Structural analysis of Si(1 1 1)-√21 × √21-Ag surface by reflection high-energy positron diffraction

The atomic structure of Si(1 1 1)-√21 × √21-Ag surface, which is formed by the adsorption of small amount of Ag atoms on the Si(1 1 1)-√3 × √3-Ag surface, was determined by using reflection high-energy positron diffraction. The rocking curve measured from the Si(1 1 1)-√21 × √21-Ag surface was analyzed by means of the intensity calculations based on the dynamical diffraction theory. The adatom height of the extra Ag atoms from the underlying Ag layer was determined to be 0.53 Å with a coverage of 0.14 ML, which corresponds to three atoms in the √21 × √21 unit cell. From the pattern analyses, the most appropriate adsorption sites of the extra Ag atoms were proposed.     

Structural study of Si(1 1 1)-6 × 1-Ag surface using surface X-ray diffraction

The surface structure of Si(1 1 1)-6 × 1-Ag was investigated using surface X-ray diffraction techniques. By analyzing the CTR scattering intensities along 00 rod, the positions of the Ag and reconstructed Si atoms perpendicular to the surface were determined. The results agreed well with the HCC model proposed for a 3 × 1 structure induced by alkali-metals on a Si(1 1 1) substrate. The heights of the surface Ag and Si atoms did not move when the surface structure changed from Si(1 1 1)-√3 × √3-Ag to Si(1 1 1)-6 × 1-Ag by the desorption of the Ag atoms. From the GIXD measurement, the in-plane arrangement of the surface Ag atoms was determined. The results indicate that the Ag atoms move large distances at the phase transition between the 6 × 1 and 3 × 1 structures.     

Study of the surface structure of Si(1 1 1)-6 × 1(3 × 1)-Ag using X-ray crystal truncation rod scattering

The structure of the Si(1 1 1)-6 × 1-Ag surface is investigated using crystal truncation rod (CTR) scattering along 00 rod. For the measurement, we developed a manipulator suitable for observing CTR scattering at large momentum transfer perpendicular to the surface. The heights of the silver and reconstructed silicon atoms from the substrate were determined. We also compared the obtained positions with those of the Si(1 1 1)-√3 × √3-Ag surface and found that the heights of those reconstructed atoms are almost the same.     

Fabrication of uniform Au silicide islands on the Si(1 1 1)-(7 × 7) substrate

The Au silicide islands have been fabricated by additional deposition of Au on the prepared surface at 270 °C where the Si islands of magic sizes were formed on the Si(1 1 1)-(7 × 7) dimer-adatom-stacking fault substrate. The surface structure on the Au silicide islands shows the Au/Si(1 1 1)-√3 × √3 reconstructed structure although the substrate remains 7 × 7 DAS structure. The size of the Au silicide islands depends on the size distribution of the preformed Si islands, because the initial size and shape of the Si islands play important roles in the formation of the Au silicide island. We have achieved the fabrication of the Au silicide islands of about the same size (∼5 nm) and the same shape by controlling the initial Si growth and the additional Au growth conditions.     

Growth of (√3 × √3)-Ag and (1 1 1) oriented Ag islands on Ge/Si(1 1 1) surfaces

We have studied the growth of Ag on Ge/Si(1 1 1) substrates. The Ge/Si(1 1 1) substrates were prepared by depositing one monolayer (ML) of Ge on Si(1 1 1)-(7 × 7) surfaces. Following Ge deposition the reflection high energy electron diffraction (RHEED) pattern changed to a (1 × 1) pattern. Ge as well as Ag deposition was carried out at 550 °C. Ag deposition on Ge/Si(1 1 1) substrates up to 10 ML has shown a prominent (√3 × √3)-R30° RHEED pattern along with a streak structure from Ag(1 1 1) surface. Scanning electron microscopy (SEM) shows the formation of Ag islands along with a large fraction of open area, which presumably has the Ag-induced (√3 × √3)-R30° structure on the Ge/Si(1 1 1) surface. X-ray diffraction (XRD) experiments show the presence of only (1 1 1) peak of Ag indicating epitaxial growth of Ag on Ge/Si(1 1 1) surfaces. The possibility of growing a strain-tuned (tensile to compressive) Ag(1 1 1) layer on Ge/Si(1 1 1) substrates is discussed.     

