Crosslinking of a polyacrylate bearing a spiroorthoester pendant group with mixtures of diglycidyl ether of bisphenol A and phosphorus‐containing glycidyl derivatives

The cationic crosslinking of a polyacrylate bearing a spiroorthoester pendant group with mixtures of diglycidyl ether of bisphenol A and three phosphorus‐containing glycidyl derivatives was carried out with ytterbium triflate as an initiator. The curing process was monitored with Fourier transform infrared spectroscopy. The thermomechanical and thermogravimetric properties were evaluated. The glass transition temperatures of the obtained materials were, in general, above 100 °C. The incorporation of phosphorus into the network increased the limiting oxygen index values, thus improving the flame retardancy of the materials. During crosslinking, all the crosslinked polymers showed slight shrinkage that was much lower than that observed in conventional epoxy resins. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 1920–1930, 2007     

Novel silicon‐containing spiroorthoester to confer combined flame retardancy and low shrinkage properties to epoxy resins

A new silicon‐containing spiroorthoester, 1,4,6‐trioxaspiro [4,4]‐2‐nonylmethyl 3‐trimethylsilyl propionate (SOE? Si), was synthesized with good yield by an esterification reaction with a previously synthesized 2‐hydroxymethyl‐1,4,6‐trioxaspiro [4,4] nonane (SOE? OH) and trimethylsilyl propionic acid. The structure of the new SOE? Si was confirmed by ¹H and ³C NMR. The SOE? Si and a mixture of DGEBA/SOE? Si were polymerized with ytterbium triflate as a cationic initiator. The curing was studied with differential scanning calorimetry (DSC) and monitored by Fourier transform infrared (FTIR) spectroscopy. The materials were characterized with DSC, termogravimetric analysis (TGA) and thermodynamomechanical analysis (DMTA). The volume change was evaluated with a Micromeritics gas pycnometer and the flame retardancy was tested by the limiting oxygen index (LOI) measurements. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4211–4224, 2007     

Synthesis and polymerization of styrene monomers bearing spiroorthoester structure and volume change during crosslinking by double ring‐opening of the pendant spiroorthoesters of the obtained polymers

Novel styrene monomers bearing a five or seven‐membered spiroorthoester structure (SOE5, SOE7) were synthesized and their radical polymerizations as well as volume change during crosslinking of the obtained polymers were investigated. SOE5 and SOE7 were prepared from 4‐vinylbenzyl glycidyl ether and γ‐butyrolactone or ε‐caprolactone using boron trifluoride diethyl ether complex as a catalyst, respectively. Radical polymerizations of these monomers using 2,2′‐azobisisobutyronitrile (AIBN) gave the corresponding styrene‐based polymers with keeping the spiroorthoester structures unchanged. These polymers could be transformed to networked polymers by heating with a sulfonium antimonate, a thermally latent cationic polymerization initiator. Copolymerization of SOE5 or SOE7 with styrene at various compositions was carried out to efficiently obtain the corresponding copolymers, respectively. These polymers and copolymers showed little volume shrinkage or slight volume expansion during the crosslinking. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 1790–1795     

Regiospecific cationic polymerization of spiroorthoesters with different cyclic ether ring sizes

Spiroorthoesters (SOEs), cis‐2,3‐tetramethylene‐1,4,6‐trioxaspiro[4,5]decane ( I ) and cis‐2,3‐tetramethylene‐1,4,6‐trioxaspiro[4,6]undecane ( II ), with different cyclic ether ring sizes were synthesized, and their stereostructure and steric energy were determined. With steric‐hindrance‐sensitized 9‐phenyl‐9,10‐dihydro‐anthracen‐10‐ylium cation as an initiator, I and II underwent regiospecific polymerization to yield trans form of stereoregular poly(ether esters)—poly(trans‐2‐oxycyclohexyl pentanoate) (? [trans‐2‐OCHP]_n? ) ( III ) and poly(trans‐2‐oxycyclohexyl hexanoate) (? [trans‐2‐OCHH]_n? ) ( V ), respectively. With SnCl₄ as another initiator, I and II underwent regiospecific polymerization through different mechanisms to afford cis form poly(cis‐2‐oxycyclohexyl pentanoate) (? [cis‐2‐OCHP]_n? ) ( IV ) and trans form (? [trans‐2‐OCHH]_n? ) ( VI ) stereoregular poly(ether esters). The polymerization mechanisms of SOEs proceeded in the regiospecific manner were determined by the relationship among the sterostructures of SOEs and its subsequently formed polymers, the steric energy of monomers, and the free energy difference in the transition state of reaction. Owing to the conversion of cis substitution at C‐2 and C‐3 in I or II to the trans form during polymerization, polymers III , V , and VI exhibited a higher volume of expansion during polymerization than IV , which showed high volume shrinkage. Group contributions of divalent trans‐ and cis‐1.2‐cyclohexyl groups were derived and confirmed by measuring the densities of the corresponding stereoregular polymers. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012