的光催化活性。 利用XRD、FTIR及GC-MS对催化剂的晶相结构、光谱特征等进行了表征。 结果表明,Gd掺杂能有效抑制TiO2的晶粒生长。 Gd掺杂量、浸涂次数影响TiO2/ACF光催化活性,Gd2O3掺杂质量分数为0.48%、浸涂2次的TiO2/ACF活性最高。 在苯光催化氧化后的Gd掺杂TiO2/ACF复合材料表面未发现醌类中间产物的存在。 Gd的掺入能减缓催化剂失活,光催化反应100 min后仍能表现出较高活性。     

Sn4+掺杂对TiO2纳米颗粒膜光催化降解苯酚活性的影响

金属离子掺杂能改善TiO2纳米微粒光催化活性,在光降解大气和水污染物的研究中,已引起人们的重视[1,2].实验证明,掺杂物的浓度、掺杂离子的分布、掺杂能级与TiO2能带匹配程度、掺杂离子d电子的组态、电荷的转移和复合等因素对催化剂的光催化活性有直接影响[3].Kamat等[4]曾利用TiO2颗粒与SnO2颗粒混合制膜,使光催化剂活性得到提高.但Sn4+掺杂TiO2用于光催化剂尚少见报道.本文采用等离子体化学气相沉积法(PECVD)[5]制备了Sn4+离子掺杂的TiO2纳米颗粒膜催化剂(TiO2-Sn),考察了其对苯酚的光催化降解活性,讨论了Sn4+离子的掺杂方式及光催化活性提高的机理.     

Gd掺杂TiO2/活性炭纤维复合材料的制备及表征

以TiCl4和Gd(NO3)3·6H2O为主要原料,采用酸催化水解法制备Gd掺杂TiO2光催化剂并通过浸涂法将其负载在活性炭纤维(ACF)表面,制得Gd掺杂TiO2/ACF复合材料。 以气相苯为模型物,考察材料的光催化活性。 利用XRD、FTIR及GC-MS对催化剂的晶相结构、光谱特征等进行了表征。 结果表明,Gd掺杂能有效抑制TiO2的晶粒生长。 Gd掺杂量、浸涂次数影响TiO2/ACF光催化活性,Gd2O3掺杂质量分数为0.48%、浸涂2次的TiO2/ACF活性最高。 在苯光催化氧化后的Gd掺杂TiO2/ACF复合材料表面未发现醌类中间产物的存在。 Gd的掺入能减缓催化剂失活,光催化反应100 min后仍能表现出较高活性。     

TiO2-石墨烯光催化剂：制备及引入石墨烯的方法对光催化性能的影响

利用溶胶-凝胶法原位制备了二氧化钛/石墨烯(TiO2-GE)复合光催化剂,研究了纯TiO2以及不同方法制备的TiO2-GE复合光催化剂对亚甲基蓝及罗丹明B光催化降解性能。结果表明:石墨烯的引入提高了TiO2的光催活性,这主要是得益于石墨烯优异的电子传输性能及较好吸附特性。不同方法制备TiO2-GE复合催化剂的光催化活性也存在较大差别。原位制备的TiO2-GE复合光催化剂表现出最佳的光催化活性。     

SO42-/TiO2-WO3光催化氧化邻硝基苯酚

采用不同浓度的硫酸溶液浸渍处理TiO2-WO3,制得不同SO42-/TiO2-WO3光催化剂.考察了光催化剂对邻硝基苯酚溶液的光催化行为.发现SO42-/TiO2-WO3的光催化活性高于TiO2-WO3的光催化活性,浸渍液中H2SO4的浓度对SO42-/TiO2的催化活性有一定的影响,H2SO4溶液的最佳浓度为0.2 mol/L,最佳焙烧温度为550℃.最佳WO3的掺杂量w(WO3)为3%.催化降解过程符合一级动力学规律.     

Sm掺杂对TiO2薄膜光催化性能的影响

 采用溶胶-凝胶法、浸渍-提拉法制备了不同形式和不同含量Sm掺杂的锐钛矿晶型TiO2的光催化剂薄膜. 采用X射线衍射、UV-Vis光谱及电化学实验对所制得的TiO2光催化剂薄膜进行了表征,并通过甲基橙溶液的光催化降解实验评价了其光催化活性. 结果表明,与未掺杂的TiO2薄膜相比,Sm掺杂的TiO2薄膜的UV-Vis吸收光波长向长波方向移动,并且光照开路电压也相应提高; 适量Sm掺杂可以明显提高TiO2薄膜的光催化活性,最佳Sm掺杂量为x(Sm3+)=0.5%; 在各种掺杂形式中以表层Sm掺杂的Sm-TiO2(S)薄膜的光催化活性最好. 讨论了Sm掺杂提高TiO2薄膜光催化活性的机理.     