Electron and lattice structure of ultra thin Ag films on Si(1 1 1) and Si(0 0 1)

We studied the low temperature (T ? 130 K) growth of Ag on Si(0 0 1) and Si(1 1 1) flat surfaces prepared by Si homo epitaxy with the aim to achieve thin metallic films. The band structure and morphology of the Ag overlayers have been investigated by means of XPS, UPS, LEED, STM and STS. Surprisingly a (√3 × √3)R30° LEED structure for Ag films has been observed after deposition of 2-6 ML Ag onto a Si(1 1 1)(√3 × √3)R30°Ag surface at low temperatures. XPS investigations showed that these films are solid, and UPS measurements indicate that they are metallic. However, after closer STM studies we found that these films consists of sharp Ag islands and (√3 × √3)R30°Ag flat terraces in between. On Si(0 0 1) the low-temperature deposition yields an epitaxial growth of Ag on clean Si(0 0 1)-2 × 1 with a twinned Ag(1 1 1) structure at coverage’s as low as 10 ML. Furthermore the conductivity of few monolayer Ag films on Si(1 0 0) surfaces has been studied as a function of temperature (40-300 K).     

Perturbation of Ge(1 1 1) and Si(1 1 1)√3α-Sn surfaces by adsorption of dopants

We test the response of the √3 × √3α reconstructions formed by 1/3 monolayer of tin adatoms on silicon and germanium (1 1 1) surfaces upon doping with electrons or holes, using potassium or iodine as probes/perturbers of the initial electronic structures. From detailed synchrotron radiation photoelectron spectroscopy studies we show that doping with either electrons or holes plays a complimentary role on the Si and Ge surfaces and, especially, leads to complete conversion of the Sn 4d two-component spectra into single line shapes. We find that the low binding energy component of the Sn core level for both Si and Ge surfaces corresponds to Sn adatoms with higher electronic charge, than the Sn adatoms that contribute to the core level high binding energy signal. This could be analyzed as Sn adatoms with different valence state.     

Bi induced step-flow growth in the homoepitaxial growth of Au(1 1 1)

Homoepitaxial growth of Au on Bi-covered Au(1 1 1) was studied at room temperature using reflection high-energy electron diffraction (RHEED) and Auger electron spectroscopy (AES). From observations of RHEED it is found that the Au(1 1 1) (23 × 1) reconstruction structure changes to a (1 × 1) by about 0.16-0.5 ML deposition of Bi and to a (2√3 × 2√3)R30° by about 1.0 ML deposition of Bi, respectively. The surface morphology evolution by Bi deposition leads to a change of Au homoepitaxial growth behavior from layer-by-layer to step flow. This indicates that the surface diffusion distance of Au atoms on the Bi-precovered (1 × 1) and (2√3 × 2√3)R30° surfaces is longer than that on the Au(1 1 1) (23 × 1) clean surfaces. A strong surface segregation of Bi was found at top of surface. It is concluded that Bi atoms acted as an effective surfactant in the Au homoepitaxial growth by promoting Au intralayer mass transport.     

Structure and electronic properties of gold adsorbed on Ti(0 0 0 1)

The Au/Ti(0 0 0 1) adsorption system was studied by low energy electron diffraction (LEED) and photoemission spectroscopy with synchrotron radiation after step-wise Au evaporation onto the Ti(0 0 0 1) surface. For adsorption of Au at 300 K, no additional superstructures were observed and the (1 × 1) pattern of the clean surface simply became diffuse. Annealing of gold layers more than 1 ML thick resulted in the formation of an ordered Au-Ti surface alloy. Depending on the temperature and annealing time, three surface reconstructions were observed by LEED: (√3 × √3) R30°, (2 × 2) and a one-dimensional incommensurate (√3 × √3) rectangular pattern. The Au 4f core level and valence band photoemission spectra provided evidence of a strong chemical interaction between gold and titanium. The data indicated formation of an intermetallic interface and associated valence orbital hybridization, together with diffusion of gold into the bulk. Au core-level shifts were found to be dependent on the surface alloy stoichiometry.     

Unoccupied band dispersion of Si(1 1 1):√3 × √3-Ag surface studied by time- and angle-resolved two-photon photoemission spectroscopy

Band dispersion and transient population of unoccupied electronic states on Si(1 1 1):√3 × √3-Ag surface have been studied by time-resolved (TR) and angle-resolved (AR) two-photon photoemission (2PPE) spectroscopy. The band dispersions originating from unoccupied electronic states have been identified from the comparison between AR-2PPE spectra and angle-resolved one-photon photoemission spectra with synchrotron radiation. A lifetime of unoccupied surface state has been determined from the TR-2PPE spectra.     

