甲烷浓度对碳化硅基底金刚石薄膜摩擦性能影响

利用热丝化学气相沉积法(HFCVD)在碳化硅基底上制备金刚石薄膜,采用场发射扫描电子显微镜、拉曼光谱仪、原子力显微镜研究了在不同甲烷浓度条件下制备的金刚石薄膜表面形貌及物相组成,在干摩擦条件下通过往复式摩擦磨损实验测试并计算了已制备金刚石薄膜的摩擦系数和磨损率,结合物相分析及摩擦磨损实验结果分析了甲烷浓度的改变对金刚石薄膜摩擦磨损性能的影响。结果表明,由于甲烷气体含量的升高,金刚石薄膜结晶质量下降,薄膜由微米晶向纳米晶转变。摩擦磨损实验结果显示:3%甲烷浓度条件下制备的金刚石薄膜耐磨性较好,磨损率为2.2×10^-7 mm³/mN;5%甲烷浓度条件下制备的金刚石薄膜摩擦系数最低(0.032),磨损率为5.7×10^-7 mm³/mN,制备的金刚石薄膜的耐磨损性能相比于碳化硅基底(磨损率为9.89×10^-5 mm³/mN)提升了两个数量级,显著提高了碳化硅基底的耐磨性。     

光学共振增强的表面铯激活银纳米结构光阴极

金属光阴极因其超短脉冲发射和运行寿命长的特性从而具有重要应用价值,但是较高的功函数和较强的电子散射使其需要采用高能量紫外光子激发且光电发射量子效率极低.本文利用Mie散射共振效应增强银纳米颗粒中的局域光学态密度,提升光吸收率和电子的输运效率,并利用激活层降低银的功函数,从而增强光阴极在可见光区的量子效率.采用时域有限差分方法分析银纳米球阵列的光学共振特性,采用磁控溅射和退火工艺在银/氧化锡铟复合衬底上制备银纳米球,紧接着在其表面沉积制备铯激活层,最后在高真空腔体中测试光电发射量子效率.实验结果表明平均粒径150 nm的银纳米球光阴极在425 nm波长的量子效率超过0.35%,为相同激活条件下银薄膜光阴极的12倍,峰值波长与理论计算的Mie共振波长相符合.     

银纳米微粒荧光猝灭法测定水中痕量ClO2

在pH 9.1的NH4Cl-NH3·H2O缓冲溶液中,银纳米微粒在470 nm处产生一个荧光峰;它能被ClO2氧化导致体系的荧光发生猝灭.ClO2浓度在0.001 1～0.185μg·mL-1范围内与荧光猝灭强度成良好的线性关系,检测限为0.004 7μg·mL-1 ClO2.据此建立了测定ClO2的荧光分析新方法,用于饮用水中ClO2的测定,结果满意.     

直接置换法制备包覆型纳米铜-银双金属粉末

 以AgNO₃为主盐，采用直接置换法初步制备了包覆型纳米铜-银双金属粉末，分析了工艺条件对包覆效果的影响，并用透射电子显微镜、X射线能量色散谱仪和X射线衍射仪进行了表征。实验结果表明：纳米铜-银双金属粉末为包覆型结构，平均粒径约70 nm，分散性较好，表面银的原子分数达到74.28%。在洗涤过程中加入一定量的保护剂，有效解决了纳米铜粉的氧化问题。     

Growth studies of m-GaN layers on LiAlO2 by MOCVD

This paper reports that the m-plane GaN layer is grown on （200）-plane LiAlO2 substrate by metal-organic chemical wpour deposition （MOCVD） method. Tetragonal-shaped crystallites appear at the smooth surface. Raman measurement illuminates the compressive stress in the layer which is released with increasing the layer＇s thickness. The high transmittance （80%）, sharp band edge and excitonic absorption peak show that the GaN layer has good optical quality. The donor acceptor pair emission peak located at -3.41 eV with full-width at half maximum of 120 meV and no yellow peaks in the photoluminescence spectra partially show that no Li incorporated into GaN layer from the LiAlO2 substrate.     

Effect of Ag Doping on Optical and Electrical Properties of ZnO Thin Films

ZnO thin films were prepared on p-type Si (100) substrates by the sol-gel process. The influence of Ag doping at a content of 0.002% on the photoluminescence and current-voltage (I - V) characteristics of ZnO thin films has been investigated. It is found that Ag doping leads to a pronounced increase in the intensity of near band edge emission at 3.23eV and a remarkable red shift of the visible broadband at room temperature. The I - V characteristics of ZnO/p-Si heterojunctions are also changed. These results could be explained by Ag substituting for Zn in Ag doped ZnO thin films.     

Specific Angular Momentum Distribution of Disc Galaxies Formed in Preheated Intergalactic Media

Assuming that baryons within a galactic halo have the same specific angular momentum as the dark matter where they locate initially and a disc forms due to the gas cooling and condensation with the conservation of angular momentum, we investigate the angular momentum distribution in a resulting galactic disc under the new preheated galaxy formation model suggested by Mo and Mao (Mon. Not. R. Astron. Soc. 333 (2002) 768).Compared with the observational results, it can be concluded that the preheated galaxy formation model can match current observations. This model can be a good approach to solve the problems of both the angular momentum catastrophe and the mismatch of angularomomentum profiles in current disc galaxy formation models.