锂离子电池正极材料LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2在LiNO_3溶液中的电化学性能研究

由溶胶凝胶法合成的锂离子电池正极材料LiNi1/3Co1/3Mn1/3O2在水溶液体系中具有优异的高倍率充放电性能,放电时能够输出极高功率密度.XRD表征证明合成的LiNi1/3Co1/3Mn1/3O2材料具有层状α-NaFeO2结构,SEM形貌显示材料的粒径约为500nm,恒电流充放电测试表明LiNi1/3Co1/3Mn1/3O2材料在pH12的2mol·L-1LiNO3溶液中,以2C(0.36A/g)倍率充放时,比容量达到了147mAh/g.如以80C(14.4A/g)、150C(27A/g)和220C(39.6A/g)的倍率充放,材料的比容量仍可达到64mAh/g、33mAh/g和16mAh/g,而全电池的功率密度分别达到2574W/kg、3925W/kg、4967W/kg.其中80C倍率充放,经1000周循环后,容量保持率为90.9%.     

锌掺杂提高LiNi1/3Co1/3Mn1/3O2正极材料的电化学稳定性

通过共沉淀法与固相法相结合制备了掺锌的高稳定性Li(Ni1/3Co1/3Mn1/3)1-xZnxO2(x=0,0.02,0.05)正极材料.循环伏安(CV)曲线表明Zn掺杂使氧化峰与还原峰的电势差减小到0.09 V,电化学阻抗谱(EIS)曲线表明Zn掺杂使电极的阻抗从266Ω减小到102Ω. Li+嵌入扩散系数从1.20×10-11 cm2·s-1增大到2.54×10-11 cm2· s-1. Li(Ni1/3Co1/3Mn1/3)0.98Zn0.02O2正极材料以0.3C充放电在较高的截止电压(4.6 V)下比其他两种材料的电化学循环性能更稳定,其第二周的放电比容量为176.2 mAh·g-1,室温下循环100周后容量几乎没衰减;高温(55°C)下充放电循环100周,其放电比容量平均每周仅衰减0.20%,远小于其他两种正极材料(LiNi1/3Co1/3Mn1/3O2平均每周衰减0.54%;Li(Ni1/3Co1/3Mn1/3)0.95Zn0.05O2平均每周衰减0.38%). Li(Ni1/3Co1/3Mn1/3)0.98Zn0.02O2正极材料以3C充放电时其放电比容量可达142 mAh·g-1,高于其他两种正极材料.电化学稳定性的提高归因于Zn掺杂后减小了电极的极化和阻抗,增大了锂离子扩散系数     

锂离子电池正极材料LiNi1/3Co1/3Mn1/3O2的制备及其电化学性能

以Ni1/3Co1/3Mn1/3(OH)2(2)和Li2CO3为原料,在空气气氛中,经过高温热处理工艺制备了高结晶度的锂离子电池正极材料LiNi1/3Co1/3Mn1/3O2(1)。正交试验确定最佳工艺条件为:2 0.3 mol,n(Li):n(2)=1.2,于950℃反应13 h。电化学性能研究结果表明,在2.7 V～4.6 V,电流密度16 mA.g-1时,1的首次放电比容量为203.4 mAh.g-1;经16 mA.g-1循环2次,32 mA.g-1循环9次,80 mA.g-1循环20次后放电比容量为164.1 mAh.g-1。     

锂离子正极材料Li(Ni_(1/3)Co_(1/3)Mn_(1/3))_(1-x)Al_xO_2的制备及电化学性能

以化学法合成Li(Ni1/3Co1/3Mn1/3)1-xAlxO2系列正极材料(0≤x≤0.1);用X射线衍射仪、扫描电子显微镜和充放电仪研究系列产物的晶体微观结构、表面形貌以及电化学性能,研究不同Al含量参杂对材料性能的影响。结果表明,合成的材料均属于六方晶系,R3m空间群,保持α-NaFeO2层状结构相;Li(Ni1/3Co1/3Mn1/3)0.95Al0.05O2的首次放电容量166.30 mA·h/g,在2.5~4.5 V区间60次循环后比容量衰竭率为4.43%。通过对比Li(Ni1/3Co1/3Mn1/3)0.95Al0.05O2和Li(Ni1/3Co1/3Mn1/3)O2的电极阻抗,分析它们的电化学循环机理,可知掺杂Al后的正极材料适合大倍率放电。     

湿化学法合成LiNi_(1/3)Mn_(1/3)Co_(1/3)O_2及其表征(英文)

