磁性纳米固体酸SO4^2ˉ-TiO2-Fe3O4催化剂的合成、表征及催化性能的研究

首先研究制备了Fe3O4和SO4^2ˉ-TiO2固体酸催化剂，在此基础上采用共沉淀和浸渍的方法制备了磁性和超细SO4^2ˉ-TiO2-Fe3O4固体酸催化剂。利用XRD，TEM和FT—IR等分析测试手段对催化剂的结构和性能进行了表征。测定结果证实该催化剂具有较小的粒度，较高的磁性表现。在乙酸丁酯合成反应中SO4^2ˉ-TiO2-Fe3O4展示了很高的催化活性（酯化率可达82．7％），而且利用Fe3O4的磁性可对催化剂进行分离和回收．     

纳米磁性固体酸SO42-/Zr（OH）4-Fe3O4催化水相不对称Aldol反应

以纳米磁性材料Fe3O4, ZrOCl2·8H2O和硫酸为原料,在不同焙烧温度下制备了纳米磁性固体酸催化剂SO42–/Zr(OH)4-Fe3O4.详细表征了该磁性固体酸的SO42–负载量、酸分布、表面形貌和孔结构等特性.在含有硝基和氰基强吸电子基苯甲醛的不对称水相Aldol反应中, SO42–/Zr(OH)4-Fe3O4表现出优良的催化性能(83%–100%收率,86.0%–95.6% eeanti和anti/syn =88–96/12–4).该类磁性固体酸可在外加磁体作用下定量地从催化反应体系中分离并回收使用,重复使用5次未见显著失活.     

纳米磁性固体酸SO42-/Zr（OH）4-Fe3O4催化水相不对称Aldol反应

以纳米磁性材料Fe3O4, ZrOCl2·8H2O和硫酸为原料,在不同焙烧温度下制备了纳米磁性固体酸催化剂SO42–/Zr(OH)4-Fe3O4.详细表征了该磁性固体酸的SO42–负载量、酸分布、表面形貌和孔结构等特性.在含有硝基和氰基强吸电子基苯甲醛的不对称水相Aldol反应中, SO42–/Zr(OH)4-Fe3O4表现出优良的催化性能(83%–100%收率,86.0%–95.6% eeanti和anti/syn =88–96/12–4).该类磁性固体酸可在外加磁体作用下定量地从催化反应体系中分离并回收使用,重复使用5次未见显著失活.     

纳米磁性固体酸SO_4~(2–)/Zr(OH)_4-Fe_3O_4催化水相不对称Aldol反应（英文）

以纳米磁性材料Fe3O4,Zr OCl2·8H2O和硫酸为原料,在不同焙烧温度下制备了纳米磁性固体酸催化剂SO42–/Zr(OH)4-Fe3O4.详细表征了该磁性固体酸的SO42–负载量、酸分布、表面形貌和孔结构等特性.在含有硝基和氰基强吸电子基苯甲醛的不对称水相Aldol反应中,SO42–/Zr(OH)4-Fe3O4表现出优良的催化性能(83%–100%收率,86.0%–95.6%ee anti和anti/syn=88–96/12–4).该类磁性固体酸可在外加磁体作用下定量地从催化反应体系中分离并回收使用,重复使用5次未见显著失活.     

磁性纳米固体酸催化剂Zr(SO4)2/Fe3O4的制备及催化性能研究

本文提出将磁性和固体酸进行组装从而合成磁性纳米固体酸催化剂的思路,首先制备了纳米级磁性前体－磁基体（Fe3O4);然后筛选出超声波法制备了不同配比的磁性纳米固体酸催化剂Zr(SO4)2/Fe3O4,对其进行了初步表征。并将其作为乙酸丁酯合成反应的催化剂,酯化转化率最高达到84％,利用其磁性即可将催化剂进行分离。     

磁性超细固体酸催化剂SO2-4-ZrO2/Fe3O4的组装及表征

将磁性Fe3O4纳米材料和SO2-4-ZrO2固体酸进行组装,制得一系列具有磁性和超细粒子结构的固体酸催化剂SO2-4-ZrO2/Fe3O4. 采用XRD,TG-DTA和XPS等分析测试手段对催化剂的结构和性能进行了表征. 并分析和测试了催化剂的磁学性能、比表面积、粒度分布和元素的组成等物理化学性质. 该催化剂具有较小的粒度、较高的磁性及酯化催化活性,对乙酸丁酯合成反应的催化活性可达66%; 利用Fe3O4的磁性可对催化剂进行分离和回收. 经高温处理后,固体超强酸的形成对催化剂磁性、比表面积、表相原子的电子结合能以及各组分形态均有显著影响.     

