Nanometric Antimony Powder Synthesis by Activated Alkaline Hydride Reduction of Antimony Pentachloride

A novel chemical reduction method using an activated alkaline hydride (LiH or NaH-t-BuONa) in tetrahydrofuran solvent has been applied to antimony salt reduction. X-ray diffraction and transmission electron microscopy studies have been carried out to characterize the morphology and structure of the materials. Alkali hydride nature influence has been proved. In both cases the process allows to prepare antimony particles in nanometer range from few nanometers to about 20nm which could be used as anodic materials for lithium–ion batteries. With lithium hydride well-crystallized particles inclined to agglomeration were observed whereas finely dispersed amorphous particles were pointing out after activated sodium hydride reduction.     

纳米碳酸锌的制备和热分解动力学参数的测定

Nanosized zinc carbonate was prepared in the droplet of nano-reactor based on microemusion. The influences of the concentration of the surfactant and reactant on the diameter of nanoparticles were studied and the kinetic pa-rameters of thermal decomposition reaction were determined. It can be shown from experimental results， the di-ameter of the droplet in the microemulsion which have dissolved reactant zinc nitrate and sal volatile is between 4.9nm and 7.7nm， 6.2nm and 12.4nm， respectively. Nanosized zinc carbonate prepared by the method of mi-croemusion has shown good dispersion， narrow distribution and light agglomeration. The particle size of nanosized zinc carbonate is between 5nm and 40nm， and its kinetic parameters of thermal decomposition reaction-activation energy E and reaction order n are 110kJ·mol^-1 and 0.9， respectively.     

CaTiO3纳米粉体溶胶-凝胶法合成、表征及介电特性

采用无机盐溶胶-凝胶法制备了CaTiO₃纳米粉体，采用TG-DTA、XRD、TEM等技术进行了表征，并探讨了CaTiO₃纳米粉体烧结特性及介电效应。结果表明，干凝胶800 ℃低温煅烧可获得粒径分布较窄、平均粒径为60～70 nm的单相CaTiO₃纳米粉。纳米CaTiO₃粉具有较大的比表面积，使作为粉体烧结驱动力的表面能剧增，促使CaTiO₃在1 200 ℃实现致密烧结，比固相法制备的微米粉烧结降低100～200 ℃，且具有较宽的烧结温区。与微米级粉体烧结体介电特性相比，纳米粉具有更高的Q_f值。纳米CaTiO₃粉制备的陶瓷在1 250 ℃烧结2 h，获得优良的介电性能：ε_r=172，Q_f=4 239 GHz，τ_f=+7.68 × 10^-4 ℃^-1。     

负载型纳米Ni催化剂用于对氯硝基苯选择加氢

以TiO2为载体,N iB为诱导剂,粉末化学镀法制备了负载型纳米N i催化剂.通过TEM、HRTEM、XRD和ICP技术对催化剂物性进行了表征.结果表明,碱性镀液可使载体表面均匀负载微晶结构纳米N i团簇,尺度为35nm左右.该负载型纳米N i在对氯硝基苯选择加氢反应中表现出很高催化加氢活性,并能有效抑制脱氯,达到了工业骨架镍水平.由酸性镀液得到的负载型非晶态纳米N i-P合金具有较弱的催化对氯硝基苯加氢活性.反应温度对反应时间和脱氯率有明显影响.     

纳米CoHCF修饰电极的制备及其对血红蛋白的电化学测定研究

A cobalt hexacyanoferrate （CoHCF） nanoparticle （size ca. 60 nm） chemically modified electrode （CME） was fabricated and the electrochemical behavior of hemoglobin （Hb） at this nanosized CoHCF CME was studied. In comparison with a bare glassy carbon electrode （GCE） and a general CoHCF CME electrodeposited in a traditional manner, the present nanosized CoHCF CME performed efficiently electrocatalytic reduction for Hb with relatively high sensitivity, stability, and longlife, Combined with liquid chromatography （LC）, the nanosized CoHCF CME was used as the electrochemical detector of Hb in the established flow injection analysis-electrochemical determination （FIA-ECD） system. The peak current was a linear function of concentrations in the range from 2.5×10^-8 to 5.0×10^-6mol/L for Hb, with detection limit of 1.4×10^-8 mol/L. The FIA-ECD system has been successfully applied to assess the Hb content of clinic blood samples with advantages of sensitiveness, speediness, easy control and small sample-consumption.     

