CaO-MgO-Al2O3-SiO2-P2O5-(F)微晶玻璃的析晶及特征

采用熔融法制备了不同P2O5及F含量的CaO-MgO-Al2O3-SiO2-P2O5-(F)基础玻璃试样,研究了CaO-MgO- Al2O3-SiO2-P2O5-(F)系微晶玻璃的析晶及特征.结果表明:在CaO-MgO-Al2O3-SiO2-8.0wt;P2O5玻璃中,表面析晶和内部析晶同时存在,析出晶体主要为钙长石(CaAl2Si2O8)相、硅灰石(CaSiO3)和α-磷酸钙(Ca3(PO4)2).玻璃中P2O5含量的提高抑制玻璃的表面析晶,同时促进了玻璃的整体析晶和α-磷酸钙晶体析出.同时添加P2O5和F的玻璃试样以整体析晶为主,析出晶体为块状氟磷灰石和粒状钙长石相.     

高热膨胀Na2O-MgO-Al2O3-SiO2微晶玻璃的制备及性能研究

采用传统熔体冷却法制备了Na2O-MgO-Al2 O3-SiO2玻璃并采用整体析晶工艺制备了微晶玻璃.利用DSC、XRD、SEM等测试手段研究了微晶玻璃的析晶行为和显微结构,探讨了热处理制度对该体系微晶玻璃热膨胀系数、密度、抗弯强度、显微硬度等性能的影响.研究结果表明,当晶化温度为800℃时该体系微晶玻璃主晶相为颗粒状霞石晶体(NaAlSiO4);当晶化温度达到900℃时玻璃中开始析出镁橄榄石(Mg2SiO4)晶体;延长保温时间可显著促进析晶但对晶体种类没有影响.析晶后微晶玻璃的密度、热膨胀系数、抗弯强度和显微硬度值显著增加,其最高热膨胀系数可达14.1×10-6℃-1.所制备的微晶玻璃具有很好的机械性能,当热处理温度为1000℃时,其抗弯强度和显微硬度分别达160 MPa和7.8 GPa.     

Fe2O3掺杂对MgO-Al2O3-SiO2系玻璃析晶和性能的影响

采用高温熔融法和两步法微晶热处理制备了MgO-Al2O3-SiO2系堇青石微晶玻璃和铁尖晶石微晶玻璃.利用DSC分析、X射线衍射、FTIR和扫描电子显微镜等手段研究了Fe2O3对玻璃的析晶性能、显微结构和物理性能的影响.结果表明,Fe2 O3的加入可有效降低析晶活化能,促进晶体的析出.当Fe2O3含量达到7.44;时,主晶相由堇青石变为铁尖晶石.Fe2O3掺杂使样品的介电常数由3.2增大至5.8、热膨胀系数由1.941× 10-7增大至7.74×10-6、维氏硬度由7.131GPa增大至11.655 GPa,同时介电损耗由0.05降低至0.015.     

烧结法制备高炉渣CMAS系统微晶玻璃的研究

利用高炉渣及其它辅助原料制备基础玻璃,采用一步烧结法制备主晶相为辉石的CaO-MgO-Al2O3-SiO2(CMAS)微晶玻璃.综合运用DSC,XRD以及场发射扫描电子显微镜等测试手段,分析热处理制度对高炉渣CMAS微晶玻璃的析晶行为及性能的影响.结果表明:随着热处理温度上升,微晶玻璃的主晶相均为辉石,次晶相均为长石,晶相析出量增加,微晶玻璃的体积密度及抗折强度均呈现先增后减趋势.随着热处理时间增加,微晶玻璃的体积密度及抗折强度均呈现下降趋势.当热处理温度为1020 ℃,晶化时间30 min时,样品的机械性能最好,体积密度为2.690 g·cm-3,抗折强度为67.00 MPa.     