磁性超细固体酸催化剂SO4^2——ZrO2／Fe3O4的组装及表征

将磁性Fe3O4纳米材料和SO4^2--ZrO2固体酸进行组装，制得一系列具有磁性和超细粒子结构的固体酸催化剂SO4^2--ZrO2/Fe3O4，采用XRD，TG－DTA和XPS等分析测试手段对催化剂的结构和性能进行了表征。并分析和测试了催化剂的磁学性能、比表面积、粒度分布和元素的组成等物理化学性质。该催化剂具有较小的粒度、较高的磁性及酯化催化活性，对乙酸丁酯合成反应的催化活性可达66％；利用Fe3O4的磁性可对催化剂进行分离和回收。经高温处理后，固体超强酸的形成对催化剂磁性、比表面积、表相原子的电子结合能以及各组分形态均有显著影响。     

磁性纳米复合氧化物固体酸催化剂的制备及酯化性能

固体酸催化剂的无腐蚀、环境友好和可循环使用等特点使其成为无机液体酸的最佳替代物.磁性纳米固体酸具有优于常规固体酸催化剂的催化活性及分离简单的特性.用共沉淀法分别合成了一系列三组分TiO2-Al2O3-Fe3O4(TAF)和CeO2-Al2O3-Fe3O4(CAF)及四组分ZrO2--Al2O3-Fe3O4(ZACF)磁性纳米复合氧化物固体酸催化剂,通过电感耦合等离子体原子发射光谱、比表面积测定、X射线衍射、透射电镜、热重分析和红外光谱等对其进行了表征,并利用酯化反应作为探针反应评价了其催化性能.结果表明,合成的磁性纳米固体酸催化剂在酯化反应中表现出很好的催化活性.     

磁性固体超强酸SO2-4/TiO2-Fe3O4的制备及表征

固体超强酸是近年来研制开发出的一类新型催化材料[1-4],其克服了传统液体酸催化剂易腐蚀设备、污染环境、副反应多、产物选择性低等缺点.尤其是近年来纳米技术的应用,使得纳米级固体超强酸的研究颇受人们的青睐.但纳米级固体超强酸催化剂在与液体产物的分离及回收中存在困难.为了进一步改良纳米固体超强酸的性能,本研究将磁基体Fe3O4与固体超强酸复合,制得磁性纳米固体超强酸SO42-/ TiO2 - Fe3O4,并对其结构和催化性能进行了表征.     

新型磁性纳米固体酸催化剂ZrO2/Fe3O4的制备及表征

根据将磁性一材料和固体酸进行组装的设想，成功制备了磁性纳米固体酸催化剂。纳米级样性前体-磁基体(Fe3O4)的磁性、粒子尺寸受到Fe^2^+/Fe^3^+投料比和用于沉淀的NaOH浓度的显著影响；不同复合方法也对磁性固体酸催化剂ZrO2/Fe3O4的酯化催化性能影响显著。XRD，XPS，TEM，比表面积测定，元素组成分析及磁学性能测定等表征结果证实，新型催化剂以磁性材料为核，固体酸催化剂活性组分包覆在其外部形成包覆型的磁性纳米催化剂。该系列催化剂均具有较小的粒子尺寸、较强的磁性及较高的酯化催化活性；并且易于通过磁场进行回收，使用寿命较长。它们对乙酸与正丁醇酯化反应的催化活性随着ZrO2含量增加而提高。催化剂中ZrO2的晶化温度因为Fe3O4的存在而升高，有利于催化剂活性的保持，热处理温度会对催化剂的磁性及催化活性产生影响。     

