Re_3W的点接触安德烈夫反射谱研究

本文通过对不同晶体结构Re_3W样品的点接触测量和对比研究,证实具有中心对称结构和非中心对称结构的Re_3W都是弱耦合Bardeen-Cooper-Schrieffer超导体,同时发现在两个相表面都可以形成很理想的点接触结,即电子通过界面时受到的非弹性散射很弱.将Re_3W样品置于大气环境近六个月后重新进行测量,仍然能够得到类似的结果,表明Re_3W具有很好的稳定性. Re_3W的这种优良特性,不仅可通过点接触实验得到的参数推算出Re_3W两个相的费米速度,而且提供了一种简单的方法,可以在点接触实验中利用Re_3W来印证针尖材料的费米速度和测量其自旋极化率等.作为尝试,本文用Re_3W/Ni点接触结测量了铁磁性金属Ni的自旋极化率,得到了与前人报道一致的结果.     

Direct Microwave Synthesis of 11-Type Fe(Te,Se) Polycrystalline Superconductors with Enhanced Critical Current Density

We report a direct microwave synthesis method for the preparation of 11-type high quality Fe(Te,Se) polycrystalline superconductors. The bulk samples are rapidly synthesized under the microwave irradiation during several minutes, with a subsequent annealing process at 400℃. The samples exhibit a nearly single phase of the tetragonal PbO-type crystal structure with minor impurities. Morphology characterization shows high density, tight grain connectivity and large grain sizes around 100 μm with small cavities inside the sample. Resistivity and magnetization measurements both show similar superconducting transitions above 14 K. The magnetic hysteresis measurements display broad and symmetric loops without magnetic background, and a high critical current density J_c about 1.2 × 10~4 A/cm~2 at 2 K and 7 T is estimated by the Bean model. Compared with the solidstate reaction synthesized samples, these superconducting bulks from microwave-assisted synthesis are possibly free of the interstitial Fe due to smaller c-axis, higher T_c in magnetic transitions, better M–H loops without magnetic background and greatly enhanced J_c, and are promising as raw materials for the non-toxic Fe-based superconducting wires for large currents and high field applications.     

112型铁基化合物EuFeAs2的单晶生长与表征

铁基超导体中含有一类特殊的112型结构化合物,其层状结构中含有一层锯齿形的As链构型.本文报道了用CsCl助熔剂法生长新型铁基112型EuFeAs₂母体单晶的具体方法,以及对该单晶的结构和物性的详细表征.通过能量色散X射线能谱扫描对单晶样品进行的化学成分分析,以及单晶X射线衍射的结构解析,确定该单晶样品属于EuFeAs₂相,结构精修得到EuFeAs₂具有空间群为Imm2（No.44）的正交晶体结构,晶格常数分别是a=21.285（9）Å,b=3.9082（10）Å,c=3.9752（9）Å.通过低温电阻测量,发现在110 K附近和46 K附近存在两个异常电阻跳变.进一步分析表明,110 K附近存在两个邻近的相变,这两个相变与铁基母体材料中常见的结构相变和Fe²⁺的反铁磁相变相符合.结合磁化率测量分析,可知46 K附近的相变属于Eu²⁺的反铁磁相变.     

Superconductivity in Sm-doped CaFe_2As_2 single crystals

In this article,the Sm-doping single crystals Ca_(1-x)Sm_xFe_2As_2(x = 0 ~0.2) were prepared by the Ca As flux method,and followed by a rapid quenching treatment after the high temperature growth.The samples were characterized by structural,resistive,and magnetic measurements.The successful Sm-substitution was revealed by the reduction of the lattice parameter c,due to the smaller ionic radius of Sm~(3+)than Ca~(2+).Superconductivity was observed in all samples with onset T_c varying from 27 K to 44 K upon Sm-doping.The coexistence of a collapsed phase transition and the superconducting transition was found for the lower Sm-doping samples.Zero resistivity and substantial superconducting volume fraction only happen in higher Sm-doping crystals with the nominal x 0.10.The doping dependences of the c-axis length and onset T_c were summarized.The high-T_c observed in these quenched crystals may be attributed to simultaneous tuning of electron carriers doping and strain effect caused by lattice reduction of Sm-substitution.