Ce-Zr-Ba-O纳米材料的制备及其结构与性能研究

以金属硝酸盐为原料,分别采用高分子前驱体法、柠檬酸盐凝胶法制备了纳米级的Ce-Zr-Ba-O复合氧化物超细粒子,采用X-射线衍射(XRD)、透射电镜(TEM)、BET比表面测定、热重-差热(TG-DTA)技术对催化剂进行了表征,并考察了催化剂的CO氧化活性和热稳定性。实验结果表明,高分子前驱体法和柠檬酸盐凝胶法制备的催化剂粉体都达到了纳米级。两种方法中,高分子前驱体法所制得的催化剂的BET比表面达118.96m²·g^-1,CO氧化反应活性较高,同时该方法制得的催化剂分散性好,无团聚,经1000℃高温焙烧后仍基本无烧结、无团聚现象,具有较高的热稳定性。     

检测易爆气体的催化发光传感器研究

报道了一种用于定量分析易爆气体混合物丙烷和异丁烷的基于碳酸锶纳米材料的催化发光传感器。基于该传感器在不同温度下对两种气体的灵敏度不同，在320℃和342℃两个工作温度下，两种气体的浓度范围均为1000mL／m^3～10000mL／m^3时，分别建立了混合组分浓度相对催化发光强度的两个线性回归方程。在342℃时，丙烷和异丁烷的检出限（3σ）分别为50mL／m^3和20mL/m^3。可通过解上述两个联立方程式求得未知混合物中两组分的浓度。外来物质甲烷、乙烷、CO、氨气通过传感器时，甲烷和乙烷分别引起5．6％和17．2％的干扰，其它气体不干扰测定。20000mL／m^3的水蒸气不干扰2000mL／m^3丙烷和异丁烷气体的测定。用该法分析了人工合成样品中两种气体的浓度。     

纳米复合固体超强酸S_2O_8~(2-)/CoFe_2O_4催化合成癸二酸二乙酯

将硫酸钴、硫酸亚铁在NaOH溶液中与NaHCO3反应制得碱式碳酸盐前驱体 ,后者用 (NH4 ) 2 S2 O8浸渍、干燥 ,再经 5 0 0℃焙烧得到固体超强酸催化剂S2 O2 -8/CoFe2 O4 。产物经XRD、TEM、BET、TG DTA及化学法等检测 ,含硫量 4 5 2 % ,粒径为 4 2nm ,比表面积为 1 4 6m2 /g ,粒度均匀。催化剂的酸强度处于 -1 6 0 2和-1 4 5 2之间。以该固体酸为催化剂 ,由癸二酸和无水乙醇合成了癸二酸二乙酯。最佳反应条件为 :n(醇 )∶n(酸 ) =4 0∶1 0 ,癸二酸 0 1mol,催化剂 1 0 g ,反应时间 2 5h。在此反应条件下 ,酯化率可达 93 6%。     

负载型纳米TiO2复合载体及其CoMo催化剂的酸性及孔特性的研究

总结了复载不同纳米尺度的复合载体及其CoMo催化剂的表面酸性及孔结构特性的表征结果。结果表明，负载型纳米TiO2与基载体γ-Al2O3存在着相互作用。当负载比较少量的纳米TiO2时，复合载体的总酸量随着TiO2含量的增加而增加，超过γ-Al2O3的酸量，但当 TiO2的含量比较高时复合载体的酸量又降低，纳米TiO2优先负载在γ-Al2O3的强酸中心位；负载了CoMo活性组分后酸量增加。不同粒径的纳米TiO2对复合载体和催化剂的酸分布没有明显影响，但对总酸量有影响。对不同尺度TiO2，随着TiO2负载量的增加以及负载金属活性组分的增加，表面积、孔容和最可几孔径均有不同程度的减少。     

TiO2/Eu-MCM纳米超分子材料的组装和光催化性能

利用有机相-水相界面共沉淀溶胶支持自组装方法制备粒径为15 nm、孔径为8 nm的分子筛Eu-MCM, 它拥有734 m²/g的比表面积和1.49 cm³/g的比孔容. 把TiO₂组装到Eu-MCM的孔道中, 组装成TiO₂/Eu-MCM纳米复合材料. XRD, RAMAN和选区电子衍射花样分析表明纳米复合材料中的TiO₂为锐钛型. TiO₂/Eu-MCM的发光表现为Eu^3＋离子的特征光谱, 激发峰分别为342 (⁵L₁₀), 358 (⁵L₉), 378 (⁵L₇), 390 (⁵L₆), 411 (⁵D₃), 462 (⁵D₂)和524 (⁵D₁) nm; 发射峰为579, 592, 613, 653和701 nm, 归属于⁵D₀→⁷F_J (J＝0, 1, 2, 3, 4)组态间的跃迁. 纳米复合材料的发光强度都要比Eu-MCM的发光强, 其中43%TiO₂/Eu-MCM的发光最强. 荧光和紫外漫反射结果表明客体TiO₂对主体分子筛存在能量传递效应. 在微弱的紫外灯光照射下, TiO₂/Eu-MCM纳米复合材料对苯酚的光催化氧化性能和其发光强度具有一定的相关性. 29%TiO₂/Eu-MCM的纳米复合材料拥有的比表面积、孔容和孔径分别为204 m²/g, 0.24 cm³/g和4.7 nm. 29%TiO₂/Eu- MCM对苯酚具有68%的最高光催化氧化产率和85%催化氧化选择性.