Fabrication of nanostructures by selective growth of C60 and Si on Si(1 1 1) substrate

Using two types of selective growth, selective C₆₀ growth and selective Si growth, on a common Si(1 1 1) substrate, an array of C₆₀ nanoribbons with controlled values of width and thickness is fabricated. On a surface that has Si(1 1 1)√3 × √3R30°-Ag (referred to as Si(1 1 1)√3-Ag hereafter) and bare Si(1 1 1) regions at the same time, the preferential growth of C₆₀ multilayered film is recognized on the Si(1 1 1)√3-Ag region. The growth of Si selectively occurs on a bare Si(1 1 1) region if the substrate surface has C₆₀-adsorbed and bare Si(1 1 1) regions at the same time. As a demonstration of the use of these selective growths, we fabricate an array of well-isolated C₆₀ nanoribbons, which show a well-ordered molecular arrangement and have sizes of about 40 nm in widths and 3-4 nm in thicknesses.     

Electronic structure study of reconstructed Au-SiC(0 0 0 1) surfaces

A study of surface and interface properties of reconstructed Au-SiC(0 0 0 1) surfaces is reported. Two reconstructions were prepared on SiC(0 0 0 1), a √3 × √3R30° and a Si-rich 3 × 3, before Au deposition and subsequent annealing at different temperatures. For the Si-rich 3 × 3 surface the existence of three stable reconstructions 2√3 × 2√3R30°, 3 × 3 and 5 × 5 are revealed after deposition of Au layers, 4-8 Å thick, and annealing at progressively higher temperatures between 500 and 950 °C. For the 2√3 surface two surface shifted Si 2p components are revealed and the Au 4f spectra clearly indicate silicide formation. The variation in relative intensity for the different core level components with photon energy suggests formation of an ordered silicide layer with some excess Si on top. Similar core level spectra and variations in relative intensity with photon energy are obtained for the 3 × 3 and 5 × 5 phases but the amount of excess Si on top is observed to be smaller and an additional weak Si 2p component becomes discernable.For the √3 surface the evolution of the core level spectra after Au deposition and annealing is shown to be distinctly different than for the Si-rich 3 × 3 surface and only one stable reconstruction, a 3 × 3 phase, is observed at similar annealing temperatures.     

Surface structure and phase transition of Ge(1 1 1)-3 × 3-Pb studied by reflection high-energy positron diffraction

We studied the structures and the phase transition of Pb/Ge(1 1 1) surface by using the reflection high-energy positron diffraction. The surface structures at 60 K and 293 K have the 3 × 3 and √3 × √3 periodicities, respectively. The rocking curves measured at both temperatures are nearly the same. This indicates that the equilibrium positions of the surface atoms do not change according to the phase transition. From the analysis of the rocking curve based on the dynamical diffraction theory, we found that at both temperatures the surface structures are composed of the so-called one-up and two-down model. The 3 × 3-√3 × √3 phase transition for the Pb/Ge(1 1 1) surface is interpreted in terms of order-disorder transition.     

A structural parallel between Ge- and Si-induced 4 × 4 and 3 × 3 reconstructions on SiC(0 0 0 1) drawn from comparative RHEED oscillations

