用于白光LED的高亮度蓝白色荧光粉Ca2SiO3Cl2：Eu2+的发光性质

采用固相法在较低温度下合成了Eu²⁺激活的Ca₂SiO₃Cl₂高亮度蓝白色发光材料,并对其发光性质进行了研究。其发射光谱由两个谱带组成,峰值分别位于420,498nm处,归结为Ca₂SiO₃Cl₂晶体中占据两种不同Ca²⁺格位的Eu²⁺离子的5d→4f跃迁发射。改变Eu²⁺浓度,可以使样品的发光在蓝白色和绿白色之间变化。当Eu²⁺浓度为0.005mol^-1时,样品呈现很亮的蓝白色发光。两个发射峰的激发光谱均分布在250~410nm的波长范围内,峰值分别位于333,369nm处。Ca₂SiO₃Cl₂:Eu²⁺可被InGaN管芯产生的近紫外辐射有效激发,是一种性能良好的白光LED用单一基质蓝白色荧光粉。     

溶胶-凝胶法制备小颗粒(Y,Gd)BO_3∶Eu及其表征

用溶胶 凝胶方法制备了平均粒径为 1～ 2 μm的小颗粒、高发射效率的 (Y ,Gd)BO3 ∶Eu红色发射荧光体。用XRD、SEM、粒度分析和PL光谱对荧光体作了表征和研究。常规固相反应合成 (Y ,Gd)BO3 ∶Eu需在 1 2 0 0℃以上才能形成均一的固溶体。而溶胶 凝胶法制取稀土正硼酸盐 80 0℃灼烧已可形成均一的单相 (Y ,Gd)BO3 ∶Eu,在 1 1 0 0℃可得到发光亮度最高的荧光体。它的亮度是常规固相反应于 1 2 0 0℃制得的荧光体的 1 2 0 %。采用溶胶 凝胶法制取 (Y ,Gd)BO3 ∶Eu荧光体 ,可在相当宽的实验条件范围内得到小粒径、窄分布和高亮度的荧光体 ,且有良好的颗粒形貌。     

绿色荧光粉YAGG∶Tb,Gd用于FED的尝试

FED器件的发展迫切需要具有化学和热稳定性 ,高亮度 ,长寿命的新型荧光材料。本文合成了Gd3 +离子共掺杂的YAGG∶Tb获得了YAGG∶Tb ,Gd ,并将其用于 0～ 30 0 0V低压范围 ,对其在不同电压和电流密度下的发光特性进行了测试。结果表明 ,该种材料特性优于ZnO∶Zn并且不存在电压与电流饱和     

Optical properties of a high-efficiency glass ceramic X-ray storage phosphor

The turbidity, photoluminescence, and photo-stimulated luminescence (PSL) of fluorozirconate glass containing barium chloride nano- and micro-crystals have been measured for samples prepared by isochronal (70 min) annealing over a temperature range of 220–283°C, and correlated with the microstructure as determined by X-ray diffraction measurements. Crystallization of hexagonal phase barium chloride commences at around 220°C, but until 275°C the material retains excellent transparency although it displays negligible PSL. Between 275°C and 277°C, the hexagonal phase converts to the orthorhombic phase, the transparency abruptly decreases, and the PSL rises to a value of around 13% of that found for the commercial storage phosphor BaFBr:Eu. For a slightly higher temperature of 280°C, new phases appear which correspond to the onset of bulk crystallization, and at 283°C the relative PSL rises to 33%, while the transparency falls further. The trade-off between optical transparency and PSL over this narrow temperature window for X-ray imaging plate applications is briefly discussed.     

New developments in X-ray storage phosphors

We found a significant PSL effect in Eu²⁺-doped fluorozirconate glasses (ZBLAN) which were additionally doped with Br⁻ or Cl⁻ ions. The PSL is attributed to the characteristic emission of Eu²⁺ present in nano-crystallites of BaBr₂ or BaCl₂, which form in the glass upon annealing. The metastable hexagonal form of BaX₂ (X=Br,Cl) is always formed first before it is converted into the stable orthorhombic form. The particle size increases upon annealing and so does the PSL efficiency of the glass ceramic. However, there is a saturation of the PSL efficiency, which is for Br⁻ doping about 9% and for Cl⁻-doping about 80% of the Eu-doped BaFBr standard. The particle size was determined by transmission electron microscopy (TEM). The TEM results show a clear tendency for bigger particles for longer annealing at the expense of its number. The particle size for the most efficient phosphor is about 100 nm.     

Eu,Dy共掺杂SrAl2O4长余辉材料制备新工艺

活化Al-Sr合金粉末水解制备SrAl₂O₄长余辉材料的前驱体,并采用高温固相反应法制备出Eu,Dy共掺杂的SrAl₂O₄长余辉材料,对其微观结构和发光特性进行了研究。实验结果表明:前驱体中Al、Sr元素在微观状态下分布均匀,所制成的长余辉发光材料的发射主峰位于520nm附近,为典型的Eu²⁺离子4f5d-4f的特征发射,初始亮度达到18cd/m²,余辉时间长达46h。     

Ce3+离子敏化Eu3+∶Cr3+∶Sm3+∶YAG外延层的荧光现象

对Ce3+ ∶Eu3+ ∶Cr3+ ∶Sm3+ ∶YAG处延层中的荧光敏化现象进行了报道和分析 ,在较高浓度的Ce3+ 离子掺杂时 ,外延层在蓝色、绿色波段出现了新的荧光谱线 ,可解释为在Ce3+ 离子敏化作用下 ,Eu3+ 离子产生了由高位激发态能级5Di(i=1,2 ,3)直接到基态能级7Fj(j =0 ,1,2 ,3)的辐射跃迁过程 ,并且这种Ce3+ ∶Eu3+ ∶Cr3+ ∶Sm3+ ∶YAG外延层还是一种新颖的白色单晶荧光材料。     

一类新的红色荧光粉MY2S4:Er3+(M=Sr2+,Ba2+)的合成与表征

Eu2 激活的CaS: Eu[1],Eu3 激活的硫氧化物[2]，Pr3 激活的Ca0.8Zn0.2TiO3[3]以及Eu2 和Mn2 掺杂的SrY2S4[4]都是重要的红色发光材料.     

助熔剂对Y3Al5O12：Ce荧光粉性能的影响

在还原气氛下采用高温固相反应法合成了白光LED用黄色荧光粉Y3Al5O12:Ce(YAG:Ce)研究了助熔剂对YAG：Ce荧光粉发光特性的影响，。XRD的测量结果表明加入合适的助熔剂有利于YAG:Ce荧光粉的晶化，并且不引入杂相，选择BaF2和H3BO3同时使用效果要好于单独使用一种助熔剂，助熔剂的加入可增大YAG：Ce荧光粉的激发和发射光谱强度，并能有效降低荧光粉的中心粒径（D50）控制粉体的粒径分布，适用于白光LED的制造。