土壤侵蚀降低土地生产力,导致土壤环境恶化,其中水力侵蚀是土壤侵蚀中最主要的一种形式。土壤可侵蚀性K值是评价土壤被降雨侵蚀难易程度的一项重要指标。使用河南、福建和浙江三省研磨干样可见-近红外(Vis-NIR)漫反射光谱数据,将其转换为吸收率后进行Savitzky-Golay(SG)平滑去噪;对土壤有机质(SOM)和机械组成进行精准预测后,分别采用EPIC和RUSLE2模型估算K值,并对预测精度进行比较分析,所得结论如下：(1)建立土壤有机质和机械组成高光谱最佳预测模型,土壤质地(砂粒、粉粒和黏粒)预测采用支持向量机(SVM)模型,SOM预测采用局部加权回归(LWR)模型,模型四分位相对预测误差(RPIQ)为2.27,3.17,2.18和3.44;(2)通过土壤质地估算的土壤渗透性等级分类效果较好,Kappa系数为0.62,同时估测的土壤质地类型与实测土壤质地类型分布特征相近,质地主要类型均是粉黏土、砂黏壤土、壤土、壤砂土和砂壤土;(3)EPIC和RUSLE2两种模型均具有较为精确的估测能力,EPIC模型预测精度更高,均方根误差(RMSEP)为0.006 6 (t·ha·h)/(ha·MJ·mm),RPIQ达1.58,而RUSLE2模型精度相对较低(其中RPIQ为1.43),因此推荐使用EPIC模型结合Vis-NIR光谱技术估测土壤可侵蚀性K值。本研究为今后快速准确预测K值提供思路,并为大面积监测土壤侵蚀提供辅助手段。     

Fe2O3对纳米晶尾矿微晶玻璃结构及性能的影响

以铁尾矿和金尾矿为主要原料,采用熔融法制备了添加0 ～ 20wt; Fe2O3的CaO-MgO-Al2O3-SiO2(CMAS)系纳米晶尾矿微晶玻璃,利用差示扫描量热分析(DSC)、X射线衍射分析(XRD)、红外光谱(IR)、扫描电镜(SEM)和综合力学性能仪等测试手段,研究了Fe2O3含量对该体系微晶玻璃显微结构及性能的影响.实验结果表明:随着Fe2O3含量的增加,样品的晶化温度和玻璃化转变温度逐渐降低;且Fe2O3可促进主晶相透辉石相(Mg0.6Fe0.2Al0.2) Ca(Si1.5Al1.5)O6的形成;同时Fe2O3能够有效减小透辉石相平均晶粒尺寸;另外,微晶玻璃的密度、显微硬度和耐碱性随晶粒尺寸的减小而增加,而抗折强度和耐酸性随晶粒尺寸的减小而降低.     

Polarographic immunoassay coupled with catalysis of non-radioactive multiple iodine label

A now polarographic immunoassay was developed In this assay,human serum albumin (HSA) as the model antigen was covalently labeled with organic compound erythrosin B(EB) containing four non-radioactive iodides through Ⅰ step chemical reaction The labeling procedure is simple and the conditions needed are moderate.The molar labeling ratio of KB HSA was 12 Ⅰ The content of iodine in the conjugate obtained by the proposed procedure is ninth higher than that by the other existing methods.A heterogeneous competitive immunoassay was established by compling the catalysis of the conjugate to substrate As(Ⅲ)-Ce(Ⅳ) reaction with the linear-sweep polarographic detec-tion of As(Ⅲ) amount HSA can be determined in the HSA concentration range from 1 to 200μg/mL,with the de-tection hum of 0 66μg/ml.     

铁含量及价态对白云鄂博尾矿微晶玻璃析晶特性及性能的影响

以白云鄂博尾矿及粉煤灰等固体废弃物为主要原料,采用熔融法、经退火、核化及晶化热处理制备得到了以辉石为主晶相的CaO-MgO-Al2O3-SiO2 (CMAS)系尾矿微晶玻璃.利用化学分析方法测定了不同氧化铁及碳含量对微晶玻璃中Fe3+/Fe2+的影响;利用XRD、DTA、SEM等研究了不同氧化铁及碳含量对微晶玻璃结构及析晶特性的影响.结果表明,不同氧化铁添加量对微晶玻璃中Fe3+/Fe2影响很小,因此对微晶玻璃的析晶特性无本质影响.而随着还原碳粉的加入,Fe3+/Fe2与未加碳粉相比减小明显,微晶玻璃中FeO质量分数的增加极大地提高了微晶玻璃的析晶特性.但过量的碳粉加入导致单质铁的析出,反而降低了微晶玻璃的析晶能力.上述析晶特性的变化直接影响到微晶玻璃的耐酸度及抗折强度.     

基础成分配比对白云鄂博尾矿微晶玻璃结构及性能的影响

以白云鄂博二次选后尾矿和粉煤灰为主要原料,采用熔融法制备得到了CaO-MgO-Al2O3-SiO2系尾矿微晶玻璃.制备流程包括熔融、退火、核化及晶化过程.其中玻璃熔融温度为1450℃,核化温度为720℃,晶化温度为850℃.利用XRD研究了基础玻璃成分配比对微晶玻璃结构的影响.结果表明基础玻璃成分配比直接决定微晶玻璃的主晶相形成.随着基础玻璃成分配比的变化,微晶玻璃可能形成辉石相、钙长石相、镁铁尖晶石相或磁铁矿相.当其他元素固定,CaO/MgO和CaO/Al2O3比值的减小会导致微晶玻璃由辉石相转变为镁铁尖晶石相和钙长石相.而当SiO2/CaO比值大于2时,主晶相则由辉石相转变为磁铁矿相.DTA测试结果表明CaO有利于析晶温度的降低,而MgO、Al2O3和SiO2相对提高了析晶温度.力学性能测试表明抗折强度、密度、耐酸碱度与微晶玻璃主晶相有直接关系.主晶相为辉石相的微晶玻璃具有更高的抗折强度、密度和耐酸性.