Influence of MgO and ZrO2 buffer layers on dielectric properties of Ba(Zr0.20Ti0.80)O3 thin films prepared by sol-gel processing

Ba(Zr_0.20Ti_0.80)O₃ (BZT) thin films are deposited on Pt(1 1 1)/Ti/SiO₂/Si, MgO and ZrO₂ buffered Pt(1 1 1)/Ti/SiO₂/Si substrates by a sol-gel process. The BZT thin films directly grown on Pt(1 1 1)/Ti/SiO₂/Si substrates exhibit highly (1 1 1) preferred orientation, while the films deposited on Pt(1 1 1)/Ti/SiO₂/Si substrates with MgO and ZrO₂ buffer layers show highly (1 1 0) preferred orientation. At 100 kHz, dielectric constants are 417, 311 and 321 for the BZT thin films grown on Pt(1 1 1)/Ti/SiO₂/Si, MgO and ZrO₂ buffered Pt(1 1 1)/Ti/SiO₂/Si substrates, respectively. The difference in dielectric properties of three BZT films can be attributed to the series capacitance effect, interface conditions and their orientations.     

Enhanced ferroelectric property of (Pb0.95Ca0.05)(Nb0.02Zr0.80Ti0.20)O3 thin films prepared by RF magnetron sputtering

(Pb_0.95Ca_0.05)(Nb_0.02Zr_0.80Ti_0.20)O₃ [PCNZT] thin films were deposited on the Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrates by RF magnetron sputtering with and without a LaNiO₃ [LNO] buffer layer. Ca and Nb elements in PZT films enhance the ferroelectric property, LaNiO₃ buffer layer improves the crystal quality of the PCNZT thin films. PCNZT thin films possess better ferroelectric property than that of PZT films for Ca and Nb ion substitution, moreover, PCNZT thin films with a LNO buffer layer possess (1 0 0) orientation and good ferroelectric properties with high remnant polarization (P_r = 38.1 μC/cm²), and low coercive field (E_c = 65 kV/cm), which is also better than that of PCNZT thin films without a LNO buffer layer (P_r = 27.9 μC/cm², E_c = 74 kV/cm). The result shows that enhanced ferroelectric property of PZT films can be obtained by ion substitution and buffer layer.     

Photoluminescence in amorphous (PbLa)TiO3 thin films deposited on different substrates

Pb_1−XLa_XTiO₃ thin films, (X=0.0; 13 and 0.27 mol%) were prepared by the polymeric precursor method. Thin films were deposited on Pt/Ti/SiO₂/Si (1 1 1), Si (1 0 0) and glass substrates by spin coating, and annealed in the 200-300°C range in an O₂ atmosphere. X-ray diffraction, scanning electron microscopy and atomic force microscopy were used for the microstructural characterization of the thin films. Photoluminescence (PL) at room temperature has been observed in thin films of (PbLa)TiO₃. The films deposited on Pt/Ti/SiO₂/Si substrates present PL intensity greater than those deposited on glass and silicon substrates. The intensity of PL in these thin films was found to be dependent on the thermal treatment and lanthanum molar concentration.     

Structural and electrical properties of (Na0.85K0.15)0.5Bi0.5TiO3 thin films deposited on LaNiO3 and Pt bottom electrodes

(Na_0.85K_0.15)_0.5Bi_0.5TiO₃ thin films were deposited on LaNiO₃(LNO)/SiO₂/Si(1 0 0) and Pt/Ti/SiO₂/Si(1 0 0) substrates by metal-organic decomposition, and the effects of bottom electrodes LNO and Pt on the ferroelectric, dielectric and piezoelectric properties were investigated by ferroelectric tester, impedance analyzer and scanning probe microscopy, respectively. For the thin films deposited on LNO and Pt electrodes, the remnant polarization 2P_r are about 22.6 and 8.8 μC/cm² under 375 kV/cm, the dielectric constants 238 and 579 at 10 kHz, the dielectric losses 0.06 and 0.30 at 10 kHz, the statistic d_33eff values 95 and 81 pm/V. The improved piezoelectric properties could make (Na_1−xK_x)_0.5Bi_0.5TiO₃ thin film as a promising candidate for piezoelectric thin film devices.     

