Effect of Co underlayer on soft magnetic properties and microstructure of FeCo thin films

High saturation magnetization soft magnetic FeCo (=Fe₆₅Co₃₅) films were prepared using a thin Co underlayer. The FeCo/Co films exhibited a well-defined in-plane uniaxial anisotropy with easy axis coercivity (H_ce) of 10 Oe and hard axis coercivity (H_ch) of 3 Oe, and a half reduction of H_c with H_ce=4.8 Oe and H_ch=1.0 Oe was obtained when the composition was adjusted to 25 at% Co. The effective permeability of the films remains flat around 250 to 800 MHz. The saturation magnetostriction was 5.2×10⁻⁵ and the intrinsic stress was 0.8 GPa in FeCo single layer, both were slightly reduced by Co underlayer. The Co underlayer changed the preferred orientation of the FeCo films from (2 0 0) to (1 1 0) but more significantly, reduced the average grain size from ∼74 to ∼8.2 nm. It also reduced the surface roughness from 2.351 to 0.751 nm. The initial stage and interface diffusion properties were examined by TEM and XPS.