磁性纳米固体酸催化剂Zr(SO_4)_2/Fe_3O_4的制备及催化性能研究

本文提出将磁性和固体酸进行组装从而合成磁性纳米固体酸催化剂的思路,首先制备了纳米级磁性前体一磁基体（Ｆｅ３Ｏ４）;然后筛选出超声波法制备了不同配比的磁性纳米固体酸催化剂Ｚｒ（ＳＯ４）２／Ｆｅ３Ｏ４,对其进行了初步表征。并将其作为乙酸丁酯合成反应的催化剂,酯化转化率最高达到８４％,利用其磁性即可将催化剂进行分离。     

氨法选择性还原氮氧化物 V2O5/TiO2-PILC催化剂的抗硫性能

选择性催化还原(SCR)是目前去除氮氧化物最有效的方法之一. V2O5/TiO2催化剂被广泛应用于氨法选择性还原氮氧化物(NH3-SCR)反应,但该催化剂存在工作温度高(300–400oC)及 SO2氧化率高引起设备腐蚀和管路堵塞等问题,开发低温 SCR催化剂具有重要意义.过渡金属氧化物(如 Fe2O3, MnOx和 CuO等)催化剂用于低温SCR先后见诸文献报道,但这些催化剂在 SO2和 H2O存在下易失活.近年来柱撑黏土(PILC)引起科学家广泛关注, Yang等首次将 V2O5/TiO2-PILC催化剂应用于 NH3-SCR反应,发现其催化活性高于传统 V2O5/TiO2催化剂.柱撑黏土基催化剂在 NH3-SCR反应中也显示出良好抗硫性能,但 V2O5/TiO2-PILC催化剂的抗硫机理至今尚未见深入研究.因此我们制备了一系列 V2O5/TiO2-PILC催化剂,采用原位漫反射红外等方法详细研究了其抗硫性能较好的原因.
　　首先采用离子交换法制备出 TiO2-PILC载体,之后采用浸渍法制备了不同钒含量(质量分数x/%=0,3,4,5)的xV2O5/TiO2-PILC催化剂.同时,制备了传统 V2O5/TiO2和 V2O5-MoO3/TiO2催化剂作为对比.活性评价结果显示,4V/TiO2-PILC催化剂具有最高的催化活性,其催化性能与传统钒钛催化剂相当.在160oC时, NO转化率可达80%以上.同时,4V/TiO2-PILC催化剂还具有较宽的反应温度窗口,在260–500oC范围内, NO转化率保持在90%以上.向反应体系中加入0.05% SO2和10% H2O后,在低温(160oC以下)时所有催化剂的反应活性都有一定提高,可能是由于 SO2的加入提高了催化剂的表面酸性.继续升高温度,4V/TiO2和4V6Mo/TiO2催化剂活性均明显下降,而4V/TiO2-PILC催化剂的活性则未出现明显下降.原位漫反射红外光谱结果显示, SO2在三种催化剂表面的吸附以表面硫酸盐或亚硫酸盐物种以及离子态 SO42–物种形式存在,而在4V/TiO2-PILC催化剂表面离子态 SO42–物种的量最少. X射线光电子能谱及 O2程序升温脱附结果显示,在4V/TiO2-PILC催化剂上,表面吸附氧(Oads)的量最少.综合上述分析可以得出,在 SO2气氛下,离子态 SO42–物种在 SCR催化剂表面的累积可能是导致其失活的主要原因,而离子态 SO42–物种的形成可能与催化剂表面吸附氧的量有关.     

