Large enhancement of room temperature magnetoresistance in Ag-added La0.67(Ca0.65Ba0.35)0.33MnO3

The electrical and magnetoresistant properties of La_0.67(Ca_0.65Ba_0.35)_0.33MnO₃/Ag_x (abbreviated by LCBMO/Ag_x) have been studied. The results show that Ag addition causes a decrease of resistivity dramatically and especially induces a large enhancement of room temperature magnetoresistance (MR). The room temperature MR ratio for x=0.27 sample in 10 kOe magnetic field is 41%, almost 20 times larger than that for x=0 sample. This enhancement is related to that the Curie temperature (T_c) of the sample is near room temperature, as well as the significant reduction of resistivity. The good fits of experimental results for x=0.27 sample to Brillouin function indicate that the MR behavior in the Ag added LCBMO is induced by the spin-dependent hopping of the electrons between the spin clusters, which is an intrinsic property of the CMR materials.