利用琥珀酸为鳌合剂的湿化学法成功合成了一系列锂离子电池正极材料LiNi1/3Mn1/3Co1/3O2,在合成过程中改变琥珀酸与金属离子摩尔比(R)并研究了这一参数对合成LiNi1/3Mn1/3Co1/3O2材料物理及电化学性质的影响.采用热重、X射线衍射、Rietveld精修、扫描电镜以及超导量子干涉仪对反应机理、材料的结构、形貌以及磁学性质进行了详细表征.得到最佳合成条件为R=1,此时LiNi1/3Mn1/3Co1/3O2的阳离子混排度最低.此外,通过Rietveld精修得到该材料阳离子混排度的结果与通过磁学方法得到的结果定量相符,如对于在R=1条件下合成的样品,Rietveld精修结果显示其阳离子混排度为1.85%,而超导量子干涉仪的测试结果为1.80%.当充放电区间为3.0-4.3V,电流密度为0.2C(1C=160mA·g-1)时,该样品的首次放电容量为161mAh·g-1,库仑效率为93.1%,经过50次循环后,容量保持率可达91.3%.     

锂离子电池正极材料xLi2MnO3·(1-x)Li[Ni1/3Mn1/3Co1/3]O2的制备及表征

以过渡金属乙酸盐和乙酸锂为原料,柠檬酸为螯合剂,通过溶胶-凝胶法结合高温煅烧法制备了锂离子电池富锂锰基正极材料xLi2MnO3·(1-x)Li[Ni1/3Mn1/3Co1/3]O2,采用X射线衍射(XRD),扫描电子显微镜(SEM)和电化学性能测试对所得样品的结构,形貌及电化学性能进行了表征.结果表明:x=0.5时,在900°C下煅烧12h得到颗粒均匀细小的层状xLi2MnO3·(1-x)Li[Ni1/3Mn1/3Co1/3]O2材料,并具有良好的电化学性能,在室温下以20mA·g-1的电流密度充放电,2.0-4.8V电位范围内首次放电比容量高达260.0mAh·g-1,循环40次后放电比容量为244.7mAh·g-1,容量保持率为94.12%.     

高镍系正极材料LiNi0.88Co0.07Al0.05O2的制备及性能表征

以镍钴氢氧化物为原料,采用异丙醇铝水解法合成Ni0.88Co0.07Al0.05(OH)2,将前驱体与锂源充分混合,通过3种烧结条件制备出球形LiNi0.88Co0.07Al0.05O2正极材料,借助X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、X射线光电子能谱(XPS)以及电化学测试等表征手段对材料的晶体结构、微观形貌和电化学性能进行了较系统的研究。研究表明,在500℃下保温3 h、700℃下保温14 h的条件下合成的LiNi0.88Co0.07Al0.05O2具有良好的综合电化学性能,0.2C放电比容量达192.2 mAh·g^-1,首次充放电效率为81.6%,1C放电比容量为190.7 mAh·g^-1,100周后放电比容量为141.1 mAh·g^-1,容量保持率达到73.4%。     

球磨微波法制备Li3V2（PO4）3/C及其电化学性能表征

本文采用球磨微波法合成锂离子电池正极材料Li3V2(PO4)3/C,并研究了微波辐射时间对样品电化学性能的影响.结果表明,640 W微波辐射18 min合成的材料,结晶度高,粒径小而均匀.该电极5C倍率下首次放电比容量达101.3 mAh·g-1,300周期循环,其放电比容量仍保持100.8 mAh·g-1,展示出良好的应用前景.     

xLi2MnO3·(1-x)LiNi1/3Co1/3Mn1/3O2(x=0.1、0.2、0.3和0.4)固溶体材料性能研究

通过LiNO3与Mn(NO3)2的混合溶液与LiNi1/3Co1/3Mn1/3O2粉体共混干燥后在900℃热处理12 h制备了xLi2MnO3.(1-x)LiNi1/3Co1/3Mn1/3O2(x=0.1、0.2、0.3和0.4)固溶体。随着x的增加,固溶体的XRD峰强度减弱,峰形变宽,而在20°~30°间的结构特征峰(LiMn6)更加明显;尽管固溶体的外观形貌为团聚状,但组成其的单颗粒平均粒径随着x增大,由x=0.1时的250 nm增大到x=0.4时的350 nm。随着充放电截止电压的升高,固溶体的放电比容量增大;在2.5~4.6 V间充放电,当x=0.2时,充放电的极化最小,放电平台最高;不同倍率充放电循环21周后发现随着x的增大,容量保持率从91.2%增加大105.6%。研究结果表明,Li2MnO3可以改善LiNi1/3Co1/3Mn1/3O2材料的电化学性能。     