Preparation and Catalytic Activity of SO42-/TiO-La2O3 in Synthesis of Butyl Butyrate

Butyl butyrate is a very important compound, which is transparent liquid and has the pear,apple flavor. Natural exist is in the fruit, such as apple, pear, banana, grape and strawberry, etc.Primarily used for to prepare the edible spice and is also widely used in industrial intermediate product, solvent and synthetic perfumery. Until now, there are many methods to synthesize it.Conventionally H2SO4 was reported, but it causes many problems, such as the erosion of equipment,easily causes the vice-reaction, difficulty for after-treatment, environment pollution etc. A new environmentally friendly catalyst, SO42-/TiO2-La2O3 was prepared. And catalytic activity of catalyst in esterification of n-butanoic acid and n-butyl alcohol with SO42-/TiO2-La2O3 as catalyst has been no report up to now. Therefore, studying on the synthetic catalyst has theoretical and practical significances. The catalytic activity of catalyst in esterification of n-butanoic acid and n-butyl alcohol was measured.In this paper, we fast reported the preparation of SO42-/riO2-La2O3 and discussed the factors influencing the synthesis catalyst. The catalyst rare earth solid superacid SO42-/TiO2-La2O3 was The precipitate was filtered and washed thoroughly with distilled water until chloride ions were free.furnace at 480 ℃ for 3 h, and finally stored in a desiccator until use.The factors influencing the synthesis were discussed and the best conditions were found out. The experiment indicated that this catalyst has the following advantage. The amount of catalyst was little and getting high yield, its product has a good quanlity and is favour of reducing erosion of equipment, avoiding environment pollution. The optimum conditions are: molar ratio of n-butanoic acid to n-butyl alcohol was 1:1.5, the quantity of catalyst was equal to 1.5% of feed stocks, the reaction temperature was 93-114 ℃, and the reaction time was 1.0 h. Rare earth solid superacid SO42-/TiO2-La2O3 is an excellent catalyst for synthetizing butyl butyrate and its yield can reach over 90.0%.A good catalyst should be able to be used repeatedly. The reusing of the catalyst was studied. We found that the catalytic activities of our catalyst are almost unchanged after it had been used five times. From the above results and discussion, we can see that the synthesis of n-butyl butyrate by SO42-/TiO2-La2O3 instead of H2SO4 has a great prospect of application. It has a good applied foreground.     

纳米固体酸催化合成无毒增塑剂柠檬酸三辛酯的研究

以柠檬酸和正辛醇为原料,采用自制的纳米固体酸S04^2-／SnO2、SO4^2-／ZrO2、SO4^2-／TiO2及SO4^2-／Fe2O3催化剂合成无毒增塑剂柠檬酸三辛酯（trioctylcitrate,TOC）。分别考察了纳米催化剂种类、催化剂用量、醇／酸物质的量比、反应时间、反应温度等因素对合成TOC反应酯化率的影响,对合成的产品进行红外光谱分析。实验结果表明,自制的固体酸SO4^2-／SnO2催化合成无毒增塑剂柠檬酸三辛酯的最佳反应条件：催化剂用量为1．0g,酸醇比为1：6.3,反应时间1．0h,反应温度190℃。在最佳反应条件下,柠檬酸三辛酯的酯化率可达到98．5％。     

稀土固体超强酸SO42-/ZrO2-SnO2-Nd2O3的制备及催化合成乙酸松油酯

采用分沉淀-共浸渍法制备了新型稀土固体超强酸SO42-/ZrO2-SnO2-Nd2O3,利用IR、TG-DTA、XRD表征了催化剂的物化性质,并用于催化乙酸酐和松油醇合成乙酸松油酯,显示了良好的反应活性和重复使用性,对反应条件进行了优化,结果表明最佳反应条件为：松油醇和乙酸酐的摩尔比1∶1.5,反应温度50 ℃,反应时间5 h,催化剂用量占松油醇质量的2 %,在此反应条件下松油醇的转化率为93%左右,产物中乙酸松油酯的含量为87%。催化剂失活主要原因是有机物在表面吸附,通过无水乙醇洗涤,干燥,即可再生。     

SO2影响V2O5/AC催化剂脱硝活性的机理

通过O2和SO2瞬态响应实验,研究了有水条件下SO2抑制V2O5/AC(活性焦)催化剂脱硝的原因.结果表明,SO2与V2O5反应生成VOSO4,导致V2O5/AC催化剂的脱硝活性下降.VOSO4的量动态变化,既与气氛中SO2的浓度有关,也与催化剂已实现的脱硫量(或硫含量)有关.催化剂的微孔(d<1nm)有利于SO3的迁移和储存,从而有利于脱硝.     