TiO2和Cr2O3作晶核剂对金矿尾砂微晶玻璃结晶性能的影响

以金矿尾砂为主要原料,方解石、硼砂等为添加原料,采用熔融法制备CaO-Al2O3-SiO2系微晶玻璃.采用X射线衍射分析(XRD)、差热分析(DSC)、扫描电镜(SEM)等分析手段对所制备样品进行性能测试与结构表征,研究了TiO2和Cr2O3对金矿尾砂微晶玻璃结晶性能的影响.结果表明,以2; TiO2为晶核剂,金矿尾砂微晶玻璃只有表面析晶,晶相从表面向内部生长;以4; TiO2为晶核剂,样品内部析出少量团聚晶体;以2; Cr2O3为晶核剂,样品内部析出少量团聚粒状晶体;以2; TiO2和2; Cr2O3为复合晶核剂,样品内部析出大量均匀分布的颗粒状晶体,极大地提高了金矿尾砂微晶玻璃的整体析晶能力,主晶相为透辉石(CaMgSi2O6),次晶相为钙长石(CaAl2Si2O8).     

晶核剂P2O5对CaO-Al2O3-SiO2系黄磷炉渣微晶玻璃析晶的影响

采用熔融法以自然冷却黄磷炉渣为主要原料,P2O5为晶核剂,制备了黄磷炉渣微晶玻璃.利用X射线衍射仪(XRD)、差热分析(DTA)和扫描电子显微镜(SEM)等分析技术手段,探究了晶核剂P2O5(以KH2PO4的形式引入)对黄磷炉渣微晶玻璃晶化行为及物化性能的影响规律.结果表明:黄磷炉渣基础玻璃的析晶峰温度Tp及析晶活化能E随着P2O5晶核剂的增加呈现先减小后增大的趋势;当晶核剂P2O5加入量达到4wt;时,黄磷炉渣基础玻璃的析晶峰温度Tp及析晶活化能E最小,析晶效果最优,物化性能最优;主晶相硅灰石(CaSiO3)并不随着晶核剂P2O5加入量的增大而发生改变,同时能够促进晶相氟磷灰石(Ca5(PQ)3F)生成.     

P2O5对CaO-MgO-Al2O3-SiO2系微晶玻璃析晶的影响

采用熔融法制备了不同P2O5含量的CaO-MgO-Al2O3-SiO2玻璃样品,研究了P2O5对该系微晶玻璃析晶的影响规律.结果表明:在所研究的CaO-MgO-Al2O3-SiO2玻璃中,P2O5的最大溶解量在10.0;质量分数左右,超过其饱和溶解度后将析出α-磷酸钙相.玻璃中添加4.0;质量分数P2O5时以表面析晶为主,析出晶体为钙长石和少量硅灰石.随着P2O5含量的提高, α-磷酸钙逐渐析出,同时钙长石和硅灰石的析出逐渐降低.进一步提高P2O5含量抑制了玻璃的表面析晶,促进了玻璃的分相和整体析晶.当P2O5的含量达到10;时,玻璃以整体析晶为主,在分相区内外区域析出晶体的形态非常相似,均呈现为细小粒状.     

Fe2O3对纳米晶尾矿微晶玻璃结构及性能的影响

以铁尾矿和金尾矿为主要原料,采用熔融法制备了添加0 ～ 20wt; Fe2O3的CaO-MgO-Al2O3-SiO2(CMAS)系纳米晶尾矿微晶玻璃,利用差示扫描量热分析(DSC)、X射线衍射分析(XRD)、红外光谱(IR)、扫描电镜(SEM)和综合力学性能仪等测试手段,研究了Fe2O3含量对该体系微晶玻璃显微结构及性能的影响.实验结果表明:随着Fe2O3含量的增加,样品的晶化温度和玻璃化转变温度逐渐降低;且Fe2O3可促进主晶相透辉石相(Mg0.6Fe0.2Al0.2) Ca(Si1.5Al1.5)O6的形成;同时Fe2O3能够有效减小透辉石相平均晶粒尺寸;另外,微晶玻璃的密度、显微硬度和耐碱性随晶粒尺寸的减小而增加,而抗折强度和耐酸性随晶粒尺寸的减小而降低.     