Infrared optical properties of Ba(Zr0.20Ti0.80)O3 and Ba(Zr0.30Ti0.70)O3 thin films prepared by sol-gel method

Ba(Zr_xTi_1−x)O₃ (BZT) (x = 0.20 and 0.30) thin films are deposited on Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrate by sol-gel method. X-ray diffraction patterns show that the thin films have a good crystallinity. Optical properties of the films in the wavelength range of 2.5-12 μm are studied by infrared spectroscopic ellipsometry (IRSE). The optical constants of the BZT thin films are determined by fitting the IRSE data using a classical dispersion formula. As the wavelength increases, the refractive index decreases, while the extinction coefficients increase. The effective static ionic charges are derived, which are smaller than that in a purely ionic material for the BZT thin films.     

Multiferroic properties of Bi0.8La0.2FeO3/CoFe2O4 multilayer thin films

Bi_0.8La_0.2FeO₃/CoFe₂O₄ (BLFO/CFO) multilayer thin films (totally 20 layers BLFO and 19 layers CFO) were prepared on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition. X-ray diffraction and transmission electron microscope measurements show that the films are polycrystalline and consisted of multilayered structure. Ferroelectric hysteresis loops with remnant polarization and saturated polarization of 4.2 and 13.3 μC/cm², respectively, were observed. On the other hand, the films show well-shaped magnetization hysteresis loops with saturated and remnant magnetization of 34.7 and 11.4 emu/cm³, respectively, which are significantly larger than pure BLFO thin films deposited under the same conditions. These results indicate that constructing epitaxial superlattice might be a promising way to fabricate multiferroics with improved properties.     

Dielectric and piezoelectric properties of the Ba0.92Ca0.08Ti0.95Zr0.05O3 thin films grown on different substrate

Lead free Ba_0.92Ca_0.08Ti_0.95Zr_0.05O₃ (BCZT) thin films were deposited on Pt/Ti/SiO₂/Si and LaNiO₃(LNO)/Pt/Ti/SiO₂/Si substrates by a sol–gel processing technique, respectively. The effects of substrate on structure, dielectric and piezoelectric properties were investigated in detail. The BCZT thin films deposited on LNO/Pt/Ti/SiO₂/Si substrates exhibit (100) orientation, larger grain size and higher dielectric tunability (64%). The BCZT thin films deposited on Pt/Ti/SiO₂/Si exhibit (110) orientation, higher Curie temperature (75 °C), better piezoelectric property (d₃₃ of 50 pm/V) and lower dielectric loss (0.02). The differences in dielectric and piezoelectric properties in the two kinds of oriented BCZT films should be attributed to the difference of structure, in-plane stress and polarization rotation in orientation engineered BCZT films.     

不同衬底上Pb(Zr0.52Ti0.48)O3择优取向铁电薄膜的制备和研究

通过MOD法在Si(100)和Pt(111)/Ti/SiO₂/Si基片上制备出LaNiO₃ ( LNO)薄膜.再通过修 正的Sol-gel法，在Pt(111)/Ti/SiO₂/Si,LNO/Si(100)和LNO/Pt/Ti/SiO_{2< /sub>/Si三种衬底上 制备出具有择优取向的Pb(Zr0.52Ti0.48)O3铁电薄膜. 经XRD分析表明，L NO薄膜具有(100)择优取向的类钙钛矿结构；PZT薄膜均具有钙钛矿结构，且在Pt(111)/Ti/S iO2/Si衬底上的薄膜以(110)择优取向，在LNO/Pt/Ti/SiO2/Si和LN O/Si(100)衬底上的 薄膜以(100)择优取向.经场发射SEM分析和介电、铁电性能测试表明，在LNO/Si和LNO/Pt/Ti /SiO2/Si衬底上的PZT薄膜的平均粒径、介电常数以及剩余极化强度均比以Pt/T i/SiO2/Si为衬底的薄膜大. 关键词： 3}薄膜')" href="#">LaNiO₃薄膜 PZT铁电薄膜 择优取向 剩余极化强度     

