Low voltage electron induced cathodoluminescence degradation and surface characterization of Sr3(PO4)2:Tb phosphor |
| |
| Authors: | IM Nagpure Shreyas S PitaleE Coetsee OM NtwaeaborwaJJ Terblans HC Swart |
| |
| Institution: | Department of Physics, University of the Free State, P.O. Box 339, Bloemfontein 9300, South Africa |
| |
| Abstract: | Tb3+-doped Sr3(PO4)2 phosphor was prepared by a sol-gel combustion method. A trigonal structure having Sr and O atoms occupying two different lattice sites were obtained. Scanning Auger nanoprobe was used to analyze the morphology of the particles. Photoluminescence (PL) and cathodoluminescence (CL) properties of Sr3(PO4)2:Tb powder phosphors were evaluated and compared. In addition, the CL intensity degradation of Sr3(PO4)2:Tb was evaluated when the powders were irradiated with a beam of electrons in a vacuum chamber maintained at an O2 pressure of 1 × 10−6 Torr or a background pressure of 1 × 10−8 Torr O2. The surface chemical composition of the degraded powders, analyzed by X-ray photoelectron spectroscopy (XPS), suggests that new compounds (metal oxides) of strontium and phosphorous were formed on the surface. It is most likely that these compounds contributed to the CL intensity degradation of the Sr3(PO4)2:Tb phosphors. The CL properties and possible mechanism by which the new metal oxides were formed on the surface due to a prolonged electron beam irradiation are discussed. |
| |
| Keywords: | AES NanoSAM Photoluminescence Cathodoluminescence XPS ESSCR Electron degradation Sr3(PO4)2 |
| 本文献已被 ScienceDirect 等数据库收录！ |