Detecting pore size distribution of activated carbon by low-field nuclear magnetic resonance

In this study, the transverse relaxation time (T₂) of activated carbon (AC) in different relative environment humidity was detected firstly by low-field nuclear magnetic resonance (LFNMR). The pore size (diameter) of AC distributions was calculated by the relationship between T₂ and surface relaxation rate (ρ), where ρ was obtained by the detection of nine porous materials with known pore size. The results showed that the pore size distributions of AC calculated by ρ < 0.19 nm/ms were in good agreement with that obtained by nitrogen adsorption method and proved that LFNMR as a new detection method was feasible for characterizing AC pore size distribution.     

Isoflavonoids from Astragalus membranaceus Hairy Roots

Chemistry of Natural Compounds -     

A Novel Ternary Composite of Polyurethane/Polyaniline/Nanosilica with Antistatic Property and Excellent Mechanical Strength: Preparation and Mechanism

Chinese Journal of Polymer Science - Antistatic and strength properties are of vital importance for polyurethane rubber used in moving parts of many industrial instruments. Herein, polyurethane was...     

基于XPS对硫铁矿去除SeO2-3的机理研究

硒是动植物及人体生长必需的十五种微量元素之一，具有清除体内自由基、抗氧化、增强免疫力等功能，但其安全剂量的范围却很窄。利用扫描电子显微镜（SEM）和X射线衍射仪（XRD）对湿法球磨制备的硫铁矿形貌进行了表征。SEM观测发现加乙醇助磨后的硫铁矿为粒径大小较均匀的球形颗粒团聚体，粒径范围在17～200 nm之间，平均粒径138 nm。XRD衍射图谱中的特征峰与FeS₂衍射图谱中各峰位置基本一致，因此判定硫铁矿中主要化学组分为FeS₂，且图谱中基本没有杂峰，表明制备过程中并未混入杂质，样品纯度较高。实验结果表明，该法制备的硫铁矿具有颗粒粒径小、比表面积大、反应活性高等优点。研究中利用X射线光电子能谱仪（XPS）对硫铁矿去除水体中SeO2-₃的机理进行了研究。研究结果表明, （1）在较为广泛的实验pH范围（pH 2.2～11.5），硫铁矿均能有效去除水体中SeO2-₃，去除效率（除pH值7.8以外）均达到90%以上；（2）硫铁矿与SeO2-₃发生反应后，其主要组成元素的XPS特征峰结合能有所减小，表明硫铁矿表面发生了一定化学变化；（3）酸碱环境下硫铁矿去除SeO2-₃的机理不完全相同，酸性环境下，硫铁矿对SeO2-₃的去除是单纯的氧化还原过程，即硫铁矿中被酸活化的S2-₂将SeO2-₃还原为单质Se(0)，并且酸性越强，SeO2-₃去除效果越好；碱性环境下，SeO2-₃的去除过程中氧化还原与络合反应并存，硫铁矿表面有络合态Fe(OH)SeO₃和单质Se(0)两种存在形态，且碱性越强，络合态Fe(OH)SeO₃含量越高。以上研究结果为硫铁矿去除固定水体和土壤中以SeO2-₃为代表的可变价金属阴离子提供重要理论依据和应用基础。     

Acridone-Based Host Materials for Green Phosphorescent and Thermally Activated Delayed Fluorescent OLEDs with Low-Efficiency Roll-Offs

