非线性光学材料Ca_9Y_(0.5)La_(0.5)(VO_4)_7的固相合成、液相合成与晶体生长

采用固相合成和液相合成两种方法成功制备了Ca9Y0.5La0.5(VO4)7晶体的多晶原料,并采用提拉法生长了尺寸分别为30 mm×33 mm(固相合成多晶原料)和20 mm×27 mm(液相合成多晶原料)的Ca9Y0.5La0.5(VO4)7晶体。测试了该晶体在紫外、可见和近红外区域的透过率,采用Kurtz法测试了晶体的粉末倍频效应。结果表明,采用液相合成原料生长的晶体透过率大于采用固相合成原料生长的晶体约10%。前者粉末倍频效应约为KDP的1.8倍,后者约为KDP的2.5倍。晶体化学腐蚀实验表明采用液相合成原料生长的晶体具有更少的缺陷。采用液相合成方法制备多晶原料有利于提高晶体的光学质量。     

掺Nd3+的Sr3 Gd(BO3)3晶体的激光特性

介绍了一种新的硼酸盐激光晶体Nd^3＋：Sr3Gd（BO3）3的激光特性．采用氙灯作为泵浦源，获得激光输出为17．84mJ，总效率ηo=0.092％，曲线的斜效率ηs=0.27％．实验表明Nd^3＋：Sr3Gd（BO3）3晶体是一种新的有潜在应用价值的激光晶体．     

掺重稀土钒酸钇RE∶YVO4晶体的光谱性质

采用Czochralski法生长了均匀透明的Tm:YVO4, Tm:Er:YVO4和Tm:Yb:YVO4晶体, 测量了其室温下吸收光谱, 研究了晶体中掺杂稀土离子的光谱性质. 根据Judd-Ofelt理论拟合出晶体场唯象强度参数: Ω2=1.13×10-20 cm2, Ω4=1.63×10-20 cm2, Ω6=0.65×10-20cm 2.     

Optical-transition Probability of Tm^3＋ Ions in Tm^3＋／Er^3＋：YVO4 Crystal

1INTRODUCTIONThelasersoperatedataround2mmwavelengthhavegainedmuchinterestbecauseofvariousappli-cations,e.g.(1)groundorspaceremotesensingforLIDARandmetrology,(2)medicalapplicationssinceliquidwaterhasastrongabsorptionbandnear2mm,and(3)eyesafelaser[1,2].The2…     

Growth and Optical Properties of Sr_6YbSc(BO_3)_6 Crystal

1INTRODUCTION As is well known,the Yb3 ion has some advan-tages in comparison with Nd3 as laser active ion,for it has only two manifolds,i.e.,the ground2F7/2state and the excited2F5/2state.There is no excited state absorption reducing effective laser cross-section,no concentration quenching,no up-conversion,and three or four times longer emission lifetime than Nd3 ion.Yb3 ion exhibits a strong and broad ab-sorption band at ca.970nm and can be easily pumped with InGaAs diode lasers.The …     

Growth and Spectroscopic Investigations of Disordered Nd3+:Li3Ba2La3(MoO4)8 Crystal

Nd3+: Li3Ba2La3(MoO4)8 crystal has been grown from a flux of Li2MoO4 by the top seeded solution growth method (TSSG) and its structure was confirmed by X-ray diffraction. The polarized absorption spectra, fluorescence spectra and fluorescence decay curve of the crystal were measured. The main spectral parameters were calculated by the Judd-Ofelt theory and compared with other Nd-doped crystals. The broad absorption bands and the large absorption cross sections around 805 nm indicate that the crystal is very suitable for diode-laser pumping. The broad emission bands around 1060 nm show that the crystal is a potential medium for tunable and short pulse lasers. The quantum efficiency of the crystal is up to 95%, which is higher than the value for Nd3+:YVO4 and Nd3+:YAG and comparable to that of other disordered molybdate crystals. The excellent spectroscopic properties show that Nd3+:Li3Ba2La3(MoO4)8 crystal may be regarded as a potential solid state laser host material for diode laser pumping.     

Nd3+:LiLa(MoO4)2晶体生长、光谱和激光特性

本论文报道了Nd3+:LiLa(MoO4)2晶体生长、光谱和激光特性.采用提拉法生长出尺寸为φ20×34mm3的Nd+3+:LiLa(MoO4)2晶体.应用Judd-Ofelt理论计算了Nd3+离子在Nd3+:LiLa(MoO4)2晶体中唯象强度、自发发射跃迁几率、荧光分支比、辐射跃迁寿命和荧光量子效率.Nd3+:LiLa(MoO4)2晶体的偏振吸收跃迁截面分别为9.52×10-20cm2(π-偏振)和4.46×10-20cm2(σ-偏振).它的偏振发射跃迁截面分别为0.67×10-19cm2(σ-偏振)和1.02×10-19cm2(σ-偏振).在氙灯泵浦下,获得74.4mJ的1.06μm的激光输出,激光阈值为0.676J,激光总效率和斜率效率分别为0.39;和0.48;.     

掺重稀土钒酸钇RE∶YVO_4晶体的光谱性质

采用Czochralski法生长了均匀透明的Tm :YVO4,Tm :Er:YVO4和Tm :Yb :YVO4晶体 ,测量了其室温下吸收光谱 ,研究了晶体中掺杂稀土离子的光谱性质。根据Judd Ofelt理论拟合出晶体场唯象强度参数 :Ω2=1 13× 10 -2 0 cm2 ,Ω4=1 6 3× 10 -2 0 cm2 ,Ω6=0 6 5× 10 -2 0 cm2 。