Ferroelectric properties of neodymium-doped Sr2Bi4Ti5O18 thin film prepared by solgel route

Sr₂Bi₄Ti₅O₁₈ (SBTi) and Nd-modified SBTi (SBNT) thin films were deposited on Pt/Ti/SiO₂/Si (1 0 0) substrates using a sol-gel method. Structure, morphology and electric properties were investigated systematically. These films were randomly oriented and composed of rod-like grains. The remanent polarization (2P_r) and coercive field (E_c) of SBNT films were 30 μC/cm² and 55 kV/cm, respectively. This value of 2P_r was much higher than the reported value of SBTi prepared by pulsed-laser deposition. More importantly, the SBNT films showed high fatigue resistance against continuous switching up to 3×10⁹ cycles and excellent charge-retaining ability up to 3×10⁴ s.     

Dependence of excess bismuth content in precursor sols on ferroelectric and dielectric properties of Bi3.25La0.75Ti3O12 thin films fabricated by chemical solution deposition

Bi_3.25La_0.75Ti₃O₁₂ (BLT) thin films were fabricated on Pt/Ti/SiO₂/Si(1 0 0) substrates by chemical solution deposition (CSD), and the dependence of ferroelectric and dielectric properties of the as-deposited BLT thin films on excess Bi content in precursor sols was studied. It is found that the prepared BLT thin film shows the best polarization-electric field, capacitance-voltage and dielectric constant (?_r)-frequency characteristics, when the value of excess Bi content in precursor sols is 10%. In detail, its remnant polarization (2P_r) value is 40 μC/cm², the capacitance tunability is 21% measured at room temperature under conditions of an applied voltage of 8 V and measurement frequency of 10 kHz, and the ?_r is 696 at 100 kHz frequency.     

The influence of Co doping on the dielectric, ferroelectric and ferromagnetic properties of Ba0.70Sr0.30TiO3 thin films

Ba_0.70Sr_0.30TiO₃ (BST) thin films doped by Co (BSTC) are fabricated by sol-gel method on a Pt/Ti/SiO₂/Si substrate. A strong correlation is observed among the microstructure, dielectric, ferroelectric, ferromagnetic properties and Co concentration. The dielectric constant of BST thin films can be tailored from 343 to 119 by manipulating the Co concentration. The dielectric loss of BSTC thin films are still kept below 0.020 and the tunability is above 30% at a dc-applied electric field of 500 kV/cm. With increasing Co doping up to 10 mol%, the coexistence of ferromagnetism and ferroelectrics is found. Suitable dielectric constant, low-dielectric loss, and high tunability of this kind of thin films can be useful for potential tunable applications.     

Electrical behavior of BaZr0.1Ti0.9O3 and BaZr0.2Ti0.8O3 thin films

BaZr_0.1Ti_0.9O₃ and BaZr_0.2Ti_0.8O₃ (BZT) thin films were deposited on Pt/Ti/LaAlO₃ (1 0 0) substrates by radio-frequency magnetron sputtering, respectively. The films were further annealed at 800 °C for 30 min in oxygen. X-ray diffraction θ-2θ and Φ-scans showed that BaZr_0.1Ti_0.9O₃ films displayed a highly (h 0 0) preferred orientation and a good cube-on-cube epitaxial growth on the LaAlO₃ (1 0 0) substrate, while there are no obvious preferential orientation in BaZr_0.2Ti_0.8O₃ thin films. The BaZr_0.1Ti_0.9O₃ films possess larger grain size, higher dielectric constant, larger tunability, larger remanent polarization and coercive electric field than that of BaZr_0.2Ti_0.8O₃ films. Whereas, BaZr_0.1Ti_0.9O₃ films have larger dielectric losses and leakage current density. The results suggest that Zr⁴⁺ ion can decrease dielectric constant and restrain non-linearity. Moreover, the enhancement in dielectric properties of BaZr_0.1Ti_0.9O₃ films may be attributed to (1 0 0) preferred orientation.     