Co~(2+)掺杂的纳米TiO_2薄膜光催化特性及电化学阻抗谱研究

本文采用交流电沉积技术,在多孔氧化铝模板中合成出Co2+掺杂的纳米TiO2薄膜(Co2+/TiO2薄膜)。以次甲基蓝为降解物,研究了纳米Co2+/TiO2薄膜在可见光下的催化性能,考察了阳极偏压对光催化活性的影响。用电化学阻抗谱(EIS)研究了纳米Co2+/TiO2薄膜在次甲基蓝溶液中的电化学行为,给出了相应的等效电路和半导体能带结构参数-空间电荷层宽度。研究表明,适量Co2+掺杂可以提高TiO2薄膜的光催化活性。在Co2+/TiO2膜电极上施加一定阳极偏压,使空间电荷层宽度增加,因此能有效实现光生电子-空穴分离,进一步提高次甲基蓝的光催化降解效率。     

Preparation and characterization of porous TiO_2/ZnO composite nanofibers via electrospinning

<正>Porous TiO_2/ZnO composite nanofibers have been successfully prepared by electrospinning technique for the first time.It was generated by calcining TiO_2/ZnCl_2/PVP[PVP:polyvinyl pyrrolidone)]nanofibers,which were electrospun from a mixture solution of TiO_2,ZnCl_2 and PVP.Transmission electron microscopy(TEM) and X-ray diffraction(XRD) analyses were used to identify the morphology of the TiO_2/ZnO nanofibers and a formation of inorganic TiO_2/ZnO fibers.The porous structure of the TiO_2/ZnO fibers was characterized by N_2 adsoption/desorption isotherm.Surface photovoltage spectroscopy(SPS) and photocatalytic activity measurements revealed advance properties of the porous TiO_2/ZnO composite nanofibers and the results were compared with pure TiO_2 nanofibers,pure ZnO nanofibers and TiO_2/ZnO nanoparticles.     

TiO2/LaFeO3微纳米纤维的可控制备及光催化性能简

利用静电纺丝技术及水热合成法制备了TiO2/LaFeO3异质结构. 采用场发射扫描电子显微镜(FE-SEM),X射线衍射(XRD),傅里叶变换红外(FTIR)光谱和紫外-可见漫反射光谱(UV-Vis)等手段对TiO2/LaFeO3微纳米纤维的结构和表面形态进行表征. 通过亚甲基蓝(MB)光降解反应研究了其光催化性能. 结果表明,不完全碳化TiO2纤维表面的缺陷位点是LaFeO3纳米粒子的有利生长点. TiO2/LaFeO3异质结材料的带隙明显窄于TiO2,光催化活性得到提高;经140 min紫外光照射后,TiO2/LaFeO3异质结催化剂对MB的降解率为65.34%,分析和探讨了其光催化机理.     

三维有序大孔杂化材料3DOM PW11Ni-APS-TiO2紫外光催化降解罗丹明B

采用甲醇法制备三维有序大孔结构(3DOM)TiO2,再经过有机胺(EtO)3Si(CH2)3NH2(APS)功能化修饰后,通过自组装技术将取代型杂多酸盐K5[Ni(H2O)PW11O39](PW11Ni)与其负载,从而制备了三维有序大孔取代型多金属氧酸盐-有机胺-TiO2杂化催化剂3DOM PW11Ni-APS-TiO2。通过FT-IR,ICP-AES,XRD,UV-Vis/DRS, XPS和SEM等测试手段对其组成、结构和形貌等进行了表征,结果表明,通过自组装技术将APS功能化修饰的3DOM TiO2与杂多酸盐PW11Ni负载后,该杂多酸盐PW11Ni通过Ni-N配位键与3DOM TiO2键合。同时,所制备的3DOM PW11Ni-APS-TiO2具有TiO2锐钛矿结构,且该合成产物由于模板剂聚苯乙烯(PS)胶球的作用呈现着规则、有序和开放性的三维有序大孔结构,其通透性的孔结构十分有利于反应过程中反应物和产物分子的扩散。紫外光催化降解罗丹明B实验结果表明,3DOM PW11Ni-APS-TiO2的紫外光催化降解活性明显高于直接光解和其他对比体系。     