The initial Ge growth stages on a (√3 × √3)R30°-reconstructed SiC(0 0 0 1) surface (√3) have been studied using a complete set of surface techniques such as reflection high energy electron diffraction (RHEED), low energy electron diffraction (LEED), atomic force microscopy (AFM) and photoemission and compared with similar Si surface enrichments in place of Ge. The investigations essentially focus on the wetting growth-regimes that are favoured by the use of the √3 surface as a starting substrate, this surface being the closest to a smooth and ideally truncated Si-terminated face of hexagonal SiC(0 0 0 1). Depending on temperature and Ge or Si coverages, varying surface organizations are obtained. They range from unorganized layer by layer growths to relaxed Ge(1 1 1) or Si(1 1 1) island growths, through intermediate attempts of coherent and strained Ge or Si surface layers, characterized by 4 × 4 and 3 × 3 surface reconstructions, respectively. RHEED intensity oscillation recordings, as a function of Ge or Si deposited amounts, have been particularly helpful to pinpoint the limited (by the high lattice mismatch) existence domains of these interesting coherent phases, either in terms of formation temperature or surface coverages. Prominently comparable data for these two Ge- and Si-related reconstructions allow us to propose an atomic model for the still unexplained Ge-4 × 4 one. It is based on a same local organization in trimer and ad-atom units for the Ge excess as admitted for the Si-excess of the 3 × 3 surface, the higher strain nevertheless favouring arrangements, for the Ge-units, in 4 × 4 arrays instead of 3 × 3 Si ones. Admitting such models, 1.25 and 1.44 monolayers of Ge and Si, should, respectively, be able to lie coherently on SiC, with respective lattice mismatches near 30% and 25%. The experimental RHEED-oscillations values are compatible with such theoretical ones. Moreover, these RHEED coverage determinations (for layer completion, for instance) inform us in turn about the initial Si richness of the starting √3 reconstruction and help us to discriminate between earlier contradictory atomic models proposed in the literature.     

Observation of a (√3 × √3)-R30° reconstruction on GaN(0 0 0 1) by RHEED and LEED

A new reconstruction of √3 × √3-R30° has been observed on a GaN film grown on a 6H-SiC (0 0 0 1)-√3 × √3 surface using RHEED and LEED experimental techniques. The experimental LEED PF shows that the GaN film is Ga-terminated hexagonal. The surface is a mixture of two structures with a single bilayer height difference between them. One is a √3 × √3-R30° reconstruction with Ga-adatoms occupying the T4 sites. Another is a Ga-terminated 1 × 1 with no extra Ga on top. The area ratio of the √3 × √3 part to the 1 × 1 part is slightly larger than 1. The first principle total energy calculations and Tensor-LEED I-V curves simulations further confirm this structure model.     

STM study of acetylene reaction with Si(1 1 1): observation of a carbon-induced Si(1 1 1)√3×√3R30° reconstruction

The first stages of acetylene reaction with the Si(1 1 1)7 × 7 reconstructed surface kept at 600 °C are studied by recording scanning tunneling microscopy (STM) images during substrate exposure at a C₂H₂ pressure of 2 × 10⁻⁴ Pa (2 × 10⁻² mbar). We observed the progressive substitution of the 7 × 7 reconstruction with a carbon induced Si(1 1 1)√3×√3R30° reconstruction characterized by an atomic distance of 0.75 ± 0.02 nm, very close to that of the silicon 7 × 7 adatoms. This means that a carbon enrichment of the silicon outermost layers occurs giving rise to the formation of a Si-C phase different from the √3×√3R30° reconstruction typical of Si terminated hexagonal SiC(0 0 0 1) surface with an atomic distance of 0.53 nm. To explain STM images, we propose a reconstruction model which involves carbon atoms in T₄ and/or S₅ sites, as occurring for B doped Si(1 1 1) surface. Step edges and areas around the silicon surface defects are the first regions involved in the reaction process, which spreads from the upper part of the step edges throughout the terraces. Step edges therefore, progressively flakes and this mechanism leads, for the highest exposures, to the formation of large inlets which makes completely irregular the straight edge typical of the Si(1 1 1)7 × 7 terraces. These observations indicate that there occurs an atomic diffusion like that driving the meandering effect. Finally, the formation of a few crystallites is shown also at the lowest acetylene exposures. This is the first STM experiment showing the possibility to have carbon incorporation in a Si(1 1 1) matrix for higher amounts than expected, at least up to 1/6 of silicon atomic layer.     

Comparative investigation of the c(2 × 2)-Si/Cu(0 1 1) and (√3 × √3)R30°-Cu2Si/Cu(1 1 1) surface alloys using DFT