By linking the carbazole unit to the nitrogen atom of acridone through phenyl or pyridyl, two compounds, named 10-(4-(9H-carbazol-9-yl)phenyl)acridin-9(10H)-one (AC-Ph-Cz) and 10-(5-(9H-carbazol-9-yl)pyridin-2-yl)acridin-9(10H)-one (AC-Py-Cz) were designed and synthesized. These two materials, characterized with highly twisted and rigid structure, good thermal stability, and balanced carrier-transporting properties, were employed as host materials for green phosphorescent and thermally activated delayed fluorescent organic light-emitting diodes (OLEDs). The carbazole group, despite its small contribution to the highest occupied molecular orbitals (HOMOs) of these two materials, plays an essential role as an intramolecular host in energy delivering and improving the hole transporting ability of these two hosts. The incorporation of the electron-deficient pyridyl group as a linking group slightly improves the electron transporting capability of AC-Py-Cz. The green phosphorescent OLED (PhOLED) based on AC-Py-Cz exhibited excellent device performance with a turn-on voltage of 2.5 V, a maximum power efficiency and an external quantum efficiency (η_ext) of 89.8 lm W⁻¹ and 25.2 %, respectively, benefitting from the better charge-balancing ability of AC-Py-Cz host due to the presence of the pyridyl bridge. More importantly, all the devices based on these two hosts showed low efficiency roll-off at high brightness due to the suppressed non-radiative transition in the emitting layer. In particular, the AC-Py-Cz-hosted green PhOLED exhibited an efficiency roll-off of 1.6 % from the maximum next at a high brightness of 1000 cd m⁻² and a roll-off of 15.9 % at an extremely high brightness of 10000 cd m⁻². This study manifests that acridone-based host materials have great potential in fabricating OLEDs with low efficiency roll-off.     

陶瓷基功能材料载体纤维增强效果及机理

以陶瓷基功能材料载体为研究对象,按照其生产工艺配方,研究了纤维种类(莫来石、氧化铝、氧化锆)及其添加量对陶瓷基功能材料载体性能的影响.在相同实验条件且不影响其功能化参数前提下,将其与未添加纤维的空白试样力学性能进行对比.结果表明,试样经1200℃烧成后,相比莫来石与氧化铝纤维增强的陶瓷基功能材料载体,氧化锆纤维的增强效果最好.当氧化锆纤维的添加量为0.8 wt;时,试样的吸水率和气孔率均较低,分别为2.0;、4.0;,相比空白对比试样抗折强度增强了42.4;.     

煤直接液化油中混合酚的分离研究

利用分子筛择形特点，对煤直接液化油中的混合酚实施高效分离。本研究选取间甲酚和对甲酚作为分离煤直接液化油馏分段混合酚的模型化合物，采用化学液相沉积法对HZSM-5吸附剂的孔口结构进行改变，分析分子筛硅铝比及颗粒粒径对模型化合物间甲酚和对甲酚吸附分离性能的影响，以获得高性能固相吸附剂，并将其应用于180-190℃馏分段混合酚分离。结果表明，当分子筛硅铝比为25、粒径为3-5 μm时，分子筛的孔口结构调节效果最优；当正硅酸乙酯的最小用量为0.2 mL/g时，固相吸附剂的吸附量为0.03 g/g，对甲酚选择性高于95%。由于外表面沉积物对吸附剂的孔口结构变化，导致对甲酚选择性的提高。进一步采用HZSM-5（1）吸附剂对真实煤直接液化油混合酚的分离中发现，苯酚和对甲酚的选择性均达到100%。     

化学法改性煤沥青脱除苯并芘的研究

在管式反应器中采用苯甲酸、聚乙二醇、固体古马隆树脂（S）、液体古马隆树脂（L）为添加剂来降低煤沥青中有害物质苯并芘的含量，以期使得煤沥青可绿色化应用。采用紫外-可见分光光度计分析煤沥青中苯并芘含量。考察了反应温度、反应时间、添加剂添加量、催化剂等工艺条件对添加剂脱除煤沥青中苯并芘的影响。结果表明，不同工艺条件能降低煤沥青中苯并芘的含量。在优化条件下，不同添加剂对苯并芘脱除率由高到低依次为：液体古马隆树脂、聚乙二醇、苯甲酸和固体古马隆树脂。分析其反应机理，这与催化剂的酸性相关，发生亲电取代反应。结果表明，液体古马隆树脂（L）在催化剂存在下对煤沥青中苯并芘脱除率可达73.0%，显示了良好的应用前景。     