Effects of texture on the dielectric properties of Ba(Zr0.2Ti0.8)O3 thin films prepared by pulsed laser deposition

Ba(Zr_0.2Ti_0.8)O₃ (BZT) thin films were deposited on Pt(111)/Ti/SiO₂/Si(100) substrates by a pulsed laser deposition process. The BZT thin films directly grown on annealed and un-annealed Pt/Ti/SiO₂/Si substrates exhibited random and high (100) orientations, respectively. The dielectric constant of a 400-nm-thick BZT film with (100) orientation was 331, which was higher than that of a BZT film with random orientation (∼236). This result is attributed to the fact that the polar axis of the (100)-oriented films was more tilted away from the normal to the film surface than that of the randomly oriented films. Also, the tunabilities of BZT thin films with random and (100) orientations were ∼50% and ∼59% at an applied field of 400 kV/cm, respectively. Improved tunability has been attributed to the (100) texture of the film leading to an enhancement of the in-plane-oriented polar axis. PACS 77.22.-d; 77.55.+f; 77.80.-e; 77.84.-s     

Surface chemical states of barium zirconate titanate thin films prepared by chemical solution deposition

Ba(Zr_0.05Ti_0.95)O₃ (BZT) thin films grown on Pt/Ti/SiO₂/Si(1 0 0) substrates were prepared by chemical solution deposition. The structural and surface morphology of BZT thin films has been studied by X-ray diffraction (XRD) and scanning electron microscope (SEM). The results showed that the random oriented BZT thin film grown on Pt/Ti/SiO₂/Si(1 0 0) substrate with a perovskite phase. The SEM surface image showed that the BZT thin film was crack-free. And the average grain size and thickness of the BZT film are 35 and 400 nm, respectively. Furthermore, the chemical states and chemical composition of the films were determined by X-ray photoelectron spectroscopy (XPS) near the surface. The XPS results show that Ba, Ti, and Zr exist mainly in the forms of BZT perovskite structure.     

Properties of K0.5Bi0.5TiO3 thin films deposited on different substrates

K_0.5Bi_0.5TiO₃ thin films were deposited on fused quartz, n-type Si(100) and Pt/TiO₂/SiO₂/Si substrates by repeated coating/dying cycles. X-ray diffraction analysis shows that the films annealed at 700 °C for 10 min present perovskite phase. Atomic force microscopy reveals that the surface morphology is smooth, the grain sizes of the films on Si(100) are quite larger than on fused quartz. The capacitance-voltage hysteresis loops at various sweeping speed are collected as are polarization types. The films in the ON and OFF states are relatively stable. The films also exhibit a hysteresis loop at an applied voltage of 4 V, with a remanent polarization of 9.3 μC/cm² and a coercive voltage of 2 V. The insulating property of negative bias voltage is better than that of positive bias voltage. The transmittance of the films is between 74 and 82% in the wavelength range of 200-2000 nm.     

Pb(Zr0.53Ti0.47)O3 thin films with different thicknesses obtained at low temperature by microwave irradiation

Pb(Zr_0.53Ti_0.47)O₃ (PZT) thin films with different thicknesses (99-420 nm) were prepared on Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrates by sol-gel method and films were annealed at 450 °C for 30 min using a single-mode cavity of 2.45 GHz microwaves. X-ray diffraction analysis indicated that the pyrochlore phase was transformed to the perovskite phase at above 166 nm films. The grain sizes were increased, surface roughnesses were decreased, and electrical properties were improved with film thickness. The leakage current density was 9 × 10⁻⁸ A/cm² at an applied electrical field of 100 kV/cm. The ohmic and field-enhanced Schottky emission mechanisms were used to explain leakage current behavior of the PZT thin films. These results suggest that microwave annealing is effective for obtaining low temperature crystallization of thin films with better properties.     