The electronic structure of the c(2 × 2)-Si/Cu(0 1 1) surface alloy has been investigated and compared to the structures seen in the three phases of the (√3 × √3)R30°Cu₂Si/Cu(1 1 1) system, using LCAO-DFT. The weighted surface energy increase between the alloyed Cu(0 1 1) and Cu(1 1 1) surfaces is 126.7 meV/Si atom. This increase in energy for the (0 1 1) system when compared to the (1 1 1) system is assigned to the transition from a hexagonal to a rectangular local bonding environment for the Si ion cores, with the hexagonal environment being energetically more favorable. The Si 3s state is shown to interact covalently with the Cu 4s and 4p states whereas the Si 3p state, and to a lesser extent the Si 3d state, forms a mixture of covalent and metallic bonds with the Cu states. The Cu 4s and 4p states are shown to be altered by approximately the same amount by both the removal of Cu ion cores and the inclusion of Si ion cores during the alloying of the Cu(0 1 1) surface. However, the Cu 3d states in the surface and second layers of the alloy are shown to be more significantly altered during the alloying process by the removal of Cu ion cores from the surface layer rather than by the addition of Si ion cores. This is compared to the behavior of the Cu 3d states in the surface and second layers of the each phase of the (√3 × √3)R30°-Cu₂Si/Cu(1 1 1) alloy and consequently the loss of Cu-Cu periodicity during alloying of the Cu(0 1 1) surface is conjectured as the driving force for changes to the Cu 3d states. The accompanying changes to the Cu 4s and 4p states in both the c(2 × 2)-Si/Cu(0 1 1) and (√3 × √3)R30°-Cu₂Si/Cu(1 1 1) alloys are quantified and compared. The study concludes with a brief quantitative study of changes in the bond order of the Cu-Cu bonds during alloying of both Cu(0 1 1) and Cu(1 1 1) surfaces.     

Reconstructions 3 × 3 and √3 × √3 on SiC(0 0 0 1) studied using RHEED

The 3 × 3 and √3 × √3 reconstructions on 6H-SiC(0 0 0 1) surface were obtained via depositing thin silicon layer and annealing it in ultrahigh vacuum (without Si flux). Rocking curves of reflection high energy electron diffraction (RHEED) were measured for integer and fractional order beams. They were fitted with results of many-beam calculation on the basis of dynamical theory of RHEED to determine structural parameters. For √3 × √3 superstructure, it was found that the occupancy of adatom states is 0.45 (incomplete coverage). In the sequence of Si-C double layers ABCACB, the lattice is terminated with the layer A. For 3 × 3 superstructure, the rocking curves support the model with twisted tetra-cluster. The best-fit twist is as half of that predicted in ab initio calculations; it is due to limited source of Si atoms to build up the superstructure. Larger twist correlates with higher occupancy of corner sites and with slower cooling rate of the sample after annealing.     

Study of buried Si(1 1 1)-5 × 2-Au by surface X-ray diffraction

The structure of buried Si(1 1 1)-5 × 2-Au capped with amorphous Si was investigated using surface X-ray diffraction. It was found that the 5 × 2 structural periodicity is kept under the amorphous Si from the in-plane measurement. Furthermore, the intensity variation along the fractional-order rod indicates that Au atoms are located almost on the same plane.     

An STM investigation of the interaction and ordering of pentacene molecules on the Ag/Si(1 1 1)-(√3×√3)R30° surface

Scanning tunneling microscopy has been used to study the ordering of pentacene (C₂₂H₁₄) molecules on the Ag/Si(1 1 1)-(√3×√3)R30° surface at room temperature. Two solid phases, S1 and S2, are observed at coverages of ∼0.35 monolayer (ML) and ∼1.0 ML respectively. It is shown that the solid phase S1 has a high-order commensurate lattice, Ag/Si(1 1 1)-(25 × 25)-pentacene, containing 75 molecules. The structure of this phase is determined from STM measurements at very low coverages where it is possible to image both the pentacene molecules and the structure of the Ag/Si(1 1 1) substrate. Two adsorption sites are identified, a three-fold hollow site at the centre of a Ag-trimer (CA-site) and a six-fold hollow site at the centre of the hexagonal arrangement of silver atoms (CB-site). A higher pentacene coverage of ∼1 ML lead to a molecular reorganization and forms a new commensurate structure Ag/Si(1 1 1)-(2 × 3)-pentacene, containing two molecules per unit cell. Because low energy electron diffraction patterns were not obtainable for this system, the structure of this second phase is determined by using the bias voltage as a tunable parameter to “focus” on either the molecular film or on the substrate. In this phase adsorption takes place exclusively on the Ag-trimer (CA) site and the CB-site is lost because of strong lateral molecule-molecule interactions. The role of competition between intermolecular and molecule-substrate interactions and the nature of the adsorption sites in determining the structure of the pentacene layers is discussed.