Transparent conductive graphene films prepared by hydroiodic acid and thermal reduction

Transparent conductive graphene films are fabricated by the transfer printing of graphene aqueous dispersion followed by hydrohalic acids and thermal reduction. Results indicate that the graphene film reduced by hydroiodic acid （HI） reduction combined with thermal treatment shows a higher electrical conductivity than that reduced only by thermal treatment at the same transparency. A film with a sheet resistance of - 2400 D./sq at a transparency over 72% is obtained at a typical wavelength of 550 nm.     

多元醇一步法制备高碳烃液体燃料的研究

在较温和的条件下,山梨醇和木糖醇被氢碘酸还原转化为高碳烃液体燃料。产物采用GC-MS和FT-IR进行定量分析与表征,并对高碳烃产品的理化性质进行了测定。结果表明,以山梨醇为原料制备的高碳烃产物主要是包括C12H16、C12H18、C12H20、C12H22和C18H26在内的烷烃、烯烃和芳香烃等化合物,烃类的总产率可达85.1%。以木糖醇为原料的反应过程与山梨醇相似,但所得高碳烃是以C10和C15为主的烃类化合物,产率为62.8%。实验还以质量分数为50%的山梨醇和50%的木糖醇混合物为原料制备了高碳烃,结果发现,产物中除C10、C12、C15和C18烃外,还有一定量的C11烃生成,高碳烃产率为65.4%。反应产物经碱化、旋转蒸发和减压蒸馏后分离得到纯度较高的高碳烃,其含水量低于0.2%,常温下运动黏度为3.15~3.17 mm2/s,密度为0.830~0.840 g/mL,含氧量为1.8%~2.1%,热值高于43 MJ/kg。高碳烃的生成是由于多元醇被还原过程中C-I键的极性反转和分子间C-C键的偶联导致。     

动态离子交换法制备氢碘酸的研究

以粗碘为原料,水合肼为还原剂,采用动态离子交换工艺制备氢碘酸。研究了过柱流速、树脂层高度、过柱次数、交换介质等因素对产品氢离子浓度和铵交换率的影响。结果表明,在过柱流速1.2mL/min、树脂层高度33cm,沸石与树脂相结合2次过柱条件下,氢离子浓度达到1.40mol/L,铵交换率达到96%。在真空度0.07MPa,蒸发温度80℃的条件下减压蒸馏成功制备出浓度47%的氢碘酸产品,产品各项指标满足行业标准HG 3-952-76的要求。     

静态离子交换法制备氢碘酸的研究

以磷酸生产过程中回收的粗碘为原料,采用静态离子交换法制备氢碘酸。通过He准数法和中断接触法相结合判断离子交换过程的控制机理,考察了树脂用量、交换时间、搅拌速度、交换温度等因素对氢离子浓度和铵交换率的影响。结果表明,离子交换过程为颗粒扩散控制;在树脂与粗碘质量比5:1、搅拌速度600r/min、交换时间20min、交换温度40℃条件下,氢离子浓度达到1.86mol/L,铵交换率达到92%。在真空度0.07MPa,蒸发温度80℃的条件下,减压蒸馏制备出浓度为47%的氢碘酸,产品各项指标均符合行业标准HG 3-952-76的要求。