Dielectric properties of continuous composition spreaded MgO-Ta2O5 thin films

The dielectric properties of MgO-Ta₂O₅ continuous composition spread (CCS) thin films were investigated. The MgO-Ta₂O₅ CCS thin films were deposited on Pt/Ti/SiO₂/Si substrates by off-Axis RF magnetron sputtering system, and then the films were annealed at 350 °C with rapid thermal annealing system in vacuum. The dielectric constant and loss of MgO-Ta₂O₅ CCS thin films were plotted via 1500 micron-step measuring. The specific point of Ta₂O₅-MgO CCS thin film (post annealed at 350 °C) showing superior dielectric properties of high dielectric constant (k ∼ 28) and low dielectric loss (tan δ < 0⋅004) at 1 MHz were found in the area of 3-5 mm apart from Ta₂O₅ side on the substrate. The cation's composition of thin film was Mg:Ta = 0.4:2 at%.     

Investigation of thin TiO2 films cosputtered with Si species

Titanium dioxide (TiO₂) films were fabricated by cosputtering titanium (Ti) target and SiO₂ or Si slice with ion-beam-sputtering deposition (IBSD) technique and were postannealed at 450 °C for 6 h. The variations of oxygen bonding, which included high-binding-energy oxygen (HBO), bridging oxygen (BO), low-binding-energy oxygen (LBO), and three chemical states of titanium (Ti⁴⁺, Ti³⁺ and Ti²⁺) were analyzed by X-ray photoelectron spectroscopy (XPS). The enhancement of HBO and reduction of BO in O 1s spectra as functions of SiO₂ or Si amount in cosputtered film imply the formation of Si-O-Ti linkage. Corresponding increase of Ti³⁺ in Ti 2p spectra further confirmed the property modification of the cosputtered film resulting from the variation of the chemical bonding. An observed correlation between the chemical structure and optical properties, refractive index and extinction coefficient, of the SiO₂ or Si cosputtered films demonstrated that the change of chemical bonding in the film results in the modification of optical properties. Furthermore, it was found that the optical properties of the cosputtered films were strongly depended on the cosputtering targets. In case of the Si cosputtered films both the refractive indices and extinction coefficients were reduced after postannealing, however, the opposite trend was observed in SiO₂ cosputtered films.     

Synthesis of bamboo-leaf-shaped ZnO nanostructures by oxidation of Zn/SiO2 composite films deposited with radio frequency magnetron co-sputtering

Bamboo-leaf-shaped ZnO nanostructures were synthesized by oxidation of metal Zn/SiO₂ matrix composite thin films deposited on Si(1 1 1) substrates with radio frequency magnetron co-sputtering. The synthesized bamboo-leaf-shaped ZnO are single crystalline in nature with widths ranging from 30 to 60 nm and lengths of up to 5-10 μm, room temperature photoluminescence spectrum of the nanostructures shows a strong and sharp UV emission band at 372 nm and a weak and broad green emission band at about 520 nm which indicates relatively excellent crystallization and optical quality of the ZnO nanostructures synthesized by this novel method.     

Characteristics of SrBi2Ta2O9 ferroelectric films in an in situ applied low electric field prepared by metalorganic decomposition

SrBi₂Ta₂O₉ (SBT) films were prepared on Pt/TiO₂/SiO₂/Si substrates at 750 °C in oxygen by metalorganic decomposition method. A low electric field was in situ applied during the film crystallization. It was first found that a low electric field and its direction have significant influence on the microstructures and ferroelectric properties of SBT films. Under a positive electric field (assuming that the bottom electrode is electrically grounded), the films show stronger c-axis-preferred orientation than without electric field and under a negative electric field. As a possible origin is proposed that the interface-induced nucleation growth between SBT and Pt coated substrate with application of low electric field plays a key role. Above all, an in situ applied low electric field during the film crystallization is a promising technique controlling film orientation for film preparation by wet chemical method.