Magnetic properties of misch-metal partially substituted Nd–Fe–B magnets sintered by dual alloy method

The misch-metal(MM) partially substituted Nd–Fe–B sintered magnets were fabricated by the dual alloy method,and the crystal structure, microstructure, and magnetic properties were analyzed comprehensively. X-ray diffraction(XRD)reveals that the increasing content of the MM has an inconsiderable effect on the crystallographic alignment of the magnets.Grains of the two main phases are uniformly distributed, and slightly deteriorate on the grain boundary. Due to the diffusion between the adjacent grains, the MM substituted Nd–Fe–B magnets contain three types of components with different Ce/La concentrations. Moreover, the first-order reversal curve(FORC) diagram is introduced to analyze the magnetization reversal process, coercivity mechanism, and distribution of reversal field in magnetic samples. The analysis indicates that there are two major reversal components, corresponding to the two different main phases. The domain nucleation and growth are determined to be the leading mechanism in controlling the magnetization reversal processes of the magnets sintered by the dual alloy method.     

Influence of misch metal content on microstructure and magnetic properties of R–Fe–B magnets sintered by dual alloy method

MM_(14)Fe_(79.9)B_(6.1)/Nd_(13.5)Fe_(80.5)B_6 magnets were fabricated by dual alloy method(MM, misch metal). Some magnets have two Curie temperatures. Curie temperatures T_(c1)corresponds to the main phase which contains more La Ce, and T_(c1) decreases from 276.5?C to 256.6?C with the content of MM increasing from 30.3 at.% to 50.6 at.%. The variation of Br with the increase of MM indicates the existence of inter-grain exchange coupling in the magnets. When MM/R ≤ 30.3 at.%,the magnetic properties can reach the level of the intrinsic coercivity Hcj≥ 7.11 kOe and the maximum energy product(BH)max≥ 41 MGOe. Compared with Nd, La and Ce are easier to diffuse to the grain boundaries in the sintering process,and this will cause the decrease of H_(cj) Due to the diffusion between the grains, the atomic ratio of La, Ce, Pr, and Nd in each grain is different and the percentage of Nd in all grains is higher than that in misch metal.