TiO2纳米管阵列覆盖Si薄膜光催化还原CO2性能的研究

本工作采用CVD法在阳极氧化TiO2纳米管阵列膜表面沉积一层非晶Si膜,通过退火后得到晶化了的Si膜/TiO2纳米管阵列的复合结构,并初步就其光催化还原CO2制备碳氢化合物的活性进行研究。拉曼光谱(Raman)、X射线衍射(XRD)、场发射扫描电镜(FE-SEM)、高分辨透射电子显微镜(TEM)等微结构表征结果表明所制备的TiO2纳米管阵列的厚度为270 nm左右,管直径约为70 nm,管壁厚度约为16 nm。覆盖的Si膜已晶化,其厚度约为300 nm。通过高效液相色谱(HPLC)及总有机碳(TOC)来检测光催化还原液相产物中的甲酸及总有机碳含量,发现负载Si膜后的TiO2纳米管阵列光催化性能有所提高,在装有400cut滤光片氙灯照射2 h下TOC含量从21.2 mg.L-1增长到29.5 mg.L-1,表明Si与TiO2的复合可有效的提高光催化还原CO2的活性,这可能与该异质结结构可增加对光的吸收并且可降低光生空穴-电子对复合有关。光催化循环实验表明所制得的催化剂在循环5次后仍可保持91.6%的催化活性。     

Ag2S/Ag3PO4/Ni复合薄膜的制备及其光催化性能

采用电化学方法制备Ag_2S/Ag_3PO_4/Ni复合薄膜,以扫描电子显微镜(SEM)、X射线衍射(XRD)、紫外-可见漫反射光谱(UVVis DRS)对薄膜的表面形貌、晶相结构、光谱特性及能带结构进行了表征,以罗丹明B为模拟污染物对薄膜的光催化活性和稳定性进行了测定,采用向溶液中加入活性物种捕获剂的方法对薄膜的光催化机理进行了探索。结果表明:最佳工艺制备的Ag_2S/Ag_3PO_4/Ni是由均匀的球形纳米颗粒构成的薄膜,其光催化活性明显优于纯Ag_3PO_4/Ni薄膜和纯Ag_2S/Ni薄膜,且在保持薄膜光催化活性基本不变的前提下可循环使用6次。提出了可见光下Ag_2S/Ag_3PO_4/Ni复合薄膜光催化降解罗丹明B的反应机理。     

Ag2S/Ag3PO4/Ni复合薄膜的制备及其光催化性能

采用电化学方法制备Ag₂S/Ag₃PO₄/Ni复合薄膜,以扫描电子显微镜（SEM）、X射线衍射（XRD）、紫外-可见漫反射光谱（UV-Vis DRS）对薄膜的表面形貌、晶相结构、光谱特性及能带结构进行了表征,以罗丹明B为模拟污染物对薄膜的光催化活性和稳定性进行了测定,采用向溶液中加入活性物种捕获剂的方法对薄膜的光催化机理进行了探索。结果表明：最佳工艺制备的Ag₂S/Ag₃PO₄/Ni是由均匀的球形纳米颗粒构成的薄膜,其光催化活性明显优于纯Ag₃PO₄/Ni薄膜和纯Ag₂S/Ni薄膜,且在保持薄膜光催化活性基本不变的前提下可循环使用6次。提出了可见光下Ag₂S/Ag₃PO₄/Ni复合薄膜光催化降解罗丹明B的反应机理。     

多酸修饰二氧化钛纳米管复合膜的制备、表征及其光催化降解甲基橙的研究

采用电沉积方法制备了H3PW12O40(PW12)-TiO2复合膜,通过SEM,EDX和XRD等手段,对其组成和结构进行了表征,并考察了该复合膜催化剂对降解甲基橙的催化活性.实验结果表明PW12存在于TiO2纳米管结构中,用PW12多酸修饰的TiO2纳米管比单独的TiO2纳米管展示出更好的光催化性能,由于电子能够从TiO2纳米管导带转移到多酸的LUMO能级,有效抑制了光生电子和空穴的复合,因而使PW12-TiO2复合膜表现出更高的光催化活性.     

玻璃微珠/Ag/TiO2可见光催化剂的制备与表征

通过离子交换法将Ag纳米颗粒负载于玻璃微珠的表面及浅表层,并以钛酸四丁酯的乙醇溶液为前驱体,将TiO₂负载于包含银的玻璃微珠表面,制得一种玻璃微珠/Ag/TiO₂复合光催化剂。由于纳米银的表面等离子体吸收效应,该复合光催化剂具有一定的可见光响应特性。利用XRD、SEM对样品进行表征,可发现玻璃微珠表面形成一层均匀多孔的锐钛矿TiO₂,其粒径均在50 nm左右。由漫反射光谱可得出该催化剂具有较强的可见光吸收,并在降解甲基橙溶液的试验中表现出较好的可见光催化活性。