Fe2O3对MgO-Al2O3-SiO2系微晶玻璃介电性能的影响

以化学纯试剂为原料采用高温熔融法制备MgO-Al2O3-SiO2 (MAS)系微晶玻璃,利用差热分析仪(DSC)、X射线衍射(XRD)、电子扫描显微镜(SEM)以及介电检测等手段对Fe2O3在MAS系微晶玻璃中介电性能的影响进行探究.结果表明:Fe2O3有降低微晶玻璃核化和晶化温度的作用;随着Fe2O3的加入,试样的主晶相由堇青石向镁铝尖晶石转变,试样的介电常数和介电损耗逐渐减小并且电阻率增高;当Fe2O3的添加量大于6;时,微晶玻璃的介电性能变化不大,趋于稳定.     

微波法热处理制备CaO-MgO-Al2O3-SiO2系微晶玻璃的研究

以二氧化硅,三氧化二铝,氧化钙和氧化镁为主要原料,分别采用微波辐射和传统电加热制备了一系列CaO-MgO-Al2O3-SiO2 (CMAS)系微晶玻璃材料,对比两种方法的热处理制度对微晶玻璃结构与性能的影响,并进一步讨论了微波非热效应的影响.利用DTA、XRD、SEM和综合力学性能仪等手段,研究了两种对该系微晶玻璃显微结构及性能的影响.实验结果表明,两种方法制备的微晶玻璃主晶相均为辉石相,力学性能也基本相当.与传统热处理方法相比,微波法可在更短时间内制备出性能较好的微晶玻璃材料,微波非热效应有助于降低其晶化温度.     

Optical properties of the germanate melilites Sr2MgGe2O7, Sr2ZnGe2O7 and Ba2ZnGe2O7

Refractive indices and their dispersion in the wavelength range from 365 nm to 2325 nm and transmission ranges of the tetragonal melilite‐type germanates Sr₂MgGe₂O₇, Sr₂ZnGe₂O₇ and Ba₂ZnGe₂O₇ were determined. The uniaxial positive crystals Sr₂MgGe₂O₇ and Ba₂ZnGe₂O₇ both offer the possibility for phase matched second harmonic generation, a detailed analysis of phase matching conditions is given. The refractive indices of Sr₂ZnGe₂O₇ show an isoindex (isotropic) point at 467 nm. The investigation was performed on Czochralski grown large single crystals. The crystal structure of all three germanates were determined by means of X ‐ray diffraction. The results corroborate unmodulated melilite‐type structures at room temperature. (© 2009 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Various Growth Shapes of Na2S2O3 5H2O Crystals

The relation between the growth shapes and supersaturations and/or supercoolings was investigated in the Na₂S₂O₃ 5H₂O crystals: (i) The growth shapes changed from a hexagonal prismatic crystal, aggregate of platy crystals and to a spherulite with an increase of supersaturations and/or supercooloings. (ii) The deposition rate suddenly increased at a certain supersaturation and/or supercooling, where the growth shape changed from the hexagonal prism to the aggregate of platy crystals. (iii) The deposition rates of spherulites become higher with increasing the solute concentrations. (iv) The formation process of the spherulites were in situ observed by the Schlieren and/or Mach‐zehnder interferometer methods.     

TiO2烧结助剂对纳米η-Al2 O3制备Al2 O3-Cr2 O3固溶体的影响研究

以纳米η-Al₂O₃粉和工业铬绿为原料,以摩尔比1:1配比制备Al₂O₃-Cr₂O₃固溶体,以TiO₂为烧结助剂,在还原气氛下经1400 ℃、1500 ℃和1600 ℃固相烧结.研究了TiO₂的加入对纳米η-Al₂O₃制备Al₂O₃-Cr₂O₃固溶体的致密度、线收缩率、相组成、晶胞参数、互扩散程度和微观结构的影响.结果表明:TiO₂的加入能促进Al₂O₃-Cr₂O₃固溶体的致密化;当温度为1600 ℃,TiO₂的添加量为2wt;时,试样的体积密度最大为4.57 g·cm^-3,线收缩率为19.8;;TiO₂的加入能使Al₂O₃-Cr₂O₃固溶体中Al³⁺和Cr³⁺的互扩散程度增加;微观结构表明,TiO₂的加入能使Al₂O₃-Cr₂O₃固溶体晶粒之间结合更紧密,实验温度范围内,随着TiO₂添加量的增加晶粒从沿晶断裂向穿晶断裂转变,只在晶间和晶内存在极少量气孔,当温度为1600 ℃,TiO₂的添加量为2wt;时,晶粒大小较均匀,平均晶粒尺寸约10μm.     