固体酸催化合成邻苯二甲酸二戊酯的研究

以苯酐和正戊醇为原料,采用自制的固体酸SO4^2-／SiO2、SO4^2-／Fe2O3、SO4^2-／SnO2及SO4^2-／TiO2作为催化剂合成邻苯二甲酸二戊酯（DAP）,分别考察固体酸催化剂的种类、固体酸催化剂的用量、醇酐比、反应时间等因素对合成DAP产率的影响。实验结果表明,其优化的工艺操作条件为：苯酐0．1mol,固体酸催化剂SO4^2-／SiO2 1．7g,醇酐比2．4：1,带水剂二甲苯20mL,反应时间3．5h,其产品收率达91．3％以上。SO4^2-／SnO2作为该反应的催化剂具有催化活性高、寿命长、可多次重复使用、产物易纯化分离且产品色泽浅等优点,可望代替传统的浓硫酸作催化剂应用于DAP的合成。     

NO-NH_3-O_2 reaction catalyzed by V_2O_5/AC at low temperatures——Effects of SO_2, V_2O_5 loading and reaction temperature

The effects of SO2, V2O5 loading and reaction temperature on the activity of activated carbon supported vanadium oxide catalyst have been studied for the reduction of NO with NH3 at low temperatures (150-250℃). It is found that SO2 significantly promotes the catalyst activity. Both V2O5 loading and reaction temperature are vital to the promoting effect of SO2. The catalysts with V2O5 loadings of 1 -5 weight percent have a positive effect on the promotion of SO2, while the catalysts with V2O5 loadings of above 7 weight percent have not such an effect or show a negative effect. At lower temperatures (<180℃) SO2 poisons the catalyst but at higher temperatures promotes it. The reason of the SO2 promotion was also discussed; it may results from the formation of SO42- on the catalyst surface, which increases the surface acidity and hence the catalytic activity.     

双相体系中凹土负载型固体酸 SO42-/In2O3-ATP催化己糖降解5-羟甲基糠醛

凹土(ATP)有“千用之土、万土之王”之美誉,我国江苏省盱眙凹土矿资源量占世界储量的49%和我国储量的74%. ATP是一种天然链层状结构的含水镁铝硅酸盐黏土矿物,其分子式为(Mg,Al)4(Si)8(O,OH,H2O)26·nH2O. ATP具有一定酸性,层结构中的结构羟基可形成 Br?nsted酸位点,暴露的 Al3+离子可形成 Lewis酸位点. ATP经酸化或离子交换后作为催化剂直接应用较少.由于 ATP具有较大的比表面积和较好的热稳定性,是良好的催化剂载体,因此多将 ATP作为载体负载催化活性组分制备负载型催化剂. 5-羟甲基糠醛(HMF)是由生物质得到的十二种平台化合物之一,是非常重要的中间体,可用于生产呋喃类衍生物,制备精细化学品、液体燃料和多种聚合物,还可生产5-羟基-4-酮-2-戊烯酸和乙酰丙酸.γ-戊内酯(GVL)是一种乙酰丙酸的加氢产物,可以代替乙醇作为汽油添加剂,也可用来生产丁烯同分异构体等化学品.本文以天然 ATP为载体,通过浸渍-焙烧法设计和制备了兼具 Br?nsted酸和 Lewis酸的新型固体酸催化剂 SO42?/In2O3-ATP.该催化剂可催化己糖直接转化为 HMF. ATP固有的微观结构和高比表面积使反应选择性提高.同时,结合固体酸活性位表征技术探索了己糖转化历程和 HMF生成机制.结果表明, In(III)的引入使 ATP催化性能更加优越.固体酸的 Lewis酸位和 Br?nsted酸位能分别有效催化葡萄糖异构和果糖脱水.优化的最佳反应条件为： GVL：H2O双相体系比例9：1,反应温度180oC,反应时间60 min.底物为葡萄糖时, HMF最高收率为40%. SO42?/In2O3-ATP固体酸比纯 ATP酸性更强,可重复使用4次,且不腐蚀设备,后处理简单,绿色环保.