A1掺杂量对正极材料LiNi_(1/3)Co_(2/3-x)A1_xO_2结构和电化学性能的影响

以共沉淀法合成的前驱体Ni_(1/3)Co_(2/3-x)Al_x(OH)_2与低共熔锂盐0.38LiOH·H_2O-0.62LiNO_3制备了锂离子电池正极材料LiNi_(1/3)Co_(2/3-x)Al_xO_2(x=1/12,1/3,1/2,7/12).采用X射线衍射(XRD)、扫描电镜(SEM)和电化学性能测试对其结构、形貌和电化学性质进行表征.结果表明,LiNi_(1/3)Co_(2/3-x)Al_xO_2在1/12≤x≤1/3范围内可以保持单一的六方层状a-NaFeO_2结构,当A1掺杂量(x)高于1/3时,会出现杂相.其中,LiNi_(1/3)Co_(1/3)Al_(1/3)O_2结晶程度最高,阳离子混排效应最小,并且颗粒小而均匀,振实密度可以达到2.88 g·cm~(-3),首次放电容量为151.5 mAh·g~(-1),循环50次后放电容量保持在91.4%,在1C和2C倍率下放电容量仍可达到133.7和120.9 mAh·g~(-1)     

Effect of Various Synthesis methods on the Electrochemical Properties of LiNi1/3Co1/3Mn1/3O2

Layered LiNi1/3Co1/3Mn1/3O2 has the isostructure of α-NaFeO2 and shows high rate capacity with stable cycleability. Furthermore, the thermal behavior of this material is milder than that of lithium nickel oxide and lithium cobalt oxide. In addition, it is expected to be stable at elevated temperatures. Therefore LiNi1/3Co1/3Mn1/3O2 may be the most promising cathode materials of lithium-ion secondary battery.In this research, LiNi1/3Co1/3Mn1/3O2 was prepared by solid-state reaction, sol-gel method and mixed hydroxide method. The influences of synthesis method on the physical and electrochemical properties of LiNi1/3Co1/3Mn1/3O2 were characterized by means of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM), charge/discharge cycling cyclic voltammetry and differential scanning calorimetry (DSC). XPS studies show that the predominant oxidation states of Ni, Co and Mn in the LiNi1/3Co1/3Mn1/3O2 compound are 2+, 3+ and 4+. From the voltage profile and cyclic voltammetry, the redox processes occurring at ～3.8V and ～4.5V are assigned to the Ni2+/Ni3+ and Co3+/Co4+ couples, respectively. Different preparation methods result in the difference in morphology (shape, particle size and specific surface area) and electrochemical behaviors. A sample prepared by solid-state reaction has the worst electrochemical performance among these three methods. Sample synthesized by mixed hydroxide method displays the better rate capacity than that prepared by sol-gel method, while the capacity retention of sample prepared by sol-gel method is superior to that synthesized by mixed hydroxide method.     

回火处理对LiNi1/3Co1/3Mn1/3O2结构和电化学性能的影响

以硝酸锂、四水合乙酸镍、四水合乙酸钴、四水合乙酸锰、氨水和草酸为原料,通过共沉淀-燃烧法合成了锂离子电池正极材料LiNi1/3Co1/3Mn1/3O2,采用XRD、SEM和充放电试验对合成产物进行了表征,研究了回火处理对合成产物结构和电化学性能的影响.实验结果表明,嫩烧反应形成的LiNi1/3C1/3Mn31/3O2结...     

高倍率性能锂离子电池Li[Ni1/3Co1/3Mn1/3]O2正极材料的制备及其电化学性能

采用改进的碳酸盐共沉淀与高温固相法相结合的方法制备出了高倍率性能的锂离子电池正极材料Li[Ni_1/3Co_1/3Mn_1/3]O₂, 通过X射线衍射(XRD)、扫描电镜(SEM)、循环伏安扫描(CV)、电化学阻抗谱(EIS)和电化学性能测试等手段对材料进行表征. 结果表明, 该方法制备的材料具有良好的α-NaFeO₂型层状结构(R3m(166)), 一次粒径平均大小为157 nm, 二次颗粒成球形. 同传统碳酸盐制备得到的材料相比, 该材料具备良好的倍率性能和循环性能, 在2.7-4.3 V 电压范围内, 0.1C (1.0C=180 mA·g^-1)倍率下, 首次放电比容量为156.4mAh·g^-1, 库仑效率为81.9%. 在较高倍率下, 即0.5C、5.0C和20C时, 其放电比容量分别为136.9、111.3、81.3mAh·g^-1. 在1C倍率下100次循环容量保持率为92.9%, 高于传统共沉淀法得到的材料(87.0%).     