Ag2O/TiO2异质结的光催化活性及耐光腐蚀性研究

以钛酸丁酯、硝酸铋和硝酸银为原料,FTO为基底,采用水热法结合超声沉积法合成了Ag2 O/TiO2异质结光催化剂.采用场发射扫描电子显微镜(FESEM)、X射线衍射仪(XRD)、紫外-可见吸收光谱(UV-Vis)分析测试手段对样品的形貌和结构进行了表征.结果表明,Ag2O/TiO2异质结是由直径约200 ～ 300 nm的TiO2纳米棒镶嵌着Ag2O纳米颗粒组成,与TiO2纳米棒阵列相比,Ag2O/TiO2异质结在可见光区有明显的光吸收.Ag2O/TiO2异质结的光催化效率明显提高.尤为重要的是,经光处理后,最终得到稳定的Ag-Ag2O/TiO2三元体系,并对Ag-Ag2 O/TiO2三元体系提高光催化稳定性和活性的机理进行了分析.     

Sr2TiSi2O8的合成和非线性光学性质研究

采用固相反应法合成了具有硅钛钡石(Ba2TiSi2O8)结构的化合物Sr2TiSi2O8,合成温度在1250℃.对Sr2TiSi2O8的XRD衍射图进行指标化表明它属于四方晶系,晶胞系数为a=b=0.83135nm,c＝0.50190nm,α＝β＝γ＝90°.Sr2TiSi2O8的粉末倍频信号强度约是KH2PO4(KDP)的8倍.反射光谱显示其紫外吸收边为270nm左右.利用自发成核法进行了Sr2TiSi2O8晶体生长研究.     

草酸根作用下Co3O4八面体的控制合成

在草酸根的作用下,采用水热法合成了暴露八个(111)晶面的Co3 O4八面体.采用XRD、SEM、TEM和HRTEM等手段对产物进行了表征和分析,结果表明该Co3 O4八面体呈立方晶相且具有很高的结晶性.详细研究了反应时间、反应温度、草酸根浓度等反应条件对Co3 O4形貌的影响.研究表明草酸根可选择吸附在Co3 O4的(111)晶面,通过其较大的空间位阻限制(111)晶面的生长,从而使该晶面得以最终暴露.由于(111)晶面具有较高的能量,该Co3 O4八面体具有良好的高氯酸铵(AP)催化热分解性能.     

La2O3对氧化铝/高岭土复合定向多孔陶瓷性能的影响

以微米级α-Al2O3、陶瓷水体分散剂为主要原料,以La2O3-水洗高岭土为烧结助剂,采用冰模板法制备了一种具有高孔隙率和较高抗压强度的氧化铝/高岭土复合定向多孔陶瓷.研究了不同添加量的La2O3对多孔陶瓷的显气孔率、体积密度、抗压强度和微观形貌的影响.结果表明:添加适量的稀土La2O3能降低多孔陶瓷烧结温度、提高体积密度和抗压强度.通过高能机械球磨法添加La2O3,在1350℃烧结制备的多孔材料样品显气孔率为82;,样品的抗压强度达到10 MPa以上.当La2O3加入量达到3;时,可使多孔陶瓷抗压强度提高到15.2 MPa,较不掺加La2O3提高了约53;.     

钙钛矿型层状化合物K2Pr2Ti3O10的合成及XRD研究

在K2CO3-镧系元素氧化物(Pr2O3)-TiO2三元体系中,用固相反应法合成K2Pr2Ti3O10,利用X射线粉晶衍射仪对K2Pr2Ti3O10进行扫描测定,获得X射线衍射数据,进行指标化,得到其晶胞参数。XRD分析结果表明,K2Pr2Ti3O10为四方晶系,空间群I4/mmm。