基于响应面法的直拉硅单晶生长工艺参数优化方法

在直拉法制备硅单晶的过程中,要得到优质的晶体必须建立合理的温度分布,而单晶炉内热场的分布与工艺参数的设定密切相关.其中以晶体转速、坩埚转速和拉速等三个工艺参数对热场分布的影响尤为显著.为了确定最佳热场分布下晶转、埚转及拉速的设定值,本文采用响应面算法通过方程拟合、回归分析等步骤求解这三个工艺参量与温度梯度之间的最佳函数模型,并在该模型下同时对这三个工艺参量进行优化分析,且通过仿真实验和拉晶实验表明该方法的有效性.     

织构C60薄膜的生长与光致发光特性

用Hot Wal方法，在氟金云母单晶上生长出了（111）织构的C₆₀薄膜．用X射线衍射、Raman散射、扫描电子显微镜和原子力显微镜研究了织构C₆₀薄膜的结晶质量和结构特性．测量了织构C₆₀薄膜在室温300K和低温77K的光致发光光谱．对所得结果进行了分析与讨论 关键词：     

Scanning tunnelling microscope studies of growth of RuO2（110） thin layer on Ru（0001）

This paper reports that the growth of RuO_x(110) thin layer growth on Ru(0001) has been investigated by means of scanning tunnelling microscope (STM). The STM images showed a domain structure with three rotational domains of RuO_x(110) rotated by an angle of 120℃. The as-grown RuO_x(110) thin layer is expanded from the bulk-truncated RuO_x(110) due to the large mismatch between RuO_x(110) and the Ru(0001) substrate. The results also indicate that growth of RuO_x(110) thin layer on the Ru(0001) substrate by oxidation tends first to formation of the Ru-O (oxygen) chains in the [001] direction of RuO_x(110).     

磁控溅射ZnO薄膜生长的等离子体发射光谱研究

通过反应磁控溅射过程中的等离子体发射光谱，研究了制备ZnO薄膜的沉积温度、氧气流量比例R=O₂/(O₂+Ar)对Zn和O原子发射光谱的影响，并结合ZnO薄膜的结构和物理性能，探讨了沉积温度在ZnO薄膜生长中的作用.研究结果显示：当R≥0.75%时， Zn的溅射产额随R的增加基本呈线性下降规律.当R介于10%—50%时，氧含量的变化相对平缓，有利于ZnO薄膜生长的稳定性控制.Zn原子发射光谱强度随沉积温度的变化可以分为三个阶段.当沉积温度低于250℃时，发射光谱强 关键词： ZnO 薄膜生长 反应磁控溅射 等离子体发射光谱     

面心立方晶体外延膜沉积生长中失配位错的结构与形成过程

用分子动力学方法对5%负失配条件下面心立方晶体铝薄膜的原子沉积外延生长进行了三维模拟.铝原子间的相互作用采用嵌入原子法(EAM)多体势计算.模拟结果再现了失配位错的形成现象.分析表明，失配位错在形成之初即呈现为Shockley扩展位错，即由两个伯格斯矢量为〈211〉/6的部分位错和其间的堆垛层错组成，两个部分位错的间距、即层错宽度为1.8 nm,与理论计算结果一致；外延晶体薄膜沉积生长中，位错对会发生滑移，但其间距保持稳定.进一步观察发现，该扩展位错产生于一种类似于“局部熔融-重结晶”的表层局部无序紊乱- 关键词： 失配位错 外延生长 薄膜 分子动力学 铝     

生长温度对碳纳米管阴极场发射性能的影响

碳纳米管(Carbon Nanotubes,CNTs)场发射平面显示器(Field Emission Display,FED)与其他显示器比较显示了其独特优点,被认为是未来理想的平面显示器之一。碳纳米管阴极作为器件的核心部分,其性能的好坏直接影响显示器的性能。针对30~60英寸(76.2~152.4cm)大屏幕显示器所用的厚膜工艺,即采用丝网印刷法制备了碳纳米管阴极阵列,研究了化学气相沉积法在不同温度下生长的CNTs的场发射电流-电压特性,找到了适合FED用碳纳米管的最佳生长温度。结果表明生长温度越高(750℃),CNTs场发射性能越好。并用荧光粉阳极测试这些CNTs的场发射发光显示效果,验证了上述结论。     

A Facile Synthesis of Silver-Coated Composite Particles by Swelling Surface Method

We report a facile and rapid method for fabrication of composite particles consisting of a polystyrene (PS) core and a uniform silver shell. The process involves the PS colloid surface swelling, the anchoring of silver ions and nanoparticles onto the surfaces, and the subsequent growth of metal seeds in a short period. The present approach has the advantages of simplicity and high efficiency. The TEM images show the morphology of the obtained PS core-silver shell particles, and their chemical composition and crystallinity are analysed by x-ray diffraction. To our knowledge, this is the first study based on swelling PS surface for synthesis of silver-coated PS particles and may be implemented for preparing other metal-coated PS particles.     

基于CAPPFramework的CAPP系统的开发与应用

在国家863CIMS目标产品CAPPFramework系统的基础上，研究了面向对象的信息建模技术、信息模型驱动的所见即所得工艺设计技术、工作流技术．并在此基础上进行集成化、智能化计算机辅助工艺设计(CAPP)的应用与开发，实现了工艺设计的自动化，基本达到了在信息集成基础上的工艺设计与工艺信息管理一体化的目的，对企业的CAPP实施具有一定的参考价值．     

碳纳米管阵列、捆束的三步升温工艺制备及其形貌与结构

使用结构简单的单温炉设备，通过三步升温热解二茂铁、三聚氰氨混合物方法，在二氧化硅、多晶陶瓷基底上分别合成了碳纳米管阵列、碳纳米管捆束.使用扫描电子显微镜、透射电子显微镜、电子能量损失谱和x射线光电子能谱对合成样品进行了结构和成分分析.结果显示：两种基底上合成的纳米管均为多壁纯碳管；生长于光滑二氧化硅表面的碳纳米管具有高度取向性和一致的外径，长度为10—40μm.碳纳米管采取催化剂顶端生长模式并展示出类杯状形貌；生长于粗糙多晶陶瓷表面的碳纳米管捆束随机取向，碳纳米管直径为15—80nm，长度在几百微米，展示 关键词： 碳纳米管 热解法 三步升温工艺     

TATB钝感炸药的小角X射线散射实验

在北京同步辐射装置上应用同步辐射X射线小角散射技术研究TATB样品微孔状况，分析了微孔结构参数的变化。采用不同制备工艺(机械研磨、化学合成、气流细化、全结晶、粉碎)和不同存放时间的TATB粉末样品共计7份。