放电温度对LiNi3/8Co2/8Mn3/8O2电化学性能的影响

采用X射线衍射（XRD）、X射线光电子能谱（XPS）、恒流充放电、循环伏安及交流阻抗法，研究了放电温度对LiNi3/8Co2/8Mn3/8O2的倍率特性、锂离子扩散及电荷传递的影响.结果表明， 提高放电温度可显著改善LiNi3/8Co2/8Mn3/8O2的放电容量与倍率放电性能.尽管温度升高使电荷传递活性与锂离子扩散速度都增加，但电荷传递活化能比锂离子扩散活化能大一倍多，表明电荷传递步骤是其电化学反应控制步骤.温度对其电荷传递的影响大于对锂离子扩散的影响.温度升高，电荷传递速率加快，电化学嵌入-迁出反应加速，是其放电容量与倍率放电特性显著改善的主要原因.     

共沸蒸馏法制备高性能LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2正极材料

三元复合氧化物镍钴锰酸锂(LiNi1/3Co1/3Mn1/3O2)因兼有LiNiO2和LiCoO2的优点,被认为是最有可能取代LiCoO2的新型正极材料而受到广泛关注.本文采用一种改进的共沉淀方法合成了LiNi1/3Co1/3Mn1/3O2,以共沸蒸馏干燥前驱物.结果表明,共沸干燥法最终得到的产物比普通干燥法得到的产物具有更高的比容量、更好的循环性能以及更优的倍率性能.究其原因,可归结为共沸干燥得到的样品颗粒更小,且粒径分布更均匀,球形度高,比表面积大,促进了锂离子的扩散,因而提高了其电化学性能.     

锌掺杂提高LiNi1/3Co1/3Mn1/3O2正极材料的电化学稳定性

通过共沉淀法与固相法相结合制备了掺锌的高稳定性Li(Ni_1/3Co_1/3Mn_1/3)_1-xZn_xO₂ (x=0, 0.02, 0.05)正极材料. 循环伏安(CV)曲线表明Zn掺杂使氧化峰与还原峰的电势差减小到0.09 V, 电化学阻抗谱(EIS)曲线表明Zn掺杂使电极的阻抗从266 Ω减小到102 Ω. Li⁺嵌入扩散系数从1.20×10^-11 cm²·s^-1增大到 2.54×10^-11 cm²·s^-1. Li(Ni_1/3Co_1/3Mn_1/3)_0.98Zn_0.02O₂正极材料以0.3C充放电在较高的截止电压(4.6 V)下比其他两种材料的电化学循环性能更稳定, 其第二周的放电比容量为176.2 mAh·g^-1, 循环100周后容量几乎没衰减; 高温(55 °C)下充放电循环100周, 其放电比容量平均每周仅衰减0.20%, 远小于其他两种正极材料(LiNi_1/3Co_1/3Mn_1/3O₂平均每周衰减0.54%; Li(Ni_1/3Co_1/3Mn_1/3)_0.95Zn_0.05O₂平均每周衰减0.38%). Li(Ni_1/3Co_1/3Mn_1/3)_0.98Zn_0.02O₂正极材料以3C充放电时其放电比容量可达142 mAh·g^-1, 高于其他两种正极材料. 电化学稳定性的提高归因于Zn掺杂后减小了电极的极化和阻抗, 增大了锂离子扩散系数.     

草酸盐共沉淀法制备锂离子电池正极材料LiNi0.5Mn0.5O2及其电化学性能

使用草酸盐共沉淀法合成了LiNi0.5Mn0.5O2, 并研究了共沉淀时的pH条件对终产物的结构、形貌及电化学性能的影响. 采用X射线衍射(XRD)和扫描电镜(SEM)表征了在pH值为4.0、5.5、7.0和8.5时得到的共沉淀和终产物LiNi0.5Mn0.5O2的结构和形貌. 使用充放电实验研究了不同pH条件下得到的LiNi0.5Mn0.5O2的电化学性能. 结果表明, pH为7.0时, 合成的材料颗粒更小、分布最均匀, 材料具有良好的层状特征, 且材料中锂镍的混排程度最小. 电化学测试结果印证了pH为7.0时合成的材料具有更好的电化学性能, 在0.1C的倍率下, 材料的首次放电比容量达到了185 mAh·g-1, 在循环20周后, 放电比容量仍然保持在160 mAh·g-1. X射线光电子能谱(XPS)测试结果表明, pH为7.0时合成的LiNi0.5Mn0.5O2中Ni为+2价, Mn为+4价.